530 Physik
Refine
Document Type
- Article (9)
- Doctoral Thesis (1)
Language
- English (10)
Is part of the Bibliography
- yes (10)
Keywords
- Energy science and technology (1)
- Extraktion (1)
- Fulleren (1)
- Generierung von Ladungsträgern (1)
- PEDOT (1)
- Polymer (1)
- Solar cells (1)
- UV nanoimprint lithography (1)
- antireflection (1)
- bulk heterojunction (1)
Multijunction solar cells can overcome the fundamental efficiency limits of single-junction devices. The bandgap tunability of metal halide perovskite solar cells renders them attractive for multijunction architectures(1). Combinations with silicon and copper indium gallium selenide (CIGS), as well as all-perovskite tandem cells, have been reported(2-5). Meanwhile, narrow-gap non-fullerene acceptors have unlocked skyrocketing efficiencies for organic solar cells(6,7). Organic and perovskite semiconductors are an attractive combination, sharing similar processing technologies. Currently, perovskite-organic tandems show subpar efficiencies and are limited by the low open-circuit voltage (V-oc) of wide-gap perovskite cells(8) and losses introduced by the interconnect between the subcells(9,10). Here we demonstrate perovskite-organic tandem cells with an efficiency of 24.0 per cent (certified 23.1 per cent) and a high V-oc of 2.15 volts. Optimized charge extraction layers afford perovskite subcells with an outstanding combination of high V-oc and fill factor. The organic subcells provide a high external quantum efficiency in the near-infrared and, in contrast to paradigmatic concerns about limited photostability of non-fullerene cells(11), show an outstanding operational stability if excitons are predominantly generated on the non-fullerene acceptor, which is the case in our tandems. The subcells are connected by an ultrathin (approximately 1.5 nanometres) metal-like indium oxide layer with unprecedented low optical/electrical losses. This work sets a milestone for perovskite-organic tandems, which outperform the best p-i-n perovskite single junctions(12) and are on a par with perovskite-CIGS and all-perovskite multijunctions(13).
Designing gentle sinusoidal nanotextures enables the realization of high-efficiency perovskite-silicon solar cells <br /> Perovskite-silicon tandem solar cells offer the possibility of overcoming the power conversion efficiency limit of conventional silicon solar cells. Various textured tandem devices have been presented aiming at improved optical performance, but optimizing film growth on surface-textured wafers remains challenging. Here we present perovskite-silicon tandem solar cells with periodic nanotextures that offer various advantages without compromising the material quality of solution-processed perovskite layers. We show a reduction in reflection losses in comparison to planar tandems, with the new devices being less sensitive to deviations from optimum layer thicknesses. The nanotextures also enable a greatly increased fabrication yield from 50% to 95%. Moreover, the open-circuit voltage is improved by 15 mV due to the enhanced optoelectronic properties of the perovskite top cell. Our optically advanced rear reflector with a dielectric buffer layer results in reduced parasitic absorption at near-infrared wavelengths. As a result, we demonstrate a certified power conversion efficiency of 29.80%.
Inorganic-organic perovskites like methylammonium-lead-iodide have proven to be an effective class of 17 materials for fabricating efficient solar cells. To improve their performance, light management techniques using textured surfaces, similar to those used in established solar cell technologies, should be considered. Here, we apply a light management foil created by UV nanoimprint lithography on the glass side of an inverted (p-i-n) perovskite solar cell with 16.3% efficiency. The obtained 1 mA cm(-2) increase in the short-circuit current density translates to a relative improvement in cell performance of 5%, which results in a power conversion efficiency of 17.1%. Optical 3D simulations based on experimentally obtained parameters were used to support the experimental findings. A good match between the simulated and experimental data was obtained, validating the model. Optical simulations reveal that the main improvement in device performance is due to a reduction in total reflection and that relative improvement in the short-circuit current density of up to 10% is possible for large-area devices. Therefore, our results present the potential of light management foils for improving the device performance of perovskite solar cells and pave the way for further use of optical simulations in the field of perovskite solar cells.
