A recently reported novel class of elastomers was tested with respect to its dielectric properties. The new elastomer material is based on a commercially available poly(dimethylsiloxane) composition, which has been modified by embedding glycerol droplets into its matrix. The approach has two major advantages that make the material useful in a dielectric actuator. First, the glycerol droplets efficiently enhance the dielectric constant, which can reach astonishingly high values in the composite. Second, the liquid filler also acts as a softener that effectively decreases the elastic modulus of the composite. In combination with very low cost and easy preparation, the two property enhancements lead to an extremely attractive dielectric elastomer material. Experimental permittivity data are compared to various theoretical models that predict relative permittivity changes as a function of filler loading, and the applicability of the models is discussed. (c) 2016 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2016, 133, 44153.
Polymer-dispersed liquid crystals (PDLCs) of ferroelectric poly(vinylidene fluoride-trifluoroethylene) and nematic 4-cyano-4ʹ-n-hexylbiphenyl (6CB) or 4-cyano-4ʹ-n-pentylbiphenyl (5CB) were prepared to study the effect of the remanent polarisation of the polymer on the liquid crystal alignment. We measured the macroscopic alignment of the liquid crystal molecules in the thickness direction by means of Infrared Transition-Moment Orientational Analysis. Electrical poling at 100 V/µm caused an increased order parameter up to 0.15. After subsequent annealing above the nematic-to-isotropic phase-transition temperature, the order parameter was reduced to 0.02. Nevertheless, the order parameter was still higher than for non-poled film indicating a slight orientation in thickness direction. Both values are lower than those expected from model calculations. In agreement with dielectric measurements, we attribute this result to the shielding effect of mobile charge carriers within the liquid crystal inclusions.
Relaxation processes at the glass transition in polyamide 11: From rigidity to viscoelasticity
(2006)
Relaxation processes associated with the glass transition in nonferroelectric and ferroelectric polyamide (PA) 11 are investigated by means of differential scanning calorimetry, dynamic mechanical analysis, and dielectric relaxation spectroscopy (DRS) in order to obtain information about the molecular mobility within the amorphous phase. In particular, the effects of melt quenching, cold drawing, and annealing just below the melting region are studied with respect to potential possibilities and limitations for improving the piezoelectric and pyroelectric properties of PA 11. A relaxation map is obtained from DRS that shows especially the crossover region where the cooperative alpha relaxation and the local beta relaxation merge into a single high-temperature process. No fundamental difference between quenched, cold-drawn, and annealed films is found, though in the cold-drawn (ferroelectric) film the alpha relaxation is suppressed and slowed down, but it is at least partly recovered by subsequent annealing. It is concluded that there exists an amorphous phase in all structures, even in the cold-drawn film. The amorphous phase can be more rigid or more viscoelastic depending on preparation. Cold drawing not only leads to crystallization in a ferroelectric form but also to higher rigidity of the remaining amorphous phase. Annealing just below the melting region after cold drawing causes a stronger phase separation between the crystalline phase and a more viscoelastic amorphous phase.
Fast, three-dimensional polarization mapping in piezoelectric sensor cables was performed by means of the novel thermal-pulse tomography (TPT) technique with a lateral resolution of 200 mum. The active piezoelectric cable material (a copolymer of polyvinylidene fluoride with trifluoroethylene) was electrically poled with a point-to-cable corona discharge. A focused laser was employed to heat the opaque outer electrode, and the short-circuit current generated by the thermal pulse was used to obtain 3D polarization maps via the scale transformation method. The article describes the TPT technique as a fast non-destructive option for studying cylindrical geometries.
The influence of relaxation processes on the thermal electret stability of high-impact polystyrene (HIPS) free-standing films filled with titanium dioxide (TiO2) of the rutile modification are investigated by means of a combination of dielectric methods (dielectric relaxation spectroscopy (DRS), thermally stimulated depolarization current (TSDC) and thermally stimulated surface-potential decay (TSSPD)), supplemented by differential scanning calorimetry (DSC) and dynamic mechanical analysis (DMA). Films with 2, 4, 6 and 8 vol.% TiO2 are compared to each other and to non-filled samples. Filling HIPS with up to 8 vol.% of TiO2 enhances the elastic modulus below the glass transition and increases the thermal electret stability above the glass transition without significantly increasing the DC conductivity. The improvement of the electret stability is caused by the build-up of an interface polarization which decays only gradually if the glass transition is exceeded. Two kinds of Arrhenius processes are considered in order to explain the decay of the composite-polymer electrets: (1) charge release from chemical traps located at the phenyl rings of the polymer chain with an activation energy of E-a = 1.1 eV after passing the glass transition at about 100 degrees C and (2) charge release from traps formed by the TiO2 particles with E-a = 2.4 eV at temperatures above 130 degrees C. Finally, the activation energies are discussed with respect to their significance.
