Amorphous calcium carbonate(ACC) is a wide spread biological material found in many organisms, such as sea Urchins and mollusks, where it serves as either a precursor phase for the crystalline biominerals or is stabilized and used in the amorphous state. As ACC readily crystallizes, stabilizers such as anions, cations or macromolecules are often present to avoid or delay unwanted crystallization. Furthermore, additives often control the properties of the materials to suit the specific function needed for the organism. E.g. cystoliths in leaves that scatter light to optimize energy uptake from the sun or calcite/aragonite crystals used in protective shells in mussels and gastropods. Lifetime of the amorphous phase is controlled by the kinetic stability against crystallization. This has often been linked to water which plays a role in the mobility of ions and hence the probability of forming crystalline nuclei to initiate crystallization. However, it is unclear how the water molecules are incorporated within the amorphous phase, either as liquid confined in pores, as structural water binding to the ions or as a mixture of both. It is also unclear how this is perturbed when additives are added, especially Mg2+, one the most common additives found in biogenic samples. Mg2+ are expected to have a strong influence on the water incorporated into ACC, given the high energy barrier to dehydration of magnesium ions compared to calcium ions in solution.
During the last 10-15 years, there has been a large effort to understand the local environment of the ions/molecules and how this affects the properties of the amorphous phase. But only a few aspects of the structure have so far been well-described in literature. The reason for this is partly caused by the low stability of ACC if exposed to air, where it tends to crystallize within minutes and by the limited quantities of ACC produced in traditional synthesis routes. A further obstacle has been the difficulty in modeling the local structure based on experimental data. To solve the problem of stability and sample size, a few studies have used stabilizers such as Mg2+ or OH- and severely dehydrated samples so as to stabilize the amorphous state, allowing for combined neutron and x-ray analysis to be performed. However, so far, a clear description of the local environments of water present in the structure has not been reported.
In this study we show that ACC can be synthesized without any stabilizing additives in quantities necessary for neutron measurements and that accurate models can be derived with the help of empirical-potential structural refinement. These analyses have shown that there is a wide range of local environments for all of the components in the system suggesting that the amorphous phase is highly inhomogeneous, without any phase separation between ions and water. We also showed that the water in ACC is mainly structural and that there is no confined or liquid-like water present in the system. Analysis of amorphous magnesium carbonate also showed that there is a large difference in the local structure of the two cations and that Mg2+ surprisingly interacts with significantly less water molecules then Ca2+ despite the higher dehydration energy. All in all, this shows that the role of water molecules as a structural component of ACC, with a strong binding to cat- and anions probably retard or prevents the crystallization of the amorphous phase.
Die vorliegende Arbeit behandelt die Synthese und Charakterisierung von funktionalisierten Alkydharzen und die photoinduzierte Polymerisation dieser unter Einsatz einer Quecksilberdampflampe oder einer UV LED mit unterschiedlicher Lichtintensität. Der Fokus dieser Arbeit bestand in der gezielten Substitution der internalen Doppelbindungen der Fettsäureester durch reaktivere Gruppen, wie Acrylate oder Methacrylate, welche für Alkydharze in dieser Form so in der Literatur nicht beschrieben sind. Untersuchungen des Polymerisationsverhaltens dieser funktionalisierten Harze wurden mit der Photo DSC durchgeführt, wobei Bis – (4 – methoxybenzoyl) diethylgermanium als Photoinitiator diente. Die Ergebnisse haben gezeigt, dass die Harze radikalisch polymerisiert werden können und eine geringere Abhängigkeit von der Umgebungsatmosphäre (Luftsauerstoff bzw. Stickstoff) vorliegt. Dies ist so in der Literatur für funktionalisierte Alkydharze nicht bekannt. Abmischungen von unterschiedlichen Monomeren und funktionalisierten Harzen bewirkten eine Steigerung der Viskosität sowie eine Verringerung der Sauerstoffinhibierung im Zuge der photoinduzierten Polymerisation unter Luftsauerstoff für die Quecksilberdampflampe und der UV LED.
Zur Untersuchung der sauerstoffinhibierenden Wirkung der Harze sind Synthesen unterschiedlicher, funktionalisierter Ölsäuremethylester als Modellsubstanzen durchgeführt worden. Ein verbessertes Polymerisationsverhalten und eine geringe Abhängigkeit von der Umgebungsatmosphäre konnte für die Modelle nachgewiesen werden. Zur Aufklärung des verbesserten Polymerisationsverhaltens sind gezielt Substituenten (Imidazol, Brom, Alkohol, Acetat) in den funktionalisierten Ölsäuremethylester eingebaut worden, um den Einfluss dieser aufzuzeigen. Im Rahmen dieser Synthesen sind neuartige Strukturen synthetisiert worden, welche so in der Literatur nicht beschrieben sind. Die Gegenüberstellung der Polymerisationszeit, der Umsatz der (Meth-)Acrylatgruppen sowie die Zeit zum Erreichen der maximalen Polymerisationsgeschwindigkeit unter Verwendung von unterschiedlichen UV Lichtquellen hat einen Einfluss der Substituenten auf das Polymerisationsverhalten gezeigt.
Various ways of preparing enantiomerically pure 2-amino[6]helicene derivatives were explored. Ni(0) mediated cyclotrimerization of enantiopure triynes provided (M)- and (P)-7,8-bis(p-tolyl)hexahelicene-2-amine in >99% ee as well as its benzoderivative in >99% ee. The stereocontrol was found to be inefficient for a 2- aminobenzo[6]helicene congener with an embedded five-membered ring. Helically chiral imidazolium salts bearing one or two helicene moieties have been synthesized and applied in enantioselective [2+2+2] cyclotrimerization catalyzed by an in situ formed Ni(0)-NHC complex. The synthesis of the first helically chiral Pd- and Ru-NHC complexes and their application in enantioselective catalysis was demonstrated. The latter shows promising results in enantioselective olefin metathesis reactions. A mechanistic proposal for asymmetric ring closing metathesis is provided.
The aim of this doctoral thesis was to establish a technique for the analysis of biomolecules with infrared matrix-assisted laser dispersion (IR-MALDI) ion mobility (IM) spectrometry. The main components of the work were the characterization of the IR-MALDI process, the development and characterization of different ion mobility spectrometers, the use of IR-MALDI-IM spectrometry as a robust, standalone spectrometer and the development of a collision cross-section estimation approach for peptides based on molecular dynamics and thermodynamic reweighting.
First, the IR-MALDI source was studied with atmospheric pressure ion mobility spectrometry and shadowgraphy. It consisted of a metal capillary, at the tip of which a self-renewing droplet of analyte solution was met by an IR laser beam. A relationship between peak shape, ion desolvation, diffusion and extraction pulse delay time (pulse delay) was established. First order desolvation kinetics were observed and related to peak broadening by diffusion, both influenced by the pulse delay. The transport mechanisms in IR-MALDI were then studied by relating different laser impact positions on the droplet surface to the corresponding ion mobility spectra. Two different transport mechanisms were determined: phase explosion due to the laser pulse and electrical transport due to delayed ion extraction. The velocity of the ions stemming from the phase explosion was then measured by ion mobility and shadowgraphy at different time scales and distances from the source capillary, showing an initially very high but rapidly decaying velocity. Finally, the anatomy of the dispersion plume was observed in detail with shadowgraphy and general conclusions over the process were drawn.
Understanding the IR-MALDI process enabled the optimization of the different IM spectrometers at atmospheric and reduced pressure (AP and RP, respectively). At reduced pressure, both an AP and an RP IR-MALDI source were used. The influence of the pulsed ion extraction parameters (pulse delay, width and amplitude) on peak shape, resolution and area was systematically studied in both AP and RP IM spectrometers and discussed in the context of the IR-MALDI process. Under RP conditions, the influence of the closing field and of the pressure was also examined for both AP and RP sources. For the AP ionization RP IM spectrometer, the influence of the inlet field (IF) in the source region was also examined. All of these studies led to the determination of the optimal analytical parameters as well as to a better understanding of the initial ion cloud anatomy.
The analytical performance of the spectrometer was then studied. Limits of detection (LOD) and linear ranges were determined under static and pulsed ion injection conditions and interpreted in the context of the IR-MALDI mechanism. Applications in the separation of simple mixtures were also illustrated, demonstrating good isomer separation capabilities and the advantages of singly charged peaks. The possibility to couple high performance liquid chromatography (HPLC) to IR-MALDI-IM spectrometry was also demonstrated. Finally, the reduced pressure spectrometer was used to study the effect of high reduced field strength on the mobility of polyatomic ions in polyatomic gases.
The last focus point was on the study of peptide ions. A dataset obtained with electrospray IM spectrometry was characterized and used for the calibration of a collision cross-section (CCS) determination method based on molecular dynamics (MD) simulations at high temperature. Instead of producing candidate structures which are evaluated one by one, this semi-automated method uses the simulation as a whole to determine a single average collision cross-section value by reweighting the CCS of a few representative structures. The method was compared to the intrinsic size parameter (ISP) method and to experimental results. Additional MD data obtained from the simulations was also used to further analyze the peptides and understand the experimental results, an advantage with regard to the ISP method. Finally, the CCS of peptide ions analyzed by IR-MALDI were also evaluated with both ISP and MD methods and the results compared to experiment, resulting in a first validation of the MD method. Thus, this thesis brings together the soft ionization technique that is IR-MALDI, which produces mostly singly charged peaks, with ion mobility spectrometry, which can distinguish between isomers, and a collision cross-section determination method which also provides structural information on the analyte at hand.
Synthesis of artificial building blocks for sortase-mediated ligation and their enzymatic linkage
(2018)
The enzyme Sortase A catalyzes the formation of a peptide bond between the recognition sequence LPXTG and an oligoglycine. While manifold ligations between proteins and various biomolecules, proteins and small synthetic molecules as well as proteins and surfaces have been reported, the aim of this thesis was to investigate the sortase-catalyzed linkage between artificial building blocks. Hence, this could pave the way for the use of sortase A for tasks from a chemical point of view and maybe even materials science.
For the proof of concept, the studied systems were kept as simple as possible at first by choosing easily accessible silica NPs and commercially available polymers. These building blocks were functionalized with peptide motifs for sortase-mediated ligation. Silica nanoparticles were synthesized with diameters of 60 and 200 nm and surface modified with C=C functionalities. Then, peptides bearing a terminal cysteine were covalently linked by means of a thiol-ene reaction. 60 nm SiO2 NPs were functionalized with pentaglycines, while peptides with LPETG motif were linked to 200 nm silica particles. Polyethyleneglycol (PEG) and poly(N isopropylacrylamide) (PNIPAM) were likewise functionalized with peptides by thiol-ene reaction between cysteine residues and C=C units in the polymer end groups. Hence, G5-PEG and PNIPAM-LPETG conjugates were obtained. With this set of building blocks, NP–polymer hybrids, NP–NP, and polymer–polymer structures were generated by sortase-mediated ligation and the product formation shown by transmission electron microscopy, MALDI-ToF mass spectrometry and dynamic light scatting, among others. Thus, the linkage of these artificial building blocks by the enzyme sortase A could be demonstrated.
However, when using commercially available polymers, the purification of the polymer–peptide conjugates was impossible and resulted in a mixture containing unmodified polymer. Therefore, strategies were developed for the own synthesis of pure peptide-polymer and polymer-peptide conjugates as building blocks for sortase-mediated ligation. The designed routes are based on preparing polymer blocks via RAFT polymerization from CTAs that are attached to N- or C-terminus, respectively, of a peptide. GG-PNIPAM was synthesized through attachment of a suitable RAFT CTA to Fmoc-GG in an esterification reaction, followed by polymerization of NIPAM and cleavage of the Fmoc protection group. Furthermore, several peptides were synthesized by solid-phase peptide synthesis. The linkage of a RAFT CTA (or
polymerization initiator) to the N-terminus of a peptide can be conducted in an automated fashion as last step in a peptide synthesizer. The synthesis of such a conjugate couldn’t be realized in the time frame of this thesis, but many promising strategies exist to continue this strategy using different coupling reagents. Such polymer building blocks can be used to synthesize protein-polymer conjugates catalyzed by sortase A and the approach can be carried on to the synthesis of block copolymers by using polymer blocks with peptide motifs on both ends.
Although the proof of concept demonstrated in this thesis only shows examples that can be also synthesized by exclusively chemical techniques, a toolbox of such building blocks will enable the future formation of new materials and pave the way for the application of enzymes in materials science. In addition to nanoparticle systems and block copolymers, this also includes combination with protein-based building blocks to form hybrid materials. Hence, sortase could become an enzymatic tool that complements established chemical linking technologies and provides specific peptide motifs that are orthogonal to all existing chemical functional groups.
Innerhalb dieser Doktorarbeit wurde eine neuartige Mikromanipulationstechnik für die lokale Flüssigkeitsabgabe am komplexen Drüsengewebe der Schabe P. americana charakterisiert und für die damit verbundene gezielte Manipulation von einzelnen Zellen in einem Zellkomplex (Gewebe) angewandt. Bei dieser Mikromanipulationstechnik handelt es sich um die seit 2009 bekannte nanofluidische Rasterkraftmikroskopie (FluidFM = fluidic force microscopy). Dabei werden sehr kleine mikrokanälige Rasterkraftspitzen bzw. Mikro-/Nanopipetten mit einer Öffnung zwischen 300 nm und 2 µm verwendet, mit denen es möglich ist, sehr kleine Volumina im Pikoliter- bis Femtoliter-Bereich (10-12 L – 10-15 L) gezielt und ortsgenau abzugeben. Das Ziel dieser Arbeit war die Analyse zellulärer Prozesse, wie z. B. Zell-Zell-Kommunikation oder Signalweiterleitung, zwischen benachbarten Zellen unter Zuhilfenahme der Fluoreszenzmikroskopie. Mit dieser Methode können die Zellen und ihre Bestandteile mittels vorheriger Farbstoffbeladung unter einem Mikroskop mit hohem Kontrast optisch dargestellt werden. Mit Hilfe der Fluoreszenzmikroskopie sollten schlussendlich die zellulären Reaktionen innerhalb des Gewebes nach der lokalen Manipulation visualisiert werden.
Zunächst wurde die Anwendung des Systems an Luft und wässriger Umgebung beschrieben. In diesem Zusammenhang wurde eine Reinigungs- und Beladungsmethode entwickelt, mit der es möglich war, die kostspieligen Mikro-/Nanopipetten zu reinigen und anschließend mehrmals wiederzuverwenden. Hierzu wurde eine alternative Methode getestet, mit der das Diffusionsverhalten von Farbstoffmolekülen in unterschiedlichen Medien untersucht werden kann. Des Weiteren wurden die Systemparameter optimiert, welche nötig sind, um zwischen der Probenoberfläche und der Pipette einen guten Pipettenöffnungs-abschluss zu erhalten. Dieser Abschluss ist essentiell, damit die abgegebene Flüssigkeit ausschließlich in der Abgaberegion mit der Probe wechselwirkt und die darauffolgenden Reaktionen nur innerhalb des Gewebes erfolgen, da ansonsten die Zell-Zell-Signalweiterleitung zwischen den Zellen nicht eindeutig nachvollzogen werden kann. Diese interzelluläre Kommunikation wurde anhand zweier sekundärer Botenstoffe (Ca2+ und NO) untersucht. Hierbei war es möglich einzelne lokale Reaktionen zu detektieren, welche sich über weitere Zellen ausbreiteten. Schlussendlich wurde die Fertigung einer speziellen Injektionspipette beschrieben, welche an zwei biologischen Systemen getestet wurde.
Health effects, attributed to the environmental pollution resulted from using solvents such as benzene, are relatively unexplored among petroleum workers, personal use, and laboratory researchers. Solvents can cause various health problems, such as neurotoxicity, immunotoxicity, and carcinogenicity. As such it can be absorbed via epidermal or respiratory into the human body resulting in interacting with molecules that are responsible for biochemical and physiological processes of the brain.
Owing to the ever-growing demand for finding a solution, an Ionic liquid can use as an alternative solvent. Ionic liquids are salts in a liquid state at low temperature (below 100 C), or even at room temperature. Ionic liquids impart a unique architectural platform, which has been interesting because of their unusual properties that can be tuned by simple ways such as mixing two ionic liquids.
Ionic liquids not only used as reaction solvents but they became a key developing for novel applications based on their thermal stability, electric conductivity with very low vapor pressure in contrast to the conventional solvents.
In this study, ionic liquids were used as a solvent and reactant at the same time for the novel nanomaterials synthesis for different applications including solar cells, gas sensors, and water splitting.
The field of ionic liquids continues to grow, and become one of the most important branches of science. It appears to be at a point where research and industry can work together in a new way of thinking for green chemistry and sustainable production.
New bio-based polymers
(2018)
Redox-responsive polymers, such as poly(disulfide)s, are a versatile class of polymers with potential applications including gene- and drug-carrier systems. Their degradability under reductive conditions allows for a controlled response to the different redox states that are present throughout the body. Poly(disulfide)s are typically synthesized by step growth polymerizations. Step growth polymerizations, however, may suffer from low conversions and therefore low molar masses, limiting potential applications. The purpose of this thesis was therefore to find and investigate new synthetic routes towards the synthesis of amino acid-based poly(disulfide)s.
The different routes in this thesis include entropy-driven ring opening polymerizations of novel macrocyclic monomers, derived from cystine derivatives. These monomers were obtained with overall yields of up to 77% and were analyzed by mass spectrometry as well as by 1D and 2D NMR spectroscopy. The kinetics of the entropy-driven ring-opening metathesis polymerization (ED-ROMP) were thoroughly investigated in dependence of temperature, monomer concentration, and catalyst concentration. The polymerization was optimized to yield poly(disulfide)s with weight average molar masses of up to 80 kDa and conversions of ~80%, at the thermodynamic equilibrium. Additionally, an alternative metal free polymerization, namely the entropy-driven ring-opening disulfide metathesis polymerization (ED-RODiMP) was established for the polymerization of the macrocyclic monomers. The effect of different solvents, concentrations and catalyst loadings on the polymerization process and its kinetics were studied. Polymers with very high weight average molar masses of up to 177 kDa were obtained. Moreover, various post-polymerization reactions were successfully performed.
This work provides the first example of the homopolymerization of endo-cyclic disulfides by ED-ROMP and the first substantial study into the kinetics of the ED-RODiMP process.
Time-dependent correlation function based methods to study optical spectroscopy involving electronic transitions can be traced back to the work of Heller and coworkers. This intuitive methodology can be expected to be computationally efficient and is applied in the current work to study the vibronic absorption, emission, and resonance Raman spectra of selected organic molecules. Besides, the "non-standard" application of this approach to photoionization processes is also explored. The application section consists of four chapters as described below.
In Chapter 4, the molar absorptivities and vibronic absorption/emission spectra of perylene and several of its N-substituted derivatives are investigated. By systematically varying the number and position of N atoms, it is shown that the presence of nitrogen heteroatoms has a negligible effect on the molecular structure and geometric distortions upon electronic transitions, while spectral properties are more sensitive: In particular the number of N atoms is important while their position is less decisive. Thus, N-substitution can be used to fine-tune the optical properties of perylene-based molecules.
In Chapter 5, the same methods are applied to study the vibronic absorption/emission and resonance Raman spectra of a newly synthesized donor-acceptor type molecule. The simulated absorption/emission spectra agree fairly well with experimental data, with discrepancies being attributed to solvent effects. Possible modes which may dominate the fine-structure in the vibronic spectra are proposed by analyzing the correlation function with the aid of Raman and resonance Raman spectra.
In the next two chapters, besides the above types of spectra, the methods are extended to study photoelectron spectra of several small diamondoid-related systems (molecules, radicals, and cations). Comparison of the photoelectron spectra with available experimental data suggests that the correlation function based approach can describe ionization processes reasonably well. Some of these systems, cationic species in particular, exhibit somewhat peculiar optical behavior, which presents them as possible candidates for functional devices.
