92-XX BIOLOGY AND OTHER NATURAL SCIENCES
Refine
Has Fulltext
- yes (7)
Document Type
- Doctoral Thesis (7)
Is part of the Bibliography
- yes (7)
Keywords
- 2D material (1)
- 2D-Material (1)
- Abbau (1)
- African medicinal plants (1)
- Afrikanische Heilpflanzen (1)
- Aggregation (1)
- Beschichtungen (1)
- Blockcopolymer (1)
- Differential mobility analysis (DMA) (1)
- Differentielle Mobilitätsanalyse (DMA) (1)
Institute
- Institut für Chemie (7) (remove)
The doctoral thesis presented provides a comprehensive view of laser-based ablation techniques promoted to new fields of operation, including, but not limited to, size, composition, and concentration analyses. It covers various applications of laser ablation techniques over a wide range of sizes, from single molecules all the way to aerosol particles. The research for this thesis started with broadening and deepening the field of application and the fundamental understanding of liquid-phase IR-MALDI. Here, the hybridization of ion mobility spectrometry and microfluidics was realized by using IR-MALDI as the coupling technique for the first time. The setup was used for monitoring the photocatalytic performance of the E-Z isomerization of olefins. Using this hybrid, measurement times were so drastically reduced that such photocatalyst screenings became a matter of minutes rather than hours. With this on hand, triple measurements screenings could not only be performed within ten minutes, but also with a minimum amount of resources highlighting its potential as a green chemistry alternative to batch-sized reactions. Along the optimizing process of the IR-MALDI source for microfluidics came its application for another liquid sample supply method, the hanging drop. This demarcated one of the first applications of IR-MALDI for the charging of sub-micron particles directly from suspensions via their gas-phase transfer, followed by their characterization with differential mobility analysis. Given the high spectral quality of the data up to octuply charged particles became experimentally accessible, this laid the foundation for deriving a new charge distribution model for IR-MALDI in that size regime. Moving on to even larger analyte sizes, LIBS and LII were employed as ablation techniques for the solid phase, namely the aerosol particles themselves. Both techniques produce light-emitting events and were used to quantify and classify different aerosols. The unique configuration of stroboscopic imaging, photoacoustics, LII, and LIBS measurements opened new realms for analytical synergies and their potential application in industry. The concept of using low fluences, below 100 J/cm2, and high repetition rates of up to 500 Hz for LIBS makes for an excellent phase-selective LIBS setup. This concept was combined with a new approach to the photoacoustic normalization of LIBS. Also, it was possible to acquire statistically relevant amounts of data in a matter of seconds, showing its potential as a real-time optimization technique. On the same time axis, but at much lower fluences, LII was used with a similar methodology to quickly quantify and classify airborne particles of different compositions. For the first time, aerosol particles were evaluated on their LII susceptibility by using a fluence screening approach.
