This paper focused on the synthesis of triangular nanoplatelets in the presence of a tubular network structure. The tubular network structure is formed by adding a strongly alternating polyampholyte, i.e., PalPhBisCarb, to a mixed vesicle system with a negatively charged bilayer containing phosphatidylcholin and AOT. Using the tubular network as a reducing agent in a one-step procedure, triangular and hexagonal nanoplatelets are formed. One can show that the nanoplatelet yield is enhanced by increasing the temperature and decreasing the reaction time. The platelet edge length can be decreased by heating the system up to 100 A degrees C. Due to specific interactions between PalPhBisCarb and the AOT/phospholipid bilayer, stacking and welding effects lead to the formation of ordered platelet structures. The reaction pathway to flat gold nanotriangles is discussed with regard to the twin plane growth model of gold nanoplates.
For the first time tubulating properties of spherical dendritic glycopolymers and linear alternating polyampholytes against non-uniform negatively charged giant vesicles are proven by light microscopy and cryo-scanning electron microscopy study. Real time observation of the morphological transformation from giant vesicles to tubular structures, simulating morphogenesis in living cells, is given by using the cationic and H-bond active dendritic glycopolymer accompanied by reducing the size of the giant vesicles and the evidence of vesicle-vesicle interaction which was only postulated in a previous study. Similar morphogenesis of non-uniform giant vesicles into tubular network structure can be observed by using a polyampholyte in the stretched conformation at pH 9. Pearl necklace and tubular network structure formation are also observed by applying anionic vesicles of significant smaller dimensions with average size dimensions of 35 nm, after adding the polyampholyte at pH 9. However, the fitting accuracy between the functional groups along the backbone chain of the polyampholyte on one side and the vesicle surface on the other side is of high importance for the transformation process by using polyampholytes. The resulting tubular and network structures offer new fields of application as microfluidic transport channels or template phases for the shape controlled formation of nanoparticles. (C) 2014 Elsevier B.V. All rights reserved.