Correlation function based methods in a more general sense can be very versatile. In fact, besides the above radiative processes, formulas for non-radiative processes such as internal conversion have been derived in literature. Further implementation of the available methods is among our next goals.
Synthesis, assembly and thermo-responsivity of polymer-functionalized magnetic cobalt nanoparticles
(2018)
This thesis mainly covers the synthesis, surface modification, magnetic-field-induced assembly and thermo-responsive functionalization of superparamagnetic Co NPs initially stabilized by hydrophobic small molecules oleic acid (OA) and trioctylphosphine oxide (TOPO), as well as the synthesis of both superparamagnetic and ferromagnetic Co NPs by using end-functionalized-polystyrene as stabilizer.
Co NPs, due to their excellent magnetic and catalytic properties, have great potential application in various fields, such as ferrofluids, catalysis, and magnetic resonance imaging (MRI). Superparamagnetic Co NPs are especially interesting, since they exhibit zero coercivity. They get magnetized in an external magnetic field and reach their saturation magnetization rapidly, but no magnetic moment remains after removal of the applied magnetic field. Therefore, they do not agglomerate in the body when they are used in biomedical applications. Normally, decomposition of metallic precursors at high temperature is one of the most important methods in preparation of monodisperse magnetic NPs, providing tunability in size and shape. Hydrophobic ligands like OA, TOPO and oleylamine are often used to both control the growth of NPs and protect them from agglomeration. The as-prepared magnetic NPs can be used in biological applications as long as they are transferred into water. Moreover, their supercrystal assemblies have the potential for high density data storage and electronic devices. In addition to small molecules, polymers can also be used as surfactants for the synthesis of ferromagnetic and superparamagnetic NPs by changing the reaction conditions. Therefore, chapter 2 gives an overview on the basic concept of synthesis, surface modification and self-assembly of magnetic nanoparticles. Various examples were used to illustrate the recent work.
The hydrophobic Co NPs synthesized with small molecules as surfactants limit their biological applications, which require a hydrophilic or aqueous environment. Surface modification (e.g., ligand exchange) is a general idea for either phase transition or surface-functionalization. Therefore, in chapter 3, a ligand exchange process was conducted to functionalize the surface of Co NPs. PNIPAM is one of the most popular smart polymers and its lower critical solution temperature (LCST) is around 32 °C, with a reversible change in the conformation structure between hydrophobic and hydrophilic. The novel nanocomposites of superparamagnetic Co NPs and thermo-responsive PNIPAM are of great interest. Thus, well-defined superparamagnetic Co NPs were firstly synthesized through the thermolysis of cobalt carbonyl by using OA and TOPO as surfactants. A functional ATRP initiator, containing an amine (as anchoring group) and a 2-bromopropionate group (SI-ATRP initiator), was used to replace the original ligands. This process is rapid and facial for efficient surface functionalization and afterwards the Co NPs can be dispersed into polar solvent DMF without aggregation. FT-IR spectroscopy showed that the TOPO was completely replaced, but a small amount of OA remained on the surface. A TGA measurement allowed the calculation of the grafting density of the initiator as around 3.2 initiator/nm2. Then, the surface-initiated ATRP was conducted for the polymerization of NIPAM on the surface of Co NPs and rendered the nanocomposites water-dispersible. A temperature-dependent dynamic light scattering study showed the aggregation behavior of PNIPAM-coated Co NPs upon heating and this process was proven to be reversible. The combination of superparamagnetic and thermo-responsive properties in these hybrid nanoparticles is promising for future applications e.g. in biomedicine.
In chapter 4, the magnetic-field-induced assembly of superparamagnetic cobalt nanoparticles both on solid substrates and at liquid-air interface was investigated. OA- and TOPO-coated Co NPs were synthesized via the thermolysis of cobalt carbonyl and dispersed into either hexane or toluene. The Co NP dispersion was dropped onto substrates (e.g., TEM grid, silicon wafer) and at liquid-air (water-air or ethylene glycol-air) interface. Due to the attractive dipolar interaction, 1-D chains formed in the presence of an external magnetic field. It is known that the concentration and the strength of the magnetic field can affect the assembly behavior of superparamagnetic Co NPs. Therefore, the influence of these two parameters on the morphology of the assemblies was studied. The formed 1-D chains were shorter and flexible at either lower concentration of the Co NP dispersion or lower strength of the external magnetic field due to thermal fluctuation. However, by increasing either the concentration of the NP dispersion or the strength of the applied magnetic field, these chains became longer, thicker and straighter. The reason could be that a high concentration led to a high fraction of short dipolar chains, and their interaction resulted in longer and thicker chains under applied magnetic field. On the other hand, when the magnetic field increased, the induced moments of the magnetic nanoparticles became larger, which dominated over the thermal fluctuation. Thus, the formed short chains connected to each other and grew in length. Thicker chains were also observed through chain-chain interaction. Furthermore, the induced moments of the NPs tended to direct into one direction with increased magnetic field, thus the chains were straighter. In comparison between the assembly on substrates, at water-air interface and at ethylene glycol-air interface, the assembly of Co NPs in hexane dispersion at ethylene glycol-air interface showed the most regular and homogeneous chain structures due to the better spreading of the dispersion on ethylene glycol subphase than on water subphase and substrates. The magnetic-field-induced assembly of superparamagnetic nanoparticles could provide a powerful approach for applications in data storage and electronic devices.
Chapter 5 presented the synthesis of superparamagnetic and ferromagnetic cobalt nanoparticles through a dual-stage thermolysis of cobalt carbonyl (Co2(CO)8) by using polystyrene as surfactant. The amine end-functionalized polystyrene surfactants with different molecular weight were prepared via atom transfer radical polymerization technique. The molecular weight determination of polystyrene was conducted by gel permeation chromatography (GPC) and matrix-assisted laser desorption/ionization time-of-flight (MALDI-ToF) mass spectrometry techniques. The results showed that, when the molecular weight distribution is low (Mw/Mn < 1.2), the measurement by GPC and MALDI-ToF MS provided nearly similar results. For example, the molecular weight of 10600 Da was obtained by MALDI-ToF MS, while GPC gave 10500 g/mol (Mw/Mn = 1.17). However, if the polymer is poly distributed, MALDI-ToF MS cannot provide an accurate value. This was exemplified for a polymer with a molecular weight of 3130 Da measured by MALDI-TOF MS, while GPC showed 2300 g/mol (Mw/Mn = 1.38). The size, size distribution and magnetic properties of the hybrid particles were different by changing either the molecular weight or concentration of the polymer surfactants. The analysis from TEM characterization showed that the size of cobalt nanoparticles stabilized with polystyrene of lower molecular weight (Mn = 2300 g/mol) varied from 12–22 nm, while the size with middle (Mn = 4500 g/mol) and higher molecular weight (Mn = 10500 g/mol) of polystyrene-coated cobalt nanoparticles showed little change. Magnetic measurements exhibited that the small cobalt particles (12 nm) were superparamagnetic, while larger particles (21 nm) were ferromagnetic and assembled into 1-D chains. The grafting density calculated from thermogravimetric analysis showed that a higher grafting density of polystyrene was obtained with lower molecular weight (Mn = 2300 g/mol) than those with higher molecular weight (Mn = 10500 g/mol). Due to the larger steric hindrance, polystyrene with higher molecular weight cannot form a dense shell on the surface of the nanoparticles, which resulted in a lower grafting density. Wide angle X-ray scattering measurements revealed the epsilon cobalt crystalline phases of both superparamagnetic Co NPs coated with polystyrene (Mn = 2300 g/mol) and ferromagnetic Co NPs coated with polystyrene (Mn = 10500 g/mol). Furthermore, a stability study showed that PS-Co NPs prepared with higher polymer concentration and polymer molecular weight exhibited a better stability.
Due to a challenging population growth and environmental changes, a need for new routes to provide required chemicals for human necessities arises. An effective solution discussed in this thesis is industrial heterogeneous catalysis. The development of an advanced industrial heterogeneous catalyst is investigated herein by considering porous carbon nano-material as supports and modifying their surface chemistry structure with heteroatoms. Such modifications showed a significant influence on the performance of the catalyst and provided a deeper insight regarding the interaction between the surface structure of the catalyst and the surrounding phase. This thesis contributes to the few present studies about heteroatoms effect on the catalyst performance and emphasizes on the importance of understanding surface structure functionalization in a catalyst in different phases (liquid and gaseous) and for different reactions (hydrogenolysis, oxidation, and hydrogenation/ polymerization). Herein, the heteroatoms utilized for the modifications are hydrogen (H), oxygen (O), and nitrogen (N). The heteroatoms effect on the metal particle size, on the polarity of the support/ the catalyst, on the catalytic performance (activity, selectivity, and stability), and on the interaction with the surrounding phase has been explored. First hierarchical porous carbon nanomaterials functionalized with heteroatoms (N) is synthesized and applied as supports for nickel nanoparticles for hydrogenolysis process of kraft lignin in liquid phase. This reaction has been performed in batch and flow reactors for three different catalysts, two of comparable hierarchical porosity, yet one is modified with N and the other is not, and a third is a prepared catalyst from a commercial carbon support. The reaction production and analyses show that the catalysts with hierarchical porosity perform catalytically much better than in presence of a commercial carbon support with lower surface area. Moreover, the modification with N-heteroatoms enhanced the catalytic performance because the heteroatom modified porous carbon material with nickel nanoparticles catalyst (Ni-NDC) performed highest among the other catalysts. In the flow reactor, Ni-NDC selectively degraded the ether bonds (β-O-4) in kraft lignin with an activity of 2.2 x10^-4 mg lignin mg Ni-1 s-1 for 50 h at 350°C and 3.5 mL min-1 flow, providing ~99 % conversion to shorter chained chemicals (mainly guaiacol derivatives). Then, the functionalization of carbon surface was further studied in selective oxidation of glucose to gluconic acid using < 1 wt. % of gold (Au) deposited on the previously-mentioned synthesized carbon (C) supports with different functionalities (Au-CGlucose, Au-CGlucose-H, Au-CGlucose-O, Au-CGlucoseamine). Except for Au-CGlucose-O, the other catalysts achieved full glucose conversion within 40-120 min and 100% selectivity towards gluconic acid with a maximum activity of 1.5 molGlucose molAu-1 s-1 in an aqueous phase at 45 °C and pH 9. Each heteroatom influenced the polarity of the carbon differently, affecting by that the deposition of Au on the support and thus the activity of the catalyst and its selectivity. The heteroatom effect was further investigated in a gas phase. The Fischer-Tropsch reaction was applied to convert synthetic gas (CO and H2) to short olefins and paraffins using surface-functionalized carbon nanotubes (CNTs) with heteroatoms as supports for ion (Fe) deposition in presence and absence of promoters (Na and S). The results showed the promoted Fe-CNT doped with nitrogen catalyst to be stable up to 180 h and selective to the formation of olefins (~ 47 %) and paraffins (~6 %) with a conversion of CO ~ 92 % at a maximum activity of 94 *10^-5 mol CO g Fe-1 s-1. The more information given regarding this topic can open wide range of applications not only in catalysis, but in other approaches as well. In conclusion, incorporation of heteroatoms can be the next approach for an advanced industrial heterogeneous catalyst, but also for other applications (e.g. electrocatalysis, gas adsorption, or supercapacitors).
Reversible-deactivation radical polymerization (RDRP) is without any doubt one of the most prevalent and powerful strategies for polymer synthesis, by which well-defined living polymers with targeted molecular weight (MW), low molar dispersity (Ɖ) and diverse morphologies can be prepared in a controlled fashion. Atom transfer radical polymerization (ATRP) as one of the most extensive studied types of RDRP has been particularly emphasized due to the high accessibility to hybrid materials, multifunctional copolymers and diverse end group functionalities via commercially available precursors. However, due to catalyst-induced side reactions and chain-chain coupling termination in bulk environment, synthesis of high MW polymers with uniform chain length (low Ɖ) and highly-preserved chain-end fidelity is usually challenging. Besides, owing to the inherited radical nature, the control of microstructure, namely tacticity control, is another laborious task. Considering the applied catalysts, the utilization of large amounts of non-reusable transition metal ions which lead to cumbersome purification process, product contamination and complicated reaction procedures all delimit the scope ATRP techniques.
Metal-organic frameworks (MOFs) are an emerging type of porous materials combing the properties of both organic polymers and inorganic crystals, characterized with well-defined crystalline framework, high specific surface area, tunable porous structure and versatile nanochannel functionalities. These promising properties of MOFs have thoroughly revolutionized academic research and applications in tremendous aspects, including gas processing, sensing, photoluminescence, catalysis and compartmentalized polymerization. Through functionalization, the microenvironment of MOF nanochannel can be precisely devised and tailored with specified functional groups for individual host-guest interactions. Furthermore, properties of high transition metal density, accessible catalytic sites and crystalline particles all indicate MOFs as prominent heterogeneous catalysts which open a new avenue towards unprecedented catalytic performance. Although beneficial properties in catalysis, high agglomeration and poor dispersibility restrain the potential catalytic capacity to certain degree.
Due to thriving development of MOF sciences, fundamental polymer science is undergoing a significant transformation, and the advanced polymerization strategy can eventually refine the intrinsic drawbacks of MOF solids reversely. Therefore, in the present thesis, a combination of low-dimensional polymers with crystalline MOFs is demonstrated as a robust and comprehensive approach to gain the bilateral advantages from polymers (flexibility, dispersibility) and MOFs (stability, crystallinity). The utilization of MOFs for in-situ polymerizations and catalytic purposes can be realized to synthesize intriguing polymers in a facile and universal process to expand the applicability of conventional ATRP methodology. On the other hand, through the formation of MOF/polymer composites by surface functionalization, the MOF particles with environment-adjustable dispersibility and high catalytic property can be as-prepared.
In the present thesis, an approach via combination of confined porous textures from MOFs and controlled radical polymerization is proposed to advance synthetic polymer chemistry. Zn2(bdc)2(dabco) (Znbdc) and the initiator-functionalized Zn MOFs, ZnBrbdc, are utilized as a reaction environment for in-situ polymerization of various size-dependent methacrylate monomers (i.e. methyl, ethyl, benzyl and isobornyl methacrylate) through (surface-initiated) activators regenerated by electron transfer (ARGET/SI-ARGET) ATRP, resulting in polymers with control over dispersity, end functionalities and tacticity with respect to distinct molecular size. While the functionalized MOFs are applied, due to the strengthened compartmentalization effect, the accommodated polymers with molecular weight up to 392,000 can be achieved. Moreover, a significant improvement in end-group fidelity and stereocontrol can be observed. The results highlight a combination of MOFs and ATRP is a promising and universal methodology to synthesize versatile well-defined polymers with high molecular weight, increment in isotactic trial and the preserved chain-end functionality.
More than being a host only, MOFs can act as heterogeneous catalysts for metal-catalyzed polymerizations. A Cu(II)-based MOF, Cu2(bdc)2(dabco), is demonstrated as a heterogeneous, universal catalyst for both thermal or visible light-triggered ARGET ATRP with expanded monomer range. The accessible catalytic metal sites enable the Cu(II) MOF to polymerize various monomers, including benzyl methacrylate (BzMA), styrene, methyl methacrylate (MMA), 2-(dimethylamino)ethyl methacrylate (DMAEMA) in the fashion of ARGET ATRP. Furthermore, due to the robust frameworks, surpassing the conventional homogeneous catalyst, the Cu(II) MOF can tolerate strongly coordinating monomers and polymerize challenging monomers (i.e. 4-vinyl pyridine, 2-vinyl pyridine and isoprene), in a well-controlled fashion. Therefore, a synthetic procedure can be significantly simplified, and catalyst-resulted chelation can be avoided as well. Like other heterogeneous catalysts, the Cu(II) MOF catalytic complexes can be easily collected by centrifugation and recycled for an arbitrary amount of times.
The Cu(II) MOF, composed of photostimulable metal sites, is further used to catalyze controlled photopolymerization under visible light and requires no external photoinitiator, dye sensitizer or ligand. A simple light trigger allows the photoreduction of Cu(II) to the active Cu(I) state, enabling controlled polymerization in the form of ARGET ATRP. More than polymerization application, the synergic effect between MOF frameworks and incorporated nucleophilic monomers/molecules is also observed, where the formation of associating complexes is able to adjust the photochemical and electrochemical properties of the Cu(II) MOF, altering the band gap and light harvesting behavior. Owing to the tunable photoabsorption property resulting from the coordinating guests, photoinduced Reversible-deactivation radical polymerization (PRDRP) can be achieved to further simplify and fasten the polymerization.
More than the adjustable photoabsorption ability, the synergistic strategy via a combination of controlled/living polymerization technique and crystalline MOFs can be again evidenced as demonstrated in the MOF-based heterogeneous catalysts with enhanced dispersibility in solution. Through introducing hollow pollen pivots with surface immobilized environment-responsive polymer, PDMAEMA, highly dispersed MOF nanocrystals can be prepared after associating on polymer brushes via the intrinsic amine functionality in each DMAEMA monomer. Intriguingly, the pollen-PDMAEMA composite can serve as a “smart” anchor to trap nanoMOF particles with improved dispersibility, and thus to significantly enhance liquid-phase photocatalytic performance. Furthermore, the catalytic activity can be switched on and off via stimulable coil-to-globule transition of the PDMAEMA chains exposing or burying MOF catalytic sites, respectively.
Thermoresponsive block copolymers of presumably highly biocompatible character exhibiting upper critical solution temperature (UCST) type phase behavior were developed. In particular, these polymers were designed to exhibit UCST-type cloud points (Tcp) in physiological saline solution (9 g/L) within the physiologically interesting window of 30-50°C. Further, their use as carrier for controlled release purposes was explored. Polyzwitterion-based block copolymers were synthesized by atom transfer radical polymerization (ATRP) via a macroinitiator approach with varied molar masses and co-monomer contents. These block copolymers can self-assemble in the amphiphilic state to form micelles, when the thermoresponsive block experiences a coil-to-globule transition upon cooling. Poly(ethylene glycol) methyl ether (mPEG) was used as the permanently hydrophilic block to stabilize the colloids formed, and polyzwitterions as the thermoresponsive block to promote the temperature-triggered assembly-disassembly of the micellear aggregates at low temperature.
Three zwitterionic monomers were used for this studies, namely 3-((2-(methacryloyloxy)ethyl)dimethylammonio)propane-1-sulfonate (SPE), 4-((2-(methacryloyl- oxy)ethyl)dimethylammonio)butane-1-sulfonate (SBE), and 3-((2-(methacryloyloxy)ethyl)- dimethylammonio)propane-1-sulfate) (ZPE). Their (co)polymers were characterized with respect to their molecular structure by proton nuclear magnetic resonance (1H-NMR) and gel permeation chromatography (GPC). Their phase behaviors in pure water as well as in physiological saline were studied by turbidimetry and dynamic light scattering (DLS). These (co)polymers are thermoresponsive with UCST-type phase behavior in aqueous solution. Their phase transition temperatures depend strongly on the molar masses and the incorporation of co-monomers: phase transition temperatures increased with increasing molar masses and content of poorly water-soluble co-monomer. In addition, the presence of salt influenced the phase transition dramatically. The phase transition temperature decreased with increasing salt content in the solution. While the PSPE homopolymers show a phase transition only in pure water, the PZPE homopolymers are able to exhibit a phase transition only in high salinity, as in physiological saline. Although both polyzwitterions have similar chemical structures that differ only in the anionic group (sulfonate group in SPE and sulfate group in ZPE), the water solubility is very different. Therefore, the phase transition temperatures of targeted block copolymers were modulated by using statistical copolymer of SPE and ZPE as thermoresponsive block, and varying the ratio of SPE to ZPE. Indeed, the statistical copolymers of P(SPE-co-ZPE) show phase transitions both in pure water as well as in physiological saline. Surprisingly, it was found that mPEG-b-PSBE block copolymer can display “schizophrenic” behavior in pure water, with the UCST-type cloud point occurring at lower temperature than the LCST-type one.