Two approaches for the synthesis of prenylated isoflavones were explored: the 2,3-oxidative rearrangement/cross metathesis approach, using hypervalent iodine reagents as oxidants and the Suzuki-Miyaura cross-coupling/cross metathesis approach. Three natural prenylated isoflavones: 5-deoxy-3′-prenylbiochanin A (59), erysubin F (61) and 7-methoxyebenosin (64), and non-natural analogues: 7,4′-dimethoxy-8,3′-diprenylisoflavone (126j) and 4′-hydroxy-7-methoxy-8,3′-diprenylisoflavone (128) were synthesized for the first time via the 2,3-oxidative rearrangement/cross metathesis approach, using mono- or diallylated flavanones as key intermediates. The reaction of flavanones with hypervalent iodine reagents afforded isoflavones via a 2,3-oxidative rearrangement and the corresponding flavone isomers via a 2,3-dehydrogenation. This afforded the synthesis of 7,4′-dimethoxy-8-prenylflavone (127g), 7,4′-dimethoxy-8,3′-diprenylflavone (127j), 7,4′-dihydroxy-8,3′-diprenylflavone (129) and 4′-hydroxy-7-methoxy-8,3′-diprenylflavone (130), the non-natural regioisomers of 7-methoxyebenosin, 126j, erysubin F and 128 respectively. Three natural prenylated isoflavones: 3′-prenylbiochanin A (58), neobavaisoflavone (66) and 7-methoxyneobavaisoflavone (137) were synthesized for the first time using the Suzuki-Miyaura cross-coupling/cross metathesis approach. The structures of 3′-prenylbiochanin A (58) and 5-deoxy-3′-prenylbiochanin A (59) were confirmed by single crystal X-ray diffraction analysis. The 2,3-oxidative rearrangement approach appears to be limited to the substitution pattern on both rings A and B of the flavanone while the Suzuki-Miyaura cross-coupling approach appears to be the most suitable for the synthesis of simple isoflavones or prenylated isoflavones whose prenyl substituents or allyl groups, the substituents that are essential precursors for the prenyl side chains, can be regioselectively introduced after the construction of the isoflavone core.
The chalcone-flavanone hybrids 146, 147 and 148, hybrids of the naturally occurring bioactive flavanones liquiritigenin-7-methyl ether, liquiritigenin and liquiritigenin-4′-methyl ether respectively were also synthesized for the first time, using Matsuda-Heck arylation and allylic/benzylic oxidation as key steps.
The intermolecular interactions of 5-deoxy-3′-prenylbiochanin A (59) and its two closely related precursors 106a and 106b was investigated by single crystal and Hirshfeld surface analyses to comprehend their different physicochemical properties. The results indicate that the presence of strong intermolecular O-H···O hydrogen bonds and an increase in the number of π-stacking interactions increases the melting point and lowers the solubility of isoflavone derivatives. However, the strong intermolecular O-H···O hydrogen bonds have a greater effect than the π-stacking interactions.
5-Deoxy-3′-prenylbiochanin A (59), erysubin F (61) and 7,4′-dihydroxy-8,3′-diprenylflavone (129), were tested against three bacterial strains and one fungal pathogen. All the three compounds were inactive against Salmonella enterica subsp. enterica (NCTC 13349), Escherichia coli (ATCC 25922), and Candida albicans (ATCC 90028), with MIC values greater than 80.0 μM. The diprenylated isoflavone erysubin F (61) and its flavone isomer 129 showed in vitro activity against methicillin-resistant Staphylococcus aureus (MRSA, ATCC 43300) at MIC values of 15.4 and 20.5 μM, respectively. 5-Deoxy-3′-prenylbiochanin A (59) was inactive against this MRSA strain. Erysubin F (61) and its flavone isomer 129 could serve as lead compounds for the development of new alternative drugs for the treatment of MRSA infections.
Polymeric films and coatings derived from semi-crystalline oligomers are of relevance for medical and pharmaceutical applications. In this context, the material surface is of particular importance, as it mediates the interaction with the biological system. Two dimensional (2D) systems and ultrathin films are used to model this interface. However, conventional techniques for their preparation, such as spin coating or dip coating, have disadvantages, since the morphology and chain packing of the generated films can only be controlled to a limited extent and adsorption on the substrate used affects the behavior of the films. Detaching and transferring the films prepared by such techniques requires additional sacrificial or supporting layers, and free-standing or self supporting domains are usually of very limited lateral extension. The aim of this thesis is to study and modulate crystallization, melting, degradation and chemical reactions in ultrathin films of oligo(ε-caprolactone)s (OCL)s with different end-groups under ambient conditions. Here, oligomeric ultrathin films are assembled at the air-water interface using the Langmuir technique. The water surface allows lateral movement and aggregation of the oligomers, which, unlike solid substrates, enables dynamic physical and chemical interaction of the molecules. Parameters like surface pressure (π), temperature and mean molecular area (MMA) allow controlled assembly and manipulation of oligomer molecules when using the Langmuir technique. The π-MMA isotherms, Brewster angle microscopy (BAM), and interfacial infrared spectroscopy assist in detecting morphological and physicochemical changes in the film. Ultrathin films can be easily transferred to the solid silicon surface via Langmuir Schaefer (LS) method (horizontal substrate dipping). Here, the films transferred on silicon are investigated using atomic force microscopy (AFM) and optical microscopy and are compared to the films on the water surface.
