The isothermal vacuum-induced dehydration of thin films made of poly(methoxy diethylene glycol acrylate) (PMDEGA), which were swollen under ambient conditions, is studied. The dehydration behavior of the homopolymer film as well as of a nanostructured film of the amphiphilic triblock copolymer polystyrene-block-poly(methoxy diethylene glycol acrylate)-block-polystyrene, abbreviated as PS-b-PMDEGA-b-PS, are probed, and compared to the thermally induced dehydration behavior of such thin thermo-responsive films when they pass through their LCST-type coil-to globule collapse transition. The dehydration kinetics is followed by in-situ neutron reflectivity measurements. Contrast results from the use of deuterated water. Water content and film thickness are significantly reduced during the process, which can be explained by Schott second order kinetics theory for both films. The water content of the dehydrated equilibrium state from this model is very close to the residual water content obtained from the final static measurements, indicating that residual water still remains in the film even after prolonged exposure to the vacuum. In the PS-b-PMDEGA-b-PS film that shows micro-phase separation, the hydrophobic PS domains modify the dehydration process by hindering the water removal, and thus retarding dehydration by about 30%. Whereas residual water remains tightly bound in the PMDEGA domains, water is completely removed from the PS domains of the block copolymer film. (C) 2017 Elsevier Ltd. All rights reserved.
A series of new sulfobetaine methacrylates, including nitrogen-containing saturated heterocycles, was synthesised by systematically varying the substituents of the zwitterionic group. Radical polymerisation via the RAFT (reversible addition–fragmentation chain transfer) method in trifluoroethanol proceeded smoothly and was well controlled, yielding polymers with predictable molar masses. Molar mass analysis and control of the end-group fidelity were facilitated by end-group labeling with a fluorescent dye. The polymers showed distinct thermo-responsive behaviour of the UCST (upper critical solution temperature) type in an aqueous solution, which could not be simply correlated to their molecular structure via an incremental analysis of the hydrophilic and hydrophobic elements incorporated within them. Increasing the spacer length separating the ammonium and the sulfonate groups of the zwitterion moiety from three to four carbons increased the phase transition temperatures markedly, whereas increasing the length of the spacer separating the ammonium group and the carboxylate ester group on the backbone from two to three carbons provoked the opposite effect. Moreover, the phase transition temperatures of the analogous polyzwitterions decreased in the order dimethylammonio > morpholinio > piperidinio alkanesulfonates. In addition to the basic effect of the polymers’ precise molecular structure, the concentration and the molar mass dependence of the phase transition temperatures were studied. Furthermore, we investigated the influence of added low molar mass salts on the aqueous-phase behaviour for sodium chloride and sodium bromide as well as sodium and ammonium sulfate. The strong effects evolved in a complex way with the salt concentration. The strength of these effects depended on the nature of the anion added, increasing in the order sulfate < chloride < bromide, thus following the empirical Hofmeister series. In contrast, no significant differences were observed when changing the cation, i.e. when adding sodium or ammonium sulfate.
Several series of presumed dual thermo-responsive diblock copolymers consisting of one non-ionic and one zwitterionic block were synthesized via consecutive reversible addition-fragmentation chain transfer (RAFT) polymerization. For all copolymers, poly(N-isopropylmethacrylamide) was chosen as non-ionic block that shows a coil-to-globule collapse transition of the lower critical solution temperature (LCST) type. In contrast, the chemical structure of zwitterionic blocks, which all belonged to the class of poly(sulfobetaine methacrylate)s, was varied broadly, in order to tune their coil-to-globule collapse transition of the upper critical solution temperature (UCST) type. All polymers were labeled with a solvatochromic fluorescent end-group. The dual thermo-responsive behavior and the resulting multifarious temperature-dependent self-assembly in aqueous solution were mapped by temperature resolved turbidimetry, H-1 NMR spectroscopy, dynamic light scattering (DLS), and fluorescence spectroscopy. Depending on the relative positions between the UCST-type and LCST-type transition temperatures, as well as on the width of the window in-between, all the four possible modes of stimulus induced micellization can be realized. This includes classical induced micellization due to a transition from a double hydrophilic, or respectively, from a double hydrophobic to an amphiphilic state, as well as "schizophrenic" behavior, where the core- and shell-forming blocks are inverted. The exchange of the roles of the hydrophilic and hydrophobic block in the amphiphilic states is possible through a homogeneous intermediate state or a heterogeneous one. (C) 2017 Elsevier Ltd. All rights reserved.
This study introduces a thermally responsive, polymer-based electrode system. The key component is a surface-attached, temperature-responsive poly(oligoethylene glycol) methacrylate (poly(OEGMA)) type polymer bearing photoreactive benzophenone and carboxy groups containing side chains. The responsive behavior of the polymer in aqueous media has been investigated by turbidimetry measurements. Polymer films are formed on gold substrates by means of the photoreactive 2(dicyclohexylphosphino)benzophenone (DPBP) through photocrosslinking. The electrochemical behavior of the resulting polymer-substrate interface has been investigated in buffered [Fe(CN)6](3-)/[Fe (CN)6](4-)solutions at room temperature and under temperature variation by cyclic voltammetry (CV). The CV experiments show that with increasing temperature structural changes of the polymer layer occur, which alter the output of the electrochemical measurement. Repeated heating/cooling cycles analyzed by CV measurements and pH changes analyzed by quartz crystal microbalance with dissipation monitoring (QCM-D) reveal the reversible nature of the restructuring process. The immobilized films are further modified by covalent coupling of two small biomolecules - a hydrophobic peptide and a more hydrophilic one. These attached components influence the hydrophobicity of the layer in a different way the resulting change of the temperature-caused behavior has been studied by CV indicating a different state of the polymer after coupling of the hydrophobic peptide.
A series of new fluorescent dye bearing monomers, including glycomonomers, based on maleamide and maleic esteramide was synthesized. The dye monomers were incorporated by radical copolymerization into thermo-responsive poly(N-vinyl-caprolactam) that displays a lower critical solution temperature (LCST) in aqueous solution. The effects of the local molecular environment on the polymers' luminescence, in particular on the fluorescence intensity and the extent of solvatochromism, were investigated below as well as above the phase transition. By attaching substituents of varying size and polarity in the close vicinity of the fluorophore, and by varying the spacer groups connecting the dyes to the polymer backbone, we explored the underlying structure-property relationships, in order to establish rules for successful sensor designs, e.g., for molecular thermometers. Most importantly, spacer groups of sufficient length separating the fluorophore from the polymer backbone proved to be crucial for obtaining pronounced temperature regulated fluorescence responses.