Refine
Year of publication
Document Type
- Article (24)
- Habilitation Thesis (1)
- Other (1)
- Postprint (1)
Language
- English (27)
Is part of the Bibliography
- yes (27)
Keywords
- dielectric barrier discharge (DBD) (2)
- piezoelectret (2)
- Cellular polypropylene (PP) (1)
- Ferroelectret (1)
- Ferroelectrets (1)
- Ferroelektrete (1)
- Forcemyography (1)
- Piezo-, Pyro-und Ferroelektrizität (1)
- charge storage (1)
- dielectric (1)
Institute
Ferroelectrets are non-polar polymer foams or polymer systems with internally charged cavities. They are charged through a series of dielectric barrier discharges (DBDs) that are caused by the electrical breakdown of the gas inside the cavities. Thus, the breakdown strength of the gas strongly influences the charging process of ferroelectrets. A gas with a lower breakdown strength has a lower threshold voltage, thus decreasing the onset voltage for DBD charging. However, a lower threshold voltage also leads to a lower value for the remanent polarization, as back discharges that are caused by the electric field of the internally deposited charges can take place already at lower charge levels. On this basis, a charging strategy is proposed where the DBDs start in a gas with a lower breakdown strength (in the present example, helium) and are completed at a higher breakdown strength (e.g., nitrogen or atmospheric air). Thus, the exchange of the gas in the cavities during charging can significantly enhance the charging efficiency, i.e., yield much higher piezoelectric coefficients in ferroelectrets at significantly lower charging voltages. Published by AIP Publishing.
Spectroscopic study of dielectric barrier discharges in cellular polypropylene ferroelectrets
(2007)
The transient light emission from the dielectric barrier discharges (DBDs) in cellular polypropylene ferroelectrets subjected to high electric poling fields was spectroscopically measured. The spectrum shows strong emission from the second positive system of molecular nitrogen, N-2(C (3)Pi(u))-> N-2(B (3)Pi(g)), and the first negative system of N-2(+), N-2(+)(B (2)Sigma(+)(u))-> N-2(+)(X (2)Sigma(+)(g)), consistent with a DBD in air. When a dc voltage is applied stepwise to the ferroelectret film, light emission starts above a threshold, coinciding with the threshold voltage in obtaining piezoelectricity. From selected vibronic band strength ratios, the electric field in the discharge was determined and found to agree with Townsend breakdown.
We describe the concept, the fabrication, and the most relevant properties of a piezoelectric-polymer system: Two fluoroethylenepropylene (FEP) films with good electret properties are laminated around a specifically designed and prepared polytetrafluoroethylene (PTFE) template at 300 degrees C. After removing the PTFE template, a two-layer FEP film with open tubular channels is obtained. For electric charging, the two-layer FEP system is subjected to a high electric field. The resulting dielectric barrier discharges inside the tubular channels yield a ferroelectret with high piezoelectricity. d(33) coefficients of up to 160 pC/N have already been achieved on the ferroelectret films. After charging at suitable elevated temperatures, the piezoelectricity is stable at temperatures of at least 130 degrees C. Advantages of the transducer films include ease of fabrication at laboratory or industrial scales, a wide range of possible geometrical and processing parameters, straightforward control of the uniformity of the polymer system, flexibility, and versatility of the soft ferroelectrets, and a large potential for device applications e.g., in the areas of biomedicine, communications, production engineering, sensor systems, environmental monitoring, etc.
Temporal evolution of the re-breakdown voltage in small gaps from nanoseconds to milliseconds
(2013)
A detailed understanding of electric breakdown in dielectrics is of scientific and technological interest. In gaseous dielectrics, a so-called re-breakdown is sometimes observed after extinction of the previous discharge. Although time-dependent re-breakdown voltage is essentially known, its behavior immediately after the previous discharge is not precisely understood. We present an electronic circuit for accurate measurements of the time-dependent re-breakdown voltage in small gaps from tens of nanoseconds to several milliseconds after the previous spark. Results from such experiments are compared with earlier findings, and relevant physical mechanisms such as heating of the gas, decay of the plasma, and ionization of excited atoms and molecules are discussed. It is confirmed that the thermal model is not valid at times below several microseconds.