The semi-crystalline morphology (lamellar thicknesses, crystal number densities, and lateral crystal dimensions) is tuned by the chemical structure of the OCL end-groups (hydroxy or methacrylate) and by the crystallization temperature (Tc; 12 or 21 °C) or MMAs. Compression to lower MMA of ~2 Å2, results in the formation of a highly crystalline film, which consists of tightly packed single crystals. Preparation of tightly packed single crystals on a cm2 scale is not possible by conventional techniques. Upon transfer to a solid surface, these films retain their crystalline morphology whereas amorphous films undergo dewetting.
The melting temperature (Tm) of OCL single crystals at the water and the solid surface is found proportional to the inverse crystal thickness and is generally lower than the Tm of bulk PCL. The impact of OCL end-groups on melting behavior is most noticeable at the air-solid interface, where the methacrylate end-capped OCL (OCDME) melted at lower temperatures than the hydroxy end-capped OCL (OCDOL). When comparing the underlying substrate, melting/recrystallization of OCL ultrathin films is possible at lower temperatures at the air water interface than at the air-solid interface, where recrystallization is not visible. Recrystallization at the air-water interface usually occurs at a higher temperature than the initial Tc.
Controlled degradation is crucial for the predictable performance of degradable polymeric biomaterials. Degradation of ultrathin films is carried out under acidic (pH ~ 1) or enzymatic catalysis (lipase from Pseudomonas cepcia) on the water surface or on a silicon surface as transferred films. A high crystallinity strongly reduces the hydrolytic but not the enzymatic degradation rate. As an influence of end-groups, the methacrylate end-capped linear oligomer, OCDME (~85 ± 2 % end-group functionalization) hydrolytically degrades faster than the hydroxy end capped linear oligomer, OCDOL (~95 ± 3 % end-group functionalization) at different temperatures. Differences in the acceleration of hydrolytic degradation of semi-crystalline films were observed upon complete melting, partial melting of the crystals, or by heating to temperatures close to Tm. Therefore, films of densely packed single crystals are suitable as barrier layers with thermally switchable degradation rates.
Chemical modification in ultrathin films is an intricate process applicable to connect functionalized molecules, impart stability or create stimuli-sensitive cross-links. The reaction of end-groups is explored for transferred single crystals on a solid surface or amorphous monolayer at the air-water interface. Bulky methacrylate end-groups are expelled to the crystal surface during chain-folded crystallization. The density of end-groups is inversely proportional to molecular weight and hence very pronounced for oligomers. The methacrylate end-groups at the crystal surface, which are present at high concentration, can be used for further chemical functionalization. This is demonstrated by fluorescence microscopy after reaction with fluorescein dimethacrylate. The thermoswitching behavior (melting and recrystallization) of fluorescein functionalized single crystals shows the temperature-dependent distribution of the chemically linked fluorescein moieties, which are accumulated on the surfaces of crystals, and homogeneously dispersed when the crystals are molten. In amorphous monolayers at the air-water interface, reversible cross-linking of hydroxy-terminated oligo(ε-caprolactone) monolayers using dialdehyde (glyoxal) lead to the formation of 2D networks. Pronounced contraction in the area occurred for 2D OCL films in dependence of surface pressure and time indicating the reaction progress. Cross linking inhibited crystallization and retarded enzymatic degradation of the OCL film. Altering the subphase pH to ~2 led to cleavage of the covalent acetal cross-links. Besides as model systems, these reversibly cross-linked films are applicable for drug delivery systems or cell substrates modulating adhesion at biointerfaces.