The fact that organic solar cells perform efficiently despite the low dielectric constant of most photoactive blends initiated a long-standing debate regarding the dominant pathways of free charge formation. Here, we address this issue through the accurate measurement of the activation energy for free charge photogeneration over a wide range of photon energy, using the method of time-delayed collection field. For our prototypical low bandgap polymer:fullerene blends, we find that neither the temperature nor the field dependence of free charge generation depend on the excitation energy, ruling out an appreciable contribution to free charge generation though hot carrier pathways. On the other hand, activation energies are on the order of the room temperature thermal energy for all studied blends. We conclude that charge generation in such devices proceeds through thermalized charge transfer states, and that thermal energy is sufficient to separate most of these states into free charges.
We report on the formation of wrinkle-patterned surface morphologies in cesium formamidinium-based Cs(x)FA(1-y)Pb(I1-yBry)(3) perovskite compositions with x = 0-0.3 and y = 0-0.3 under various spin-coating conditions. By varying the Cs and Br contents, the perovskite precursor solution concentration and the spin-coating procedure, the occurrence and characteristics of the wrinkle-shaped morphology can be tailored systematically. Cs(0.17)FA(0.83)Pb(I0.83Br0.17)(3) perovskite layers were analyzed regarding their surface roughness, microscopic structure, local and overall composition, and optoelectronic properties. Application of these films in p-i-n perovskite solar cells (PSCs) with indium-doped tin oxide/NiOx/perovskite/C-60/bathocuproine/Cu architecture resulted in up to 15.3 and 17.0% power conversion efficiency for the flat and wrinkled morphology, respectively. Interestingly, we find slightly red-shifted photoluminescence (PL) peaks for wrinkled areas and we are able to directly correlate surface topography with PL peak mapping. This is attributed to differences in the local grain size, whereas there is no indication for compositional demixing in the films. We show that the perovskite composition, crystallization kinetics, and layer thickness strongly influence the formation of wrinkles which is proposed to be related to the release of compressive strain during perovskite crystallization. Our work helps us to better understand film formation and to further improve the efficiency of PSCs with widely used mixed-perovskite compositions.
The performance of perovskite solar cells is predominantly limited by non-radiative recombination, either through trap-assisted recombination in the absorber layer or via minority carrier recombination at the perovskite/transport layer interfaces. Here, we use transient and absolute photoluminescence imaging to visualize all non-radiative recombination pathways in planar pintype perovskite solar cells with undoped organic charge transport layers. We find significant quasi-Fermi-level splitting losses (135 meV) in the perovskite bulk, whereas interfacial recombination results in an additional free energy loss of 80 meV at each individual interface, which limits the open-circuit voltage (V-oc) of the complete cell to similar to 1.12 V. Inserting ultrathin interlayers between the perovskite and transport layers leads to a substantial reduction of these interfacial losses at both the p and n contacts. Using this knowledge and approach, we demonstrate reproducible dopant-free 1 cm(2) perovskite solar cells surpassing 20% efficiency (19.83% certified) with stabilized power output, a high V-oc (1.17 V) and record fill factor (>81%).
The incorporation of even small amounts of strontium (Sr) into lead-base hybrid quadruple cation perovskite solar cells results in a systematic increase of the open circuit voltage (V-oc) in pin-type perovskite solar cells. We demonstrate via absolute and transient photoluminescence (PL) experiments how the incorporation of Sr significantly reduces the non-radiative recombination losses in the neat perovskite layer. We show that Sr segregates at the perovskite surface, where it induces important changes of morphology and energetics. Notably, the Sr-enriched surface exhibits a wider band gap and a more n-type character, accompanied with significantly stronger surface band bending. As a result, we observe a significant increase of the quasi-Fermi level splitting in the neat perovskite by reduced surface recombination and more importantly, a strong reduction of losses attributed to non-radiative recombination at the interface to the C-60 electron-transporting layer. The resulting solar cells exhibited a V-oc of 1.18 V, which could be further improved to nearly 1.23 V through addition of a thin polymer interlayer, reducing the non-radiative voltage loss to only 110 meV. Our work shows that simply adding a small amount of Sr to the precursor solutions induces a beneficial surface modification in the perovskite, without requiring any post treatment, resulting in high efficiency solar cells with power conversion efficiency (PCE) up to 20.3%. Our results demonstrate very high V-oc values and efficiencies in Sr-containing quadruple cation perovskite pin-type solar cells and highlight the imperative importance of addressing and minimizing the recombination losses at the interface between perovskite and charge transporting layer.
