Refine
Has Fulltext
- yes (555) (remove)
Year of publication
Document Type
- Doctoral Thesis (303)
- Postprint (237)
- Habilitation Thesis (10)
- Article (2)
- Master's Thesis (2)
- Monograph/Edited Volume (1)
Keywords
- Nanopartikel (25)
- nanoparticles (18)
- Selbstorganisation (13)
- self-assembly (13)
- thermoresponsive (11)
- DNA origami (10)
- Polymer (9)
- RAFT (9)
- ionic liquids (9)
- polymer (9)
Institute
- Institut für Chemie (555) (remove)
Cinnamic acid moieties were incorporated into amphiphilic compounds containing one and two alkyl chains. These lipid-like compounds with photoreactive units undergo self-organization to form monolayers at the gas-water interface and bilayer structures (vesicles) in aqueous solutions. The photoreaction of the cinnamic acid moiety induced by 254 nm UV light was investigated in the crystalline state, in monolayers, in vesicles and in solution in organic solvents. The single-chain amphiphiles undergo dimerization to yield photoproducts with twice the molecular weight of the corresponding monomers in organized systems. The photoreaction of amphiphiles containing two cinnamic acid groups occurs via two mechanisms: The intramolecular dimerization produces bicycles, with retention of the molecular weight of the corresponding monomer. The intermolecular reaction leads to oligomeric and polymeric photoproducts. In contrast to the single-chain amphiphiles, photodimerization processes of lipoids containing two cinnamic acid moieties also occur in solution in organic solvents.
Sinefungin inhibited the S-adenosylmethionine-dependent farnesoic acid methyltransferase in a cell-free system containing a homogenate of corpora allata from female locusts, Locusta migratoria. The enzyme catalyzed the penultimate step of juvenile hormone biosynthesis in the insects. Culturing corpora allata in the presence of sinefungin greatly suppressed juvenile hormone production. The following in vivo effects were visible after injection of the inhibitor: increase in mortality and reduction of total haemolymph protein liter and ovary fresh weight, as well as length of terminal oocytes. Attempts to reverse these effects by topical application of the juvenile hormone analog ZR-515 (methoprene) were only partly successful. Therefore, the in vivo effects may be due to a general inhibition of methyltransferase enzymes in the insect. Sinefungin appeared to be of potential interest as the first representative of a new class of insect growth regulators.
The inhibitory effect of sinefungin on juvenile hormone biosynthesis and development in locusts
(1987)
The antibiotic fungal metabolite sinefungin is a potent inhibitor of S-adenosylmethionine-acceptor methyltransferases. Its effect on insect metabolism and especially on corpora allata farnesoic acid methyltransferase, which catalyzes the penultimate step of juvenile hormone biosynthesis, was investigated in Locusta migratoria. Injection of sinefungin results in a delay of imaginal molt and in suppression of ovary development. Isolated corpora allata are unable to synthesize juvenile hormone III in the presence of more than 1.0 mM sinefungin. In a cell-free system containing the S-adenosylmethionine-dependent farnesoic acid methyltransferase from corpora allata sinefungin is a competitive inhibitor of the synthesis of methylfarnesoate with Ki of 1 μM.
Several types of insect cuticle contain enzymes catalyzing the formation ofof adducts between N-acetyldopamine (NADA) and N-acetylhistidine (NAH). Two such adducts, NAH-NADA-I and NAH NADA-II, have been isolated and their structures determined. In one of the adducts the link connecting the two residues occurs between the I-position (ß-position) in the NADA side chain and the 1-N atom (τ-N) in the imidazole ring of histidine. Diphenoloxidase activity alone is not sufficient for formation of this adduct, whereas extracts containing both diphenoloxidase and o-quinone-p-quinone methide isomerase activities catalyze the coupling reaction. The adduct consists of a mixture of two diastereomers and they are presumably formed by spontaneous reaction between enzymatically produced NADA-p-quinone methide and N-acetylhistidine. The other adduct has been identified as a ring addition product of N-acetylhistidine and NADA. In contrast to the former adduct it can be formed by incubation of the two substrates with mushroom tyrosinase alone. An adduct between N-acetylhistidine and the benzodioxan-type NADA-dimer is produced in vitro, when the N-acetylhistidine-NADA adduct is incubated with NADA and locust cuticle containing a 1,2-dehydro-NADA generating enzyme system. Trimeric NADA-polymerization products of the substituted benzodioxan-type have been obtained from in vivo sclerotized locust cuticle, confirming the ability of cuticle to produce NADA-oligomers. The results indicate that some insect cuticles contain enzymes promoting linkage of oxidized NADA to histidine residues. It is suggested that histidine residues in the cuticular proteins can serve as acceptors for oxidized NADA and that further addition of NADA-residues to the phenolic groups of bound NADA can occur, resulting in formation of protein-linked NADA-oligomers. The coupling reactions identified may be an important step in natural cuticular sclerotization.