The self-assembly of amphiphilic polymers in aqueous systems is important for a plethora of applications, in particular in the field of cosmetics and detergents. When introducing thermoresponsive blocks, the aggregation behavior of these polymers can be controlled by changing the temperature. While confined to simple diblock copolymer systems for long, the complexity - and thus the versatility - of such smart systems can be strongly enlarged, once designed monomers, specific block sizes, different architectures, or additional functional groups such as hydrophobic stickers are implemented. In this work, the structure-property relationship of such thermoresponsive amphiphilic block copolymers was investigated by varying their structure systematically. The block copolymers were generally composed of a permanently hydrophobic sticker group, a permanently hydrophilic block, and a thermoresponsive block exhibiting a Lower Critical Solution Temperature (LCST) behavior. While the hydrophilic block consisted of N,N dimethylacrylamide (DMAm), different monomers were used for the thermoresponsive block, such as N n propylacrylamide (NPAm), N iso propylacrylamide (NiPAm), N,N diethylacrylamide (DEAm), N,N bis(2 methoxyethyl)acrylamide (bMOEAm), or N acryloylpyrrolidine (NAP) with different reported LCSTs of 25, 32, 33, 42 and 56 °C, respectively. The block copolymers were synthesized by successive reversible addition fragmentation chain transfer (RAFT) polymerization. For the polymers with the basic linear, the twinned hydrophobic and the symmetrical quasi miktoarm architectures, the results were well defined block sizes and end groups as well as narrow molar mass distributions (Ɖ ≤ 1.3). More complex architectures, such as the twinned thermoresponsive and the non-symmetrical quasi miktoarm one, were achieved by combining RAFT polymerization with a second technique, namely atom transfer radical polymerization (ATRP) or single unit monomer insertion (SUMI), respectively. The obtained block copolymers showed well defined block sizes, but due to the complexity of these reaction paths, the dispersities were generally higher (Ɖ ≤ 1.8) and some end groups were lost.
The thermoresponsive behavior of the block copolymers was investigated by turbidimetry and dynamic light scattering (DLS). Below the phase transition temperature, the polymers were soluble in water and small micellar structures were visible. However, above the phase transition temperature, the aggregation behavior was strongly dependent on the architecture and the chemical structure of the thermoresponsive block. Thermoresponsive blocks comprising PNAP and PbMOEAm with DPn = 40 showed no cloud point (CP), since their already high LCSTs were further increased by the attached hydrophilic block. Depending on the architecture as well as on the block size, block copolymers with PNiPAm, PDEAm and PNPAm showed different CP’s. Large aggregates were visible for block copolymers with PNiPAm and PDEAm above their CP. For PNPAm containing block copolymers, the phase transition was very sensitive towards the architecture resulting in either small or large aggregates.
In addition, fluorescence studies were performed using PDMAm and PNiPAm homo and block copolymers with linear architecture, functionalized with complementary fluorescence dyes introduced at the opposite chain ends. The thermoresponsive behavior was studied in pure aqueous solution as well as in an oil in water (o/w) microemulsion. The findings indicate that the block copolymer behaves as polymeric surfactant at low temperatures, with one relatively small hydrophobic end group and an extended hydrophilic chain forming ‘hairy micelles’ similar as the other synthesized architectures. Above the phase transition temperature of the PNiPAm block, however, the copolymer behaves as associative telechelic polymer with two non-symmetrical hydrophobic end groups, which do not mix. Thus, instead of a network of bridged ‘flower micelles’, large dynamic aggregates are formed. These are connected alternatingly by the original micellar cores as well as by clusters of the collapsed PNiPAm blocks. This type of bridged micelles is even more favored in the o/w microemulsion than in pure aqueous solution.
