The use of a catalyst support for the design of nanoscale heterogeneous catalysts based on cerium oxide offers vast possibilities for future catalyst development, particularly with regard to an increased focus on the use of renewable biogas and an emerging hydrogen economy. In this study, zirconia-supported ceria catalysts were synthesized, activated by using different thermochemical treatments, and characterized by way of temperature-programmed reduction (TPR), oxygen storage capacity, Xray diffraction, electron microscopy, and luminescence spectroscopy using Eu3+ as a spectroscopic probe. Through reduction-oxidation pretreatment routines, reactive pyrochlore structures were created at temperatures as low as 600 degrees C and identified through TPR and electron microscopy experiments. A structural relationship and alignment of the crystal planes is revealed in high-resolution scanning transmission electron microscopy experiments through the digital diffraction patterns. Low-temperature pretreatment induces the formation of reactive pyrochlore domains under retention of the surface area of the catalyst system, and no further morphological changes are detected. Furthermore, the formation of pyrochlore domains achieved through severe reduction and mild reoxidation (SRMO) treatments is reversible. Over multiple alternating SRMO and severe reduction and severe reoxidation (SRSO) treatments, europium spectroscopy and TPR results indicate that pyrochlore structures are recreated over consecutive treatments, whenever the mild oxidation step at 500 degrees C is the last treatment (SRMO, SRMO-SRSO-SRMO, etc.).
We present a systematic study on the properties of Na(Y,Gd)F-4-based upconverting nanoparticles (UCNP) doped with 18% Yb3+, 2% Tm3+, and the influence of Gd3+ (10-50 mol% Gd3+). UCNP were synthesized via the solvothermal method and had a range of diameters within 13 and 50 nm. Structural and photophysical changes were monitored for the UCNP samples after a 24-month incubation period in dry phase and further redispersion. Structural characterization was performed by means of X-ray diffraction (XRD), transmission electron microscopy (TEM) as well as dynamic light scattering (DLS), and the upconversion luminescence (UCL) studies were executed at various temperatures (from 4 to 295 K) using time-resolved and steady-state spectroscopy. An increase in the hexagonal lattice phase with the increase of Gd3+ content was found, although the cubic phase was prevalent in most samples. The Tm3+-luminescence intensity as well as the Tm3+-luminescence decay times peaked at the Gd3+ concentration of 30 mol%. Although the general upconverting luminescence properties of the nanoparticles were preserved, the 24-month incubation period lead to irreversible agglomeration of the UCNP and changes in luminescence band ratios and lifetimes.