Lithium is an important component of some tourmalines, especially in chemically evolved granites and pegmatites. All attempts at synthesizing Li-rich tourmaline have so far been unsuccessful. Here we describe the first synthesis of rossmanitic tourmaline at 4 GPa and 700 degrees C in the system Li2OAl2O3SiO2B2O3H2O (LASBH) from seed-free solid starting materials consisting of a homogenous mixture of Li2O, gamma-Al2O3, quartz and H3BO3. The solid run products after 12-day run duration comprise rossmanitic tourmaline (68 wt%), dumortierite (28 wt%) and traces of spodumene (3 wt%) and coesite (1 wt%). Tourmaline forms idiomorphic, large prismatic crystals (30 X 100 mu m), which are inclusion free and chemically unzoned. The refined cell dimensions of the tourmaline are: a = 15.7396(9) angstrom, c = 7.0575(5) angstrom, V = 1514.1(2) angstrom 3. Conventionally, the Li+ ion is assumed to exclusively occupy the octahedral Y site in the tourmaline structure to a maximum of 2 Li per formula unit (pfu). However, the chemical composition of our synthetic tourmaline determined by electron microprobe and secondary ion mass spectroscopy results in the formula: (X)(square Li-0.67(11)(0.33(11)))(Y)(Al2.53(10)Li0.47(10))(Z)(Al-6)T(Si5.42(15)B0.58(15))O-18(B)(BO3)(3)(V+W)[(OH)(2.40(3))O-1.60(3)], wherein a significant amount of Li occupies the X site for charge balance requirements. Reliable assignment of the OH-stretching vibrations in a polarized single-crystal Raman spectrum such as a single-crystal XRD structure refinement, confirms the incorporation of Li at the X site [0.24(9) and 0.15(5) Li-X pfu, respectively]. The SREF data show that the LiO1 distances are shortened significantly in order to compensate for the smaller ionic radius of Li+ compared to Na+, K+ or Ca2+ at the X site, i.e., Li is closer to the Si6O18 ring and to a sevenfold coordination with oxygen.
Silicate melts are major components of the Earth’s interior and as such they make an essential contribution in igneous processes, in the dynamics of the solid Earth and the chemical development of the entire Earth. Macroscopic physical and chemical properties such as density, compressibility, viscosity, degree of polymerization etc. are determined by the atomic structure of the melt. Depending on the pressure, but also on the temperature and the chemical composition, silicate melts show different structural properties. These properties are best described by the local coordination environment, i.e. symmetry and number of neighbors (coordination number) of an atom, as well as the distance between the central atom and its neighbors (inter-atomic distance). With increasing pressure and temperature, i.e. with increasing depth in the Earth, the density of the melt increases, which can lead to changes in coordination number and distances. If the coordination number remains the same, the distance usually decreases. If the coordination number increases, the distance can increase. These general trends can, however, vary greatly, which can be attributed in particular to the chemical composition.
Due to the fact that natural melts of the deep earth are not accessible to direct investigations, in order to understand their properties under the relevant conditions, extensive experimental and theoretical investigations have been carried out so far. This has often been studied using the example of amorphous samples of the end-members SiO2 and GeO2 , with the latter serving as a structural and chemical analog model to SiO2. Commonly, the experiments were carried out at high pressure and at room temperature. Natural melts are chemically much more complex than the simple end-member SiO2 and GeO2, so that observations made on them may lead to incorrect compression models. Furthermore, the investigations on glasses at room temperature can show potentially strong deviations from the properties of melts under natural thermodynamic conditions.
The aim of this thesis was to explain the influence of the composition and the temperature on the structural properties of the melts at high pressures. To understand this, we studied complex alumino-germanate and alumino-silicate glasses. More precisely, we studied synthetic glasses that have a composition like the mineral albite and like a mixture of albite-diopside at the eutectic point. The albite glass is structurally similar to a simplified granitic melt, while the albite-diopside glass simulates a simplified basaltic melt. To study the local coordination environment of the elements, we used X-ray absorption spectroscopy in combination with a diamond anvil cell. Because the diamonds have a high absorbance for X-rays with energies below 10 keV, the direct investigation of the geologically relevant elements such as Si, Al, Ca, Mg etc. with this spectroscopic probe technique in combination with a diamond anvil cell is not possible. Therefore the glasses were doped with Ge and Sr. These elements serve partially or fully as substitutes for important major elements. In this sense, Ge serves as an a substitute for Si and other network formers, while Sr replaces network modifiers such as Ca, Na, Mg etc.,
as well as other cations with a large ionic radius.
In the first step we studied the Ge K-edge in Ge-Albit-glass, NaAlGe3O8, at room temperature up to 131 GPa. This glass has a higher chemical complexity than SiO2 and GeO2, but it is still fully polymerized. The differences in the compression mechanism between this glass and the simple oxides can clearly be attributed to higher chemical complexity. The albite and albite-diopside compositions partially doped with Ge and Sr were probed at room temperature for Ge up to 164 GPa and for Sr up to 42 GPa. While the albite glass is nominally fully polymerized like NaAlGe3O8, the albite-diopside glass is partially depolymerized. The results show that structural changes take place in all three glasses in the first 25 to a maximum of 30 GPa, with both Ge and Sr reaching the maximum coordination number 6 and ∼9, respectively. At higher pressures, only isostructural shrinkage of the coordination polyhedra takes place in the glasses. The most important finding of the high pressure studies on the alumino-silicate and alumino-germanate glasses is that in these complex glasses the polyhedra show a much higher compressibility than what can be observed in the end-members. This is shown in particular by the strong shortening of the Ge-O distances in the amorphous NaAlGe3O8 and albite-diopside glass at pressures above 30 GPa.