The haemolymph of the adult Colorado potato beetle, Lepinotarsa decemlineata Say, contains a high molecular weight (MW > 200,000) JH-III specific binding protein. The Kd value of the protein for racemic JH-III is 1.3 ± 0.2 × 10−7 M. It has a lower affinity for racemic JH-I and it does not bind JH-III-diol or JH-III-acid. The binding protein does discriminate between the enantiomers of synthetic, racemic JH-III as was determined by stereochemical anaysis of the bound and the free JH-III. Incubation of racemic JH-III with crude haemolymph results in preferential formation of (10S)-JH-III-acid, the unnatural configuration. The JH-esterase present in L. decemlineata haemolymph is not enantioselective. It is concluded that the most important function of the binding protein is that of a specific carrier, protecting the natural hormone against degradation by esterases. The carrier does not protect JH-I as efficiently as the lower homologue.
This thesis provides a novel view on the early stage of crystallization utilizing calcium carbonate as a model system. Calcium carbonate is of great economical, scientific and ecological importance, because it is a major part of water hardness, the most abundant Biomineral and forms huge amounts of geological sediments thus binding large amounts of carbon dioxide. The primary experiments base on the evolution of supersaturation via slow addition of dilute calcium chloride solution into dilute carbonate buffer. The time-dependent measurement of the Ca2+ potential and concurrent pH = constant titration facilitate the calculation of the amount of calcium and carbonate ions bound in pre-nucleation stage clusters, which have never been detected experimentally so far, and in the new phase after nucleation, respectively. Analytical Ultracentrifugation independently proves the existence of pre-nucleation stage clusters, and shows that the clusters forming at pH = 9.00 have a proximately time-averaged size of altogether 70 calcium and carbonate ions. Both experiments show that pre-nucleation stage cluster formation can be described by means of equilibrium thermodynamics. Effectively, the cluster formation equilibrium is physico-chemically characterized by means of a multiple-binding equilibrium of calcium ions to a ‘lattice’ of carbonate ions. The evaluation gives GIBBS standard energy for the formation of calcium/carbonate ion pairs in clusters, which exhibits a maximal value of approximately 17.2 kJ mol^-1 at pH = 9.75 and relates to a minimal binding strength in clusters at this pH-value. Nucleated calcium carbonate particles are amorphous at first and subsequently become crystalline. At high binding strength in clusters, only calcite (the thermodynamically stable polymorph) is finally obtained, while with decreasing binding strength in clusters, vaterite (the thermodynamically least stable polymorph) and presumably aragonite (the thermodynamically intermediate stable polymorph) are obtained additionally. Concurrently, two different solubility products of nucleated amorphous calcium carbonate (ACC) are detected at low binding strength and high binding strength in clusters (ACC I 3.1EE-8 M^2, ACC II 3.8EE-8 M^2), respectively, indicating the precipitation of at least two different ACC species, while the clusters provide the precursor species of ACC. It is proximate that ACC I may relate to calcitic ACC –i.e. ACC exhibiting short range order similar to the long range order of calcite and that ACC II may relate to vateritic ACC, which will subsequently transform into the particular crystalline polymorph as discussed in the literature, respectively. Detailed analysis of nucleated particles forming at minimal binding strength in clusters (pH = 9.75) by means of SEM, TEM, WAXS and light microscopy shows that predominantly vaterite with traces of calcite forms. The crystalline particles of early stages are composed of nano-crystallites of approximately 5 to 10 nm size, respectively, which are aligned in high mutual order as in mesocrystals. The analyses of precipitation at pH = 9.75 in presence of additives –polyacrylic acid (pAA) as a model compound for scale inhibitors and peptides exhibiting calcium carbonate binding affinity as model compounds for crystal modifiers- shows that ACC I and ACC II are precipitated in parallel: pAA stabilizes ACC II particles against crystallization leading to their dissolution for the benefit of crystals that form from ACC I and exclusively calcite is finally obtained. Concurrently, the peptide additives analogously inhibit the formation of calcite and exclusively vaterite is finally obtained in case of one of the peptide additives. These findings show that classical nucleation theory is hardly applicable for the nucleation of calcium carbonate. The metastable system is stabilized remarkably due to cluster formation, while clusters forming by means of equilibrium thermodynamics are the nucleation relevant species and not ions. Most likely, the concept of cluster formation is a common phenomenon occurring during the precipitation of hardly soluble compounds as qualitatively shown for calcium oxalate and calcium phosphate. This finding is important for the fundamental understanding of crystallization and nucleation-inhibition and modification by additives with impact on materials of huge scientific and industrial importance as well as for better understanding of the mass transport in crystallization. It can provide a novel basis for simulation and modelling approaches. New mechanisms of scale formation in Bio- and Geomineralization and also in scale inhibition on the basis of the newly reported reaction channel need to be considered.
