Dielectric spectra of a partially fluorinated chromophore / amorphous Teflon AF guest-host system
(1999)
The thermal-wave technique or laser-intensity modulation method is an important tool for the non-destructive probing of space-charge and polarization profiles in electrets. Analysing the experimental data requires solving a Fredholm integral equation which is known to be an ill-conditioned problem. This paper presents an iterative approach that is capable of reconstructing inherently unsmooth distributions. The deviations from the true profiles are slightly smaller than those obtained with Tikhonov regularization, while the computational burden is not a limiting factor on modem personal computers. The optimum number of iterations is estimated using the randomized generalized cross- validation technique. Results are shown for a number of model distributions, as well as for experimental data from a layered polyvinylidene fluoride film sandwich
The stability of space charge in electrets such as polytetrafluoroethylene (PTFE), polyethylene terephthalate (PETP) and polypropylene (PP) under ultraviolet irradiation has been investigated using photostimulated discharge spectroscopy. While only weak discharge currents were observed in PTFE coated with semitransparent gold electrodes, up to 15 pA/cm(2) were found in PETP around the UV absorption edge near 310 nm. Space charge profiles obtained with the piezoelectrically generated pressure step method indicate that near-surface charges were almost completely removed. In PP foam, recent findings of a UV-reduced d(33) coefficient were confirmed for exposure times of up to 3.5 h, and a discharge peak at 200 urn could be assigned to the charges stored on the surfaces of the voids. The unique morphology and the (quasi-) piezoelectric properties of cellular PP make it a role model for the future investigation of charge storage in electrets
A package of programs written using the symbolic mathematics program, Mathematicatrademark, has been developed. Its principal usage is in teaching the LIMM method to students and demonstrating data analysis by means of the Polynomial Regularization Method (PRM). A large number of variables can be changed in the program and their effects can be shown graphically. Students at the University of Potsdam and Monash University have used the program successfully
Space-charge depth profiles in various electret polymers have been measured in both the time and the frequency domain using thermal pulses and waves, respectively. A comparison of the two techniques on corona-charged polytetrafluoroethylene showed that the thermal-pulse method yielded similar results as the thermal-wave technique, but approximately 20-50 times faster. The article discusses sensitivity limitations as well as possible applications, including the real-time monitoring of space-charge decay under UV irradiation. (C) 2005 American Institute of Physics
High-resolution, large-area three-dimensional mapping of polarization profiles in electret polymers was carried out by means of a fast thermal pulse technique with a focused laser beam. A lateral resolution of 38 mu m and a near- surface depth resolution of less than 0.5 mu m was achieved. At larger depths, fast thermal diffusion in the metal electrode rather than the laser spot size becomes the limiting factor for the lateral resolution. (c) 2005 American Institute of Physics