In the present study, the charge distribution and the charge transport across the thickness of 2- and 3-dimensional polymer nanodielectrics was investigated. Chemically surface-treated polypropylene (PP) films and low-density polyethylene nanocomposite films with 3 wt % of magnesium oxide (LDPE/MgO) served as examples of 2-D and 3-D nanodielectrics, respectively. Surface charges were deposited onto the non-metallized surfaces of the one-side metallized polymer films and found to broaden and to thus enter the bulk of the films upon thermal stimulation at suitable elevated temperatures. The resulting space-charge profiles in the thickness direction were probed by means of Piezoelectrically-generated Pressure Steps (PPSs). It was observed that the chemical surface treatment of PP which led to the formation of nano-structures or the use of bulk nanoparticles from LDPE/MgO nanocomposites enhance charge trapping on or in the respective polymer films and also reduce charge transport inside the respective samples.
Previous work has shown that surface modification with orthophosphoric acid can significantly enhance the charge stability on polypropylene (PP) surface by generating deeper traps. In the present study, thermally stimulated potential-decay measurements revealed that the chemical treatment may also significantly increase the number of available trapping sites on the surface. Thus, as a consequence, the so-called "cross-over" phenomenon, which is observed on as-received and thermally treated PP electrets, may be overcome in a certain range of initial charge densities. Furthermore, the discharge behavior of chemically modified samples indicates that charges can be injected from the treated surface into the bulk, and/or charges of opposite polarity can be pulled from the rear electrode into the bulk at elevated temperatures and at the high electric fields that are caused by the deposited charges. In the bulk, a lack of deep traps causes rapid charge decay already in the temperature range around 95 degrees C.