Bipolar electrets from polypropylene (PP) are essential, e.g., in electret air filters and in cellular-foam ferroelectrets. Therefore, the mechanism of surface-charge stability enhancement on PP electrets via orthophosphoric-acid surface treatment is investigated in detail. It is shown that the significant charge-stability enhancement can be mainly attributed to deeper surface traps originating from deposited chemicals and topographic features on the modified surfaces. Thermally stimulated discharge of chemically treated and non-treated PP films with different surface-charge densities is used to test the limits of the newly formed deep traps in terms of the capacity for hosting surface charges. When the initial surface-charge density is very high, more charges are forced into shallower original traps on the surface or in the bulk of the treated PP samples, reducing the effect of the deeper surface traps brought by the surface modification. The well-known crossover phenomenon (of the surface-charge decay curves) has been observed between modified PP electrets charged to +/- 2kV and to +/- 3kV. Acoustically probed charge distributions in the thickness direction of PP electrets at different stages of thermal discharging indicate that the deep surface trapping sites may have preference for negative charges, resulting in the observed asymmetric charge stability of the modified PP films.
A double-layer transcrystalline polypropylene (PP) film with a flat central interface layer between its two transcrystalline layers is obtained by recrystallization from the melt between two polytetrafluoroethylene (PTFE) surfaces on both sides of the PP film. Its electret properties are studied and compared with those of a single-layer transcrystalline PP film re-crystallized in contact with only one PTFE surface. Within experimental uncertainty, the two types of transcrystalline films exhibit the same thermal properties and crystallinities. After thermal poling, however, two hetero-charge layers of opposite polarity are found on the internal interfaces of the double-layer transcrystalline films and may together be considered as micrometer-sized dipoles. The unexpected phenomenon does not occur in single-layer transcrystalline samples without a central interface layer, suggesting that the interfaces between the transcrystalline layers and the micrometer-thick central interface layer may be the origin of deeper traps rather than the crystalline structures in the transcrystallites or the spherulites. The origin of the interfacial charges was also studied by means of an injection-blocking charging method, which revealed that intrinsic charge carriers introduced during recrystallization are most likely responsible for the interfacial charges. It is fascinating that a material as familiar as PP can exhibit such intriguing properties with a special bipolar space-charge polarization across the central interface layer after quasi-epitaxial surface moulding into a double-layer transcrystalline form. In addition to applications in electret (micro-)devices for electro-mechanical transduction, the highly ordered structures may also be employed as a new paradigm for studying charge storage and transport in polymer electrets and in dielectrics for DC electrical insulation.
Previous work has shown that surface modification with orthophosphoric acid can significantly enhance the charge stability on polypropylene (PP) surface by generating deeper traps. In the present study, thermally stimulated potential-decay measurements revealed that the chemical treatment may also significantly increase the number of available trapping sites on the surface. Thus, as a consequence, the so-called "cross-over" phenomenon, which is observed on as-received and thermally treated PP electrets, may be overcome in a certain range of initial charge densities. Furthermore, the discharge behavior of chemically modified samples indicates that charges can be injected from the treated surface into the bulk, and/or charges of opposite polarity can be pulled from the rear electrode into the bulk at elevated temperatures and at the high electric fields that are caused by the deposited charges. In the bulk, a lack of deep traps causes rapid charge decay already in the temperature range around 95 degrees C.
Spherulite-related space-charge electret properties of polypropylene (PP) have been widely discussed in the past decades. In the present paper, a less-common crystalline structure in PP-transcrystalline PP-is studied regarding its electret behavior in comparison with the typical spherulitic morphology. Polarized light microscopy and differential scanning calorimetry were employed to characterize the crystallite types and crystallinities of transcrystalline and spherulitic PP. Their electret functionality is investigated by means of thermally stimulated discharge experiments, where the cross-over phenomenon is observed on transcrystalline PP films, whereas surface-potential saturation and undercharging on the surface occur on the spherulitic samples. Besides, an asymmetrical behavior of positive and negative surface-charge stabilities is found on PP with spherulites, the negatively charged spherulitic surfaces show a better charge stability. It is shown that PP electrets are very sensitive to changes in the microscopic crystalline structures and their interfaces as well as in the molecular conformations controlled through adjustments of the respective processing steps. In addition, surface and bulk nanocomposites of PP or low-density polyethylene with inorganic particles are included in the comparison. In view of recent developments in the areas of PP-based electret-fiber filters and cellular-foam ferroelectrets, the observed changes in the charge-storage properties may have particular relevance, as the required film, fiber, or foam processing might significantly modify crystalline morphologies and nano-scale interfaces in PP electrets. Limitations in the charge-storage capabilities of interface structures may also be of interest in the context of high-voltage electrical-insulation materials where reduced space-charge accumulation and slightly increased charge transport can be advantageous.
Tailoring the secondary surface morphology of electro-spun nanofibers has been highly desired, as such delicate structures equip nanofibers with distinct functions. Here, we report a simple strategy to directly reconstruct the surface of polyvinyl alcohol/polyvinylpyrrolidone (PVA/PVP) nanofibers by water evaporation. The roughness and diameter of the nanofibers depend on the temperature during vacuum drying. Surface changes of the nanofibers from smooth to rough were observed at 55 degrees C, with a significant drop in nanofiber diameter. We attribute the formation of the secondary surface morphology to the intermolecular forces in the water vapor, including capillary and the compression forces, on the basis of the results from the Fourier-transform infrared (FTIR) and X-ray photoelectron (XPS) spectroscopy. The strategy is universally effective for various electro-spun polymer nanofibers, thus opening up avenues toward more detailed and sophisticated structure design and implementation for nanofibers.