Nanostructured inorganic materials are routinely synthesized by the use of templates. Depending on the synthesis conditions of the product material, either “soft” or “hard” templates can be applied. For sol-gel processes, usually “soft” templating techniques are employed, while “hard” templates are used for high temperature synthesis pathways. In classical templating approaches, the template has the unique role of structure directing agent, in the sense that it is not participating to the chemical formation of the resulting material. This work investigates a new templating pathway to nanostructured materials, where the template is also a reagent in the formation of the final material. This concept is described as “reactive templating” and opens a synthetic path toward materials which cannot be synthesised on a nanometre scale by classical templating approaches. Metal nitrides are such kind of materials. They are usually produced by the conversion of metals or metal oxides in ammonia flow at high temperature (T > 1000°C), which make the application of classical templating techniques difficult. Graphitic carbon nitride, g-C3N4, despite its fundamental and theoretical importance, is probably one of the most promising materials to complement carbon in material science and many efforts are put in the synthesis of this material. A simple polyaddition/elimination reaction path at high temperature (T = 550°C) allows the polymerisation of cyanamide toward graphitic carbon nitride solids. By hard templating, using nanostructured silica or aluminium oxide as nanotemplates, a variety of nanostructured graphitic carbon nitrides such as nanorods, nanotubes, meso- and macroporous powders could be obtained by nanocasting or nanocoating. Due to the special semi-conducting properties of the graphitic carbon nitride matrix, the nanostructured graphitic carbon nitrides show unexpected catalytic activity for the activation of benzene in Friedel-Crafts type reactions, making this material an interesting metal free catalyst. Furthermore, due to the chemical composition of g-C3N4 and the fact that it is totally decomposed at temperatures between 600°C and 800°C even under inert atmosphere, g-C3N4 was shown to be a good nitrogen donor for the synthesis of early transition metal nitrides at high temperatures. Thus using the nanostructured carbon nitrides as “reactive templates” or “nanoreactors”, various metal nitride nanostructures, such as nanoparticles and porous frameworks could be obtained at high temperature. In this approach the carbon nitride nanostructure played both the role of the nitrogen source and of the exotemplate, imprinting its size and shape to the resulting metal nitride nanostructure.
In der vorliegenden Arbeit wurde ein Ansatz verfolgt, die besonderen Eigenschaften der Strukturbildung sequenzdefinierter Peptide mit den vielseitigen Materialeigenschaften synthetischer Blockcopolymere zu kombinieren. Dazu wurde ein synthetisches Polymer kovalent mit einer definierten Peptidsequenz verknüpft. Der Peptidblock (die Organisationseinheit) wurde speziell designt, um später die Strukturbildung des Peptid-Polymerkonjugates induzieren und leiten zu können. Als Organisationsmotiv diente hierbei das aus der Natur bekannte β-Faltblatt Strukturmotiv. Das Peptidsegment wurde in einer festphasengebundenen Synthese aufgebaut. Dabei wurden temporäre Stör-Segmente (Switch-Segmente) in die Peptidsequenz integriert. Diese Segmente unterdrücken die Aggregationstendenz während der Synthese und können durch einen pH-abhängigen Schaltvorgang in das natürliche Peptidrückgrat überführt werden. Zusätzlich zu der verbesserten Ausbeute und Reinheit der entsprechenden Peptide war auf diese Weise eine kontrollierte Aktivierung der Mikrostrukturbildung möglich. Mit Hilfe zwei verschiedener Synthesestrategien (Kupplungs- bzw. Polymerisationsstrategie) wurde ein Satz von definierten Peptid-Polymerkonjugaten mit unterschiedlich großen Polymersegmenten synthetisiert. Diese wurden anschließend im Hinblick auf ihre Strukturbildungseigenschaften in organischen Lösungsmitteln untersucht. Durch mikroskopische Verfahren (AFM, TEM), konnte für alle Konjugate, die Bildung faserartiger Aggregate mit Dimensionen im Nano- bis Mikrometerbereich beobachtet werden. Genauere Untersuchungen zeigten, dass die Peptidsegmente in diesen Faserstrukturen ein β-Faltblatt ausbilden. Dies ist ein deutlicher Hinweis darauf, dass die Strukturbildung der Konjugate tatsächlich durch den Peptidblock gesteuert und kontrolliert wurde.