The block copolymer, which satisfied best the boundary conditions, is block copolymer mPEG114-b-P(SPE43-co-ZPE39) with a cloud point of 45°C in physiological saline. Therefore, it was chosen for solubilization studies of several solvatochromic dyes as models of active agents, using the thermoresponsive block copolymer as “smart” carrier. The uptake and release of the dyes were explored by UV-Vis and fluorescence spectroscopy, following the shift of the wavelength of the absorbance or emission maxima at low and high temperature. These are representative for the loaded and released state, respectively. However, no UCST-transition triggered uptake and release of these dyes could be observed. Possibly, the poor affinity of the polybetaines to the dyes in aqueous environtments may be related to the widely reported antifouling properties of zwitterionic polymers.
The utilization of lignin as renewable electrode material for electrochemical energy storage is a sustainable approach for future batteries and supercapacitors. The composite electrode was fabricated from Kraft lignin and conductive carbon and the charge storage contribution was determined in terms of electrical double layer (EDL) and redox reactions. The important factors at play for achieving high faradaic charge storage capacity contribute to high surface area, accessibility of redox sites in lignin and their interaction with conductive additives. A thinner layer of lignin covering the high surface area of carbon facilitates the electron transfer process with a shorter pathway from the active sites of nonconductive lignin to the current collector leading to the improvement of faradaic charge storage capacity.
Composite electrodes from lignin and carbon would be even more sustainable if the fluorinated binder can be omitted. A new route to fabricate a binder-free composite electrode from Kraft lignin and high surface area carbon has been proposed by crosslinking lignin with glyoxal. A high molecular weight of lignin is obtained to enhance both electroactivity and binder capability in composite electrodes. The order of the processing step of crosslinking lignin on the composite electrode plays a crucial role in achieving a stable electrode and high charge storage capacity. The crosslinked lignin based electrodes are promising since they allow for more stable, sustainable, halogen-free and environmentally benign devices for energy storage applications. Furthermore, improvement of the amount of redox active groups (quinone groups) in lignin is useful to enhance the capacity in lithium battery applications. Direct oxidative demethylation by cerium ammonium nitrate has been carried out under mild conditions. This proves that an increase of quinone groups is able to enhance the performance of lithium battery. Thus, lignin is a promising material and could be a good candidate for application in sustainable energy storage devices.
Nowadays, the need to protect the environment becomes more urgent than ever. In the field of chemistry, this translates to practices such as waste prevention, use of renewable feedstocks, and catalysis; concepts based on the principles of green chemistry. Polymers are an important product in the chemical industry and are also in the focus of these changes. In this thesis, more sustainable approaches to make two classes of polymers, polypeptoids and polyesters, are described.
Polypeptoids or poly(alkyl-N-glycines) are isomers of polypeptides and are biocompatible, as well as degradable under biologically relevant conditions. In addition to that, they can have interesting properties such as lower critical solution temperature (LCST) behavior. They are usually synthesized by the ring opening polymerization (ROP) of N-carboxy anhydrides (NCAs), which are produced with the use of toxic compounds (e.g. phosgene) and which are highly sensitive to humidity. In order to avoid the direct synthesis and isolation of the NCAs, N-phenoxycarbonyl-protected N-substituted glycines are prepared, which can yield the NCAs in situ. The conditions for the NCA synthesis and its direct polymerization are investigated and optimized for the simplest N-substituted glycine, sarcosine. The use of a tertiary amine in less than stoichiometric amounts compared to the N-phenoxycarbonyl--sarcosine seems to accelerate drastically the NCA formation and does not affect the efficiency of the polymerization. In fact, well defined polysarcosines that comply to the monomer to initiator ratio can be produced by this method. This approach was also applied to other N-substituted glycines.
Dihydroxyacetone is a sustainable diol produced from glycerol, and has already been used for the synthesis of polycarbonates. Here, it was used as a comonomer for the synthesis of polyesters. However, the polymerization of dihydroxyacetone presented difficulties, probably due to the insolubility of the macromolecular chains. To circumvent the problem, the dimethyl acetal protected dihydroxyacetone was polymerized with terephthaloyl chloride to yield a soluble polymer. When the carbonyl was recovered after deprotection, the product was insoluble in all solvents, showing that the carbonyl in the main chain hinders the dissolution of the polymers. The solubility issue can be avoided, when a 1:1 mixture of dihydroxyacetone/ ethylene glycol is used to yield a soluble copolyester.
Photocatalysis is considered significant in this new energy era, because the inexhaustibly abundant, clean, and safe energy of the sun can be harnessed for sustainable, nonhazardous, and economically development of our society. In the research of photocatalysis, the current focus was held by the design and modification of photocatalyst.
As one of the most promising photocatalysts, g-C3N4 has gained considerable attention for its eye-catching properties. It has been extensively explored in photocatalysis applications, such as water splitting, organic pollutant degradation, and CO2 reduction. Even so, it also has its own drawbacks which inhibit its further application. Inspired by that, this thesis will mainly present and discuss the process and achievement on the preparation of some novel photocatalysts and their photocatalysis performance. These materials were all synthesized via the alteration of classic g-C3N4 preparation method, like using different pre-compositions for initial supramolecular complex and functional group post-modification. By taking place of cyanuric acid, 2,5-Dihydroxy-1,4-benzoquinone and chloranilic acid can form completely new supramolecular complex with melamine. After heating, the resulting products of the two complex shown 2D sheet-like and 1D fiber-like morphologies, respectively, which maintain at even up to high temperature of 800 °C. These materials cover crystals, polymers and N-doped carbons with the increase of synthesis temperature. Based on their different pre-compositions, they show different dye degradation performances. For CLA-M-250, it shows the highest photocatalytic activity and strong oxidation capacity. It shows not only great photo-performance in RhB degradation, but also oxygen production in water splitting. In the post-modification method, a novel photocatalysis solution was proposed to modify carbon nitride scaffold with cyano group, whose content can be well controlled by the input of sodium thiocyanate. The cyanation modification leads to narrowed band gap as well as improved photo-induced charges separation. Cyano group grafted carbon nitride thus shows dramatically enhanced performance in the photocatalytic coupling reaction between styrene and sodium benzenesulfinate under green light irradiation, which is in stark contrast with the inactivity of pristine g-C3N4.
The valorization of carbohydrates is one of the most promising fields in green chemistry, as it enables to produce bulk chemicals and fuels out of renewable and abundant resources, instead of further exploiting fossil feedstocks. The focus in this thesis is the conversion of fructose, using dehydration and hydrodeoxygenation reactions. The main goal is to find an easy continuous process, including the solubility of the sugar in a green solvent, the conversion over a solid acid as well as over a metal@tungsten carbide catalyst.
At the beginning of this thesis, solid acid catalysts are synthesized by using carbohydrate material like glucose and starch at high temperatures (up to 600 °C). Additionally a third carbon is synthesized, using an activation method based on Ca(OH)2. After carbonization and further sulfonation, using fuming sulfuric acid, the three resulting catalysts are characterized together with sulfonated carbon black and Amberlyst 15 as references. In order to test all solid acid catalysts in reaction, a 250 mm x 4.6 mm stainless steel column is used as a fixed-bed continuous reactor. The temperature (110 °C to 250 °C) and residence time (2 to 30 minutes) is varied, and a direct relationship between contact time and selectivity is determined. The reaction mechanism, as well as the product distribution is showing a dehydration step of fructose towards 5-hydroxymethylfurfural (HMF). These furan-ring molecules are considered as “sleeping giants”, due to the possibility of using them as fuel, but also for upgrading them to chemicals like terephthalic acid or p-xylene. Consecutive reactions are producing levulinic acid, as well as condensation products with ethanol and formic acid. The activated carbon is additionally showing a 2 % yield of 2,5-Dimethylfuran (DMF) production, pointing towards the extraordinary properties of this catalyst. Without a metal catalyst present, what is normally necessary for hydrogenation reactions, a transferhydrogenation (with formic acid) is observed. The active catalyst was therefore carbon itself, what activated the hydrogen on its surface. This phenomenon was just very rarely observed so far. Expensive noble metals are the material of choice, when it comes to hydrogenation reactions nowadays and cheaper alternatives are necessary.
By postulating a similar electronic structure of tungsten carbide (WC) to platinum by Lewy and Boudart, research is focusing on the replacement of Pt. The production of nano-sized tungsten carbide particles (7.5 ± 2.5 nm, 70 m2 g-1) is enabled by the so called “urea glass route” and its catalytic performances are compared to commercial material. It is shown, that the activity is strongly dependent on the size of the particles as well as the surface area. Nano-sized tungsten carbide is showing activity for hydrogenation reactions under mild conditions (maximum 150 °C, 30 bar). This material therefore opens up new possibilities for replacing the rare and expensive platinum with tungsten carbide based catalysts.
Additionally different metal nanoparticles of palladium, copper and nickel are deposited on top of WC to further promote its reactivity. The nickel nanoparticles are strongly connected to WC and showed the best activity as well as selectivity for upgrading HMF with hydrodeoxygenation. The Ni@WC is not leaching and is showing very good hydrodeoxygenation properties with DMF yields up to 90 percent. Copper@WC is not showing good activity and palladium@WC enables undesired consecutive reactions, hydrogenating the furan ring system.
In order to enable the upgrade of fructose to DMF directly in a continuous system, the current H CUBE Pro TM hydrogenation system is customized with a second reaction column. A 250 mm x 4.6 mm stainless steel reactor column is connected ahead of the hydrogen insertion, enabling the dehydration of fructose to HMF derivatives, before pumping these products into the second column for hydrogenation. The overall residence time in the two column reactor system is 14 minutes. The overall results are an almost full conversion with a yield of 38.5 % DMF and 47 % yield of EL. The main disadvantage is the formation of higher mass products, so called humins, which start depositing on top of the catalysts, blocking their active sites.
In general it can be stated, that a two column system goes along with a higher investment as well as more maintenance costs, compared to a one column catalytic approach. To develop a catalyst, which is on the one hand able to dehydrate as well as hydrodeoxygenate the reactants, is aimed for at the last part of the thesis. The activated carbon however shows already activity for hydrodeoxygenation without any metal present and offers itself therefore as an alternative to overcome the temperature instability of Amberlyst 15 (max. 120 °C) for a combined DMF production directly from fructose. The activity for the upgrade to DMF is increased from 2 % to 12 % DMF yield in one mixed continuous column.
In order to scale up the entire one column approach, an 800 mm x 28.5 mm inner diameter column was planned and manufactured. The system is scaled up and assembled, whereas this flow reactor system is able to be run with 50 mL min-1 maximum flow rate, to stand a pressure of maximum 100 bar and be heated to around 500 °C. The tubing and connections, as well as the used devices are planned according to be safe and easy in use. The scaled-up approach offers a reaction column 120 times bigger (510 ml) then the first extension of the commercial system. This further extension offers the possibility of ranging between 1 and 1000 mL min-1, making it possible to use the approach in pilot plant applications.
Development of a reliable and environmentally friendly synthesis for fluorescence carbon nanodots
(2017)
Carbon nanodots (CNDs) have generated considerable attention due to their promising properties, e.g. high water solubility, chemical inertness, resistance to photobleaching, high biocompatibility and ease of functionalization. These properties render them ideal for a wide range of functions, e.g. electrochemical applications, waste water treatment, (photo)catalysis, bio-imaging and bio-technology, as well as chemical sensing, and optoelectronic devices like LEDs. In particular, the ability to prepare CNDs from a wide range of accessible organic materials makes them a potential alternative for conventional organic dyes and semiconductor quantum dots (QDs) in various applications. However, current synthesis methods are typically expensive and depend on complex and time-consuming processes or severe synthesis conditions and toxic chemicals. One way to reduce overall preparation costs is the use of biological waste as starting material. Hence, natural carbon sources such as pomelo peal, egg white and egg yolk, orange juice, and even eggshells, to name a few; have been used for the preparation of CNDs. While the use of waste is desirable, especially to avoid competition with essential food production, most starting-materials lack the essential purity and structural homogeneity to obtain homogeneous carbon dots. Furthermore, most synthesis approaches reported to date require extensive purification steps and have resulted in carbon dots with heterogeneous photoluminescent properties and indefinite composition. For this reason, among others, the relationship between CND structure (e.g. size, edge shape, functional groups and overall composition) and photophysical properties is yet not fully understood. This is particularly true for carbon dots displaying selective luminescence (one of their most intriguing properties), i.e. their PL emission wavelength can be tuned by varying the excitation wavelength.
In this work, a new reliable, economic, and environmentally-friendly one-step synthesis is established to obtain CNDs with well-defined and reproducible photoluminescence (PL) properties via the microwave-assisted hydrothermal treatment of starch, carboxylic acids and Tris-EDTA (TE) buffer as carbon- and nitrogen source, respectively. The presented microwave-assisted hydrothermal precursor carbonization (MW-hPC) is characterized by its cost-efficiency, simplicity, short reaction times, low environmental footprint, and high yields of approx. 80% (w/w). Furthermore, only a single synthesis step is necessary to obtain homogeneous water-soluble CNDs with no need for further purification.
Depending on starting materials and reaction conditions different types of CNDs have been prepared. The as-prepared CNDs exhibit reproducible, highly homogeneous and favourable PL properties with narrow emission bands (approx. 70nm FWHM), are non-blinking, and are ready to use without need for further purification, modification or surface passivation agents. Furthermore, the CNDs are comparatively small (approx. 2.0nm to 2.4nm) with narrow size distributions; are stable over a long period of time (at least one year), either in solution or as a dried solid; and maintain their PL properties when re-dispersed in solution. Depending on CND type, the PL quantum yield (PLQY) can be adjusted from as low as 1% to as high as 90%; one of the highest reported PLQY values (for CNDs) so far.
An essential part of this work was the utilization of a microwave synthesis reactor, allowing various batch sizes and precise control over reaction temperature and -time, pressure, and heating- and cooling rate, while also being safe to operate at elevated reaction conditions (e.g. 230 ±C and 30 bar). The hereby-achieved high sample throughput allowed, for the first time, the thorough investigation of a wide range of synthesis parameters, providing valuable insight into the CND formation. The influence of carbon- and nitrogen source, precursor concentration and -combination, reaction time and -temperature, batch size, and post-synthesis purification steps were carefully investigated regarding their influence on the optical properties of as-synthesized CNDs. In addition, the change in photophysical properties resulting from the conversion of CND solution into solid and back into the solution was investigated. Remarkably, upon freeze-drying the initial brown CND-solution turns into a non-fluorescent white/slightly yellow to brown solid which recovers PL in aqueous solution. Selected CND samples were also subject to EDX, FTIR, NMR, PL lifetime (TCSPC), particle size (TEM), TGA and XRD analysis. Besides structural characterization, the pH- and excitation dependent PL characteristics (i.e. selective luminescence) were examined; giving inside into the origin of photophysical properties and excitation dependent behaviour of CNDs. The obtained results support the notion that for CNDs the nature of the surface states determines the PL properties and that excitation dependent behaviour is caused by the “Giant Red-Edge Excitation Shift” (GREES).
Nanolenses are linear chains of differently-sized metal nanoparticles, which can theoretically provide extremely high field enhancements. The complex structure renders their synthesis challenging and has hampered closer analyses so far. Here, the technique of DNA origami was used to self-assemble DNA-coated 10 nm, 20 nm, and 60 nm gold or silver nanoparticles into gold or silver nanolenses. Three different geometrical arrangements of gold nanolenses were assembled, and for each of the three, sets of single gold nanolenses were investigated in detail by atomic force microscopy, scanning electron microscopy, dark-field scattering and Raman spectroscopy. The surface-enhanced Raman scattering (SERS) capabilities of the single nanolenses were assessed by labelling the 10 nm gold nanoparticle selectively with dye molecules. The experimental data was complemented by finite-difference time-domain simulations. For those gold nanolenses which showed the strongest field enhancement, SERS signals from the two different internal gaps were compared by selectively placing probe dyes on the 20 nm or 60 nm gold particles. The highest enhancement was found for the gap between the 20 nm and 10 nm nanoparticle, which is indicative of a cascaded field enhancement. The protein streptavidin was labelled with alkyne groups and served as a biological model analyte, bound between the 20 nm and 10 nm particle of silver nanolenses. Thereby, a SERS signal from a single streptavidin could be detected. Background peaks observed in SERS measurements on single silver nanolenses could be attributed to amorphous carbon. It was shown that the amorphous carbon is generated in situ.
Ziel der vorliegenden Arbeit war die Synthese und Charakterisierung von anisotropen Goldnanopartikeln in einer geeigneten Polyelektrolyt-modifizierten Templatphase. Der Mittelpunkt bildet dabei die Auswahl einer geeigneten Templatphase, zur Synthese von einheitlichen und reproduzierbaren anisotropen Goldnanopartikeln mit den daraus resultierenden besonderen Eigenschaften. Bei der Synthese der anisotropen Goldnanopartikeln lag der Fokus in der Verwendung von Vesikeln als Templatphase, wobei hier der Einfluss unterschiedlicher strukturbildender Polymere (stark alternierende Maleamid-Copolymere PalH, PalPh, PalPhCarb und PalPhBisCarb mit verschiedener Konformation) und Tenside (SDS, AOT – anionische Tenside) bei verschiedenen Synthese- und Abtrennungsbedingungen untersucht werden sollte.
Im ersten Teil der Arbeit konnte gezeigt werden, dass PalPhBisCarb bei einem pH-Wert von 9 die Bedingungen eines Röhrenbildners für eine morphologische Transformation von einer vesikulären Phase in eine röhrenförmige Netzwerkstruktur erfüllt und somit als Templatphase zur formgesteuerten Bildung von Nanopartikeln genutzt werden kann.
Im zweiten Teil der Arbeit wurde dargelegt, dass die Templatphase PalPhBisCarb (pH-Wert von 9, Konzentration von 0,01 wt.%) mit AOT als Tensid und PL90G als Phospholipid (im Verhältnis 1:1) die effektivste Wahl einer Templatphase für die Bildung von anisotropen Strukturen in einem einstufigen Prozess darstellt. Bei einer konstanten Synthesetemperatur von 45 °C wurden die besten Ergebnisse bei einer Goldchloridkonzentration von 2 mM, einem Gold-Templat-Verhältnis von 3:1 und einer Synthesezeit von 30 Minuten erzielt. Ausbeute an anisotropen Strukturen lag bei 52 % (Anteil an dreieckigen Nanoplättchen von 19 %). Durch Erhöhung der Synthesetemperatur konnte die Ausbeute auf 56 % (29 %) erhöht werden.
Im dritten Teil konnte durch zeitabhängige Untersuchungen gezeigt werden, dass bei Vorhandensein von PalPhBisCarb die Bildung der energetisch nicht bevorzugten Plättchen-Strukturen bei Raumtemperatur initiiert wird und bei 45 °C ein Optimum annimmt.
Kintetische Untersuchungen haben gezeigt, dass die Bildung dreieckiger Nanoplättchen bei schrittweiser Zugabe der Goldchlorid-Präkursorlösung zur PalPhBisCarb enthaltenden Templatphase durch die Dosierrate der vesikulären Templatphase gesteuert werden kann. In umgekehrter Weise findet bei Zugabe der Templatphase zur Goldchlorid-Präkursorlösung bei 45 °C ein ähnlicher, kinetisch gesteuerter Prozess der Bildung von Nanodreiecken statt mit einer maximalen Ausbeute dreieckigen Nanoplättchen von 29 %.