In addition to the effects of the composition on the compaction process, we investigated the influence of temperature on the structural changes. To do this, we probed the albite-diopside glass, as it is chemically most similar to the melts in the lower mantle. We studied the Ge K edge of the sample with a resistively heated and a laser-heated diamond anvil cell, for a pressure range of up to 48 GPa and a temperature range of up to 5000 K. High temperatures at which the sample is liquid and that are relevant for the Earth mantle, have a significant impact on the structural transformation, with a shift of approx. 30% to significantly lower pressures, compared to the glasses at room temperature and below 1000 K.
The results of this thesis represent an important contribution to the understanding of the properties of melts at conditions of the lower mantle. In the context of the discussion about the existence and origin of ultra-dense silicate melts at the core-mantle boundary, these investigations show that the higher density compared to the surrounding material cannot be explained by only structural features, but by a distinct chemical composition. The results also suggest that only very low solubilities of noble gases are to be expected for melts in the lower mantle, so that the structural properties clearly influence the overall budget and transport of noble gases in the Earth’s mantle.
Pressure induced structural changes in silicate melts have a great impact on their physico-chemical properties and hence on their behaviour in the deep Earth's interior. In order to gain a deeper understanding we have studied the densification mechanism in multicomponent aluminosilicate glasses (albitic and albit-diopside composition) by means of extended X-ray absorption fine structure spectroscopy coupled to a diamond anvil cell up to 164 GPa. We have monitored the structural modifications from the network-former Ge as well as the network-modifier Sr. Notably, we tracked the evolution of Ge-O and Sr-O bond lengths (RGe-O, RSr-O) and their coordination number with pressure. We show that RGe-O increases strongly up to about 32 GPa, whereas RSr-O increases only slightly up to similar to 26 GPa. We assign these extensions to the increase of the coordination number from 4 to 6 (Ge) and from similar to 6 to at least 9 (Sr). Upon further compression RGe-O and RSr-O exhibit a continuous decrease to the highest probed pressure. These bond contractions, notably of RGe-O, that are continuous and exceed the one observed in pure SiO2 and GeO2, reflect a higher structural flexibility of multi-component glasses compared to those simple systems. Particularly, the high fraction of non-bridging oxygen atoms due to the presence of Na, Sr, Ca, Mg in the studied glasses, favours the simple compression of the highly-coordinated polyhedra of Si and Ge at pressure greater than 30 GPa. This is in strong contrast to pure oxides where cation polyhedral distortions govern the densification mechanism of the glass. The results of this study demonstrate that low field-strength alkali and alkaline earth cations, ubiquitous in deep Earth's melts, have a profound influence on the densification mechanism of glasses. Our results provide important constrains for interpreting the observed low velocity anomalies at the Earth's core-mantle boundary that have been, beyond others, referred to the presence of high-density melts. The hypothesis that non-buoyant melts at the Earth's core-mantle boundary can be formed by peculiar structural transformations in melts leading to higher coordination numbers compared to their crystalline equivalents is not supported from the present observations. The present results rather suggest that if velocity anomalies are to be explained by melts, these likely have considerable differences in chemical composition to the surrounding crystalline phase assemblage.
Effect of temperature on the densification of silicate melts to lower earth's mantle conditions
(2022)
Physical properties of silicate melts play a key role for global planetary dynamics, controlling for example volcanic eruption styles, mantle convection and elemental cycling in the deep Earth. They are significantly modified by structural changes at the atomic scale due to external parameters such as pressure and temperature or due to chemistry. Structural rearrangements such as 4- to 6-fold coordination change of Si with increasing depth may profoundly influence melt properties, but have so far mostly been studied at ambient temperature due to experimental difficulties. In order to investigate the structural properties of silicate melts and their densification mechanisms at conditions relevant to the deep Earth's interior, we studied haplo basaltic glasses and melts (albite-diopside composition) at high pressure and temperature conditions in resistively and laser-heated diamond anvil cells using X-ray absorption near edge structure spectroscopy. Samples were doped with 10 wt% of Ge, which is accessible with this experimental technique and which commonly serves as a structural analogue for the network forming cation Si. We acquired spectra on the Ge K edge up to 48 GPa and 5000 K and derived the average Ge-O coordination number NGe-O, and bond distance RGe-O as functions of pressure. Our results demonstrate a continuous transformation from tetrahedral to octahedral coordination between ca. 5 and 30 GPa at ambient temperature. Above 1600 K the data reveal a reduction of the pressure needed to complete conversion to octahedral coordination by ca. 30 %. The results allow us to determine the influence of temperature on the Si coordination number changes in natural melts in the Earth's interior. We propose that the complete transition to octahedral coordination in basaltic melts is reached at about 40 GPa, corresponding to a depth of ca. 1200 km in the uppermost lower mantle. At the core-mantle boundary (2900 km, 130 GPa, 3000 K) the existence of non-buoyant melts has been proposed to explain observed low seismic wave velocity features. Our results highlight that the melt composition can affect the melt density at such extreme conditions and may strongly influence the structural response.