For the first time stabilizer-free vinylidene fluoride (VDF) polymerizations were carried out in homogeneous phase with supercritical CO₂. Polymerizations were carried out at 140°C, 1500 bar and were initiated with di-tert-butyl peroxide (DTBP). In-line FT-NIR (Fourier Transform- Near Infrared) spectroscopy showed that complete monomer conversion may be obtained. Molecular weights were determined via size-exclusion chromatography (SEC) and polymer end group analysis by 1H-NMR spectroscopy. The number average molecular weights were below 104 g∙mol−1 and polydispersities ranged from 3.1 to 5.7 depending on DTBP and VDF concentration. To allow for isothermal reactions high CO₂ contents ranging from 61 to 83 wt.% were used. The high-temperature, high-pressure conditions were required for homogeneous phase polymerization. These conditions did not alter the amount of defects in VDF chaining. Scanning electron microscopy (SEM) indicated that regular stack-type particles were obtained upon expansion of the homogeneous polymerization mixture. To reduce the required amount of initiator, further VDF polymerizations using chain transfer agents (CTAs) to control molecular weights were carried out in homogeneous phase with supercritical carbon dioxide (scCO₂) at 120 °C and 1500 bar. Using perfluorinated hexyl iodide as CTA, polymers of low polydispersity ranging from 1.5 to 1.2 at the highest iodide concentration of 0.25 mol·L-1 were obtained. Electrospray ionization- mass spectroscopy (ESI-MS) indicates the absence of initiator derived end groups, supporting livingness of the system. The “livingness” is based on the labile C-I bond. However, due to the weakness of the C-I bond perfluorinated hexyl iodide also contributes to initiation. To allow for kinetic analyses of VDF polymerizations the CTA should not contribute to initiation. Therefore, additional CTAs were applied: BrCCl3, C6F13Br and C6F13H. It was found that C6F13H does not contribute to initiation. At 120°C and 1500 bar kp/kt0.5~ 0.64 (L·mol−1·s−1)0.5 was derived. The chain transfer constant (CT) at 120°C has been determined to be 8·10−1, 9·10−2 and 2·10−4 for C6F13I, C6F13Br and C6F13H, respectively. These CT values are associated with the bond energy of the C-X bond. Moreover, the labile C-I bond allows for functionalization of the polymer to triazole end groups applying click reactions. After substitution of the iodide end group by an azide group 1,3 dipolar cycloadditions with alkynes yield polymers with 1,2,3 triazole end groups. Using symmetrical alkynes the reactions may be carried out in the absence of any catalyst. This end-functionalized poly (vinylidene fluoride) (PVDF) has higher thermal stability as compared to the normal PVDF. PVDF samples from homogeneous phase polymerizations in supercritical CO₂ and subsequent expansion to ambient conditions were analyzed with respect to polymer end groups, crystallinity, type of polymorphs and morphology. Upon expansion the polymer was obtained as white powder. Scanning electron microscopy (SEM) showed that DTBP derived polymer end groups led to stack-type particles whereas sponge- or rose-type particles were obtained in case of CTA fragments as end groups. Fourier-Transform Infrared spectroscopy and wide angle X-ray diffraction indicated that the type of polymorph, α or β crystal phase was significantly affected by the type of end group. The content of β-phase material, which is responsible for piezoelectricity of PVDF, is the highest for polymer with DTBP-derived end groups. In addition, the crystallinity of the material, as determined via differential scanning calorimetry is affected by the end groups and polymer molecular weights. For example, crystallinity ranges from around 26 % for DTBP-derived end groups to a maximum of 62 % for end groups originating from perfluorinated hexyl iodide for polymers with Mn ~2200 g·mol–1. Expansion of the homogeneous polymerization mixture results in particle formation by a non-optimized RESS (Rapid Expansion from Supercritical Solution) process. Thus, it was tested how polymer end groups affect the particles size distribution obtained from RESS process under controlled conditions (T = 50°C and P = 200 bar). In all RESS experiments, small primary PVDF with diameters less than 100 nm without the use of liquid solvents, surfactants, or other additives were produced. A strong correlation between particle size and particle size distribution with polymer end groups and molecular weight of the original material was observed. The smallest particles were found for RESS of PVDF with Mn~ 4000 g·mol–1 and PFHI (C6F13I) - derived end groups.