Im letzten Kapitel erfolgten erste Versuche zur Abtrennung dreieckiger Nanoplättchen von den übrigen Geometrien der gemischten Nanopartikellösung mittels tensidinduzierter Verarmungsfällung. Bei Verwendung von AOT mit einer Konzentration von 0,015 M wurde eine Ausbeute an Nanoplättchen von 99 %, wovon 72 % dreieckiger Geometrien hatten, erreicht.
In der vorliegenden Arbeit werden Wege zur Gewinnung verschiedener phenolischer Substanzen wie Lignin, Diarylheptanoide und 4-(3-Oxobutyl)phenol (Himbeerketon) aus dem Stamm der Hängebirke (Betula pendula) aufgezeigt. Durch Methacrylierung des 4-(3-Oxobutyl)phenols wurde ein Monomer erzeugt, welches mittels freier radikalischer Masse- und Lösungspolymerisation, sowie enzymatischer Polymerisation polymerisiert werden kann.
Eine erste Isolierung von Bestandteilen wurde durch Extraktion von Innenholz bzw. Rinde mit Methanol erzielt. Die in Methanol unlöslichen Bestandteile des Innenholzes und der Rinde wurden anschließend mit ausgewählten ionischen Flüssigkeiten extrahiert. Es wurde ein Verfahren zum selektiven Trennen der mit diesen ionischen Flüssigkeiten extrahierten Bestandteile in Cellulose, Hemicellulose, Lignin und mit Ethylacetat extrahierbare Bestandteile entwickelt. Hierdurch war es möglich, sowohl die verwendeten ionischen Flüssigkeiten als auch das Innenholz und die Rinde hinsichtlich ihres Extraktionsverhaltens miteinander zu vergleichen.
Ferner wurden verschiedene Strategien aufgezeigt, um insgesamt drei Spezies an Diarylheptanoiden aus dem methanolischen Extrakt der Rinde zu isolieren. Eines der gefundenen Diarylheptanoide (5 Hydroxy-1,7-bis(4-hydroxyphenyl)-3-heptanon) wurde via Retroaldolreaktion in 4 (3 Oxobutyl)phenol (Himbeerketon) und 3 (4 Hydroxyphenyl)propanal gespalten.
Es wurde die Verwendung des 4-(3-Oxobutyl)phenol als Monomerbestandteil untersucht. Hierfür wurde 4-(3-Oxobutyl)phenylmethacrylat synthetisiert und Wege zur Reinigung mittels Säulenchromatographie und Umkristallisation aufgezeigt. Anschließend wurde Poly(4-(3-oxobutyl)phenylmethacrylat) (PObMA) und Polybenzylmethacrylats (PBzMA) aus Massen- und Lösungspolymerisation hergestellt. Die Ausbeuten an PObpMA im Vergleich zum PBzMA liegen bei gleichen Reaktionsbedingungen auf gleichem Niveau. Im Kontrast hierzu ist der Polymerisationsgrad aus freier radikalischer Polymerisation in Masse des PObpMA im Vergleich zum PBzMA um den Faktor 3,7 größer. Die Glasübergangstemperaturen des PObpMA liegen bei gleichen Reaktionsbedingungen sowohl bei freier radikalischer Polymerisation in Masse, als auch bei Lösungspolymerisation über denen des PBzMA. Darüber hinaus wurde die Polymerisation von 4-(3-Oxobutyl)phenylmethacrylat und Benzylmethacrylat mit einem Initiatorsystem bestehend aus Meerrettichperoxidase, Acetylaceton und Wasserstoffperoxid bei Raumtemperatur beschrieben. Die mit enzymatischem Initiatorsystem erzeugten Produkte zeigten starke Übereinstimmung mit Produkten aus Lösungspolymerisationen, welche mit Azobis(isobutyronitril) initiiert wurden.
Die Elektrosprayionisation (ESI) ist eine der weitverbreitetsten Ionisationstechniken für flüssige Pro-ben in der Massen- und Ionenmobilitäts(IM)-Spektrometrie. Aufgrund ihrer schonenden Ionisierung wird ESI vorwiegend für empfindliche, komplexe Moleküle in der Biologie und Medizin eingesetzt. Überdies ist sie allerdings für ein sehr breites Spektrum an Substanzklassen anwendbar. Die IM-Spektrometrie wurde ursprünglich zur Detektion gasförmiger Proben entwickelt, die hauptsächlich durch radioaktive Quellen ionisiert werden. Sie ist die einzige analytische Methode, bei der Isomere in Echtzeit getrennt und über ihre charakteristische IM direkt identifiziert werden können. ESI wurde in den 90ger Jahren durch die Hill Gruppe in die IM-Spektrometrie eingeführt. Die Kombination wird bisher jedoch nur von wenigen Gruppen verwendet und hat deshalb noch ein hohes Entwick-lungspotential. Ein vielversprechendes Anwendungsfeld ist der Einsatz in der Hochleistungs-flüssigkeitschromatographie (HPLC) zur mehrdimensionalen Trennung. Heutzutage ist die HPLC die Standardmethode zur Trennung komplexer Proben in der Routineanalytik. HPLC-Trennungsgänge sind jedoch häufig langwierig und der Einsatz verschiedener Laufmittel, hoher Flussraten, von Puffern, sowie Laufmittelgradienten stellt hohe Anforderungen an die Detektoren. Die ESI-IM-Spektrometrie wurde in einigen Studien bereits als HPLC-Detektor eingesetzt, war dort bisher jedoch auf Flussratensplitting oder geringe Flussraten des Laufmittels beschränkt.
In dieser kumulativen Doktorarbeit konnte daher erstmals ein ESI IM-Spektrometer als HPLC-Detektor für den Flussratenbereich von 200-1500 μl/min entwickelt werden. Anhand von fünf Publi-kationen wurden (1) über eine umfassende Charakterisierung die Eignung des Spektrometers als HPLC-Detektor festgestellt, (2) ausgewählte komplexe Trenngänge präsentiert und (3) die Anwen-dung zum Reaktionsmonitoring und (4, 5) mögliche Weiterentwicklungen gezeigt.
Erfolgreich konnten mit dem selbst-entwickelten ESI IM-Spektrometer typische HPLC-Bedingungen wie Wassergehalte im Laufmittel von bis zu 90%, Pufferkonzentrationen von bis zu 10 mM, sowie Nachweisgrenzen von bis zu 50 nM erreicht werden. Weiterhin wurde anhand der komplexen Trennungsgänge (24 Pestizide/18 Aminosäuren) gezeigt, dass die HPLC und die IM-Spektrometrie eine hohe Orthogonalität besitzen. Eine effektive Peakkapazität von 240 wurde so realisiert. Auf der HPLC-Säule koeluierende Substanzen konnten über die Driftzeit getrennt und über ihre IM identifi-ziert werden, sodass die Gesamttrennzeiten erheblich minimiert werden konnten. Die Anwend-barkeit des ESI IM-Spektrometers zur Überwachung chemischer Synthesen wurde anhand einer dreistufigen Reaktion demonstriert. Es konnten die wichtigsten Edukte, Zwischenprodukte und Produkte aller Stufen identifiziert werden. Eine quantitative Auswertung war sowohl über eine kurze HPLC-Vortrennung als auch durch die Entwicklung eines eigenen Kalibrierverfahrens, welches die Ladungskonkurrenz bei ESI berücksichtigt, ohne HPLC möglich. Im zweiten Teil der Arbeit werden zwei Weiterentwicklungen des Spektrometers präsentiert. Eine Möglichkeit ist die Reduzierung des Drucks in den intermediären Bereich (300 - 1000 mbar) mit dem Ziel der Verringerung der benötigten Spannungen. Mithilfe von Streulichtbildern und Strom-Spannungs-Kurven wurden für geringe Drücke eine verminderte Freisetzung der Analyt-Ionen aus den Tropfen festgestellt. Die Verluste konnten jedoch über höhere elektrische Feldstärken ausgeglichen werden, sodass gleiche Nachweisgrenzen bei 500 mbar und bei 1 bar erreicht wurden. Die zweite Weiterentwicklung ist ein neuartiges Ionentors mit Pulsschaltung, welches eine Verdopplung der Auflösung auf bis zu R > 100 bei gleicher Sensitivität ermöglichte. Eine denkbare Anwendung im Bereich der Peptidanalytik wurde mit beachtlichen Auflösungen der Peptide von R = 90 gezeigt.
The motivation of this work was to investigate the self-assembly of a block copolymer species that attended little attraction before, double hydrophilic block copolymers (DHBCs). DHBCs consist of two linear hydrophilic polymer blocks. The self-assembly of DHBCs towards suprastructures such as particles and vesicles is determined via a strong difference in hydrophilicity between the corresponding blocks leading to a microphase separation due to immiscibility. The benefits of DHBCs and the corresponding particles and vesicles, such as biocompatibility, high permeability towards water and hydrophilic compounds as well as the large amount of possible functionalizations that can be addressed to the block copolymers make the application of DHBC based structures a viable choice in biomedicine. In order to assess a route towards self-assembled structures from DHBCs that display the potential to act as cargos for future applications, several block copolymers containing two hydrophilic polymer blocks were synthesized. Poly(ethylene oxide)-b-poly(N-vinylpyrrolidone) (PEO-b-PVP) and Poly(ethylene oxide)-b-poly(N-vinylpyrrolidone-co-N-vinylimidazole) (PEO-b-P(VP-co-VIm) block copolymers were synthesized via reversible deactivation radical polymerization (RDRP) techniques starting from a PEO-macro chain transfer agent. The block copolymers displayed a concentration dependent self-assembly behavior in water which was determined via dynamic light scattering (DLS). It was possible to observe spherical particles via laser scanning confocal microscopy (LSCM) and cryogenic scanning electron microscopy (cryo SEM) at highly concentrated solutions of PEO-b-PVP. Furthermore, a crosslinking strategy with (PEO-b-P(VP-co-VIm) was developed applying a diiodo derived crosslinker diethylene glycol bis(2-iodoethyl) ether to form quaternary amines at the VIm units. The formed crosslinked structures proved stability upon dilution and transfer into organic solvents. Moreover, self-assembly and crosslinking in DMF proved to be more advantageous and the crosslinked structures could be successfully transferred to aqueous solution. The afforded spherical submicron particles could be visualized via LSCM, cryo SEM and Cryo TEM.
Double hydrophilic pullulan-b-poly(acrylamide) block copolymers were synthesized via copper catalyzed alkyne azide cycloaddition (CuAAC) starting from suitable pullulan alkyne and azide functionalized poly(N,N-dimethylacrylamide) (PDMA) and poly(N-ethylacrylamide) (PEA) homopolymers. The conjugation reaction was confirmed via SEC and 1H-NMR measurements. The self-assembly of the block copolymers was monitored with DLS and static light scattering (SLS) measurements indicating the presence of hollow spherical structures. Cryo SEM measurements could confirm the presence of vesicular structures for Pull-b-PEA block copolymers. Solutions of Pull-b-PDMA displayed particles in cryo SEM. Moreover, an end group functionalization of Pull-b-PDMA with Rhodamine B allowed assessing the structure via LSCM and hollow spherical structures were observed indicating the presence of vesicles, too.
An exemplified pathway towards a DHBC based drug delivery vehicle was demonstrated with the block copolymer Pull-b-PVP. The block copolymer was synthesized via RAFT/MADIX techniques starting from a pullulan chain transfer agent. Pull-b-PVP displayed a concentration dependent self-assembly in water with an efficiency superior to the PEO-b-PVP system, which could be observed via DLS. Cryo SEM and LSCM microscopy displayed the presence of spherical structures. In order to apply a reversible crosslinking strategy on the synthesized block copolymer, the pullulan block was selectively oxidized to dialdehydes with NaIO4. The oxidation of the block copolymer was confirmed via SEC and 1H-NMR measurements. The self-assembled and oxidized structures were subsequently crosslinked with cystamine dihiydrochloride, a pH and redox responsive crosslinker resulting in crosslinked vesicles which were observed via cryo SEM. The vesicular structures of crosslinked Pull-b-PVP could be disassembled by acid treatment or the application of the redox agent tris(2-carboxyethyl)-phosphin-hydrochloride. The successful disassembly was monitored with DLS measurements.
To conclude, self-assembled structures from DHBCs such as particles and vesicles display a strong potential to generate an impact on biomedicine and nanotechnologies. The variety of DHBC compositions and functionalities are very promising features for future applications.
In Zeiten eines sich schnell ändernden und vielseitigen Energiemarktes müssen Kohlenstoffmaterialien für verschiedene Anforderungen einsetzbar sein. Dies erfordert flexibel synthetisierbare Kohlenstoffmaterialien bevorzugt aus günstigen und nachhaltigen Kohlenstoffquellen. Es ist allerdings nicht leicht Vorläuferverbindungen auszumachen, welche sich einerseits für verschiedene Herstellungsverfahren eignen und deren Kohlenstoffprodukte andererseits in spezifischen Eigenschaften, wie der Struktur, des Stickstoffanteils, der Oberfläche und der Porengrößen, eingestellt werden können. In diesem Zusammenhang können natürliche Polyphenole, etwa überschüssige Tannine aus der Weinproduktion, eine neue Welt zu hoch funktionalen und vielseitig einstellbaren Kohlenstoffmaterialien mit hohen Ausbeuten öffnen.
Das Hauptziel dieser vorliegenden Thesis war es neue funktionale, einstellbare und skalierbare nanostrukturierte Kohlenstoffmaterialien aus Tanninen (insbesondere Tanninsäure) für unterschiedliche elektrochemische Zwecke zu synthetisieren und zu charakterisieren. Ermöglicht wurde dies durch unterschiedliche synthetische Herangehensweisen, wie etwa der polymeren Strukturdirektion, dem ionothermalen Templatieren und der weichen Templatierung. An Stelle des weitläufig gebräuchlichen, aber kanzerogenen Vernetzungsagens Formaldehyd wurden bei den vorgestellten Synthesen Harnstoff und Thioharnstoff gewählt, um zugleich die synthetisierten Kohlenmaterialien variabel dotieren zu können.
Daher wurden im ersten Teil der Arbeit die Wechselwirkungen, Reaktionen und thermischen Verhaltensweisen von Tanninsäure und Mixturen von Tanninsäure und Harnstoff bzw. Thioharnstoff untersucht, um daraus wichtige Erkenntnisse für die verschiedenen Kohlenstoffsynthesen zu gewinnen.
Durch die Verwendung eines polymeren Strukturierungsagenz Pluronic P123 konnten in einer ersten Kohlenstoffsynthese nachhaltige und dotierbare Kohlenstoffpartikel mit Durchmessern im Nanometerbereich aus Tanninsäure und Harnstoff hergestellt werden. Es konnte dabei gezeigt werden, dass durch die Modifikation der verschiedenen Syntheseparameter die Kohlenstoffnanopartikel gemäß ihres gemittelten Partikeldurchmessers, ihrer BET-Oberfläche, ihrer Komposition, ihrer Leitfähigkeit und ihrer chemischen Stabilität einstellbar sind. Dies eröffnete die Möglichkeit diese Kohlenstoffpartikel als alternatives und nachhaltiges Rußmaterial einzusetzen.
Weiterhin war es durch die ionothermale Templatierung möglich poröse, dotierte und kontrollierbare Kohlenstoffpartikel mit hohen spezifischen Oberflächen aus den gewählten Präkursorverbindungen zu synthetisieren, die sich für den Einsatz in Superkondensatoren eignen.
Auf diesen Erkenntnissen aufbauend konnten mittels der Rotationsbeschichtung poröse binderfreie und strukturierte Kohlenstofffilme synthetisiert werden, die eine spinodale Struktur aufwiesen. Anhand der Modifikation der Stammlösungskonzentration, der Rotationsgeschwindigkeit und der verwendeten Substrate konnten die Filmdicke (100-1000 nm), die Morphologie und Gesamtoberfläche gezielt beeinflusst werden. Die erweiterte elektrochemische Analyse zeigte außerdem ein sehr gut zugängliches Porensystem der porösen Kohlenstofffilme.
Allumfassend konnten demnach verschiedene Synthesewege für Kohlenstoffmaterialien aus Tanninen aufgezeigt werden, die verschiedenartig strukturiert und kontrolliert werden können und sich für diverse Anwendungsgebiete eignen.
Functional nanoporous carbon-based materials derived from oxocarbon-metal coordination complexes
(2017)
Nanoporous carbon based materials are of particular interest for both science and industry due to their exceptional properties such as a large surface area, high pore volume, high electroconductivity as well as high chemical and thermal stability. Benefiting from these advantageous properties, nanoporous carbons proved to be useful in various energy and environment related applications including energy storage and conversion, catalysis, gas sorption and separation technologies. The synthesis of nanoporous carbons classically involves thermal carbonization of the carbon precursors (e.g. phenolic resins, polyacrylonitrile, poly(vinyl alcohol) etc.) followed by an activation step and/or it makes use of classical hard or soft templates to obtain well-defined porous structures. However, these synthesis strategies are complicated and costly; and make use of hazardous chemicals, hindering their application for large-scale production. Furthermore, control over the carbon materials properties is challenging owing to the relatively unpredictable processes at the high carbonization temperatures.
In the present thesis, nanoporous carbon based materials are prepared by the direct heat treatment of crystalline precursor materials with pre-defined properties. This synthesis strategy does not require any additional carbon sources or classical hard- or soft templates. The highly stable and porous crystalline precursors are based on coordination compounds of the squarate and croconate ions with various divalent metal ions including Zn2+, Cu2+, Ni2+, and Co2+, respectively. Here, the structural properties of the crystals can be controlled by the choice of appropriate synthesis conditions such as the crystal aging temperature, the ligand/metal molar ratio, the metal ion, and the organic ligand system. In this context, the coordination of the squarate ions to Zn2+ yields porous 3D cube crystalline particles. The morphology of the cubes can be tuned from densely packed cubes with a smooth surface to cubes with intriguing micrometer-sized openings and voids which evolve on the centers of the low index faces as the crystal aging temperature is raised. By varying the molar ratio, the particle shape can be changed from truncated cubes to perfect cubes with right-angled edges.
These crystalline precursors can be easily transformed into the respective carbon based materials by heat treatment at elevated temperatures in a nitrogen atmosphere followed by a facile washing step. The resulting carbons are obtained in good yields and possess a hierarchical pore structure with well-organized and interconnected micro-, meso- and macropores. Moreover, high surface areas and large pore volumes of up to 1957 m2 g-1 and 2.31 cm3 g-1 are achieved, respectively, whereby the macroscopic structure of the precursors is preserved throughout the whole synthesis procedure.
Owing to these advantageous properties, the resulting carbon based materials represent promising supercapacitor electrode materials for energy storage applications. This is exemplarily demonstrated by employing the 3D hierarchical porous carbon cubes derived from squarate-zinc coordination compounds as electrode material showing a specific capacitance of 133 F g-1 in H2SO4 at a scan rate of 5 mV s-1 and retaining 67% of this specific capacitance when the scan rate is increased to 200 mV s-1.
In a further application, the porous carbon cubes derived from squarate-zinc coordination compounds are used as high surface area support material and decorated with nickel nanoparticles via an incipient wetness impregnation. The resulting composite material combines a high surface area, a hierarchical pore structure with high functionality and well-accessible pores. Moreover, owing to their regular micro-cube shape, they allow for a good packing of a fixed-bed flow reactor along with high column efficiency and a minimized pressure drop throughout the packed reactor. Therefore, the composite is employed as heterogeneous catalyst in the selective hydrogenation of 5-hydroxymethylfurfural to 2,5-dimethylfuran showing good catalytic performance and overcoming the conventional problem of column blocking.
Thinking about the rational design of 3D carbon geometries, the functions and properties of the resulting carbon-based materials can be further expanded by the rational introduction of heteroatoms (e.g. N, B, S, P, etc.) into the carbon structures in order to alter properties such as wettability, surface polarity as well as the electrochemical landscape. In this context, the use of crystalline materials based on oxocarbon-metal ion complexes can open a platform of highly functional materials for all processes that involve surface processes.