In der vorliegenden Arbeit wird die Herstellung und Charakterisierung von Mixed-Matrix-Membranen (MMM) für die Gastrennung thematisiert. Dazu wurden verschiedene Füllstoffe genutzt, um in Verbindung mit dem Membranmaterial Polysulfon MMMs herzustellen. Als Füllstoffe wurden 3 aktive und 2 passive Füllstoffe verwendet. Die aktiven Füllstoffe besaßen Porenöffnungen, die in der Lage sind Gase in Abhängigkeit der Molekülgröße zu trennen. Daraus folgt ein höherer idealer Trennfaktor für bestimmte Gaspaare als in Polysulfon selbst. Aufgrund der durch die Poren gebildeten permanenten Kanäle in den aktiven Füllstoffen ergibt sich ein schnellerer Gastransport (Permeabilität) als in Polysulfon. Es handelte sich bei den aktiven Füllstoffen um den Zeolith SAPO-34 und 2 Chargen eines Zeolitic Imidazolate Framework (ZIF) ZIF-8. Die beiden Chargen ZIF-8 unterschieden sich in ihrer spezifischen Oberfläche, was diesen Einfluss speziell in die Untersuchungen zum Gastransport einbeziehen sollte. Bei den passiven Füllstoffen handelte es sich um ein aminofunktionalisiertes Kieselgel und unporöse (dichte) Glaskügelchen. Das Kieselgel besaß Poren, die zu groß waren, um Gase effektiv zu trennen. Die Glaskügelchen konnten keine Gastrennung ermöglichen, da sie keine Poren besaßen.
Aus der Literatur ist bekannt, dass die Einbettung von Füllstoffen oft zu Defekten in MMMs führt. Ein Ziel dieser Arbeit war es daher die Einbettung zu optimieren. Weiterhin sollte der Gastransport in MMMs dieser Arbeit mit dem in einer unbeladenen Polysulfonmembran verglichen werden. Aufgrund des selektiveren Trennverhaltens der aktiven Füllstoffe im Vergleich zum Membranmaterial, sollte mit der Einbettung aktiver Füllstoffe die Trennleistung der MMMs mit steigender Füllstoffbeladung immer weiter verbessert werden.
Um die Eigenschaften der MMMs zu untersuchen, wurden diese mittels Rasterelektronenmikroskop (REM), Gaspermeationsmessungen (GP) und Thermogravimetrischer Analyse gekoppelt mit Massenspektrometrie (TGA-MS) charakterisiert.
Untersuchungen am REM konnten eine Verbesserung der Einbettung zeigen, wenn ein polymerer Haftvermittler verwendet wurde. Verglichen wurde die optimierte Einbettung mit der Einbettung ohne Haftvermittler und Ergebnissen aus der Literatur, in der die Verwendung verschiedener Silane als Haftvermittler beschrieben wurde. Trotz der verbesserten Einbettung konnte lediglich bei geringen Beladungen an Füllstoff (10 und 20 Ma-% bezogen auf das Membranmaterial) eine geringe Steigerung des idealen Trennfaktors in den MMMs gegenüber der unbeladenen Polysulfonmembranen beobachtet werden. Bei höheren Füllstoffbeladungen (30, 40 und 50 Ma-%) war ein deutlicher Anstieg der Permeabilität bei stark sinkendem idealen Trennfaktor zu beobachten. Mit Hilfe von TGA-MS Messungen konnte darüber hinaus festgestellt werden, dass der verwendete Zeolith SAPO-34 durch Wassermoleküle blockierte Porenöffnungen besaß. Das verhinderte den Gastransport im Füllstoff, wodurch die Trennleistung des Füllstoffes nicht ausgenutzt werden konnte. Die Füllstoffe ZIF-8 (chargenunabhängig) und aminofunktionalisiertes Kieselgel wiesen keine blockierten Poren auf. Dennoch zeigte sich in diesen MMMs keine Verbesserung der Gastrenn- oder Gastransporteigenschaften. MMMs mit dichten Glaskügelchen als Füllstoff zeigten dasselbe Gastrenn- und Gastransportverhalten, wie alle MMMs mit den zuvor genannten Füllstoffen.