Im Rahmen der Arbeit werden hierarchisch strukturierte Silikakompositfasern präsentiert, deren Bildung ähnlich zu natürlichen Silifizierungsreaktionen verläuft. Als Analoga zu Proteinfilamenten in Silika Morphogeneseorganismen werden selbstorganisierte, funktionale Polyethylenoxid-Peptid-Nanobänder eingesetzt. Mit der Isolierung einheitlicher Nanokompositfasern wird gezeigt, dass die PEO-Peptid-Nanobänder eine starke Bindungsaffinität gegenüber Kieselsäure besitzen, diese aus sehr stark verdünnten Lösungen anreichern und deren Kondensation zu Silikanetzwerken kontrollieren können. In höheren Konzentrationen entstehen durch die peptidgeleitete Silifizierung der PEO-Peptid-Nanobänder spontan makroskopische Kompositfasern mit sechs Hierarchieebenen. Diese verbinden Längen von bis zu 3 cm und Durchmesser von 1-2 mm mit einer definierten Feinstruktur im Submikrometerbereich. Als Resultat der komplexen inneren Struktur und der Kontrolle der Grenzflächen zwischen Nanobändern und Silika wird eine Nanohärte erreicht, die schon ~1/3 der Härte von Bioglasfasern darstellt. Für die Elastizität (reduziertes Eindrückmodul) dagegen konnte durch den relativ hohen Anteil (~40%) an verformbaren, organischen Komponenten ein ~4-mal größer Wert im Vergleich mit Bioglasfasern bestimmt werden. Des Weiteren wird die Prozessierung der makroskopischen Kompositfasern in einem 2D-Plotprozess vorgestellt. Mit Verwendung der PEO-Peptid-Nanobänder als „Tinte“ können Kompositobjekte in beliebigen Formen geplottet werden, deren Linienbreite sowie anisotrope Ausrichtung der Nano- und Submikrometerstrukturelemente direkt mit der Plotgeschwindigkeit korrelieren. Außerdem können die Kompositobjekte als Vorstufen für orientierte, mesoporöse Silikaobjekte verwendet werden. Nachdem Calcinieren werden Silikastrukturen mit einer hohen spezifischen Oberfläche und in Plotrichtung ausgerichteten zylindrischen Poren erhalten. Im Kontrast zu den anorganisch-bioorganischen Kompositfasern sollten unter Ausnutzung ionischer Wechselwirkungen oder Metallkoordination Kompositmaterialien mit anderen mechanischen Eigenschaften dargestellt werden. Es wird gezeigt, dass durch Variationen in der Aminosäuresequenz des Peptidkerns, die Oberflächen der PEO-Peptid-Nanobänder gezielt mit funktionellen Gruppen versehen werden können. Eine gerichtete Vernetzung dieser modifizierten Nanobänder wurde nicht erreicht, dafür könnten die imidazolfunktionalisierten Nanobänder als eindimensionale Protonenleiter, die mit photochromen Gruppen (Spiropyran) funktionalisierten Nanobänder für die Modifizierung von Oberflächenpolaritäten oder für gerichtete Kristallisationsprozesse eingesetzt werden.