In dieser Arbeit werden drei Themen im Zusammenhang mit den spektroskopischen Eigenschaften von Cumarin- (Cou) und DBD-Farbstoffen ([1,3]Dioxolo[4,5-f][1,3]benzodioxol) behandelt. Der erste Teil zeigt die grundlegende spektroskopische Charakterisierung von 7-Aminocumarinen und ihre potentielle Anwendung als Fluoreszenzsonde für Fluoreszenzimmunassays. Im zweiten Teil werden mit die photophysikalischen Eigenschaften der Cumarine genutzt um Cou- und DBD-funktionalisierte Oligo-Spiro-Ketal-Stäbe (OSTK) und ihre Eigenschaften als Membransonden zu untersuchen. Der letzte Teil beschäftigt sich mit der Synthese und der Charakterisierung von Cou- und DBD-funktionalisierten Polyprolinen als Referenzsysteme für schwefelfunktionalisierte OSTK-Stäbe und ihrer Kopplung an Goldnanopartikel.
Immunochemische Analysemethoden sind in der klinischen Diagnostik sehr erfolgreich und werden heute auch für die Nahrungsmittelkontrolle und Überwachung von Umweltfragen mit einbezogen. Dadurch sind sie von großem Interesse für weitere Forschungen. Unter den verschiedenen Immunassays zeichnen sich lumineszenzbasierte Formate durch ihre herausragende Sensitivität aus, die dieses Format für zukünftige Anwendungen besonders attraktiv macht. Die Notwendigkeit von Multiparameterdetektionsmöglichkeiten erfordert einen Werkzeugkasten mit Farbstoffen, um die biochemische Reaktion in ein optisch detektierbares Signal umzuwandeln. Hier wird bei einem Multiparameteransatz jeder Analyt durch einen anderen Farbstoff mit einer einzigartigen Emissionsfarbe, die den blauen bis roten Spektralbereich abdecken, oder eine einzigartige Abklingzeit detektiert. Im Falle eines kompetitiven Immunassayformats wäre für jeden der verschiedenen Farbstoffe ein einzelner Antikörper erforderlich. In der vorliegenden Arbeit wird ein leicht modifizierter Ansatz unter Verwendung einer Cumarineinheit, gegen die hochspezifische monoklonale Antikörper (mAb) erzeugt wurden, als grundlegendes Antigen präsentiert. Durch eine Modifikation der Stammcumarineinheit an einer Position des Moleküls, die für die Erkennung durch den Antikörper nicht relevant ist, kann auf den vollen Spektralbereich von blau bis tiefrot zugegriffen werden. In dieser Arbeit wird die photophysikalische Charakterisierung der verschiedenen Cumarinderivate und ihrer entsprechenden Immunkomplexe mit zwei verschiedenen, aber dennoch hochspezifischen, Antikörpern präsentiert. Die Cumarinfarbstoffe und ihre Immunkomplexe wurden durch stationäre und zeitaufgelöste Absorptions- sowie Fluoreszenzemissionsspektroskopie charakterisiert. Darüber hinaus wurden Fluoreszenzdepolarisationsmessungen durchgeführt, um die Daten zu vervollständigen, die die verschiedenen Bindungsmodi der beiden Antikörper betonten. Im Gegensatz zu häufig eingesetzten Nachweissystemen wurde eine massive Fluoreszenzverstärkung bei der Bildung des Antikörper-Farbstoffkomplexes bis zu einem Faktor von 50 gefunden. Wegen der leichten Emissionsfarbenänderung durch das Anpassen der Cumarinsubstitution in der für die Antigenbindung nicht relevanten Position des Elternmoleküls, ist eine Farbstoff-Toolbox vorhanden, die bei der Konstruktion von kompetitiven Multiparameterfluoreszenzverstärkungsimmunassays verwendet werden kann.
Oligo-Spiro-Thio-Ketal-Stäbe werden aufgrund ihres hydrophoben Rückgrats leicht in Doppellipidschichten eingebaut und deshalb als optische Membransonde verwendet. Wegen ihres geringen Durchmessers wird nur eine minimale Störung der Doppellipidschicht verursacht. Durch die Markierung mit Fluoreszenzfarbstoffen sind neuartige Förster-Resonanz-Energietransfersonden mit hoch definierten relativen Orientierungen der Übergangsdipolmomente der Donor- und Akzeptorfarbstoffe zugänglich und macht die Klasse der OSTK-Sonden zu einem leistungsstarken, flexiblen Werkzeugkasten für optische Biosensoranwendungen. Mit Hilfe von stationären und zeitaufgelösten Fluoreszenzexperimenten wurde der Einbau von Cumarin- und DBD markierten OSTK-Stäben in großen unilamellaren Vesikeln untersucht und die Ergebnisse durch Fluoreszenzdepolarisationsmessungen untermauert.
Der letzte Teil dieser Arbeit beschäftigt sich mit der Synthese und Charakterisierung von Cou- und DBD-funktionalisierten Polyprolinen und ihrer Kopplung an Goldnanopartikel. Die farbstoffmarkierten Polyproline konnten erfolgreich hergestellt werden. Es zeigten sich deutlich Einflüsse auf die spektroskopischen Eigenschaften der Farbstoffe durch die Bindung an die Polyprolinhelix. Die Kopplung an die 5 nm großen AuNP konnte erfolgreich durchgeführt werden. Die Erfahrungen, die durch die Kopplung der Polyproline an die AuNP, gewonnen wurde, ist die Basis für eine Einzelmolekül-AFM-FRET-Nanoskopie mit OSTK-Stäben.
In der vorliegenden Arbeit wurden verschiedene Polymere hergestellt, die bestimmte funktionelle Gruppen beinhalten. Diese Gruppen werden zum Teil durch Alkylketten geschützt, zum Teil liegen sie ungeschützt im Polymer vor. Mit diesen Polymeren wurden Untersuchungen mit knochenähnlichen Materialien sogenanntem Calciumphosphat durchgeführt. Es wurde der Einfluss der verschiedenen Polymere auf die Bildung dieser knochenähnlichen Substanzen untersucht und auch der Einfluss auf die Stabilität und das Auflösungsverhalten der Calciumphosphate. Dabei sollte ein besonderes Augenmerk auf die funktionellen Gruppen, sogenannte Phosphonsäuren und deren Ester, die die Phosphonsäuren schützen, gesetzt werden. Es stellte sich heraus, dass bei der Bildung der knochenähnlichen Materialien die Polymere mit Estergruppen eine leichte Förderung der Calciumphosphat-Bildung verursachen, während die ungeschützten Polymere die Bildung des „Knochenmaterials“ sehr stark verzögern. Dieser Effekt verstärkt sich noch, wenn eine weitere bestimmte Komponente zum Polymer hinzukommt und somit ein Copolymer gebildet wird. Diese Copolymere beschleunigen bzw. verlangsamen die Calciumphosphatbildung noch stärker. Werden Polymere mit einem anderen Polymergerüst aber den gleichen Phosphonsäuresetern in den Seitenketten verwendet, ändert sich der Einfluss der Calciumphosphat-Bildung wenig. Verglichen mit Polymeren ohne solche Phosphonsäuregruppen wird erkennbar, dass es weniger die Phosphonsäuregruppe ist, die die Mineralisation beeinflusst, sondern es eher eine Folge der Säure im Polymer ist.
Wird die Stabilisierung und Auflösung der Knochenähnlichen Substanzen betrachtet, fällt auf, dass auch hier wieder die Säuren den größten Effekt ausüben. Die Phosphonsäuregruppen scheinen dabei jedoch tatsächlich einen besonderen Effekt auszuüben, da bei diesen die Stabilisierung und auch das Auflösungsvermögen von Calciumphospaht von allen untersuchten Polymeren am größten sind.
In der Arbeit konnte außerdem gezeigt werden, dass die Polymere und Copolymere mit Phosphonsäuregruppen einen leicht positiven Effekt auf die Zahngesundheit zeigen. Die Zahl von Bakterien auf der Zahnoberfläche konnte reduziert werden und bei der Untersuchung der Zahnauflösung wurde eine glattere Zahnoberfläche erhalten, jedoch wurde auch mit den untersuchten Polymeren der Zahn im Inneren angegriffen. Weitere Untersuchungen können hier noch genaueren Aufschluss geben. Außerdem sollten auch die Polymere mit dem unterschiedlichen Polymergerüst und Phosphonsäureestergruppen untersucht werden.
Letztere Polymere wurden verwendet, um festere “gelartige“ Polymernetzwerke herzustellen und deren Einfluss auf die Calciumphosphatmineralisation zu untersuchen. Es stellte sich heraus, dass ohne das Einbetten einiger Calciumphosphatteilchen keine Bildung von Calciumphospaht an den Materialien ausgelöst wurde, wurden die sogenannten Hydrogele jedoch mit Calciumphosphatpartikeln geimpft, konnte deutliches weiteres Calciumphosphatwachstum beobachtet werden. Das Material lässt sich auch in verschiedene Formen bringen. Somit könnte das System nach weiteren Untersuchungen zur Verträglichkeit mit Zellen oder Geweben ein mögliches Material für Implantate darstellen, mit denen gezielt Knochenwachstum eingeleitet werden könnte.
Magnetische Eisenoxidnanopartikel werden bereits seit geraumer Zeit erfolgreich als MRT-Kontrastmittel in der klinischen Bildgebung eingesetzt. Durch Optimierung der magnetischen Eigenschaften der Nanopartikel kann die Aussagekraft von MR-Aufnahmen verbessert und somit der diagnostische Wert einer MR-Anwendung weiter erhöht werden. Neben der Verbesserung bestehender Verfahren wird die bildgebende Diagnostik ebenso durch die Entwicklung neuer Verfahren, wie dem Magnetic Particle Imaging, vorangetrieben. Da hierbei das Messsignal von den magnetischen Nanopartikeln selbst erzeugt wird, birgt das MPI einen enormen Vorteil hinsichtlich der Sensitivität bei gleichzeitig hoher zeitlicher und räumlicher Auflösung. Da es aktuell jedoch keinen kommerziell vertriebenen in vivo-tauglichen MPI-Tracer gibt, besteht ein dringender Bedarf an geeigneten innovativen Tracermaterialien. Daraus resultierte die Motivation dieser Arbeit biokompatible und superparamagnetische Eisenoxidnanopartikel für den Einsatz als in vivo-Diagnostikum insbesondere im Magnetic Particle Imaging zu entwickeln. Auch wenn der Fokus auf der Tracerentwicklung für das MPI lag, wurde ebenso die MR-Performance bewertet, da geeignete Partikel somit alternativ oder zusätzlich als MR-Kontrastmittel mit verbesserten Kontrasteigenschaften eingesetzt werden könnten.
Die Synthese der Eisenoxidnanopartikel erfolgte über die partielle Oxidation von gefälltem Eisen(II)-hydroxid und Green Rust sowie eine diffusionskontrollierte Kopräzipitation in einem Hydrogel.
Mit der partiellen Oxidation von Eisen(II)-hydroxid und Green Rust konnten erfolgreich biokompatible und über lange Zeit stabile Eisenoxidnanopartikel synthetisiert werden. Zudem wurden geeignete Methoden zur Formulierung und Sterilisierung etabliert, wodurch zahlreiche Voraussetzungen für eine Anwendung als in vivo-Diagnostikum geschaffen wurden. Weiterhin ist auf Grundlage der MPS-Performance eine hervorragende Eignung dieser Partikel als MPI-Tracer zu erwarten, wodurch die Weiterentwicklung der MPI-Technologie maßgeblich vorangetrieben werden könnte. Die Bestimmung der NMR-Relaxivitäten sowie ein initialer in vivo-Versuch zeigten zudem das große Potential der formulierten Nanopartikelsuspensionen als MRT-Kontrastmittel. Die Modifizierung der Partikeloberfläche ermöglicht ferner die Herstellung zielgerichteter Nanopartikel sowie die Markierung von Zellen, wodurch das mögliche Anwendungsspektrum maßgeblich erweitert wurde.
Im zweiten Teil wurden Partikel durch eine diffusionskontrollierte Kopräzipitation im Hydrogel, wobei es sich um eine bioinspirierte Modifikation der klassischen Kopräzipitation handelt, synthetisiert, wodurch Partikel mit einer durchschnittlichen Kristallitgröße von 24 nm generiert werden konnten. Die Bestimmung der MPS- und MR-Performance elektrostatisch stabilisierter Partikel ergab vielversprechende Resultate. In Vorbereitung auf die Entwicklung eines in vivo-Diagnostikums wurden die Partikel anschließend erfolgreich sterisch stabilisiert, wodurch der kolloidale Zustand in MilliQ-Wasser über lange Zeit aufrechterhalten werden konnte. Durch Zentrifugation konnten die Partikel zudem erfolgreich in verschiedene Größenfraktionen aufgetrennt werden. Dies ermöglichte die Bestimmung der idealen Aggregatgröße dieses Partikelsystems in Bezug auf die MPS-Performance.
Thermal cis-trans isomerization of azobenzene studied by path sampling and QM/MM stochastic dynamics
(2017)
Azobenzene-based molecular photoswitches have extensively been applied to biological systems, involving photo-control of peptides, lipids and nucleic acids. The isomerization between the stable trans and the metastable cis state of the azo moieties leads to pronounced changes in shape and other physico-chemical properties of the molecules into which they are incorporated. Fast switching can be induced via transitions to excited electronic states and fine-tuned by a large number of different substituents at the phenyl rings. But a rational design of tailor-made azo groups also requires control of their stability in the dark, the half-lifetime of the cis isomer. In computational chemistry, thermally activated barrier crossing on the ground state Born-Oppenheimer surface can efficiently be estimated with Eyring’s transition state theory (TST) approach; the growing complexity of the azo moiety and a rather heterogeneous environment, however, may render some of the underlying simplifying assumptions problematic.
In this dissertation, a computational approach is established to remove two restrictions at once: the environment is modeled explicitly by employing a quantum mechanical/molecular mechanics (QM/MM) description; and the isomerization process is tracked by analyzing complete dynamical pathways between stable states. The suitability of this description is validated by using two test systems, pure azo benzene and a derivative with electron donating and electron withdrawing substituents (“push-pull” azobenzene). Each system is studied in the gas phase, in toluene and in polar DMSO solvent. The azo molecules are treated at the QM level using a very recent, semi-empirical approximation to density functional theory (density functional tight binding approximation). Reactive pathways are sampled by implementing a version of the so-called transition path sampling method (TPS), without introducing any bias into the system dynamics. By analyzing ensembles of reactive trajectories, the change in isomerization pathway from linear inversion to rotation in going from apolar to polar solvent, predicted by the TST approach, could be verified for the push-pull derivative. At the same time, the mere presence of explicit solvation is seen to broaden the distribution of isomerization pathways, an effect TST cannot account for.
Using likelihood maximization based on the TPS shooting history, an improved reaction coordinate was identified as a sine-cosine combination of the central bend angles and the rotation dihedral, r (ω,α,α′). The computational van’t Hoff analysis for the activation entropies was performed to gain further insight into the differential role of solvent for the case of the unsubstituted and the push-pull azobenzene. In agreement with the experiment, it yielded positive activation entropies for azobenzene in the DMSO solvent while negative for the push-pull derivative, reflecting the induced ordering of solvent around the more dipolar transition state associated to the latter compound. Also, the dynamically corrected rate constants were evaluated using the reactive flux approach where an increase comparable to the experimental one was observed for a high polarity medium for both azobenzene derivatives.
In der vorliegenden Arbeit konnten erfolgreich zwei unterschiedliche Hybridmaterialien (HM) über die Sol-Gel-Methode synthetisiert werden. Bei den HM handelt es sich um Monolithe mit einem Durchmesser von bis zu 4,5 cm. Das erste HM besteht aus Titandioxid und Bombyx mori Seide und wird als TS bezeichnet, während das zweite weniger Seide und zusätzlich Polyethylenoxid (PEO) enthält und daher als TPS abgekürzt wird. Einige der HM wurden nach der Synthese in eine wässrige Tetrachloridogoldsäure-Lösung getaucht, wodurch sich auf der Oberfläche Goldnanopartikel gebildet haben.
Die Materialien wurden mittels Elektronenmikroskopie, energiedispersiver Röntgenspektroskopie, Ramanspektroskopie sowie Röntgenpulverdiffraktometrie charakterisiert. Die Ergebnisse zeigen, dass beide HM aus etwa 5 nm großen, sphärischen Titandioxidnanopartikeln aufgebaut sind, die primär aus Anatas und zu einem geringen Anteil aus Brookit bestehen. Die Goldnanopartikel bei TPS_Au waren größer und polydisperser als die Goldnanopartikel auf dem TS_Au HM. Darüber hinaus sind die Goldnanopartikel im TS HM tiefer in das Material eingedrungen als beim TPS HM.
Die weiterführende Analyse der HM mittels Elementaranalyse und thermogravimetrischer Analyse ergab für TPS einen geringeren Anteil an organischen Bestandteilen im HM als für TS, obwohl für beide Synthesen die gleiche Masse an organischen Materialien eingesetzt wurde. Es wird vermutet, dass das PEO während der Synthese teilweise wieder aus dem Material herausgewaschen wird. Diese Theorie korreliert mit den Ergebnissen aus der Stickstoffsorption und der Quecksilberporosimetrie, die für das TPS HM eine höhere Oberfläche als für das TS HM anzeigten.
Die Variation einiger Syntheseparameter wie die Menge an Seide und PEO oder die Zusammensetzung der Titandioxidvorläuferlösung hatte einen großen Einfluss auf die synthetisierten HM. Während unterschiedliche Mengen an PEO die Größe des HM beeinflussten, konnte ohne Seide kein HM in einer ähnlichen Größe hergestellt werden. Die Bildung der HM wird stark von der Zusammensetzung der Titandioxidvorläuferlösung beeinflusst. Eine Veränderung führte daher nur selten zur Bildung eines homogenen HM.
Die in dieser Arbeit synthetisierten HM wurden als Photokatalysatoren für die Wasserspaltung und den Abbau von Methylenblau eingesetzt. Bei der photokatalytischen Wasserspaltung wurde zunächst der Einfluss unterschiedlicher Goldkonzentrationen beim TPS HM auf die Wasserstoffausbeute untersucht. Die besten Ergebnisse wurden bei einer Menge von 2,5 mg Tetrachloridogoldsäure erhalten. Darüber hinaus wurde gezeigt, dass mit dem TPS HM eine deutlich höhere Menge an Wasserstoff gewonnen werden konnte als mit dem TS HM. Die Ursachen für die schlechtere Aktivität werden in der geringeren spezifischen Oberfläche, der unterschiedlichen Porenstruktur, dem höheren Anteil an Seide und besonders in der geringeren Größe und höheren Eindringtiefe der Goldnanopartikel vermutet. Darüber hinaus konnte mit einem höheren UV-Anteil in der Lichtquelle sowie durch die Zugabe von Ethanol als Opferreagenz eine Zunahme der Wasserstoffausbeute erzielt werden.
Bei dem Methylenblauabbau wurde für beide HM zunächst nur eine Adsorption des Methylenblaus beobachtet. Nach der Zugabe von Wasserstoffperoxid konnte nach 8 h bereits eine fast vollständige Oxidation des Methylenblaus unter sichtbarem Licht beobachtet werden. Die Ursache für die etwas höhere Aktivität von TPS gegenüber TS wird in der unterschiedlichen Porenstruktur und dem höheren Anteil an Seide im TS HM vermutet. Insgesamt zeigen beide HM eine gute photokatalytische Aktivität für den Abbau von Methylenblau im Vergleich zu den erhaltenen Werten aus der Literatur.