The low surface-charge stability of polypropylene (PP) frequently limits its application as an electret material. In this paper, we demonstrate how the treatment of PP-film surfaces with orthophosphoric acid (H3PO4) enhances their charge stability. To discriminate between the effects of chemical modification and thermal treatment, as-received and annealed PP films are used as reference samples. The electret properties of treated and non-treated PP films are characterized with thermally stimulated discharge (TSD) and isothermal surface-potential decay (ISPD) experiments, from which considerable improvement in thermal and temporal charge stability is observed for samples modified with H3PO4. The half-value temperature (T-1/2) observed on TSD curves of chemically treated PP increases to 131 and 145 degrees C for positive and negative charges, respectively. The enhancement might be attributed to the phosphoric compounds detected on the H3PO4-modified surfaces via attenuated-total-reflection infrared spectroscopy. Deeper surface traps formed at the "foreign" phosphorus-containing structures are able to capture the charges over longer time periods and at higher temperatures, thus leading to significant improvements in the temporal and thermal surface-charge stabilities of PP electrets. Published by AIP Publishing.
The existence of an intermediate transition between the glass and the Curie/melting temperatures in Poly(vinylidene fluoride) (PVDF) and some of its co- and ter-polymers has been reported by several authors. In spite (or because?) of various different explanations in the literature, the origins of the transition are still not clear. Here, we try to understand the extra transition in more detail and study it with thermal and dielectric methods on PVDF, on its co-polymers with trifluoroethylene (P(VDF-TrFE)) and tetrafluoroethylene (P(VDF-TFE)), and on its ter-polymer with trifluoroethylene and chlorofluoroethylene (P(VDF-TrFE-CFE). Based on interpretations from the literature and our experimental studies, we propose the new hypothesis that the intermediate transition should have several interrelated origins. Especially since the relevant range is not far above room temperature, better understanding and control of their properties may also have practical implications for the use of the respective polymer materials in devices.
Dielectric Relaxation Spectroscopy (DRS) and Thermally Stimulated Depolarization Current (TSDC) measurements were employed to study dielectric-relaxation processes, structural transitions and electric-polarization phenomena in poly(vinylidenefluoride-trifluoroethylene-chlorofluoroethylene) (P(VDF-TrFE-CFE)) terpolymer films. Results from DRS confirm the existence of two separate dispersion regions related to a para-to-ferroelectric phase transition and to the glass transition. The dipolar TSDC peak correlates with the loss peak of the ? relaxation that represents the glass transition. The electric polarization calculated from the dipolar TSDC peak (glass transition) shows a non-linear electric-field dependence and saturates at high electric poling fields. As the observed behaviour is essentially the same as that of the electric polarization obtained from direct polarization-versus-electric-field hysteresis measurements, TSDC experiments are also suitable for studying the polarization in relaxor-ferroelectric polymers. A saturation polarization of 44 mC m(?2) was found for an electric field of 190 MV m(?1).
The effects of thermal processing on the micro- and nanostructural features and thus also on the relaxor-ferroelectric properties of a P(VDF-TrFE-CFE) terpolymer were investigated in detail by means of dielectric experiments, such as dielectric relaxation spectroscopy (DRS), dielectric hysteresis loops, and thermally stimulated depolarization currents (TSDCs). The results were correlated with those obtained from differential scanning calorimetry (DSC), wide-angle X-ray diffraction (WAXD), and Fourier-transform infrared spectroscopy (FTIR). The results from DRS and DSC show that annealing reduces the Curie transition temperature of the terpolymer, whereas the results from WAXD scans and FTIR spectra help to understand the shift in the Curie transition temperatures as a result of reducing the ferroelectric phase fraction, which by default exists even in terpolymers with relatively high CFE contents. In addition, the TSDC traces reveal that annealing has a similar effect on the midtemperature transition by altering the fraction of constrained amorphous phase at the interphase between the crystalline and the amorphous regions. Changes in the transition temperatures are in turn related to the behavior of the hysteresis curves on differently heat-treated samples. During heating, evolution of the hysteresis curves from ferroelectric to relaxor-ferroelectric, first exhibiting single hysteresis loops and then double hysteresis loops near the Curie transition of the sample, is observed. When comparing the dielectric-hysteresis loops obtained at various temperatures, we find that annealed terpolymer films show higher electric-displacement values and lower coercive fields than the nonannealed sample, irrespective of the measurement temperature, and also exhibit ideal relaxor- ferroelectric behavior at ambient temperatures, which makes them excellent candidates for applications at or near room temperature. By tailoring the annealing conditions, it has been shown that the application temperature could be increased by fine tuning the induced micro- and nanostructures.
In Memoriam Siegfried Bauer
(2019)
Siegfried Bauer, an internationally renowned, very creative applied physicist, who also was a prolific materials scientist and engineer, died on December 30, 2018, in Linz, Austria, after a one-year battle with cancer. He was full professor of soft-matter physics at the Johannes Kepler University Linz, Austria, and a scientific leader and innovator across the fields but mainly in the areas of electro-active materials (including electrets) and stretchable and imperceptible electronics.