Doped spiro-OMeTAD at present is the most commonly used hole transport material (HTM) in n-i-p-type perovskite solar cells, enabling high efficiencies around 22%. However, the required dopants were shown to induce nonradiative recombination of charge carriers and foster degradation of the solar cell. Here, in a novel approach, highly conductive and inexpensive water-free poly(3,4-ethylenedioxythiophene) (PEDOT) is used to replace these dopants. The resulting spiro-OMeTAD/PEDOT (SpiDOT) mixed films achieve higher lateral conductivities than layers of doped spiro-OMeTAD. Furthermore, combined transient and steady-state photoluminescence studies reveal a passivating effect of PEDOT, suppressing nonradiative recombination losses at the perovskite/HTM interface. This enables excellent quasi-Fermi level splitting values of up to 1.24 eV in perovskite/SpiDOT layer stacks and high open-circuit voltages (V-OC) up to 1.19 V in complete solar cells. Increasing the amount of dopant-free spiro-OMeTAD in SpiDOT layers is shown to enhance hole extraction and thereby improves the fill factor in solar cells. As a consequence, stabilized efficiencies up to 18.7% are realized, exceeding cells with doped spiro-OMeTAD as a HTM in this study. Moreover, to the best of our knowledge, these results mark the lowest nonradiative recombination loss in the V-OC (140 mV with respect to the Shockley-Queisser limit) and highest efficiency reported so far for perovskite solar cells using PEDOT as a HTM.
Charge transport layers (CTLs) are key components of diffusion controlled perovskite solar cells, however, they can induce additional non-radiative recombination pathways which limit the open circuit voltage (V-OC) of the cell. In order to realize the full thermodynamic potential of the perovskite absorber, both the electron and hole transport layer (ETL/HTL) need to be as selective as possible. By measuring the photoluminescence yield of perovskite/CTL heterojunctions, we quantify the non-radiative interfacial recombination currents in pin- and nip-type cells including high efficiency devices (21.4%). Our study comprises a wide range of commonly used CTLs, including various hole-transporting polymers, spiro-OMeTAD, metal oxides and fullerenes. We find that all studied CTLs limit the V-OC by inducing an additional non-radiative recombination current that is in most cases substantially larger than the loss in the neat perovskite and that the least-selective interface sets the upper limit for the V-OC of the device. Importantly, the V-OC equals the internal quasi-Fermi level splitting (QFLS) in the absorber layer only in high efficiency cells, while in poor performing devices, the V-OC is substantially lower than the QFLS. Using ultraviolet photoelectron spectroscopy and differential charging capacitance experiments we show that this is due to an energy level mis-alignment at the p-interface. The findings are corroborated by rigorous device simulations which outline important considerations to maximize the V-OC. This work highlights that the challenge to suppress non-radiative recombination losses in perovskite cells on their way to the radiative limit lies in proper energy level alignment and in suppression of defect recombination at the interfaces.
A dramatic efficiency improvement of bulk heterojunction solar cells based on electron-donating conjugated polymers in combination with soluble fullerene derivatives has been achieved over the past years. Certified and reported power conversion efficiencies now reach over 9% for single junctions and exceed the 10% benchmark for tandem solar cells. This trend brightens the vision of organic photovoltaics becoming competitive with inorganic solar cells including the realization of low-cost and large-area organic photovoltaics. For the best performing organic materials systems, the yield of charge generation can be very efficient. However, a detailed understanding of the free charge carrier generation mechanisms at the donor acceptor interface and the energy loss associated with it needs to be established. Moreover, organic solar cells are limited by the competition between charge extraction and free charge recombination, accounting for further efficiency losses. A conclusive picture and the development of precise methodologies for investigating the fundamental processes in organic solar cells are crucial for future material design, efficiency optimization, and the implementation of organic solar cells into commercial products.