Im Rahmen dieser Arbeit wurden zum einen erste Oligospiro(thio)ketal (OS(T)K)-basierte Modellsysteme (molekulare Sonden) für abstandsabhängige Messungen mittels Förster-Resonanz-Energietransfer (FRET) und zum anderen Sensorfluorophore, basierend auf einem DBD-Fluorophor und BAPTA, zur Messung der intrazellulären Calcium-Konzentration dargestellt.
Für die Synthese von molekularen Sonden für abstandsabhängige Messungen wurden verschiedenste einfach- und doppelt-markierte OS(T)K-Stäbe entwickelt und spektroskopisch untersucht. Die OS(T)K-Stäbe, sogenannte molekulare Stäbe, dienten als starre Abstandshalter zwischen den Fluorophoren. Als Fluorophore wurden Derivate von 6,7-Dihydroxy-4-methylcoumarin (Donor) und Acyl-DBD (Akzeptor) verwendet, die zusammen ein FRET-Paar bilden. Die Fluorophore wurden so funktionalisiert, dass sie sowohl unbeweglich bzw. „starr“, als auch beweglich bzw. „flexibel“ an den OS(T)K-Stab gebunden werden konnten. Für die Synthese der OS(T)K-Stäbe wurden ebenfalls eine Reihe an unterschiedlich langen und kurzen Stabbausteinen synthetisiert. Auf diese Weise wurden eine Vielzahl an verschiedensten einfach- und doppelt-markierten OS(T)K-Stäben dargestellt, deren Fluorophore sowohl „starr“ als auch „flexibel“ gebunden sind. Die dargestellten Stäbe wurden in verschiedensten Lösungsmitteln spektroskopisch untersucht, um anschließend das Verhalten in Vesikel, die eine biomimetische Umgebung darstellen, zu beurteilen. Es wurde festgestellt, dass sich die Stäbe erfolgreich in die Vesikelmembran einlagerten und hohe FRET-Effizienzen aufweisen.
Des Weiteren wurde ein FRET-Paar dargestellt, das sich durch 2-Photonenabsorpion im NIR-Bereich anregen lässt. Es wurde in den lebenden Zellen mittels Fluoreszenzlebenszeitmikroskopie (FLIM) untersucht.
Zur Untersuchung von intrazellulärem Calcium wurden zwei verschiedene DBD-Fluorophore über einen kurzen Linker mit dem Calcium-Chelator BAPTA verknüpft. Die dargestellten Fluorophore wurden sowohl in vitro als auch in vivo auf ihre Calcium-Sensitivität überprüft. Mittels FLIM wurden in lebenden Zellen die Fluoreszenzlebenszeitverteilungen der Fluorophore nach Calcium-Konzentrationsänderungen detektiert.
This project was focused on generating ultra thin stimuli responsive membranes with an embedded transmembrane protein to act as the pore. The membranes were formed by crosslinking of transmembrane protein polymer conjugates. The conjugates were self assembled on air water interface and the polymer chains crosslinked using a UV crosslinkable comonomer to engender the membrane. The protein used for the studies reported herein was one of the largest transmembrane channel proteins, ferric hydroxamate uptake protein component A (FhuA), found in the outer membrane of Escherichia coli (E. coli). The wild type protein and three genetic variants of FhuA were provided by the group of Prof. Schwaneberg in Aachen. The well known thermo responsive poly(N isopropylacrylamide) (PNIPAAm) and the pH and thermo responsive polymer poly((2-dimethylamino)ethyl methacrylate) (PDMAEMA) were conjugated to FhuA and the genetic variants via controlled radical polymerization (CRP) using grafting from technique. These polymers were chosen because they would provide stimuli handles in the resulting membranes. The reported polymerization was the first ever attempt to attach polymer chains onto a membrane protein using site specific modification.
The conjugate synthesis was carried out in two steps – a) FhuA was first converted into a macroinitiator by covalently linking a water soluble functional CRP initiator to the lysine residues. b) Copper mediated CRP was then carried out in pure buffer conditions with and without sacrificial initiator to generate the conjugates.
The challenge was carrying out the modifications on FhuA without denaturing it. FhuA, being a transmembrane protein, requires amphiphilic species to stabilize its highly hydrophobic transmembrane region. For the experiments reported in this thesis, the stabilizing agent was 2 methyl 2,4-pentanediol (MPD). Since the buffer containing MPD cannot be considered a purely aqueous system, and also because MPD might interfere with the polymerization procedure, the reaction conditions were first optimized using a model globular protein, bovine serum albumin (BSA). The optimum conditions were then used for the generation of conjugates with FhuA.
The generated conjugates were shown to be highly interfacially active and this property was exploited to let them self assemble onto polar apolar interfaces. The emulsions stabilized by particles or conjugates are referred to as Pickering emulsions. Crosslinking conjugates with a UV crosslinkable co monomer afforded nano thin micro compartments. Interfacial self assembly at the air water interface and subsequent UV crosslinking also yielded nano thin, stimuli responsive membranes which were shown to be mechanically robust. Initial characterization of the flux and permeation of water through these membranes is also reported herein. The generated nano thin membranes with PNIPAAm showed reduced permeation at elevated temperatures owing to the resistance by the hydrophobic and thus water-impermeable polymer matrix, hence confirming the stimulus responsivity.
Additionally, as a part of collaborative work with Dr. Changzhu Wu, TU Dresden, conjugates of three enzymes with current/potential industrial relevance (candida antarctica lipase B, benzaldehyde lyase and glucose oxidase) with stimuli responsive polymers were synthesized. This work aims at carrying out cascade reactions in the Pickering emulsions generated by self assembled enzyme polymer conjugate.
Herstellung anisotroper Kolloide mittels templatgesteuerter Assemblierung und Kontaktdruckverfahren
(2017)
Diese Arbeit befasste sich mit neuen Konzepten zur Darstellung anisotroper Partikelsysteme durch Anordnung von funktionalisierten Partikeln unter Zuhilfenahme etablierter Methoden wie der templatgestützten Assemblierung von Partikeln und dem Mikrokontaktdruck.
Das erste Teilprojekt beschäftigte sich mit der kontrollierten Herstellung von Faltenstrukturen im Mikro- bis Nanometerbereich. Die Faltenstrukturen entstehen durch die Relaxation eines Systems bestehend aus zwei übereinander liegender Schichten unterschiedlicher Elastizität. In diesem Fall wurden Falten auf einem elastischen PDMS-Substrat durch Generierung einer Oxidschicht auf der Substratoberfläche mittels Plasmabehandlung erzeugt. Die Dicke der Oxidschicht, die über verschiedene Parameter wie Behandlungszeit, Prozessleistung, Partialdruck des plasmaaktiven Gases, Vernetzungsgrad, Deformation sowie Substratdicke einstellbar war, bestimmte Wellenlänge und Amplitude der Falten.
Das zweite Teilprojekt hatte die Darstellung komplexer, kolloidaler Strukturen auf Basis supramolekularer Wechselwirkungen zum Ziel. Dazu sollte vor allem die templatgestützte Assemblierung von Partikeln sowohl an fest-flüssig als auch flüssig-flüssig Grenzflächen genutzt werden. Für Erstere sollten die in Teilprojekt 1 hergestellten Faltenstrukturen als Templat, für Letztere Pickering-Emulsionen zur Anwendung kommen. Im ersten Fall wurden verschiedene, modifizierte Silicapartikel und Magnetitnanopartikel, deren Größe und Oberflächenfunktionalität (Cyclodextrin-, Azobenzol- und Arylazopyrazolgruppen) variierte, in Faltenstrukturen angeordnet. Die Anordnung hing dabei nicht nur vom gewählten Verfahren, sondern auch von Faktoren wie der Partikelkonzentration, der Oberflächenladung oder dem Größenverhältnis der Partikel zur Faltengeometrie ab.
Die Kombination von Cyclodextrin (CD)- und Arylazopyrazol-modifizierten Partikeln ermöglichte, auf Basis einer Wirt-Gast-Wechselwirkung zwischen den Partikeltypen und einer templatgesteuerten Anordnung, die Bildung komplexer und strukturierter Formen in der Größenordnung mehrerer Mikrometer. Dieses System kann einerseits als Grundlage für die Herstellung verschiedener Janus-Partikel herangezogen werden, andererseits stellt die gerichtete Vernetzung zweier Partikelsysteme zu größeren Aggregaten den Grundstein für neuartige, funktionale Materialien dar. Neben der Anordnung an fest-flüssig Grenzflächen konnte außerdem nachgewiesen werden, dass Azobenzol-funktionalisierte Silicapartikel in der Lage sind, Pickering-Emulsionen über mehrere Monate zu stabilisieren. Die Stabilität und Größe der Emulsionsphase kann über Parameter, wie das Volumenverhältnis und die Konzentration, gesteuert werden. CD-funktionalisierte Silicapartikel besaßen dagegen keine Grenzflächenaktivität, während es CD-basierten Polymeren wiederum möglich war, durch die Ausbildung von Einschlusskomplexen mit den hydrophoben Molekülen der Ölphase stabile Emulsionen zu bilden. Dagegen zeigte die Kombination zwei verschiedener Partikelsysteme keinen oder einen destabilisierenden Effekt bezüglich der Ausbildung von Emulsionen.
Im letzten Teilprojekt wurde die Herstellung multivalenter Silicapartikel mittels Mikrokontaktdruck untersucht. Die Faltenstrukturen wurden dabei als Stempel verwendet, wodurch es möglich war, die Patch-Geometrie über die Wellenlänge der Faltenstrukturen zu steuern. Als Tinte diente das positiv geladene Polyelektrolyt Polyethylenimin (PEI), welches über elektrostatische Wechselwirkungen auf unmodifizierten Silicapartikeln haftet. Im Gegensatz zum Drucken mit flachen Stempeln fiel dabei zunächst auf, dass sich die Tinte bei den Faltenstrukturen nicht gleichmäßig über die gesamte Substratfläche verteilt, sondern hauptsächlich in den Faltentälern vorlag. Dadurch handelte es sich bei dem Druckprozess letztlich nicht mehr um ein klassisches Mikrokontaktdruckverfahren, sondern um ein Tiefdruckverfahren. Über das Tiefdruckverfahren war es dann aber möglich, sowohl eine als auch beide Partikelhemisphären gleichzeitig und mit verschiedenen Funktionalitäten zu modifizieren und somit multivalente Silicapartikel zu generieren. In Abhängigkeit der Wellenlänge der Falten konnten auf einer Partikelhemisphäre zwei bis acht Patches abgebildet werden. Für die Patch-Geometrie, sprich Größe und Form der Patches, spielten zudem die Konzentration der Tinte auf dem Stempel, das Lösungsmittel zum Ablösen der Partikel nach dem Drucken sowie die Stempelhärte eine wichtige Rolle. Da die Stempelhärte aufgrund der variierenden Dicke der Oxidschicht bei verschiedenen Wellenlängen nicht kontant ist, wurden für den Druckprozess meist Abgüsse der Faltensubstrate verwendet. Auf diese Weise war auch die Vergleichbarkeit bei variierender Wellenlänge gewährleistet. Neben dem erfolgreichen Nachweis der Modifikation mittels Tiefdruckverfahren konnte auch gezeigt werden, dass über die Komplexierung mit PEI negativ geladene Nanopartikel auf die Partikeloberfläche aufgebracht werden können.
Among modern functional materials, the class of nitrogen-containing carbons combines non-toxicity and sustainability with outstanding properties. The versatility of this materials class is based on the opportunity to tune electronic and catalytic properties via the nitrogen content and –motifs: This ranges from the electronically conducting N-doped carbon, where few carbon atoms in the graphitic lattice are substituted by nitrogen, to the organic semiconductor graphitic carbon nitride (g-C₃N₄), with a structure based on tri-s-triazine units.
In general, composites can reveal outstanding catalytic properties due to synergistic behavior, e.g. the formation of electronic heterojunctions. In this thesis, the formation of an “all-carbon” heterojunction was targeted, i.e. differences in the electronic properties of the single components were achieved by the introduction of different nitrogen motives into the carbon lattice. Such composites are promising as metal-free catalysts for the photocatalytic water splitting. Here, hydrogen can be generated from water by light irradiation with the use of a photocatalyst. As first part of the heterojunction, the organic semiconductor g-C₃N₄ was employed, because of its suitable band structure for photocatalytic water splitting, high stability and non-toxicity. The second part was chosen as C₂N, a recently discovered semiconductor. Compared to g-C₃N₄, the less nitrogen containing C₂N has a smaller band gap and a higher absorption coefficient in the visible light range, which is expected to increase the optical absorption in the composite eventually leading to an enhanced charge carrier separation due to the formation of an electronic heterojunction.
The aim of preparing an “all-carbon” composite included the research on appropriate precursors for the respective components g-C₃N₄ and C₂N, as well as strategies for appropriate structuring. This was targeted by applying precursors which can form supramolecular pre-organized structures. This allows for more control over morphology and atom patterns during the carbonization process.
In the first part of this thesis, it was demonstrated how the photocatalytic activity of g-C₃N₄ can be increased by the targeted introduction of defects or surface terminations. This was achieved by using caffeine as a “growth stopping” additive during the formation of the hydrogen-bonded supramolecular precursor complexes. The increased photocatalytic activity of the obtained materials was demonstrated with dye degradation experiments.
The second part of this thesis was focused on the synthesis of the second component C₂N. Here, a deep eutectic mixture from hexaketocyclohexane and urea was structured using the biopolymer chitosan. This scaffolding resulted in mesoporous nitrogen-doped carbon monoliths and beads. CO₂- and dye-adsorption experiments with the obtained monolith material revealed a high isosteric heat of CO₂-adsorption and showed the accessibility of the monolithic pore system to larger dye molecules. Furthermore, a novel precursor system for C₂N was explored, based on organic crystals from squaric acid and urea. The respective C₂N carbon with an unusual sheet-like morphology could be synthesized by carbonization of the crystals at 550 °C. With this precursor system, also microporous C₂N carbon with a BET surface area of 865 m²/g was obtained by “salt-templating” with ZnCl₂.
Finally, the preparation of a g-C₃N₄/C₂N “all carbon” composite heterojunction was attempted by the self-assembly of g-C₃N₄ and C₂N nanosheets and tested for photocatalytic water splitting. Indeed, the composites revealed high rates of hydrogen evolution when compared to bulk g-C₃N₄. However, the increased catalytic activity was mainly attributed to the high surface area of the nanocomposites rather than to the composition. With regard to alternative composite synthesis ways, first experiments indicated N-Methyl-2-pyrrolidon to be suitable for higher concentrated dispersion of C₂N nanosheets. Eventually, the results obtained in this thesis provide precious synthetic contributions towards the preparation and processing of carbon/nitrogen compounds for energy applications.
In the present work side-chain polystyrenes were synthesized and characterized, in order to be applied in multilayer OLEDs fabricated by solution process techniques. Manufacture of optoelectronic devices by solution process techniques is meant to decrease significantly fabrication cost and allow large scale production of such devices.
This dissertation focusses in three series, enveloped in two material classes. The two classes differ to each other in the type of charge transport exhibited, either ambipolar transport or electron transport. All materials were applied in all-organic solution processed green Ir-based devices.
In the first part, a series of ambipolar host materials were developed to transport both charge types, holes and electrons, and be applied especially as matrix for green Ir-based emitters. It was possible to increase devices efficacy by modulating the predominant charge transport type. This was achieved by modification of molecules electron transport part with more electron-deficient heterocycles or by extending the delocalization of the LUMO. Efficiencies up to 28.9 cd/A were observed for all-organic solution-process three layer devices.
In the second part, suitability of triarylboranes and tetraphenylsilanes as electron transport materials was studied. High triplet energies were obtained, up to 2.95 eV, by rational combination of both molecular structures. Although the combination of both elements had a low effect in materials electron transport properties, high efficiencies around 24 cd/A were obtained for the series in all-organic solution-processed two layer devices.
In the last part, benzene and pyridine were chosen as the series electron-transport motif. By controlling the relative pyridine content (RPC) solubility into methanol was induced for polystyrenes with bulky side-chains. Materials with RPC ≥ 0.5 could be deposited orthogonally from solution without harming underlying layers. From the best of our knowledge, this is the first time such materials are applied in this architecture showing moderate efficiencies around 10 cd/A in all-organic solution processed OLEDs.
Overall, the outcome of these studies will actively contribute to the current research on materials for all-solution processed OLEDs.
In this work, a sensor system based on thermoresponsive materials is developed by utilizing a modular approach. By synthesizing three different key monomers containing either a carboxyl, alkene or alkyne end group connected with a spacer to the methacrylic polymerizable unit, a flexible copolymerization strategy has been set up with oligo ethylene glycol methacrylates. This allows to tune the lower critical solution temperature (LCST) of the polymers in aqueous media. The molar masses are variable thanks to the excurse taken in polymerization in ionic liquids thus stretching molar masses from 25 to over 1000 kDa. The systems that were shown shown to be effective in aqueous solution could be immobilized on surfaces by copolymerizing photo crosslinkable units. The immobilized systems were formulated to give different layer thicknesses, swelling ratios and mesh sizes depending on the demand of the coupling reaction.
The coupling of detector units or model molecules is approached via reactions of the click chemistry pool, and the reactions are evaluated on their efficiency under those aspects, too. These coupling reactions are followed by surface plasmon resonance spectroscopy (SPR) to judge efficiency. With these tools at hand, Salmonella saccharides could be selectively detected by SPR. Influenza viruses were detected in solution by turbidimetry in solution as well as by a copolymerized solvatochromic dye to track binding via the changes of the polymers’ fluorescence by said binding event. This effect could also be achieved by utilizing the thermoresponsive behavior. Another demonstrator consists of the detection system bound to a quartz surface, thus allowing the virus detection on a solid carrier.
The experiments show the great potential of combining the concepts of thermoresponsive materials and click chemistry to develop technically simple sensors for large biomolecules and viruses.
In der vorliegenden Arbeit konnte gezeigt werden, dass die beiden verwendeten Amphiphile mit Cholesterol als hydrophoben Block, gute Template für die Mineralisation von Calciumphosphat an der Wasser/Luft-Grenzfläche sind. Mittels Infrarot-Reflexions-Absorptions-Spektroskopie (IRRAS), Röntgenphotoelektronenspektroskopie (XPS), Energie dispersiver Röntgenspektroskopie (EDXS), Elektronenbeugung (SAED) und hochauflösende Transmissionselektronenmikroskopie (HRTEM) konnte die erfolgreiche Mineralisation von Calciumphosphat für beide Amphiphile an der Wasser/Luft-Grenzfläche nachgewiesen werden. Es konnte auch gezeigt werden, dass das Phasenverhalten der beiden Amphiphile und die bei der Mineralisation von Calciumphosphat gebildeten Kristallphasen nicht identisch sind. Beide Amphiphile üben demnach einen unterschiedlichen Einfluss auf den Mineralisationsverlauf aus.
Beim CHOL-HEM konnte sowohl nach 3 h als auch nach 5 h Octacalciumphosphat (OCP) als einzige Kristallphase mittels XPS, SAED, HRTEM und EDXS nachgewiesen werden. Das A-CHOL hingegen zeigte bei der Mineralisation von Calciumphosphat nach 1 h zunächst eine nicht eindeutig identifizierbare Vorläuferphase aus amorphen Calciumphosphat, Brushit (DCPD) oder OCP. Diese wandelte sich dann nach 3 h und 5 h in ein Gemisch, bestehend aus OCP und ein wenig Hydroxylapatit (HAP) um.
Die Schlussfolgerung daraus ist, dass das CHOL-HEM in der Lage ist, dass während der Mineralisation entstandene OCP zu stabilisieren. Dies geschieht vermutlich durch die Adsorption des Amphiphils bevorzugt an der OCP Oberfläche in [100] Orientierung. Dadurch wird die Spaltung entlang der c-Achse unterdrückt und die Hydrolyse zum HAP verhindert.