A new variant of the Laser-Induced Pressure-Pulse (LIPP) method for repeatable, time-resolved space-charge profile measurements is proposed and demonstrated. Automated deposition of a fresh laser-target film before each illumination leads to good repeatability of the LIPP and thus allows for the detection of time-resolved changes in the space-charge distribution over many hours. We describe and discuss the experimental setup and its features, compare the repeatability of the LIPP measurements on the same sample without and with re-preparation of the test cell, and present the time-resolved evolution of the space-charge profile in a two-layer arrangement of a silicone-grease and a silicone-elastomer film as an example. Finally, the temperature dependence of the space-charge evolution during polarization under high voltage and during depolarization in short circuit is shown. Possible uses and future developments of the new LIPP approach are also discussed.
Tetrafluoroethylene-hexafluoropropylene copolymer (FEP) films were treated with titanium-tetrachloride vapor by means of molecular-layer deposition. The treatment leads to considerable improvements of the electret-charge stability on positively charged films. A slight improvement is also observed for negatively charged films. In line with our previous findings, we attribute the improvement in electret properties to the formation of deeper traps on the chemically modified polymer surfaces. Here, we investigate the influence of the charge density on electret stability of FEP films with modified surfaces. Trap-energy spectra obtained from thermally-stimulated-discharge measurements indicate that the charge stability on modified FEP films depends on how the surface traps are populated and on the availability of additional deeper traps.
Poly(vinylidenefluoride-trifluoroethylene)-based (P(VDF-TrFE)-based) terpolymers represent a new class of electroactive polymer materials that are relaxor-ferroelectric (RF) polymers and that offer unique and attractive property combinations in comparison with conventional ferroelectric polymers. The RF state is achieved by introducing a fluorine-containing termonomer as a "defect" into the ferroelectric P(VDF-TrFE) copolymer, which reduces the interaction between the VDF/TrFE dipoles. The resulting terpolymer exhibits a low Curie transition temperature and small remanent and coercive fields yielding a slim hysteresis loop that is typical for RF materials. Though the macroscopic behavior is similar to RF ceramics, the mechanisms of relaxor ferroelectricity in semi-crystalline polymers are different and not fully understood yet. Structure-property relationships play an important role in RF terpolymers, as they govern the final RF properties. Hence, a review of important characteristics, previous studies and relevant developments of P(VDF-TrFE)-based terfluoropolymers with either chlorofluoroethylene (CFE) or chlorotrifluoroethylene (CTFE) as the termonomer is deemed useful. The role of the termonomer and of its composition, as well as the effects of the processing conditions on the semi-crystalline structure which in turn affects the final RF properties are discussed in detail. In addition, the presence of noteworthy transition(s) in the mid-temperature range and the influence of preparation conditions on those transitions are reviewed. A better understanding of the fundamental aspects affecting the semi-crystalline structures will help to elucidate the nature of RF activity in VDF-based terpolymers and also help to further improve their applications-relevant electroactive properties.
Non-linear dielectric spectroscopy (NLDS) is employed as an effective tool to study relaxation processes and phase transitions of a poly(vinylidenefluoride-trifluoroethylene-chlorofluoroethylene) (P(VDF-TrFE-CFE)) relaxor-ferroelectric (R-F) terpolymer in detail. Measurements of the non-linear dielectric permittivity epsilon 2 ' reveal peaks at 30 and 80 degrees C that cannot be identified in conventional dielectric spectroscopy. By combining the results from NLDS experiments with those from other techniques such as thermally stimulated depolarization and dielectric-hysteresis studies, it is possible to explain the processes behind the additional peaks. The former peak, which is associated with the mid-temperature transition, is found in all other vinylidene fluoride-based polymers and may help to understand the non-zero epsilon 2 ' values that are detected on the paraelectric phase of the terpolymer. The latter peak can also be observed during cooling of P(VDF-TrFE) copolymer samples at 100 degrees C and is due to conduction and space-charge polarization as a result of the accumulation of real charges at the electrode-sample interface.
The effects of thermal processing on the micro- and nanostructural features and thus also on the relaxor-ferroelectric properties of a P(VDF-TrFE-CFE) terpolymer were investigated in detail by means of dielectric experiments, such as dielectric relaxation spectroscopy (DRS), dielectric hysteresis loops, and thermally stimulated depolarization currents (TSDCs). The results were correlated with those obtained from differential scanning calorimetry (DSC), wide-angle X-ray diffraction (WAXD), and Fourier-transform infrared spectroscopy (FTIR). The results from DRS and DSC show that annealing reduces the Curie transition temperature of the terpolymer, whereas the results from WAXD scans and FTIR spectra help to understand the shift in the Curie transition temperatures as a result of reducing the ferroelectric phase fraction, which by default exists even in terpolymers with relatively high CFE contents. In addition, the TSDC traces reveal that annealing has a similar effect on the midtemperature transition by altering the fraction of constrained amorphous phase at the interphase between the crystalline and the amorphous regions. Changes in the transition temperatures are in turn related to the behavior of the hysteresis curves on differently heat-treated samples. During heating, evolution of the hysteresis curves from ferroelectric to relaxor-ferroelectric, first exhibiting single hysteresis loops and then double hysteresis loops near the Curie transition of the sample, is observed. When comparing the dielectric-hysteresis loops obtained at various temperatures, we find that annealed terpolymer films show higher electric-displacement values and lower coercive fields than the nonannealed sample, irrespective of the measurement temperature, and also exhibit ideal relaxor- ferroelectric behavior at ambient temperatures, which makes them excellent candidates for applications at or near room temperature. By tailoring the annealing conditions, it has been shown that the application temperature could be increased by fine tuning the induced micro- and nanostructures.