Nowadays, reactions on surfaces are attaining great scientific interest because of their diverse applications. Some well known examples are production of ammonia on metal surfaces for fertilizers and reduction of poisonous gases from automobiles using catalytic converters. More recently, also photoinduced reactions at surfaces, useful, \textit{e.g.}, for photocatalysis, were studied in detail. Often, very short laser pulses are used for this purpose. Some of these reactions are occurring on femtosecond (1 fs=$10^{-15}$ s) time scales since the motion of atoms (which leads to bond breaking and new bond formation) belongs to this time range. This thesis investigates the femtosecond laser induced associative photodesorption of hydrogen, H$_2$, and deuterium, D$_2$, from a ruthenium metal surface. Many interesting features of this reaction were explored by experimentalists: (i) a huge isotope effect in the desorption probability of H$_2$ and D$_2$, (ii) the desorption yield increases non-linearly with the applied visible (vis) laser fluence, and (iii) unequal energy partitioning to different degrees of freedom. These peculiarities are due to the fact that an ultrashort vis pulse creates hot electrons in the metal. These hot electrons then transfer energy to adsorbate vibrations which leads to desorption. In fact, adsorbate vibrations are strongly coupled to metal electrons, \textit{i.e.}, through non-adiabatic couplings. This means that, surfaces introduce additional channels for energy exchange which makes the control of surface reactions more difficult than the control of reactions in the gas phase. In fact, the quantum yield of surface photochemical reactions is often notoriously small. One of the goals of the present thesis is to suggest, on the basis of theoretical simulations, strategies to control/enhance the photodesorption yield of H$_2$ and D$_2$ from Ru(0001). For this purpose, we suggest a \textit{hybrid scheme} to control the reaction, where the adsorbate vibrations are initially excited by an infrared (IR) pulse, prior to the vis pulse. Both \textit{adiabatic} and \textit{non-adiabatic} representations for photoinduced desorption problems are employed here. The \textit{adiabatic} representation is realized within the classical picture using Molecular Dynamics (MD) with electronic frictions. In a quantum mechanical description, \textit{non-adiabatic} representations are employed within open-system density matrix theory. The time evolution of the desorption process is studied using a two-mode reduced dimensionality model with one vibrational coordinate and one translational coordinate of the adsorbate. The ground and excited electronic state potentials, and dipole function for the IR excitation are taken from first principles. The IR driven vibrational excitation of adsorbate modes with moderate efficiency is achieved by (modified) $\pi$-pulses or/and optimal control theory. The fluence dependence of the desorption reaction is computed by including the electronic temperature of the metal calculated from the two-temperature model. Here, our theoretical results show a good agreement with experimental and previous theoretical findings. We then employed the IR+vis strategy in both models. Here, we found that vibrational excitation indeed promotes the desorption of hydrogen and deuterium. To summarize, we conclude that photocontrol of this surface reaction can be achieved by our IR+vis scheme.
The three major biopolymers, proteins, nucleic acids and glycoconjugates are mainly responsible for the information transfer, which is a fundamental process of life. The biological importance of proteins and nucleic acids are well explored and oligosaccharides in the form of glycoconjugates have gained importance recently. The β-(1→4) linked N-acetylglucosamine (GlcNAc) moiety is a frequently occurring structural unit in various naturally and biologically important oligosaccharides and related conjugates. Chitin which is the most abundant polymer of GlcNAc is widely distributed in nature whereas the related polysaccharide chitosan (polymer of GlcN and GlcNAc) occurs in certain fungi. Chitooligosaccharides of mixed acetylation patterns are of interest for the determination of the substrate specificities and mechanism of chitinases. In this report, we describe the chemical synthesis of three chitotetraoses namely GlcNAc-GlcN-GlcNAc-GlcN, GlcN-GlcNAc-GlcNAc-GlcN and GlcN-GlcN-GlcNAc-GlcNAc. Benzyloxycarbonyl (Z) and p-nitrobenzyloxycarbonyl (PNZ) were used for the amino functionality due to their ability to form the β-linkage during the glycosylation reactions through neighboring group participation and the trichloroacetimidate approach was utilized for the donor. Monomeric, dimeric acceptors and donors have been prepared by utilizing the Z and PNZ groups and coupling between the appropriate donor and acceptors in the presence of Lewis acid yielded the protected tetrasaccharides. Finally cleavage of PNZ followed by reacetylation and the deblocking of other protecting groups afforded the N,N’-diacetyl chitotetraoses in good yield. Successful syntheses for the protected diacetyl chitotetraoses by solid phase synthesis have also been described.