In dieser Arbeit konnte, trotz optimierter Einbettung anorganischer Füllstoffe, für MMMs keine Verbesserung der Gastrenn- oder Gastransporteigenschaften nachgewiesen werden. Vielmehr wurde ein Einfluss der Füllstoffmenge auf die Gastransporteigenschaften in MMMs festgestellt. Die Änderungen der MMMs gegenüber Polysulfon stammen von den Folgen der Einbettung von Füllstoffen in das Matrixpolymer. Durch die Einbettung werden die Eigenschaften des Matrixpolymers ändern, sodass auch der Gastransport beeinflusst wird. Des Weiteren wurde dokumentiert, dass in Abhängigkeit der Füllstoffbeladung die entstehende Membranstruktur beeinflusst wird. Die Beeinflussung war dabei unabhängig von der Füllstoffart. Es wurde eine Korrelation zwischen Füllstoffmenge und veränderter Membranstruktur gefunden.
Zentrales Element dieser Arbeit ist die Synthese und Charakterisierung praktisch nutzbarer Ionogele. Die Basis der Polymerionogele bildet das Modellpolymer Polymethylmethacrylat. Als Additive kommen ionische Flüssigkeiten zum Einsatz, deren Grundlage Derivate des vielfach verwendeten Imidazoliumkations sind. Die Eigenschaften der eingebetteten ionischen Flüssigkeiten sind für die Ionogele funktionsgebend. Die Funktionalität der jeweiligen Gele und damit der Transfer der Eigenschaften von ionischen Flüssigkeiten auf die Ionogele wurde in der vorliegenden Arbeit mittels zahlreicher Charakterisierungstechniken überprüft und bestätigt. In dieser Arbeit wurden durch Ionogelbildung makroskopische Ionogelobjekte in Form von Folien und Vliesen erzeugt. Dabei kamen das Filmgießen und das Elektrospinnen als Methoden zur Erzeugung dieser Folien und Vliese zum Einsatz, woraus jeweils ein Modellsystem resultiert. Dadurch wird die vorliegende Arbeit in die Themenkomplexe „elektrisch halbleitende Ionogelfolien“ und „antimikrobiell aktive Ionogelvliese“ gegliedert. Der Einsatz von triiodidhaltigen ionischen Flüssigkeiten und einer Polymermatrix in einem diskontinuierlichen Gießprozess resultiert in elektrisch halbleitenden Ionogelfolien. Die flexiblen und transparenten Folien können Mittelpunkt zahlreicher neuer Anwendungsfelder im Bereich flexibler Elektronik sein. Das Elektrospinnen von Polymethylmethacrylat mit einer ionischen Flüssigkeit führte zu einem homogen Ionogelvlies, welches ein Modell für die Übertragung antimikrobiell aktiver Eigenschaften ionischer Flüssigkeiten auf poröse Strukturen zur Filtration darstellt. Gleichzeitig ist es das erste Beispiel für ein kupferchloridhaltiges Ionogel. Ionogele sind attraktive Materialien mit zahlreichen Anwendungsmöglichkeiten. Mit der vorliegenden Arbeit wird das Spektrum der Ionogele um ein elektrisch halbleitendes und ein antimikrobiell aktives Ionogel erweitert. Gleichzeitig wurden durch diese Arbeit der Gruppe der ionischen Flüssigkeiten drei Beispiele für elektrisch halbleitende ionische Flüssigkeiten sowie zahlreiche kupfer(II)chloridbasierte ionische Flüssigkeiten hinzugefügt.
