Refine
Year of publication
Document Type
- Article (67)
- Postprint (8)
- Review (3)
- Conference Proceeding (1)
- Habilitation Thesis (1)
- Other (1)
- Preprint (1)
Language
- English (82)
Is part of the Bibliography
- yes (82)
Keywords
- ring-opening polymerization (6)
- biomaterials (5)
- biodegradable polymers (4)
- self-assembly (4)
- XPS (3)
- crystallization (3)
- metathesis (3)
- nanoparticles (3)
- photochemistry (3)
- spider silk (3)
Institute
The acyclic monoterpene beta-myrcene is polymerized by anionic polymerization at room temperature using sec-butyllithium as the initiator and the cyclic monoterpene DL-limonene as an unsaturated hydrocarbon solvent. The polymerization is a living process and allows production of polymyrcenes with narrow molar mass distribution ((sic) similar to 1.06) and high content of 1,4 units (similar to 90%) as well as block copolymers.
A set of new functionalized poly(2-oxazoline) homopolymers and copolymers carrying protected catecholic side chains were prepared by microwave-assisted cationic ring-opening (co)polymerization. The copolymerizations of 2-ethyl-2-oxazoline with either 2-(3,4-dimethoxyphenyl)-, 2-(3,4-dimethoxybenzyl)-, or 2-(3,4-dimethoxycinnamyl)-2-oxazoline (comonomer ratio 90 : 10) produced gradient or random copolymers with narrow molar mass distributions. During the copolymerization with the 2-(3,4-dimethoxycinnamyl)-2-oxazoline, however, chain coupling reactions occurred at monomer conversions of >50%, supposedly via Michael-type addition of intermediately formed ketene N,O-acetal end groups to 3,4-dimethoxycinnamyl amide side chains. A poly[(2-ethyl-2-oxazoline)-grad-(2-(3,4-dimethoxyphenyl)-2-oxazoline)] was examplarily subjected to partial demethylation and acidic hydrolysis to give a hydrophilic copolymer carrying both catecholic and cationic units, which is designed as a bioinspired adhesive copolymer mimicking mussel adhesive protein.
A series of biomass-derived levoglucosenyl alkyl ethers (alkyl = methyl, ethyl, n-propyl, isopropyl, and n-butyl) were synthesized and polymerized by ring-opening olefin metathesis polymerization using the Grubbs catalyst C793 at room temperature. Polymerizations were successfully performed in conventional solvents such as 1,4-dioxane and dichloromethane as well as in polar aprotic "green" solvents such as 2-methyltetrahydrofuran, dihydrolevoglucosenone (Cyrene), and ethyl acetate. The prepared polyacetals with degrees of polymerization of similar to 100 exhibit Schulz-Flory-type molar mass distributions and are thermoplastic materials with rather low glass transition temperatures in the range of 43-0 degrees C depending on the length of the alkyl substituent. Kinetic studies revealed that the polymerization proceeded rapidly to a steady state with a certain minimum monomer concentration threshold. When the steady state was reached, just about half of the [Ru] catalyst had been effective to initiate the polymerization, indicating that the initiation step was a slow process. The remaining catalyst was still active and did no longer react with monomers but with in-chain double bonds, cutting the formed polymer chains into shorter fragments. In the long term, all catalyst was consumed and propagating [Ru] chain ends were deactivated by the elimination of [Ru] from the chain ends to form inactive chains with terminal aldehyde groups.
Modular toolkit of multifunctional block copoly(2-oxazoline)s for the synthesis of nanoparticles
(2021)
Post-polymerization modification provides an elegant way to introduce chemical functionalities onto macromolecules to produce tailor-made materials with superior properties. This concept was adapted to well-defined block copolymers of the poly(2-oxazoline) family and demonstrated the large potential of these macromolecules as universal toolkit for numerous applications. Triblock copolymers with separated water-soluble, alkyne- and alkene-containing segments were synthesized and orthogonally modified with various low-molecular weight functional molecules by copper(I)-catalyzed azide-alkyne cycloaddition (CuAAC) and thiol-ene (TE) click reactions, respectively. Representative toolkit polymers were used for the synthesis of gold, iron oxide and silica nanoparticles.
