Surface relief gratings were inscribed on azobenzene polymer films using a pulselike exposure of an Ar+ laser. The inscription process was initiated by a sequence of short pulses followed by much longer relaxation pauses. The development of the surface relief grating was probed by a He-Ne laser measuring the scattering intensity of the first- order grating peak. The growth time of the surface relief grating was found to be larger than the length of the pulses used. This unusual behavior can be considered as a nonlinear material response associated with the trans-cis isomerization of azobenzene moieties. In this study the polymer stress was assumed to be proportional to the number of cis-isomers. One-dimensional viscoelastic analysis was used to derive the polymer deformation. The rate of trans-cis isomerization increases with the intensity of the inscribing light; in the dark it is equal to the rate of thermal cis- trans isomerization. The respective relaxation times were estimated by fitting theoretical deformation curves to experimental data
The molecular orientation of azobenzene side groups in polymer films before (nonpatterned) and after (patterned) development of a surface relief grating has been investigated by photoelectron spectroscopy using synchrotron radiation. The photoemission spectra obtained for 60-100 eV photons of a patterned and a nonpatterned surface are similar when the polarization vector of the synchrotron light is parallel to the grating vector. However, for perpendicular excitation, considerable spectral intensity differences can be observed for 9-14 eV electron binding energy. The observed changes are attributed to the formation of well-oriented azobenzenes at the surface. (C) 2004 American Institute of Physics
Formation of a buried density grating on thermal erasure of azobenzene polymer surface gratings
(2002)
The development of surface relief and density patterns in azobenzene polymer films was studied by diffraction at two different wavelengths. We used x-ray diffraction of synchrotron radiation at 0.124 nm in combination with visible light diffraction at a wavelength of 633 nm. In contrast to visible light scattering x-ray diffraction allows the separation of a surface relief and a density grating contribution due to the different functional dependence of the scattering power. Additionally, the x-ray probe is most sensitive for the onset of the surface grating formation