Funktionalisierte Poly(2-oxazoline) als neue Materialien stellen sowohl unter strukturellen Gesichtspunkten als auch im Hinblick auf potentielle Anwendungen eine interessante Polymerklasse dar. Die Ausbildung von hierarchischen Strukturen mit Poly(2-oxazolinen) über intermolekulare Wasserstoffbrückenbindungen ist hierbei ein bisher nicht beachteter Aspekt. Über einen bioinspirierten Ansatz sollten gezielt funktionelle Gruppen, die für einen hierarchischen Aufbau, z.B. in Proteinen, verantwortlich sind, in vereinfachter Weise auf die synthetische Substanzklasse der Poly(2-oxazoline) übertragen werden. Die vorliegende Arbeit beschäftigt sich mit der modularen Synthese neuer, funktionalisierter Poly(2-oxazolin) Homo- und Copolymere. Ausgehend von der Synthese von 2-(3-Butenyl)-2-oxazolin wurden definierte Präpolymere in einer kationischen Isomerisierungspolymerisation unter kontrolliert/„lebenden“ Bedingungen hergestellt. In einer anschließenden „Thio-Click“ (Thiol-En-Reaktion) Modifizierungsreaktion wurden die gewünschten funktionellen Gruppen quantitativ eingeführt. Hydroxylierte Poly(2-oxazoline) wurden hinsichtlich ihres Aggregationsverhaltens in Wasser untersucht. Bereits die jeweiligen Homopolymere bildeten aufgrund von intermolekularen Wasserstoffbrückenbindungen supramolekulare tubuläre Nanofasern aus. Durch Einsatz verschiedener analytischer Methoden konnte die innere Struktur der Nanoröhren beschrieben und ein entsprechendes Modell aufgestellt werden. Die dargestellten funktionellen Poly(2-oxazoline) wurden hinsichtlich ihrer Anwendung als potentielle, synthetische „antifreeze additives“ untersucht. Alle Polymere besitzen eine ausgeprägte Tendenz zur Nukleierung von Wasser und führen daher zu signifikanten Änderungen der Eismorphologie. Des weiteren wurde ein carboxyliertes Derivat zur biomimetischen Mineralisation von Kalziumcarbonat eingesetzt und nach phänomenologischen Gesichtspunkten untersucht.
Nanostructured materials are materials consisting of nanoparticulate building blocks on the scale of nanometers (i.e. 10-9 m). Composition, crystallinity and morphology can enhance or even induce new properties of the materials, which are desirable for todays and future technological applications. In this work, we have shown new strategies to synthesise metal oxide and metal nitride nanomaterials. The first part of the work deals with the study of nonaqueous synthesis of metal oxide nanoparticles. We succeeded in the synthesis of In2O3 nanopartcles where we could clearly influence the morphology by varying the type of the precursors and the solvents; of ZnO mesocrystals by using acetonitrile as a solvent; of transition metal oxides (Nb2O5, Ta2O5 and HfO2) that are particularly hard to obtain on the nanoscale and other technologically important materials. Solvothermal synthesis however is not restricted to formation of oxide materials only. In the second part we show examples of nonaqueous, solvothermal reactions of metal nitrides, but the main focus lies on the investigation of the influence of different morphologies of metal oxide precursors on the formation of the metal nitride nanoparticles. In spite of various reports, the number and variety of nanocrystalline metal nitrides is marginally small by comparison to metal oxides; hence preformed metal oxides as precursors for the preparation of metal nitrides are a logical choice. By reacting oxide nanoparticles with cyanamide, urea or melamine, at temperatures of 800 to 900 °C under nitrogen flow metal nitrides could be obtained. We studied in detail the influence of the starting material and realized that size, crystallinity, type of nitrogen source and temperature play the most important role. We have managed to propose and verify a dissolution-recrystallisation model as the formation mechanism. Furthermore we could show that the initial morphology of the oxides could be retained when ammonia flow was used instead.
4-Phenylphenoxazinones were isolated after biomimetic oxidation, using diphenoloxidases of insect cuticle, mushroom tyrosinase, or after autoxidation of N-acetyldopamine (Image ) in the presence of β-alanine, β-alanine methyl ester or N-acetyl-L-lysine. They are formed presumably by addition of 2-aminoalkyl-5-alkylphenols to the o-quinone of biphenyltetrol which, in turn, arises from oxidative coupling of. The structures of present the first examples for the assembly of reasonably stable intermediates in the rather complex process of chemical modifications of aliphatic amino acid residues by o-quinones.