In order to advance the development of organic photovoltaics, my thesis focuses on the comprehensive understanding of charge generation, recombination and extraction in organic bulk heterojunction solar cells summarized in 6 chapters on the cumulative basis of 7 individual publications.
The general motivation guiding this work was the realization of an efficient hybrid inorganic/organic tandem solar cell with sub-cells made from amorphous hydrogenated silicon and organic bulk heterojunctions. To realize this project aim, the focus was directed to the low band-gap copolymer PCPDTBT and its derivatives, resulting in the examination of the charge carrier dynamics in PCPDTBT:PC70BM blends in relation to by the blend morphology. The phase separation in this blend can be controlled by the processing additive diiodooctane, enhancing domain purity and size. The quantitative investigation of the free charge formation was realized by utilizing and improving the time delayed collection field technique. Interestingly, a pronounced field dependence of the free carrier generation for all blends is found, with the field dependence being stronger without the additive. Also, the bimolecular recombination coefficient for both blends is rather high and increases with decreasing internal field which we suggest to be caused by a negative field dependence of mobility. The additive speeds up charge extraction which is rationalized by the threefold increase in mobility.
By fluorine attachment within the electron deficient subunit of PCPDTBT, a new polymer F-PCPDTBT is designed. This new material is characterized by a stronger tendency to aggregate as compared to non-fluorinated PCPDTBT. Our measurements show that for F-PCPDTBT:PCBM blends the charge carrier generation becomes more efficient and the field-dependence of free charge carrier generation is weakened. The stronger tendency to aggregate induced by the fluorination also leads to increased polymer rich domains, accompanied in a threefold reduction in the non-geminate recombination coefficient at conditions of open circuit. The size of the polymer domains is nicely correlated to the field-dependence of charge generation and the Langevin reduction factor, which highlights the importance of the domain size and domain purity for efficient charge carrier generation. In total, fluorination of PCPDTBT causes the PCE to increase from 3.6 to 6.1% due to enhanced fill factor, short circuit current and open circuit voltage. Further optimization of the blend ratio, active layer thickness, and polymer molecular weight resulted in 6.6% efficiency for F-PCPDTBT:PC70BM solar cells.
Interestingly, the double fluorinated version 2F-PCPDTBT exhibited poorer FF despite a further reduction of geminate and non-geminate recombination losses. To further analyze this finding, a new technique is developed that measures the effective extraction mobility under charge carrier densities and electrical fields comparable to solar cell operation conditions. This method involves the bias enhanced charge extraction technique. With the knowledge of the carrier density under different electrical field and illumination conditions, a conclusive picture of the changes in charge carrier dynamics leading to differences in the fill factor upon fluorination of PCPDTBT is attained. The more efficient charge generation and reduced recombination with fluorination is counterbalanced by a decreased extraction mobility. Thus, the highest fill factor of 60% and efficiency of 6.6% is reached for F-PCPDTBT blends, while 2F-PCPDTBT blends have only moderate fill factors of 54% caused by the lower effective extraction mobility, limiting the efficiency to 6.5%.
To understand the details of the charge generation mechanism and the related losses, we evaluated the yield and field-dependence of free charge generation using time delayed collection field in combination with sensitive measurements of the external quantum efficiency and absorption coefficients for a variety of blends. Importantly, both the yield and field-dependence of free charge generation is found to be unaffected by excitation energy, including direct charge transfer excitation below the optical band gap. To access the non-detectable absorption at energies of the relaxed charge transfer emission, the absorption was reconstructed from the CT emission, induced via the recombination of thermalized charges in electroluminescence. For a variety of blends, the quantum yield at energies of charge transfer emission was identical to excitations with energies well above the optical band-gap. Thus, the generation proceeds via the split-up of the thermalized charge transfer states in working solar cells. Further measurements were conducted on blends with fine-tuned energy levels and similar blend morphologies by using different fullerene derivatives. A direct correlation between the efficiency of free carrier generation and the energy difference of the relaxed charge transfer state relative to the energy of the charge separated state is found. These findings open up new guidelines for future material design as new high efficiency materials require a minimum energetic offset between charge transfer and the charge separated state while keeping the HOMO level (and LUMO level) difference between donor and acceptor as small as possible.