Die vorliegende Arbeit thematisiert die Synthese und Charakterisierung von neuen funktionalisierten ionischen Flüssigkeiten und deren Polymerisation. Die ionischen Flüssigkeiten wurden dabei sowohl mit polymerisierbaren Kationen als auch Anionen hergestellt. Zum einen wurden bei thermisch initiierten Polymerisationen Azobis(isobutyronitril) (AIBN) verwendet und zum anderen dienten bei photochemisch initiierten Polymerisationen Bis-4-(methoxybenzoyl)diethylgermanium (Ivocerin®) als Radikalstarter.
Mittels Gelpermeationschromatographie konnte das Homopolymer Polydimethylaminoethylmethacrylat untersucht werden, welches erst im Anschluss an die GPC-Messungen polymeranalog modifiziert wurde. Dabei wurden nach einer Quaternisierung und anschließender Anionenmetathese bei diesen Polymeren die Grenzviskositäten bestimmt und mit den Grenzviskositäten der direkt polymerisierten ionischen Flüssigkeiten verglichen. Bei der direkten Polymerisation von Poly(N-[2-(Methacryloyloxy)ethyl]-N-butyl-N,N-dimethyl-ammoniumbis(trifluormethylsulfonyl)imid) lag [η_Huggins] bei 100 mL/g und bei dem polymeranalog hergestellten Polymer betrug [η_Huggins] = 40 mL/g.
Die ionischen Flüssigkeiten mit polymerisierbaren funktionellen Gruppen wurden mittels Photo-DSC hinsichtlich der maximalen Polymerisationsgeschwindigkeit (Rpmax), der Zeit, in der dieses Maximum erreicht wurde, tmax, ihrer Glasüberganstemperatur (Tg) und des Umsatzes an Vinylprotonen untersucht. Bei diesen Messungen wurde zum einen der Einfluss der unterschiedlichen Alkylkettenlänge am Ammoniumion und der Einfluss von verschiedenen Anionen bei gleichbleibender Kationenstruktur analysiert. So polymerisierte das ethylsubstituierte Kation mit einer tmax von 21 Sekunden am langsamsten. Die maximale Polymerisationsgeschwindigkeit (Rpmax) betrug 3.3∙10-2 s-1. Die tmax Werte der übrigen alkylsubstituierten ionischen Flüssigkeiten mit einer polymerisierbaren funktionellen Gruppe hingegen lagen zwischen 10 und 15 Sekunden. Die Glasübergangstemperaturen der mittels photoinduzierter Polymerisation hergestellten Polymere lagen mit 44 bis 55 °C nahe beieinander. Alle Monomere zeigten einen hohen Umsatz der Vinylprotonen; er betrug zwischen 93 und 100%.
Mithilfe einer Bandanlage, ausgerüstet mit einer LED (λ = 395 nm), konnten Polymerfilme hergestellt werden. Der Umsatz an Doppelbindungsäquivalenten dieser Filme wurde anhand der 1H-NMR Spektroskopie bestimmt. Bei der dynamisch-mechanischen Analyse wurden die Polymerfilme mit einer konstanten Heizrate und Frequenz periodisch wechselnden Beanspruchungen ausgesetzt, um die Glasübergangstemperaturen zu bestimmen. Die niedrigste Tg mit 26 °C besaß das butylsubstituierte N-[2-(Methacryloyloxy)ethyl]-N-butyl-N,N-dimethyl-ammoniumbis(trifluormethylsulfonyl)imid, welches als Polymerfilm mit Ivocerin® als Initiator hergestellt wurde, wohingegen die höchste Tg bei dem gleichen Polymer, welches direkt durch freie radikalische Polymerisation der ionischen Flüssigkeit in Masse mit AIBN hergestellt wurde, 51 °C betrug. Zusätzlich wurden die Filme unter dem Aspekt der Topographie mit einem Rasterkraftmikroskop untersucht, welches eine Domänenstruktur des Polymers N-[2-(methacryloyloxy)ethyl]-N-butyl-N,N-dimethyl-ammonium tris(pentafluorethyl)trifluorphosphat offenbarte.