Contents: 1. Discotic Liquid Crystals 2. Monolayers and Langmuir-Blodgett Multilayers 3. Theoretical Considerations on the Molecular Packing of Discotic LCs in Monolayers and Multilayers 4. Spreading Experiments with Discotic LCs 5. LB-Multilayers of Discotic LCs 6. Polymeric Discotic LCs 7. Summary
Mixed monolayers and Langmuir-Blodgett multilayers of functional low molecular weight guest compounds, especially nonlinear optical (NLO) dyes, within the matrix of an amphotropic spacer polymer have been prepared. The polymer matrix enabled the transfer of guest compounds not capable of self-organizing at the air-water interface by themselves. The structure of the LB multilayers and the transfer process were studied by small angle X-ray scattering and UV-visible spectroscopy. Good NLO coefficients were found in the mixed films.
In dieser Arbeit wird durch Modellrechnungen gezeigt, wie die Stickstoffinversion in Azacyclen als molekularer Schalter genutzt werden könnte. Hierzu werden ein Fluorazetidin- und ein Fluorazacyclopentanderviat quantenchemisch untersucht. Das letztere Molekül wird auch quantendynamisch untersucht. Jedes der beiden Moleküle besitzt zwei stabile Konformationen. Es wird gezeigt, dass das Azabicyclopentanderivat von der einen Konformation mittels zweier linear polarisierter IR-Laserpulse durch sogenanntes “ladder climbing” in die andere überführt werden kann.
For more than 70 years, understanding of the mechanism of particle nucleation in emulsion polymerization has been one of the most challenging issues in heterophase polymerization research. Within this work a comprehensive experimental study of particle nucleation in emulsion polymerization of styrene at 70 °C and variety of conditions has been performed. To follow the onset of nucleation, on-line conductivity measurements were applied. This technique is highly sensitive to the mobility of conducting species and hence, it can be employed to follow aggregation processes leading to particle formation. On the other hand, by recording the optical transmission (turbidity) of the reaction mixture particle growth was followed. Complementary to the on-line investigations, off-line characterizations of the particle morphology and the molecular weight have been performed. The aim was to achieve a better insight in the processes taking place after starting the reaction via particle nucleation until formation of colloidally stable latex particles. With this experimental protocol the initial period of styrene emulsion polymerization in the absence as well as in the presence of various surfactants (concentrations above and below the critical micellization concentration) and also in the presence of seed particles has been investigated. Ionic and non-ionic initiators (hydrophilic and hydrophobic types) have been applied to start the polymerizations. Following the above algorithm, experimental evidence has been obtained showing the possibility of performing surfactant-free emulsion polymerization of styrene with oil-soluble initiators. The duration of the pre-nucleation period (that is the time between starting the polymerization and nucleation) can be precisely adjusted with the initiator hydrophobicity, the equilibration time of styrene in water, and the surfactant concentration. Spontaneous emulsification of monomer in water, as soon as both phases are brought into contact, is a key factor to explain the experimental results. The equilibration time of monomer in water as well as the type and concentration of other materials in water (surfactants, seed particles, etc.) control the formation rate and the size of the emulsified droplets and thus, have a strong influence on the particle nucleation and the particle morphology. One of the main tasks was to investigate the effect of surfactant molecules and especially micelles on the nucleation mechanism. Experimental results revealed that in the presence of emulsifier micelles the conductivity pattern does not change essentially. This means that the presence of emulsifiers does not change the mechanism of particle formation qualitatively. However, surfactants assist in the nucleation process as they lower the activation free energy of particle formation. Contrary, seed particles influence particle nucleation, substantially. In the presence of seed particles above a critical volume fraction the formation of new particles can be suppressed. However, micelles and seed particles as absorbers exhibit a common behavior under conditions where monomer equilibration is not allowed. Results prove that the nucleation mechanism comprises the initiation of water soluble oligomers in the aqueous phase followed by their aggregation. The process is heterogeneous in nature due to the presence of monomer droplets.
Cationic and zwitterionic polymerizable surfactants bearing tri- and tetraethyleneglycol spacer groups between the polymerizable moiety and the surfactant structure were prepared and polymerized. Monomers and polymers were investigated with respect to their aggregation behavior in aqueous systems and compared to analogous monomers and polymers lacking spacer groups. In the case of the monomeric surfactants, the spacer groups depress both the Kraffttemperature and the critical micelle concentration. the area occupied per molecule at the air-water interface is substantially enlarged by the spacers, whereas the depression of surface tension is nearly constant. Although the monomers with and without spacers are true surfactants, all the polymers are water-insoluble, but form monomolecular layers at the air-water interface. In analogy to the monomer behavior, the incorporation of the spacer groups increases the area occupied per repeat unit at the air-water interface substantially, but hardly affects the surface activity.