Control of crystallographic texture from mostly face-on to edge-on is observed for the film morphology of the n-type semicrystalline polymer [N,N-9-bis(2-octyldodecyl)naphthalene-1,4,5,8-bis(dicarboximide)-2,6-diy1]alt-5,59-(2,29-bithiophene)}, P(NDI2OD-T2), when annealing the film to the polymer melting point followed by slow cooling to ambient temperature. A variety of X-ray diffraction analyses, including pole figure construction and Fourier transform peak shape deconvolution, are employed to quantify the texture change, relative degree of crystallinity and lattice order. We find that annealing the polymer film to the melt leads to a shift from 77.5% face-on to 94.6% edge-on lamellar texture as well as to a 2-fold increase in crystallinity and a 40% decrease in intracrystallite cumulative disorder. The texture change results in a significant drop in the electron-only diode current density through the film thickness upon melt annealing while little change is observed in the in-plane transport of bottom gated thin film transistors. This suggests that the texture change is prevalent in the film interior and that either the (bottom) surface structure is different from the interior structure or the intracrystalline order and texture play a secondary role in transistor transport for this material.
New polymers with high electron mobilities have spurred research in organic solar cells using polymeric rather than fullerene acceptors due to their potential of increased diversity, stability, and scalability. However, all-polymer solar cells have struggled to keep up with the steadily increasing power conversion efficiency of polymer: fullerene cells. The lack of knowledge about the dominant recombination process as well as the missing concluding picture on the role of the semi-crystalline microstructure of conjugated polymers in the free charge carrier generation process impede a systematic optimization of all-polymer solar cells. These issues are examined by combining structural and photo-physical characterization on a series of poly(3-hexylthiophene) (donor) and P(NDI2OD-T2) (acceptor) blend devices. These experiments reveal that geminate recombination is the major loss channel for photo-excited charge carriers. Advanced X-ray and electron-based studies reveal the effect of chloronaphthalene co-solvent in reducing domain size, altering domain purity, and reorienting the acceptor polymer crystals to be coincident with those of the donor. This reorientation correlates well with the increased photocurrent from these devices. Thus, effi cient split-up of geminate pairs at polymer/polymer interfaces may necessitate correlated donor/acceptor crystal orientation, which represents an additional requirement compared to the isotropic fullerene acceptors.