The influence of the temperature in the gas-filled cavities on the charging process of ferroelectret film systems has been studied in hysteresis measurements. The threshold voltage and the effective polarization of the ferroelectrets were determined as functions of the charging temperature TP. With increasing TP, the threshold voltage for triggering dielectric barrier discharges in ferroelectrets decreases. Thus, increasing the temperature facilitates the charging of ferroelectrets. However, a lower threshold voltage reduces the attainable remanent polarization because back discharges occur at lower charge levels, as soon as the charging voltage is turned off. The results are discussed in view of Paschen's law for electrical breakdown, taking into account the respective gas temperature and a simplified model for ferroelectrets. Our results indicate that the thermal poling scheme widely used for conventional ferroelectrics is also useful for electrically charging ferroelectrets.
Ferroelectrets (sometimes also called piezoelectrets) are relatively new members of the family of piezo-, pyro-, and ferroelectric materials.1–5 As their name indicates, ferroelectrets are space-charge electrets that show ferroic behavior. They are non-uniform electret materials or materials systems with electrically charged internal cavities. As space-charge electrets, ferroelectrets usually do not contain any molecular dipoles. However, the cavities inside the material can be turned into macroscopic dipoles through a series of micro-plasma discharges at high electric fields, so-called dielectric barrier discharges (DBDs).6–8 The gas inside the cavities is ionized when the internal electric field exceeds the threshold for electrical breakdown, generating charges of both polarities.9 The positive and negative charges travel in opposite directions, and are eventually trapped at the internal top and bottom surfaces of the cavities, respectively. After charging, the cavities may be regarded as macroscopic dipoles that can be switched by reversing the applied voltage.
An electric-polarization-vs.-electric-field (P(E)) hysteresis is considered as an essential criterion for ferroelectricity. P(E)-hysteresis curves are usually characterized by the spontaneous polarization, the coercive field, and the remanent polarization. Recently, we have demonstrated P(E)-hysteresis loops on two different types of ferroelectrets, namely, cellular polypropylene ferroelectrets and tubular-channel fluoroethylene-polypropylene copolymer ferroelectrets.10,11 The P(E)-hysteresis loops not only prove the ferroic behavior of ferroelectrets, but also allow us to determine such parameters as the coercive field and the remanent polarization.
It is widely accepted that Paschen breakdown is the underlying mechanism for the inception of DBDs in ferroelectrets.12–14 On this basis, the charging behavior and the resulting piezoelectricity of ferroelectrets in different gases at various pressures have been studied.15–17 Paschen's law describes the conditions for electrical breakdown in a gas at a constant temperature (usually room temperature), and it needs to be modified for gas breakdown at other temperatures. The temperature stability of the piezoelectricity in ferroelectrets after charging at elevated temperatures was investigated by several researchers.18–21 Recently, a preliminary report about the effects of the charging temperature on the hysteresis loops in ferroelectrets has been presented.22
In this letter, the influence of the gas temperature on the charging of ferroelectret systems is investigated in more detail by means of quasi-ferroelectric hysteresis-loop measurements. Teflon™ fluoroethylenepropylene (FEP) copolymer samples with tubular channels were prepared via thermal lamination as described previously.23 To this end, two FEP films with a thickness of 50 μm each were laminated at 300 ° C
around a 100 μm thick polytetrafluoroethylene (PTFE) template (total area 35 mm × 45 mm) that contains parallel rectangular openings (area 1.5 mm × 40 mm each). After lamination, the template was removed, which results in an FEP film system with open tubular channels. The samples were metallized on both surfaces with aluminum electrodes of 20 mm diameter.
