Hybrid nanomaterials offer the combination of individual properties of different types of nanoparticles. Some strategies for the development of new nanostructures in larger scale rely on the self-assembly of nanoparticles as a bottom-up approach. The use of templates provides ordered assemblies in defined patterns. In a typical soft-template, nanoparticles and other surface-active agents are incorporated into non-miscible liquids. The resulting self-organized dispersions will mediate nanoparticle interactions to control the subsequent self-assembly. Especially interactions between nanoparticles of very different dispersibility and functionality can be directed at a liquid-liquid interface.
In this project, water-in-oil microemulsions were formulated from quasi-ternary mixtures with Aerosol-OT as surfactant. Oleyl-capped superparamagnetic iron oxide and/or silver nanoparticles were incorporated in the continuous organic phase, while polyethyleneimine-stabilized gold nanoparticles were confined in the dispersed water droplets. Each type of nanoparticle can modulate the surfactant film and the inter-droplet interactions in diverse ways, and their combination causes synergistic effects. Interfacial assemblies of nanoparticles resulted after phase-separation. On one hand, from a biphasic Winsor type II system at low surfactant concentration, drop-casting of the upper phase afforded thin films of ordered nanoparticles in filament-like networks. Detailed characterization proved that this templated assembly over a surface is based on the controlled clustering of nanoparticles and the elongation of the microemulsion droplets. This process offers versatility to use different nanoparticle compositions by keeping the surface functionalization, in different solvents and over different surfaces. On the other hand, a magnetic heterocoagulate was formed at higher surfactant concentration, whose phase-transfer from oleic acid to water was possible with another auxiliary surfactant in ethanol-water mixture. When the original components were initially mixed under heating, defined oil-in-water, magnetic-responsive nanostructures were obtained, consisting on water-dispersible nanoparticle domains embedded by a matrix-shell of oil-dispersible nanoparticles.
Herein, two different approaches were demonstrated to form diverse hybrid nanostructures from reverse microemulsions as self-organized dispersions of the same components. This shows that microemulsions are versatile soft-templates not only for the synthesis of nanoparticles, but also for their self-assembly, which suggest new approaches towards the production of new sophisticated nanomaterials in larger scale.
Due to the enhanced electromagnetic field at the tips of metal nanoparticles, the spiked structure of gold nanostars (AuNSs) is promising for surface-enhanced Raman scattering (SERS). Therefore, the challenge is the synthesis of well designed particles with sharp tips. The influence of different surfactants, i.e., dioctyl sodium sulfosuccinate (AOT), sodium dodecyl sulfate (SDS), and benzylhexadecyldimethylammonium chloride (BDAC), as well as the combination of surfactant mixtures on the formation of nanostars in the presence of Ag⁺ ions and ascorbic acid was investigated. By varying the amount of BDAC in mixed micelles the core/spike-shell morphology of the resulting AuNSs can be tuned from small cores to large ones with sharp and large spikes. The concomitant red-shift in the absorption toward the NIR region without losing the SERS enhancement enables their use for biological applications and for time-resolved spectroscopic studies of chemical reactions, which require a permanent supply with a fresh and homogeneous solution. HRTEM micrographs and energy-dispersive X-ray (EDX) experiments allow us to verify the mechanism of nanostar formation according to the silver underpotential deposition on the spike surface in combination with micelle adsorption.
Synthesis of artificial building blocks for sortase-mediated ligation and their enzymatic linkage
(2018)
The enzyme Sortase A catalyzes the formation of a peptide bond between the recognition sequence LPXTG and an oligoglycine. While manifold ligations between proteins and various biomolecules, proteins and small synthetic molecules as well as proteins and surfaces have been reported, the aim of this thesis was to investigate the sortase-catalyzed linkage between artificial building blocks. Hence, this could pave the way for the use of sortase A for tasks from a chemical point of view and maybe even materials science.
For the proof of concept, the studied systems were kept as simple as possible at first by choosing easily accessible silica NPs and commercially available polymers. These building blocks were functionalized with peptide motifs for sortase-mediated ligation. Silica nanoparticles were synthesized with diameters of 60 and 200 nm and surface modified with C=C functionalities. Then, peptides bearing a terminal cysteine were covalently linked by means of a thiol-ene reaction. 60 nm SiO2 NPs were functionalized with pentaglycines, while peptides with LPETG motif were linked to 200 nm silica particles. Polyethyleneglycol (PEG) and poly(N isopropylacrylamide) (PNIPAM) were likewise functionalized with peptides by thiol-ene reaction between cysteine residues and C=C units in the polymer end groups. Hence, G5-PEG and PNIPAM-LPETG conjugates were obtained. With this set of building blocks, NP–polymer hybrids, NP–NP, and polymer–polymer structures were generated by sortase-mediated ligation and the product formation shown by transmission electron microscopy, MALDI-ToF mass spectrometry and dynamic light scatting, among others. Thus, the linkage of these artificial building blocks by the enzyme sortase A could be demonstrated.