Isoprene and beta-myrcene were polymerized by anionic polymerization in bulk and in the 'green' ether solvents cyclopentyl methyl ether and 2-methyltetrahydrofuran and, for comparison, in cyclohexane and tetrahydrofuran. The polydienes produced in bulk and in cyclohexane contained high amounts of 1,4 units (>90%) whereas those produced in ether solvents were rich in 1,2 and 3,4 units (36%-86%). Comparison of the microstructures and glass transition temperatures of the polydienes obtained in the various solvents suggests that conventionally used solvents can be substituted by environmentally more friendly alternatives.
Epoxidized 1,4-polymyrcene
(2020)
1,4-Polymyrcene was synthesized by anionic polymerization and epoxidized using meta-chloroperbenzoic acid. Samples with different degrees of epoxidation (25%, 49%, 74%, and 98%) were prepared and examined according to their chemical and thermal properties. Epoxidation was found to increase the glass transition temperature (T-g = 14 degrees C for the 98% epoxidized 1,4-polymyrcene) as well as the shelf live (>10 months). The trisubstituted epoxide groups were remarkably stable against nucleophiles under basic conditions but cross-linked or hydrolyzed in the presence of an acid. Also, highly epoxidized 1,4-polymyrcene readily cross-linked upon annealing at 260 degrees C to produce an epoxy resin.
Focusing on the phase-coexistence region in Langmuir films of poly(L-lactide), we investigated changes in nonequilibrated morphologies and the corresponding features of the isotherms induced by different experimental pathways of lateral compression and expansion. In this coexistence region, the surface pressure II was larger than the expected equilibrium value and was found to increase upon compression, i.e., exhibited a nonhorizontal plateau. As shown earlier by using microscopic techniques [Langmuir 2019, 35, 6129-6136], in this plateau region, well-ordered mesoscopic clusters coexisted with a surrounding matrix phase. We succeeded in reducing Pi either by slowing down the rate of compression or through increasing the waiting time after stopping the movement of the barriers, which allowed for relaxations in the coexistence region. Intriguingly, the most significant pressure reduction was observed when recompressing a film that had already been compressed and expanded, if the recompression was started from an area value smaller than the one anticipated for the onset of the coexistence region. This observation suggests a "self-seeding" behavior, i.e., pre-existing nuclei allowed to circumvent the nucleation step. The decrease in Pi was accompanied by a transformation of the initially formed metastable mesoscopic clusters into a thermodynamically favored filamentary morphology. Our results demonstrate that it is practically impossible to obtain fully equilibrated coexisting phases in a Langmuir polymer film, neither under conditions of extremely slow continuous compression nor for long waiting times at a constant area in the coexistence region which allow for reorganization.
Aminolysis induced functionalization of (RAFT) polymer-dithioester with thiols and disulfides
(2020)
A series of polystyrene- and poly(methyl methacrylate)-dithioesters was subjected to aminolysis under ambient atmospheric conditions, i.e., in the presence of oxygen. Polymer disulfide coupling by oxidation occurred within tens of minutes and the yield of disulfide-coupled polymer increased with decreasing polymer molar mass. Oxidation of thiolates is usually an unwanted side reaction, here it is employed to obtain exclusively polymeric mixed disulfides through in situ aminolysis/functionalization in the presence of a thiol. The in situ aminolysis/functionalization in the presence of a disulfide, Ellman's reagent or polymer disulfide, resulted in the exclusive formation of polymer-dithionitrobenzoic acid, which can be further reacted with a thiol to exchange the terminal functionality, or block copolymer with dynamic disulfide linker, respectively.