P(E)-hysteresis loops were obtained with a modified Sawyer–Tower (ST) circuit.10,11 A high-voltage (HV) capacitor C1 (3 nF) and a large standard capacitor Cm (1 μF) were connected in series with the sample. A bipolar sinusoidal voltage with a frequency of 10 mHz was applied from an HV power supply (FUG HCB 7-6500) controlled by an arbitrary-waveform generator (HP 33120a). The voltage Vout
on Cm is measured by means of an electrometer (HP 3458a), and the charge flowing through the circuit is determined as Q(t)=CmVout(t)
. The experiments were carried out at isothermal conditions in a Novocontrol® Quatro cryosystem.
With the modified ST circuit, Q–V loops have been measured on a tubular-channel FEP ferroelectret system at different temperatures. The sample capacitance of about 34.5 pF is determined by a linear fit of the initial part of the Q–V curve recorded at 20 °C
, where the voltage has been raised up from zero on a fresh sample. The hysteresis loops are obtained from the Q–V curves by subtracting the contribution that results from charging of the sample capacitance.10 Figure 1 shows the hysteresis loops of the sample at −100, 0, and +100 ° C, respectively. According to previous theoretical and experimental studies,24,25 the length of each of the horizontal sides of the parallelogram-like hysteresis loops is given by 2Vth where Vth is the threshold voltage. As the charging temperature decreases, the hysteresis loop becomes wider and less high, i.e., the threshold voltage increases, while the polarization at maximum voltage decreases.
Ferroelectrets have been fabricated from low-density polyethylene (LDPE) films by means of a template-based lamination. The temperature dependence of the piezoelectric d(33) coefficient has been investigated. It was found that low-density polyethylene ferroelectrets have rather low thermal stability with the piezoelectric coefficient decaying almost to zero already at 100 degrees C. This behavior is attributed to the poor electret properties of the polyethylene films used for the fabrication of the ferroelectrets. In order to improve the charge trapping and the thermal stability of electret charge and piezoelectricity, LDPE ferroelectrets were treated with orthophosphoric acid. The treatment resulted in considerable improvements of the charge stability in LDPE films and in ferroelectret systems made from them. For example, the charge and piezoelectric-coefficient decay curves shifted to higher temperatures by 60 K and 40 K, respectively. It is shown that the decay of the piezoelectric coefficient in LDPE ferroelectrets is governed by the relaxation of less stable positive charges. The treatment also leads to noticeable changes in the chemical composition of the LDPE surface. Infrared spectroscopy reveals absorption bands attributed to phosphorus-containing structures, while scanning electron microscopy shows new island-like structures, 50-200 nm in diameter, on the modified surface.
Polymer foams and void-containing polymer-film systems with internally charged voids combine large piezoelectricity with mechanical flexibility and elastic compliance. This new class of soft materials (often called ferro-or piezoelectrets) has attracted considerable attention from science and industry. It has been found that the voids can be internally charged by means of dielectric barrier discharges (DBDs) under high electric fields. The charged voids can be considered as man-made macroscopic dipoles. Depending on the ferroelectret structure and the pressure of the internal gas, the voids may be highly compressible. Consequently, very large dipole-moment changes can be induced by mechanical or electrical stresses, leading to large piezoelectricity. DBD charging of the voids is a critical process for rendering polymer foams piezoelectric. Thus a comprehensive exploration of DBD charging is essential for the understanding and the optimization of piezoelectricity in ferroelectrets. Recent studies show that DBDs in the voids are triggered when the internal electric field reaches a threshold value according to Townsend's model of Paschen breakdown. During the DBDs, charges of opposite polarity are generated and trapped at the top and bottom internal surfaces of the gas-filled voids, respectively. The deposited charges induce an electric field opposite to the externally applied one and thus extinguish the DBDs. Back discharges may eventually be triggered when the external voltage is reduced or turned off. In order to optimize the efficiency of DBD charging, the geometry (in particular the height) of the voids, the type of gas and its pressure inside the voids are essential factors to be considered and to be optimized. In addition, the influence of the plasma treatment on the internal void surfaces during the DBDs should be taken into consideration.