However, when using commercially available polymers, the purification of the polymer–peptide conjugates was impossible and resulted in a mixture containing unmodified polymer. Therefore, strategies were developed for the own synthesis of pure peptide-polymer and polymer-peptide conjugates as building blocks for sortase-mediated ligation. The designed routes are based on preparing polymer blocks via RAFT polymerization from CTAs that are attached to N- or C-terminus, respectively, of a peptide. GG-PNIPAM was synthesized through attachment of a suitable RAFT CTA to Fmoc-GG in an esterification reaction, followed by polymerization of NIPAM and cleavage of the Fmoc protection group. Furthermore, several peptides were synthesized by solid-phase peptide synthesis. The linkage of a RAFT CTA (or
polymerization initiator) to the N-terminus of a peptide can be conducted in an automated fashion as last step in a peptide synthesizer. The synthesis of such a conjugate couldn’t be realized in the time frame of this thesis, but many promising strategies exist to continue this strategy using different coupling reagents. Such polymer building blocks can be used to synthesize protein-polymer conjugates catalyzed by sortase A and the approach can be carried on to the synthesis of block copolymers by using polymer blocks with peptide motifs on both ends.
Although the proof of concept demonstrated in this thesis only shows examples that can be also synthesized by exclusively chemical techniques, a toolbox of such building blocks will enable the future formation of new materials and pave the way for the application of enzymes in materials science. In addition to nanoparticle systems and block copolymers, this also includes combination with protein-based building blocks to form hybrid materials. Hence, sortase could become an enzymatic tool that complements established chemical linking technologies and provides specific peptide motifs that are orthogonal to all existing chemical functional groups.
Functional nanoporous carbon-based materials derived from oxocarbon-metal coordination complexes
(2017)
Nanoporous carbon based materials are of particular interest for both science and industry due to their exceptional properties such as a large surface area, high pore volume, high electroconductivity as well as high chemical and thermal stability. Benefiting from these advantageous properties, nanoporous carbons proved to be useful in various energy and environment related applications including energy storage and conversion, catalysis, gas sorption and separation technologies. The synthesis of nanoporous carbons classically involves thermal carbonization of the carbon precursors (e.g. phenolic resins, polyacrylonitrile, poly(vinyl alcohol) etc.) followed by an activation step and/or it makes use of classical hard or soft templates to obtain well-defined porous structures. However, these synthesis strategies are complicated and costly; and make use of hazardous chemicals, hindering their application for large-scale production. Furthermore, control over the carbon materials properties is challenging owing to the relatively unpredictable processes at the high carbonization temperatures.
In the present thesis, nanoporous carbon based materials are prepared by the direct heat treatment of crystalline precursor materials with pre-defined properties. This synthesis strategy does not require any additional carbon sources or classical hard- or soft templates. The highly stable and porous crystalline precursors are based on coordination compounds of the squarate and croconate ions with various divalent metal ions including Zn2+, Cu2+, Ni2+, and Co2+, respectively. Here, the structural properties of the crystals can be controlled by the choice of appropriate synthesis conditions such as the crystal aging temperature, the ligand/metal molar ratio, the metal ion, and the organic ligand system. In this context, the coordination of the squarate ions to Zn2+ yields porous 3D cube crystalline particles. The morphology of the cubes can be tuned from densely packed cubes with a smooth surface to cubes with intriguing micrometer-sized openings and voids which evolve on the centers of the low index faces as the crystal aging temperature is raised. By varying the molar ratio, the particle shape can be changed from truncated cubes to perfect cubes with right-angled edges.
These crystalline precursors can be easily transformed into the respective carbon based materials by heat treatment at elevated temperatures in a nitrogen atmosphere followed by a facile washing step. The resulting carbons are obtained in good yields and possess a hierarchical pore structure with well-organized and interconnected micro-, meso- and macropores. Moreover, high surface areas and large pore volumes of up to 1957 m2 g-1 and 2.31 cm3 g-1 are achieved, respectively, whereby the macroscopic structure of the precursors is preserved throughout the whole synthesis procedure.