Das A-CHOL ist hingegen sterisch anspruchsvoller und kann wahrscheinlich aufgrund seiner Größe nicht so gut an der OCP Kristalloberfläche adsorbieren verglichen zum CHOL HEM. Das CHOL-HEM kann also die Hydrolyse von OCP zu HAP besser unterdrücken als das A-CHOL. Da jedoch auch beim A-CHOL nach einer Mineralisationszeit von 5 h nur wenig HAP zu finden ist, wäre auch hier ein Stabilisierungseffekt der OCP Kristalle möglich. Um eine genaue Aussage darüber treffen zu können, sind jedoch zusätzliche Kontrollexperimente notwendig. Es wäre zum einen denkbar, die Mineralisationsexperimente über einen längeren Zeitraum durchzuführen. Diese könnten zeigen, ob das CHOL-HEM die Hydrolyse vom OCP zum HAP komplett unterdrückt. Außerdem könnte nachgewiesen werden, ob beim A-CHOL das OCP weiter zum HAP umgesetzt wird oder ob ein Gemisch beider Kristallphasen erhalten bleibt.
Um die Mineralisation an der Wasser/Luft-Grenzfläche mit der Mineralisation in Bulklösung zu vergleichen, wurden zusätzlich Mineralisationsexperimente in Bulklösung durchgeführt. Dazu wurden Nitrilotriessigsäure (NTA) und Ethylendiamintetraessigsäure (EDTA) als Mineralisationsadditive verwendet, da NTA unter anderem der Struktur der hydrophilen Kopfgruppe des A-CHOLs ähnelt. Es konnte gezeigt werden, dass ein Vergleich der Mineralisation an der Grenzfläche mit der Mineralisation in Bulklösung nicht ohne weiteres möglich ist. Bei der Mineralisation in Bulklösung wird bei tiefen pH-Werten DCPD und bei höheren pH-Werten HAP gebildet. Diese wurde mittels Röntgenpulverdiffraktometrie Messungen nachgewiesen und durch Infrarotspektroskopie bekräftigt. Die Bildung von OCP wie an der Wasser/Luft-Grenzfläche konnte nicht beobachtet werden.
Es konnte auch gezeigt werden, dass beide Additive NTA und EDTA einen unterschiedlichen Einfluss auf den Verlauf der Mineralisation nehmen. So unterscheiden sich zum einen die Morphologien des gebildeten DCPDs und zum anderen wurde beispielsweise in Anwesenheit von 10 und 15 mM NTA neben DCPD auch HAP bei einem Ausgangs-pH-Wert von 7 nachgewiesen.
Da unser Augenmerk speziell auf der Mineralisation von Calciumphosphat an der Wasser/Luft-Grenzfläche liegt, könnten Folgeexperimente wie beispielsweise GIXD Messungen durchgeführt werden. Dadurch wäre es möglich, einen Überblick über die gebildeten Kristallphasen nach unterschiedlichen Reaktionszeiten direkt auf dem Trog zu erhalten.
Es konnte weiterhin gezeigt werden, dass auch einfache Amphiphile in der Lage sind, die Mineralisation von Calciumphosphat zu steuern. Amphiphile mit Cholesterol als hydrophoben Block bilden offensichtlich besonders stabile Monolagen an der Wasser/Luft-Grenzfläche. Eine Untersuchung des Einflusses ähnlicher Amphiphile mit unterschiedlichen hydrophilen Kopfgruppen auf das Mineralisationsverhalten von Calciumphosphat wäre durchaus interessant.
I. Ceric ammonium nitrate (CAN) mediated thiocyanate radical additions to glycals
In this dissertation, a facile entry was developed for the synthesis of 2-thiocarbohydrates and their transformations. Initially, CAN mediated thiocyanation of carbohydrates was carried out to obtain the basic building blocks (2-thiocyanates) for the entire studies. Subsequently, 2-thiocyanates were reduced to the corresponding thiols using appropriate reagents and reaction conditions. The screening of substrates, stereochemical outcome and the reaction mechanism are discussed briefly (Scheme I).
Scheme I. Synthesis of the 2-thiocyanates II and reductions to 2-thiols III & IV.
An interesting mechanism was proposed for the reduction of 2-thiocyanates II to 2-thiols III via formation of a disulfide intermediate. The water soluble free thiols IV were obtained by cleaving the thiocyanate and benzyl groups in a single step. In the subsequent part of studies, the synthetic potential of the 2-thiols was successfully expanded by simple synthetic transformations.
II. Transformations of the 2-thiocarbohydrates
The 2-thiols were utilized for convenient transformations including sulfa-Michael additions, nucleophilic substitutions, oxidation to disulfides and functionalization at the anomeric position. The diverse functionalizations of the carbohydrates at the C-2 position by means of the sulfur linkage are the highlighting feature of these studies. Thus, it creates an opportunity to expand the utility of 2-thiocarbohydrates for biological studies.
Reagents and conditions: a) I2, pyridine, THF, rt, 15 min; b) K2CO3, MeCN, rt, 1 h; c) MeI, K2CO3, DMF, 0 °C, 5 min; d) Ac2O, H2SO4 (1 drop), rt, 10 min; e) CAN, MeCN/H2O, NH4SCN, rt, 1 h; f) NaN3, ZnBr2, iPrOH/H2O, reflux, 15 h; g) NaOH (1 M), TBAI, benzene, rt, 2 h; h) ZnCl2, CHCl3, reflux, 3 h.
Scheme II. Functionalization of 2-thiocarbohydrates.
These transformations have enhanced the synthetic value of 2-thiocarbohydrates for the preparative scale. Worth to mention is the Lewis acid catalyzed replacement of the methoxy group by other nucleophiles and the synthesis of the (2→1) thiodisaccharides, which were obtained with complete β-selectivity. Additionally, for the first time, the carbohydrate linked thiotetrazole was synthesized by a (3 + 2) cycloaddition approach at the C-2 position.
III. Synthesis of thiodisaccharides by thiol-ene coupling.
In the final part of studies, the synthesis of thiodisaccharides by a classical photoinduced thiol-ene coupling was successfully achieved.
Reagents and conditions: 2,2-Dimethoxy-2-phenylacetophenone (DPAP), CH2Cl2/EtOH, hv, rt.
Scheme III. Thiol-ene coupling between 2-thiols and exo-glycals.
During the course of investigations, it was found that the steric hindrance plays an important role in the addition of bulky thiols to endo-glycals. Thus, we successfully screened the suitable substrates for addition of various thiols to sterically less hindered alkenes (Scheme III). The photochemical addition of 2-thiols to three different exo-glycals delivered excellent regio- and diastereoselectivities as well as yields, which underlines the synthetic potential of this convenient methodology.
The field of nanophotonics focuses on the interaction between electromagnetic radiation and matter on the nanometer scale. The elements of nanoscale photonic devices can transfer excitation energy non-radiatively from an excited donor molecule to an acceptor molecule by Förster resonance energy transfer (FRET). The efficiency of this energy transfer is highly dependent on the donor-acceptor distance. Hence, in these nanoscale photonic devices it is of high importance to have a good control over the spatial assembly of used fluorophores. Based on molecular self-assembly processes, various nanostructures can be produced. Here, DNA nanotechnology and especially the DNA origami technique are auspicious self-assembling methods. By using DNA origami nanostructures different fluorophores can be introduced with a high local control to create a variety of nanoscale photonic objects. The applications of such nanostructures range from photonic wires and logic gates for molecular computing to artificial light harvesting systems for artificial photosynthesis.
In the present cumulative doctoral thesis, different FRET systems on DNA origami structures have been designed and thoroughly analyzed. Firstly, the formation of guanine (G) quadruplex structures from G rich DNA sequences has been studied based on a two-color FRET system (Fluorescein (FAM)/Cyanine3 (Cy3)). Here, the influences of different cations (Na+ and K+), of the DNA origami structure and of the DNA sequence on the G-quadruplex formation have been analyzed. In this study, an ion-selective K+ sensing scheme based on the G-quadruplex formation on DNA origami structures has been developed. Subsequently, the reversibility of the G-quadruplex formation on DNA origami structures has been evaluated. This has been done for the simple two-color FRET system which has then been advanced to a switchable photonic wire by introducing additional fluorophores (FAM/Cy3/Cyanine5 (Cy5)/IRDye®700). In the last part, the emission intensity of the acceptor molecule (Cy5) in a three-color FRET cascade has been tuned by arranging multiple donor (FAM) and transmitter (Cy3) molecules around the central acceptor molecule. In such artificial light harvesting systems, the excitation energy is absorbed by several donor and transmitter molecules followed by an energy transfer to the acceptor leading to a brighter Cy5 emission. Furthermore, the range of possible excitation wavelengths is extended by using several different fluorophores (FAM/Cy3/Cy5). In this part of the thesis, the light harvesting efficiency (antenna effect) and the FRET efficiency of different donor/transmitter/acceptor assemblies have been analyzed and the artificial light harvesting complex has been optimized in this respect.
Proteins are natural polypeptides produced by cells; they can be found in both animals and plants, and possess a variety of functions. One of these functions is to provide structural support to the surrounding cells and tissues. For example, collagen (which is found in skin, cartilage, tendons and bones) and keratin (which is found in hair and nails) are structural proteins. When a tissue is damaged, however, the supporting matrix formed by structural proteins cannot always spontaneously regenerate. Tailor-made synthetic polypeptides can be used to help heal and restore tissue formation.
Synthetic polypeptides are typically synthesized by the so-called ring opening polymerization (ROP) of α-amino acid N-carboxyanhydrides (NCA). Such synthetic polypeptides are generally non-sequence-controlled and thus less complex than proteins. As such, synthetic polypeptides are rarely as efficient as proteins in their ability to self-assemble and form hierarchical or structural supramolecular assemblies in water, and thus, often require rational designing. In this doctoral work, two types of amino acids, γ-benzyl-L/D-glutamate (BLG / BDG) and allylglycine (AG), were selected to synthesize a series of (co)polypeptides of different compositions and molar masses.
A new and versatile synthetic route to prepare polypeptides was developed, and its mechanism and kinetics were investigated. The polypeptide properties were thoroughly studied and new materials were developed from them. In particular, these polypeptides were able to aggregate (or self-assemble) in solution into microscopic fibres, very similar to those formed by collagen. By doing so, they formed robust physical networks and organogels which could be processed into high water-content, pH-responsive hydrogels. Particles with highly regular and chiral spiral morphologies were also obtained by emulsifying these polypeptides. Such polypeptides and the materials derived from them are, therefore, promising candidates for biomedical applications.
Diese Arbeit befasst sich mit der Herstellung und Charakterisierung von thermoresponsiven Filmen auf Goldelektroden durch Fixierung eines bereits synthetisierten thermoresponsiven Polymers. Als Basis für die Entwicklung der responsiven Grenzfläche dienten drei unterschiedliche Copolymere (Polymere I, II und III) aus der Gruppe der thermisch schaltbaren Poly(oligo(ethylenglykol)methacrylate).
Die turbidimetrischen Messungen der Copolymere in Lösungen haben gezeigt, dass der Trübungspunkt vom pH-Wert, der Gegenwart von Salzen sowie von der Ionenstärke der Lösung abhängig ist. Nach der Charakterisierung der Polymere in Lösung wurden Experimente der kovalenten Kopplung der Polymere I bis III an die Oberfläche der Gold-Elektroden durchgeführt. Während bei Polymeren I und II die Ankopplung auf einer Amidverbrückung basierte, wurde bei Polymer III als alternative Methode zur Immobilisierung eine photoinduzierte Anbindung unter gleichzeitiger Vernetzung gewählt. Der Nachweis der erfolgreichen Ankopplung erfolgte bei allen Polymeren elektrochemisch mittels Cyclovoltammetrie und Impedanzspektroskopie in K3/4[Fe(CN)6]-Lösungen. Wie die Ellipsometrie-Messungen zeigten, waren die erhaltenen Polymer-Filme unterschiedlich dick. Die Ankopplung über Amidverbrückung lieferte dünne Filme (10 – 15 nm), während der photovernetzte Film deutlich dicker war (70-80 nm) und die darunter liegende Oberfläche relativ gut isolierte.
Elektrochemische Temperaturexperimente an Polymer-modifizierten Oberflächen in Lösungen in Gegenwart von K3/4[Fe(CN)6] zeigten, dass auch die immobilisierten Polymere I bis III responsives Temperaturverhalten zeigen. Bei Elektroden mit den immobilisierten Polymeren I und II ist der Temperaturverlauf der Parameterwerte diskontinuierlich – ab einem kritischen Punkt (37 °C für Polymer I und 45 °C für Polymer II) wird zunächst langsame Zunahme der Peakströme wird deutlich schneller. Das Temperaturverhalten von Polymer III ist dagegen bis 50 °C kontinuierlich, der Peakstrom sinkt hier durchgehend.
Weiterhin wurde mit den auf Polymeren II und III basierten Elektroden deren Anwendung als responsive Matrix für Bioerkennungsreaktionen untersucht. Es wurde die Ankopplung von kleinen Biorezeptoren, TAG-Peptiden, an Polymer II- und Polymer III-modifizierten Elektroden durchgeführt. Das hydrophile FLAG-TAG-Peptid verändert das Temperaturverhalten des Polymer II-Films unwesentlich, da es die Hydrophilie des Netzwerkes nicht beeinflusst. Weiterhin wurde der Effekt der Ankopplung der ANTI-FLAG-TAG-Antikörper an FLAG-TAG-modifizierte Polymer II-Filme untersucht. Es konnte gezeigt werden, dass die Antikörper spezifisch an FLAG-TAG-modifiziertes Polymer II binden. Es wurde keine unspezifische Anbindung von ANTI-FLAG-TAG an Polymer II beobachtet. Die Temperaturexperimente haben gezeigt, dass die thermische Restrukturierung des Polymer II-FLAG-TAG-Filmes auch nach der Antikörper-Ankopplung noch stattfindet. Der Einfluss der ANTI-FLAG-TAG-Ankopplung ist gering, da der Unterschied in der Hydrophilie zwischen Polymer II und FLAG-TAG bzw. ANTI-FLAG-TAG zu gering ist.
Für die Untersuchungen mit Polymer III-Elektroden wurde neben dem hydrophilen FLAG-TAG-Peptid das deutlich hydrophobere HA-TAG-Peptid ausgewählt. Wie im Falle der Polymer II Elektrode beeinflusst das gekoppelte FLAG-TAG-Peptid das Temperaturverhalten des Polymer III-Netzwerkes nur geringfügig. Die gemessenen Stromwerte sind geringer als bei der Polymer III-Elektrode. Das Temperaturverhalten der FLAG-TAG-Elektrode ähnelt dem der reinen Polymer III-Elektrode – die Stromwerte sinken kontinuierlich bis die Temperatur von ca. 40 °C erreicht ist, bei der ein Plateau beobachtet wird. Offensichtlich verändert FLAG-TAG auch in diesem Fall nicht wesentlich die Hydrophilie des Polymer III-Netzwerkes. Das an Polymer III-Elektroden gekoppelte hydrophobe HA-TAG-Peptid beeinflusst dagegen im starken Maße den Quellzustand des Netzwerkes. Die Ströme für die HA-TAG-Elektroden sind deutlich geringer als die für die FLAG-TAG-Polymer III-Elektroden, was auf geringeren Wassergehalt und dickeren Film zurückzuführen ist. Bereits ab 30 °C erfolgt der Anstieg von Stromwerten, der bei Polymer III- bzw. bei Polymer III-FLAG-TAG-Elektroden nicht beobachtet werden kann. Das gekoppelte hydrophobe HA-TAG-Peptid verdrängt Wasser aus dem Polymer III-Netzwerk, was in der Stauchung des Films bereits bei Raumtemperatur resultiert. Dies führt dazu, dass der Film im Laufe des Temperaturanstieges kaum noch komprimiert. Die Stromwerte steigen in diesem Fall entsprechend des Anstiegs der temperaturabhängigen Diffusion des Redoxpaares. Diese Untersuchungen zeigen, dass das HA-TAG-Peptid als Ankermolekül deutlich besser für eine potentielle Verwendung der Polymer III-Filme für sensorische Zwecke geeignet ist, da es sich deutlich in der Hydrophilie von Polymer III unterscheidet.
This cumulative doctoral dissertation, based on three publications, is devoted to the investigation of several aspects of azobenzene molecular switches, with the aid of computational chemistry.
In the first paper, the isomerization rates of a thermal cis → trans isomerization of azobenzenes for species formed upon an integer electron transfer, i.e., with added or removed electron, are calculated from Eyring’s transition state theory and activation energy barriers, computed by means of density functional theory. The obtained results are discussed in connection with an experimental study of the thermal cis → trans isomerization of azobenzene derivatives in the presence of gold nanoparticles, which is demonstrated to be greatly accelerated in comparison to the same isomerization reaction in the absence of nanoparticles.
The second paper is concerned with electronically excited states of (i) dimers, composed of two photoswitchable units placed closely side-by-side, as well as (ii) monomers and dimers adsorbed on a silicon cluster. A variety of quantum chemistry methods, capable of calculating molecular electronic absorption spectra, based on density functional and wave function theories, is employed to quantify changes in optical absorption upon dimerization and covalent grafting to a surface. Specifically, the exciton (Davydov) splitting between states of interest is determined from first-principles calculations with the help of natural transition orbital analysis, allowing for insight into the nature of excited states.
In the third paper, nonadiabatic molecular dynamics with trajectory surface hopping is applied to model the photoisomerization of azobenzene dimers, (i) for the isolated case (exhibiting the exciton coupling between two molecules) as well as (ii) for the constrained case (providing the van der Waals interaction with environment in addition to the exciton coupling between two monomers). For the latter, the additional azobenzene molecules, surrounding the dimer, are introduced, mimicking a densely packed self-assembled monolayer. From obtained results it is concluded that the isolated dimer is capable of isomerization likewise the monomer, whereas the steric hindrance considerably suppresses trans → cis photoisomerization.
Furthermore, the present dissertation comprises the general introduction describing the main features of the azobenzene photoswitch and objectives of this work, theoretical basis of the employed methods, and discussion of gained findings in the light of existing literature. Also, additional results on (i) activation parameters of the thermal cis → trans isomerization of azobenzenes, (ii) an approximate scheme to account for anharmonicity of molecular vibrations in calculation of the activation entropy, as well as (iii) absorption spectra of photoswitch–silicon composites obtained from time-demanding wave function-based methods are presented.
Die vorgelegte Dissertation präsentiert wissenschaftliche Ergebnisse, die in der Zeit vom Dezember 2012 bis August 2016, erarbeitet wurden. Der zentrale Inhalt der Arbeit ist die Simulation von Röntgenabsorptionsprozessen von verschiedenen Systemen in kondensierter Phase. Genauer gesagt, werden Nahkantenabsorptions- (NEXAFS) sowie Röntgenphotoelektronenspektren (XPS) berechnet. In beiden Fällen wird ein Röntgenphoton von einem molekularen System absorbiert. Aufgrund der hohen Photonenenergie wird ein stark gebundenes kernnahes Elektron angeregt. Bei der XPS gelangt dieses mit einer zu messenden kinetischen Energie in Kontinuumszustände. In Abhängigkeit der eingestrahlten Photonenenergie und der kinetischen Energie des austreten Elektrons, kann die Bindungsenergie berechnet werden, welche die zentrale Größe der XPS ist. Im Falle der NEXAFS-Spektroskopie wird das kernnahe Elektron in unbesetzte gebundene Zustände angeregt. Die zentrale Größe ist die Absorption als Funktion der eingestrahlten Photonenenergie. Das erste Kapitel meiner Arbeit erörtert detailliert die experimentellen Methoden sowie die daraus gewonnenen charakteristischen Größen.
Die experimentellen Spektren zeigen oft viele Resonanzen, deren Interpretation aufgrund fehlender Referenzmaterialien schwierig ist. In solchen Fällen bietet es sich an, die Spektren mittels quantenchemischer Methoden zu simulieren. Der dafür erforderliche mathematisch-physikalische Methodenkatalog wird im zweiten Kapitel der Arbeit erörtert.