This opinion article describes recent approaches to use the "biorefinery" concept to lower the carbon footprint of typical mass polymers, by replacing parts of the fossil monomers with similar or even the same monomer made from regrowing dendritic biomass. Herein, the new and green catalytic synthetic routes are for lactic acid (LA), isosorbide (IS), 2,5-furandicarboxylic acid (FDCA), and p-xylene (pXL). Furthermore, the synthesis of two unconventional lignocellulosic biomass derivable monomers, i.e., alpha-methylene-gamma-valerolactone (MeGVL) and levoglucosenol (LG), are presented. All those have the potential to enter in a cost-effective way, also the mass market and thereby recover lost areas for polymer materials. The differences of catalytic unit operations of the biorefinery are also discussed and the challenges that must be addressed along the synthesis path of each monomers.
This study aims to explore the photoinitiated cationic ring-opening polymerization of levoglucosenyl methyl ether (LGME), a chemical obtained from the most abundant biomass - cellulose. Direct and sensitized photopolymerizations of LGME using photoinitiators acting at the near UV or visible range in conjunction with diphenyliodonium hexafluoroantimonate (DPI) yielded unsaturated polyacetals with varying molar masses and distributions.
This opinion article describes recent approaches to use the "biorefinery" concept to lower the carbon footprint of typical mass polymers, by replacing parts of the fossil monomers with similar or even the same monomer made from regrowing dendritic biomass. Herein, the new and green catalytic synthetic routes are for lactic acid (LA), isosorbide (IS), 2,5-furandicarboxylic acid (FDCA), and p-xylene (pXL). Furthermore, the synthesis of two unconventional lignocellulosic biomass derivable monomers, i.e., alpha-methylene-gamma-valerolactone (MeGVL) and levoglucosenol (LG), are presented. All those have the potential to enter in a cost-effective way, also the mass market and thereby recover lost areas for polymer materials. The differences of catalytic unit operations of the biorefinery are also discussed and the challenges that must be addressed along the synthesis path of each monomers.
A one-step moderate energy vibrational emulsification method was successfully employed to produce thermo-responsive olive/silicone-based Janus emulsions stabilized by poly(N,N-diethylacrylamide) carrying 0.7 mol% oleoyl side chains. Completely engulfed emulsion droplets remained stable at room temperature and could be destabilized on demand upon heating to the transition temperature of the polymeric stabilizer. Time-dependent light micrographs demonstrate the temperature-induced breakdown of the Janus droplets, which opens new aspects of application, for instance in biocatalysis.
Near-ambient pressure x-ray photoelectron spectroscopy (NAP-XPS) is a less traditional form of XPS that allows samples to be analyzed at relatively high pressures, i. e., at greater than 2500 Pa. In this study, poly(.- benzyl L- glutamate) (PBLG) with a molar mass of 11.3 kg/mol was analyzed by NAP-XPS; here, we show the survey, C 1s, N 1s, and O 1s narrow scans of PBLG. The C 1s peak envelope was fitted in three different ways, to five, six, or seven synthetic peaks. In each fit, there was also a shake-up signal. The O 1s narrow scan was well fit with three peaks: CZO and CvO in a 1:2 ratio from the polymer, and a higher energy signal from water vapor. Hartree-Fock orbital energies of a model monomer served as a guide to an additional fit of the C 1s envelope.
We studied morphological changes in a quasi-two-dimensional Langmuir film of low molar mass poly(L-lactide) upon increasing the surface density, starting from randomly distributed molecules to a homogeneous monolayer of closely packed molecules, followed by nucleation and growth of mesoscopic, three-dimensional clusters from an overcompressed monolayer. The corresponding nucleation density of mesoscopic clusters within the monolayer can be tailored through variation of the rate of compression. For a given surface density and temperature, the nucleation probability was found to increase linearly with the rate of compression, allowing to adjust the density of mesoscopic clusters over nearly 2 orders magnitude.
