Ferroelectrets have been fabricated from low-density polyethylene (LDPE) films by means of a template-based lamination. The temperature dependence of the piezoelectric d(33) coefficient has been investigated. It was found that low-density polyethylene ferroelectrets have rather low thermal stability with the piezoelectric coefficient decaying almost to zero already at 100 degrees C. This behavior is attributed to the poor electret properties of the polyethylene films used for the fabrication of the ferroelectrets. In order to improve the charge trapping and the thermal stability of electret charge and piezoelectricity, LDPE ferroelectrets were treated with orthophosphoric acid. The treatment resulted in considerable improvements of the charge stability in LDPE films and in ferroelectret systems made from them. For example, the charge and piezoelectric-coefficient decay curves shifted to higher temperatures by 60 K and 40 K, respectively. It is shown that the decay of the piezoelectric coefficient in LDPE ferroelectrets is governed by the relaxation of less stable positive charges. The treatment also leads to noticeable changes in the chemical composition of the LDPE surface. Infrared spectroscopy reveals absorption bands attributed to phosphorus-containing structures, while scanning electron microscopy shows new island-like structures, 50-200 nm in diameter, on the modified surface.
In ferroelectrets, the piezoelectricity stems from the charges of both polarities trapped on the inner surfaces of the cavities in the material, so that its thermal stability is defined by the stability of the respective charges. In the present work, a template-based lamination technique has been employed to fabricate tubular-channel ferroelectrets from fluoroethylenepropylene (FEP) films. It has been shown that the piezoelectricity in FEP ferroelectrets decays at relatively low temperatures due to the inherently lower thermal stability of the positive charge. In order to improve charge trapping, we have treated both FEP films and inner surfaces of the ferroelectret cavities with titanium-tetrachloride vapor, using the atomic-layer-deposition technique. Using surface-potential-decay measurements on FEP films, we have found that the charge-decay curves shift by more than 100 degrees C to the higher temperatures as a result of the surface treatment. Direct measurements of piezoelectric d(33) coefficients as a function of temperature have shown that the piezoelectric stability is likewise improved with the d(33)-decay curves shifted by 60 degrees C to the right. The improvement of electret/ferroelectret properties can be attributed to the formation of the deeper traps on the chemically modified FEP surface. SEM micrographs and EDS analysis reveal island-like structures with titanium- and oxygen-containing species that can be responsible for the deeper trapping of the electret charges. Published by AIP Publishing.
The influence of the solvent-evaporation rate on the formation of of. and P crystalline phases in solution-cast poly(vinylidene fluoride) (PVDF) films was systematically investigated. Films were crystallized from PVDF/N,N- dimethylformamide solutions with concentrations of 2.5, 5.0, 10, and 20 wt % at different temperatures. During crystallization, the solvent evaporation rate was monitored in situ by means of a semianalytic balance. With this system, it was possible to determine the evaporation rate for different concentrations and temperatures of the solution under specific ambient conditions (pressure, temperature, and humidity). Fourier-Transform InfraRed spectroscopy with Attenuated Total Reflectance revealed the P-phase content in the PVDF films and its dependence on previous evaporation rates. Based on the relation between the evaporation rate and the PVDF phase composition, a consistent explanation for the different amounts of P phase observed at the upper and lower sample surfaces is achieved. Furthermore, the role of the sample thickness has also been studied. The experimental results show that not only the temperature but also the evaporation rate have to be controlled to obtain the desired crystalline phases in solution-cast PVDF films.
Here, a promising approach for producing piezo-polymer transducers in a one-step process is presented. Using 3D-printing technology and polypropylene (PP) filaments, we are able to print a two-layered film structure with regular cavities of precisely controlled size and shape. It is found that the 3D-printed samples exhibit piezoelectric coefficients up to 200 pC/N, similar to those of other PP ferroelectrets, and their temporal and thermal behavior is in good agreement with those known of PP ferroelectrets. The piezoelectric response strongly decreases for applied pressures above 20 kPa, as the pressure in the air-filled cavities strongly influences the overall elastic modulus of ferroelectrets.
A template-based lamination technique for the manufacture of ferroelectrets from uniform electret films was recently reported. In the present work, this technique is used to prepare similar ferroelectret structures from low-density polyethylene (LDPE) films and from fluoro-ethylene-propylene (FEP) copolymer films. A comparative analysis of the pressure-, temperature-, and frequency-dependent piezoelectric properties has been performed on the two ferroelectret systems. It is observed that the FEP ferroelectrets exhibit better piezoelectric responses and are thermally more stable. The difference between the piezoelectric d(33) coefficients of the two ferroelectret systems is partially explained here by their different elastic moduli. The anti-resonance peaks of both structures have been investigated by means of dielectric resonance spectroscopy and electroacoustic sound-pressure measurements. A difference of more than 10 kHz is observed between the anti-resonance frequencies of the two ferroelectret systems.
We describe the concept, the fabrication, and the most relevant properties of a piezoelectric-polymer system: Two fluoroethylenepropylene (FEP) films with good electret properties are laminated around a specifically designed and prepared polytetrafluoroethylene (PTFE) template at 300 degrees C. After removing the PTFE template, a two-layer FEP film with open tubular channels is obtained. For electric charging, the two-layer FEP system is subjected to a high electric field. The resulting dielectric barrier discharges inside the tubular channels yield a ferroelectret with high piezoelectricity. d(33) coefficients of up to 160 pC/N have already been achieved on the ferroelectret films. After charging at suitable elevated temperatures, the piezoelectricity is stable at temperatures of at least 130 degrees C. Advantages of the transducer films include ease of fabrication at laboratory or industrial scales, a wide range of possible geometrical and processing parameters, straightforward control of the uniformity of the polymer system, flexibility, and versatility of the soft ferroelectrets, and a large potential for device applications e.g., in the areas of biomedicine, communications, production engineering, sensor systems, environmental monitoring, etc.
The acetone extracts of the root bark and stem bark of Erythrina sacleuxii showed antiplasmodial activities against the chloroquine-sensitive (D6) and chloroquine-resistant (W2) strains of Plasmodium falciparum. Chromatographic separation of the acetone extract of the root bark afforded a new isoflavone, 7-hydroxy-4 -methoxy-3'- prenylisoflavone (trivial name 5-deoxy-3' - prenylbiochanin A) along with known isoflavonoids as the antiplasmodial principles. Flavonoids and isoflavonoids isolated from the stem bark of E. sucleuxii were also tested and showed antiplasmodial activities. The structures were determined on the basis of spectroscopic evidence.