Das erste von mir untersuchte System ist Graphen. In experimentellen Arbeiten wurde die Oberfläche mittels Bromplasma modifiziert. Die im Anschluss gemessenen NEXAFS-Spektren unterscheiden sich maßgeblich von den Spektren der unbehandelten Oberfläche. Mithilfe periodischer DFT-Rechnungen wurden verschiedene Gitterdefekte sowie bromierte Systeme untersucht und die NEXAFS-Spektren simuliert. Mittels der Simulationen können die Beiträge verschiedener Anregungszentren analysiert werden. Die Berechnungen erlauben den Schluss, dass Gitterdefekte maßgeblich für die entstandenen Veränderungen verantwortlich sind.
Polyvinylalkohol (PVA) wurde als zweites System behandelt. Hierbei sollte untersucht werden, wie groß der Einfluss der Molekularbewegung auf die Verbreiterung der Peaks im XP-Spektrum ist. Des Weiteren wurde untersucht, wie groß der Einfluss von intermolekularen Wechselwirkungen auf die Peakpositionen und Peakverbreiterung ist. Für die Berechnung dieses Systems wurde eine Kombination aus molekulardynamischen und quantenchemischen Methoden verwendet. Als Strukturen dienten Oligomermodelle, die unter dem Einfluss eines (ab initio) Potentials propagiert wurden. Entlang der erstellten Trajektorie wurden Schnappschüsse der Geometrien extrahiert und für die Berechnung der XP-Spektren verwendet. Die Spektren werden bereits mithilfe klassischer Molekulardynamik sehr gut reproduziert. Die erhaltenen Peakbreiten sind verglichen mit dem Experiment allerdings zu klein. Die Hauptursache der Peakverbreiterung ist die Molekularbewegung. Intermolekulare Wechselwirkungen verschieben die Peakpositionen um 0.6 eV zu kleineren Anregungsenergien.
Im dritten Teil der Arbeit stehen die NEXAFS-Spektren von ionischen Flüssigkeiten (ILs) im Fokus. Die experimentell gefundenen Spektren zeigen eine komplexe Struktur mit vielen Resonanzen. In der Arbeit wurden zwei ILs untersucht. Als Geometrien verwenden wir Clustermodelle, die aus experimentellen Kristallstrukturen extrahiert wurden. Die berechneten Spektren erlauben es, die Resonanzen den Anregungszentren zuzuordnen. Außerdem kann eine erstmals gemessene Doppelresonanz simuliert und erklärt werden. Insgesamt kann die Interpretation der Spektren mithilfe der Simulation signifikant erweitert werden.
In allen Systemen wurde zur Berechnung des NEXAFS-Spektrums eine auf Dichtefunktionaltheorie basierende Methode verwendet (die sogenannte Transition-Potential Methode). Gängige wellenfunktionsbasierte Methoden, wie die Konfigurationswechselwirkung mit Einfachanregungen (CIS), zeigen eine starke Blauverschiebung, wenn als Referenz eine Hartree-Fock Slaterdeterminante verwendet wird. Wir zeigen, dass die Verwendung von kernnah-angeregten Determinanten sowohl das resultierende Spektrum als auch die Anregungsenergien deutlich verbessert. Des Weiteren werden auch Referenzen aus Dichtefunktionalrechnungen getestet. Zusätzlich werden auch Referenzen mit gebrochenen Besetzungszahlen für kernnahe Elektronen verwendet. In der Arbeit werden die Resultate der verschiedenen Referenzen miteinander verglichen. Es zeigt sich, dass Referenzen mit gebrochenen Besetzungszahlen das Spektrum nicht weiter verbessern. Der Einfluss der verwendeten Elektronenstrukturmethode ist eher gering.
Surface-enhanced Raman scattering (SERS) is a promising tool to obtain rich chemical information about analytes at trace levels. However, in order to perform selective experiments on individual molecules, two fundamental requirements have to be fulfilled. On the one hand, areas with high local field enhancement, so-called “hot spots”, have to be created by positioning the supporting metal surfaces in close proximity to each other. In most cases hot spots are formed in the gap between adjacent metal nanoparticles (NPs). On the other hand, the analyte has to be positioned directly in the hot spot in order to profit from the highest signal amplification. The use of DNA origami substrates provides both, the arrangement of AuNPs with nm precision as well as the ability to bind analyte molecules at predefined positions. Consequently, the present cumulative doctoral thesis aims at the development of a novel SERS substrate based on a DNA origami template. To this end, two DNA-functionalized gold nanoparticles (AuNPs) are attached to one DNA origami substrate resulting in the formation of a AuNP dimer and thus in a hot spot within the corresponding gap. The obtained structures are characterized by correlated atomic force microscopy (AFM) and SERS imaging which allows for the combination of structural and chemical information.
Initially, the proof-of principle is presented which demonstrates the potential of the novel approach. It is shown that the Raman signal of 15 nm AuNPs coated with dye-modified DNA
(dye: carboxytetramethylrhodamine (TAMRA)) is significantly higher for AuNP dimers arranged on a DNA origami platform in comparison to single AuNPs. Furthermore, by attaching single TAMRA molecules in the hot spot between two 5 nm AuNPs and optimizing the size of the AuNPs by electroless gold deposition, SERS experiments at the few-molecule level are presented. The initially used DNA origami-AuNPs design is further optimized in many respects. On the one hand, larger AuNPs up to a diameter of 60 nm are used which are additionally treated with a silver enhancement solution to obtain Au-Ag-core-shell NPs. On the other hand, the arrangement of both AuNPs is altered to improve the position of the dye molecule within the hot spot as well as to decrease the gap size between the two particles. With the optimized design the detection of single dye molecules (TAMRA and cyanine 3 (Cy3)) by means of SERS is demonstrated. Quantitatively, enhancement factors up to 10^10 are estimated which is sufficiently high to detect single dye molecules.
In the second part, the influence of graphene as an additional component of the SERS substrate is investigated. Graphene is a two-dimensional material with an outstanding combination of electronical, mechanical and optical properties. Here, it is demonstrated that
single layer graphene (SLG) replicates the shape of underlying non-modified DNA origami
substrates very well, which enables the monitoring of structural alterations by AFM imaging.
In this way, it is shown that graphene encapsulation significantly increases the structural
stability of bare DNA origami substrates towards mechanical force and prolonged exposure
to deionized water.
Furthermore, SLG is used to cover DNA origami substrates which are functionalized with a
40 nm AuNP dimer. In this way, a novel kind of hybrid material is created which exhibits
several advantages compared to the analogue non-covered SERS substrates. First, the fluorescence background of dye molecules that are located in between the AuNP surface and SLG is efficiently reduced. Second, the photobleaching rate of the incorporated dye molecules is decreased up to one order of magnitude. Third, due to the increased photostability of the investigated dye molecules, the performance of polarization-dependent series measurements on individual structures is enabled. This in turn reveals extensive information about the dye molecules in the hot spot as well as about the strain induced within the graphene lattice.
Although SLG can significantly influence the SERS substrate in the aforementioned ways, all
those effects are strongly related to the extent of contact with the underlying AuNP dimer.
Lignin valorization
(2017)
The topic of this project is the use of lignin as alternative source of aromatic building blocks and oligomers to fossil feedstocks. Lignin is known as the most abundant aromatic polymer in nature and is isolated from the lignocellulosic component of plants by different possible extraction treatments. Both the biomass source and the extraction method affect the structure of the isolated lignin, therefore influencing its further application. Lignin was extracted from beech wood by two different hydrothermal alkaline treatments, which use NaOH and Ba(OH)2 as base and by an acid-catalyzed organosolv process. Moreover, lignin was isolated from bamboo, beech wood and coconut by soda treatment of the biomasses. A comparison of the structural features of such isolated lignins was performed through the use of a wide range of analytical methods. Alkaline lignins resulted in a better candidate as carbon precursor and macromonomers for the synthesis of polymer than organosolv lignin. In fact, alkaline lignins showed higher residual mass after carbonization and higher content of the reactive hydroxy functionalities. In contrast, the lignin source turned out to slightly affect the lignin hydroxyl content.
One of the most common lignin modifications is its deconstruction to obtain aromatic molecules, which can be used as starting materials for the synthesis of fine chemicals. Lignin deconstruction leads to a complex mixture of aromatic molecules. A gas chromatographic analytical method was developed to characterize the mixture of products obtained by lignin deconstruction via heterogeneous catalytic hydrogenolysis. The analytical protocol allowed the quantification of three main groups of molecules by means of calibration curves, internal standard and a preliminary silylation step of the sample. The analytical method was used to study the influence of the hydrogenolysis catalyst, temperature and system (flow and batch reactor) on the yield and selectivity of the aromatic compounds.
Lignin extracted from beech wood by a hydrothermal process using Ba(OH)2 as base, was functionalized by aromatic nitration in order to add nitrogen functionalities. The final goal was the synthesis of a nitrogen doped carbon. Nitrated lignin was reduced to the amino form in order to compare the influence of different nitrogen functionalities on the porosity of the final carbon. The carbons were obtained by ionothermal treatment of the precursors in the presence of the eutectic salt mixture KCl/ZnCl2 Such synthesized carbons showed micro-, macro- and mesoporosity and were tested for their electrocatalytic activity towards the oxygen reduction reaction. Mesoporous carbon derived from nitro lignin displayed the highest electrocatalytic activity.
Lignins isolated from coconut, beech wood and bamboo were used as macromonomers for the synthesis of biobased polyesters. A condensation reaction was performed between lignin and a hyper branched poly(ester-amine), previously obtained by condensation of triethanolamine and adipic acid. The influence of the lignin source and content on the thermochemical and mechanical properties of the final material was investigated. The prepolymer showed adhesive properties towards aluminum and its shear strength was therefore measured. The gluing properties of such synthesized glues turned out to be independent from the lignin source but affected by the amount of lignin in the final material.
This work shows that, although still at a laboratory scale, the valorization of lignin can overcome the critical issues of lignin´s structure variability and complexity.
Physikalische Hydrogele gewinnen derzeit als Zellsubstrate zunehmend an Interesse, da Viskoelastizität oder Stressrelaxation ein bedeutender Parameter in der Mechanotransduktion ist, der bisher vernachlässigt wurde. In dieser Arbeit wurden multi-funktionelle Polyurethane entworfen, die über einen neuartigen Gelierungsmechanismus physikalische Hydrogele bilden. In Wasser bilden die anionischen Polyurethane spontan Aggregate, welche durch elektrostatische Abstoßung in Lösung gehalten werden. Eine schnelle Gelierung kann von hier aus durch Ladungsabschirmung erreicht werden, wodurch die Aggregation voranschreitet und ein Netzwerk ausgebildet wird. Dies kann durch die Zugabe von verschiedenen Säuren oder Salzen geschehen, sodass sowohl saure (pH 4 - 5) als auch pH-neutrale Hydrogele erhalten werden können. Während konventionelle Hydrogele auf Polyurethan-Basis in der Regel durch toxische isocyanat-haltige Präpolymere hergestellt werden, eignet sich der hier beschriebene physikalische Gelierungsmechanismus für in situ Anwendungen in sensitiven Umgebungen. Sowohl Härte als auch Stressrelaxation der Hydrogele können unabhängig voneinander über einen breiten Bereich eingestellt werden. Darüberhinaus zeichnen sich die Hydrogele durch exzellente Stressregeneration aus.
Diese Arbeit zu Grunde liegenden Forschung zielte darauf ab, neue schmelzbare Acrylnitril-Copolymere zu entwickeln. Diese sollten im Anschluss über ein Schmelzspinnverfahren zur Chemiefaser geformt und im letzten Schritt zur Carbonfaser konvertiert werden. Zu diesem Zweck wurden zunächst orientierende Untersuchungen an unterschiedlichen Copolymeren des Acrylnitril aus Lösungspolymerisation durchgeführt. Die Untersuchungen zeigten, dass elektrostatische Wechselwirkungen besser als sterische Abschirmung dazu geeignet sind, Schmelzbarkeit unterhalb der Zersetzungstemperatur von Polyacrylnitril zu bewirken. Aus der Vielzahl untersuchter Copolymere stellten sich jene mit Methoxyethylacrylat (MEA) als am effektivsten heraus. Für diese Copolymere wurden sowohl die Copolymerisationsparameter bestimmt als auch die grundlegende Kinetik der Lösungspolymerisation untersucht. Die Copolymere mit MEA wurden über Schmelzspinnen zur Faser umgeformt und diese dann untersucht. Hierbei wurden auch Einflüsse verschiedener Parameter, wie z.B. die der Molmasse, auf die Fasereigenschaften und -herstellung untersucht. Zuletzt wurde ein Heterophasenpolymerisationsverfahren zur Herstellung von Copolymeren aus AN/MEA entwickelt; dadurch konnten die Materialeigenschaften weiter verbessert werden. Zur Unterdrückung der thermoplastischen Eigenschaften der Fasern wurde ein geeignetes Verfahren entwickelt und anschließend die Konversion zu Carbonfasern durchgeführt.
In complement to the well-established zwitterionic monomers 3-((2-(methacryloyloxy)ethyl)dimethylammonio)propane-1-sulfonate (“SPE”) and 3-((3-methacrylamidopropyl)dimethylammonio)propane-1-sulfonate (“SPP”), the closely related sulfobetaine monomers were synthesized and polymerized by reversible addition-fragmentation chain transfer (RAFT) polymerization, using a fluorophore labeled RAFT agent. The polyzwitterions of systematically varied molar mass were characterized with respect to their solubility in water, deuterated water, and aqueous salt solutions. These poly(sulfobetaine)s show thermoresponsive behavior in water, exhibiting upper critical solution temperatures (UCST). Phase transition temperatures depend notably on the molar mass and polymer concentration, and are much higher in D2O than in H2O. Also, the phase transition temperatures are effectively modulated by the addition of salts. The individual effects can be in parts correlated to the Hofmeister series for the anions studied. Still, they depend in a complex way on the concentration and the nature of the added electrolytes, on the one hand, and on the detailed structure of the zwitterionic side chain, on the other hand. For the polymers with the same zwitterionic side chain, it is found that methacrylamide-based poly(sulfobetaine)s exhibit higher UCST-type transition temperatures than their methacrylate analogs. The extension of the distance between polymerizable unit and zwitterionic groups from 2 to 3 methylene units decreases the UCST-type transition temperatures. Poly(sulfobetaine)s derived from aliphatic esters show higher UCST-type transition temperatures than their analogs featuring cyclic ammonium cations. The UCST-type transition temperatures increase markedly with spacer length separating the cationic and anionic moieties from 3 to 4 methylene units. Thus, apparently small variations of their chemical structure strongly affect the phase behavior of the polyzwitterions in specific aqueous environments.
Water-soluble block copolymers were prepared from the zwitterionic monomers and the non-ionic monomer N-isopropylmethacrylamide (“NIPMAM”) by the RAFT polymerization. Such block copolymers with two hydrophilic blocks exhibit twofold thermoresponsive behavior in water. The poly(sulfobetaine) block shows an UCST, whereas the poly(NIPMAM) block exhibits a lower critical solution temperature (LCST). This constellation induces a structure inversion of the solvophobic aggregate, called “schizophrenic micelle”. Depending on the relative positions of the two different phase transitions, the block copolymer passes through a molecularly dissolved or an insoluble intermediate regime, which can be modulated by the polymer concentration or by the addition of salt. Whereas, at low temperature, the poly(sulfobetaine) block forms polar aggregates that are kept in solution by the poly(NIPMAM) block, at high temperature, the poly(NIPMAM) block forms hydrophobic aggregates that are kept in solution by the poly(sulfobetaine) block. Thus, aggregates can be prepared in water, which switch reversibly their “inside” to the “outside”, and vice versa.
In the interest of producing functional catalysts from sustainable building-blocks, 1, 3-dicarboxylate imidazolium salts derived from amino acids were successfully modified to be suitable as N-Heterocyclic carbene (NHC) ligands within metal complexes. Complexes of Ag(I), Pd(II), and Ir(I) were successfully produced using known procedures using ligands derived from glycine, alanine, β-alanine and phenylalanine. The complexes were characterized in solid state using X-Ray crystallography, which allowed for the steric and electronic comparison of these ligands to well-known NHC ligands within analogous metal complexes.
The palladium complexes were tested as catalysts for aqueous-phase Suzuki-Miyaura cross-coupling. Water-solubility could be induced via ester hydrolysis of the N-bound groups in the presence of base. The mono-NHC–Pd complexes were seen to be highly active in the coupling of aryl bromides with phenylboronic acid; the active catalyst of which was determined to be mostly Pd(0) nanoparticles. Kinetic studies determined that reaction proceeds quickly in the coupling of bromoacetophenone, for both pre-hydrolyzed and in-situ hydrolysis catalyst dissolution. The catalyst could also be recycled for an extra run by simply re-using the aqueous layer.
The imidazolium salts were also used to produce organosilica hybrid materials. This was attempted via two methods: by post-grafting onto a commercial organosilica, and co-condensation of the corresponding organosilane. The co-condensation technique harbours potential for the production of solid-support catalysts.
Ionothermal carbon materials
(2016)
Alternative concepts for energy storage and conversion have to be developed, optimized and employed to fulfill the dream of a fossil-independent energy economy. Porous carbon materials play a major role in many energy-related devices. Among different characteristics, distinct porosity features, e.g., specific surface area (SSA), total pore volume (TPV), and the pore size distribution (PSD), are important to maximize the performance in the final device. In order to approach the aim to synthesize carbon materials with tailor-made porosity in a sustainable fashion, the present thesis focused on biomass-derived precursors employing and developing the ionothermal carbonization.
During the ionothermal carbonization, a salt melt simultaneously serves as solvent and porogen. Typically, eutectic mixtures containing zinc chloride are employed as salt phase. The first topic of the present thesis addressed the possibility to precisely tailor the porosity of ionothermal carbon materials by an experimentally simple variation of the molar composition of the binary salt mixture. The developed pore tuning tool allowed the synthesis of glucose derived carbon materials with predictable SSAs in the range of ~ 900 to ~ 2100 m2 g-1. Moreover, the nucleobase adenine was employed as precursor introducing nitrogen functionalities in the final material. Thereby, the chemical properties of the carbon materials are varied leading to new application fields. Nitrogen doped carbons (NDCs) are able to catalyze the oxygen reduction reaction (ORR) which takes place on the cathodic site of a fuel cell. The herein developed porosity tailoring allowed the synthesis of adenine derived NDCs with outstanding SSAs of up to 2900 m2 g-1 and very large TPV of 5.19 cm3 g-1. Furthermore, the influence of the porosity on the ORR could be directly investigated enabling the precise optimization of the porosity characteristics of NDCs for this application. The second topic addressed the development of a new method to investigate the not-yet unraveled mechanism of the oxygen reduction reaction using a rotating disc electrode setup. The focus was put on noble-metal free catalysts. The results showed that the reaction pathway of the investigated catalysts is pH-dependent indicating different active species at different pH-values. The third topic addressed the expansion of the used salts for the ionothermal approach towards hydrated calcium and magnesium chloride. It was shown that hydrated salt phases allowed the introduction of a secondary templating effect which was connected to the coexistence of liquid and solid salt phases. The method enabled the synthesis of fibrous NDCs with SSAs of up to 2780 m2 g-1 and very large TPV of 3.86 cm3 g-1. Moreover, the concept of active site implementation by a facile low-temperature metalation employing the obtained NDCs as solid ligands could be shown for the first time in the context of ORR.
Overall, the thesis may pave the way towards highly porous carbon with tailor-made porosity materials prepared by an inexpensive and sustainable pathway, which can be applied in energy related field thereby supporting the needed expansion of the renewable energy sector.