Cystine was used as a platform chemical to prepare cyclic and acyclic monomers for entropy-driven ringopening polymerization (ED-ROMP) via olefin or disulfide metathesis and for step-growth polymerization. The olefin ED-ROMP of an olefin/disulfide containing 16-atom macrocycle using the 3rd generation Grubbs catalyst was examined in greater detail. Kinetic studies revealed that the catalyst turned inactive during the polymerization, which limited the achievable (apparent) polymer molar mass to similar to 70 kg mol(-1). Such limitation could be overcome with the disulfide ED-ROMP of the same macrocycle to yield polymers with molar masses of up to 180 kg mol(-1). The step-growth polymerizations of acyclic diene and dithiol monomers via olefin metathesis or oxidation were far less effective and yielded just low molar mass polymers or oligomers; photopolymerization of a thiol-ene monomer produced a polyester with a molar mass of 35 kg mol(-1).
A series of phenolic-acid-based 2-oxazoline monomers with methoxy-substituted phenyl and cinnamyl side chains is synthesized and polymerized in a microwave reactor at 140 °C using methyl tosylate as the initiator. The obtained poly(2-oxazoline)s are characterized by NMR spectroscopy, MALDI-TOF mass spectrometry, and size-exclusion chromatography (SEC). Kinetic studies reveal that the microwave-assisted polymerization is fast and completed within less than ≈10 min for low monomer-to-initiator ratios of ≤25. Polymers with number-average molar masses of up to 6500 g mol−1 and low dispersity (1.2–1.3) are produced. The aryl methyl ethers are successfully cleaved with aluminum triiodide/N,N′-diisopropylcarbodiimide to give a poly(2-oxazoline) with pendent catechol groups.
A one-step moderate energy vibrational emulsification method was successfully employed to produce thermo-responsive olive/silicone-based Janus emulsions stabilized by poly(N,N-diethylacrylamide) carrying 0.7 mol% oleoyl side chains. Completely engulfed emulsion droplets remained stable at room temperature and could be destabilized on demand upon heating to the transition temperature of the polymeric stabilizer. Time-dependent light micrographs demonstrate the temperature-induced breakdown of the Janus droplets, which opens new aspects of application, for instance in biocatalysis.
Near ambient pressure - x-ray photoelectron spectroscopy (NAP-XPS) is a less traditional form of XPS that allows samples to be analyzed at relatively high pressures, i.e., at 2500Pa or higher. With NAP-XPS, one can analyze moderately volatile liquids, biological samples, porous materials, and/or polymeric materials that outgas significantly. In this submission we show C 1s, O 1s, and survey NAP-XPS spectra from poly(L-lactic acid). The C 1s and O 1s envelopes were fit with three and two Gaussian-Lorentzian sum functions, respectively. Water vapor (800Pa) was used as the residual gas for charge compensation, which was confirmed by the sharp peak at 535.0 eV in the O 1s narrow scan. The uniqueness plot corresponding to the C 1s fit shows that the fit parameters had statistical significance. C 1s and O 1s spectra of PLLA damaged by exposure to x-rays for ca. 1 hour are also included. Published by the AVS.
The readily available cellulose-derived bicyclic compound levoglucosenol was polymerized through ring-opening metathesis polymerization (ROMP) to yield polylevoglucosenol as a novel type of biomass-derived thermoplastic polyacetal, which, unlike polysaccharides, contains cyclic as well as linear segments in its main chain. High-molar-mass polyacetals with apparent weight-average molar masses of up to 100kgmol(-1) and dispersities of approximately 2 were produced despite the non-living/controlled character of the polymerization due to irreversible deactivation or termination of the catalyst/active chain ends. The resulting highly functionalized polyacetals are glassy in bulk with a glass transition temperature of around 100 degrees C. In analogy to polysaccharides, polylevoglucosenol degrades slowly in an acidic environment.