Owing to these advantageous properties, the resulting carbon based materials represent promising supercapacitor electrode materials for energy storage applications. This is exemplarily demonstrated by employing the 3D hierarchical porous carbon cubes derived from squarate-zinc coordination compounds as electrode material showing a specific capacitance of 133 F g-1 in H2SO4 at a scan rate of 5 mV s-1 and retaining 67% of this specific capacitance when the scan rate is increased to 200 mV s-1.
In a further application, the porous carbon cubes derived from squarate-zinc coordination compounds are used as high surface area support material and decorated with nickel nanoparticles via an incipient wetness impregnation. The resulting composite material combines a high surface area, a hierarchical pore structure with high functionality and well-accessible pores. Moreover, owing to their regular micro-cube shape, they allow for a good packing of a fixed-bed flow reactor along with high column efficiency and a minimized pressure drop throughout the packed reactor. Therefore, the composite is employed as heterogeneous catalyst in the selective hydrogenation of 5-hydroxymethylfurfural to 2,5-dimethylfuran showing good catalytic performance and overcoming the conventional problem of column blocking.
Thinking about the rational design of 3D carbon geometries, the functions and properties of the resulting carbon-based materials can be further expanded by the rational introduction of heteroatoms (e.g. N, B, S, P, etc.) into the carbon structures in order to alter properties such as wettability, surface polarity as well as the electrochemical landscape. In this context, the use of crystalline materials based on oxocarbon-metal ion complexes can open a platform of highly functional materials for all processes that involve surface processes.
In this work, three ligands produced from amino acids were synthesized and used to produce five bis- and PEPPSI-type palladium–NHC complexes using a novel synthesis route from sustainable starting materials. Three of these complexes were used as precatalysts in the aqueous-phase Suzuki–Miyaura coupling of various substrates displaying high activity. TEM and mercury poisoning experiments provide evidence for Pd-nanoparticle formation stabilized in water.
The aim of this study was to develop a one-step synthesis of gold nanotriangles (NTs) in the presence of mixed phospholipid vesicles followed by a separation process to isolate purified NTs. Negatively charged vesicles containing AOT and phospholipids, in the absence and presence of additional reducing agents (polyampholytes, polyanions or low molecular weight compounds), were used as a template phase to form anisotropic gold nanoparticles. Upon addition of the gold chloride solution, the nucleation process is initiated and both types of particles, i.e., isotropic spherical and anisotropic gold nanotriangles, are formed simultaneously. As it was not possible to produce monodisperse nanotriangles with such a one-step procedure, the anisotropic nanoparticles needed to be separated from the spherical ones. Therefore, a new type of separation procedure using combined polyelectrolyte/micelle depletion flocculation was successfully applied. As a result of the different purification steps, a green colored aqueous dispersion was obtained containing highly purified, well-defined negatively charged flat nanocrystals with a platelet thickness of 10 nm and an edge length of about 175 nm. The NTs produce promising results in surface-enhanced Raman scattering.
Within this work, three physicochemical methods for the hydrophobization of initially hydrophilic solid particles are investigated. The modified particles are then used for the stabilization of oil-in-water (o/w) emulsions. For all introduced methods electrostatic interactions between strongly or weakly charged groups in the system are es-sential. (i) Short chain alkylammonium bromides (C4 – C12) adsorb on oppositely charged solid particles. Macroscopic contact angle measurements of water droplets under air and hexane on flat silica surfaces in dependency of the surface charge density and alkylchain-length allow the calculation of the surface energy and give insights into the emulsification properties of solid particles modified with alkyltrimethylammonium bromides. The measure-ments show an increase of the contact angle with increasing surface charge density, due to the enhanced adsorp-tion of the oppositely charged alkylammonium bromides. Contact angles are higher for longer alkylchain lengths. The surface energy calculations show that in particular the surface-hexane or surface-air interfacial en-ergy is being lowered upon alkylammonium adsorption, while a significant increase of the surface-water interfa-cial energy occurs only at long alkyl chain lengths and high surface charge densities. (ii) The thickness and the charge density of an adsorbed weak polyelectrolyte layer (e.g. PMAA, PAH) influence the wettability of nanoparticles (e.g. alumina, silica, see Scheme 1(b)). Furthermore, the isoelectric point and the pH range of colloidal stability of particle-polyelectrolyte composites depend on the thickness of the weak polye-lectrolyte layer. Silica nanoparticles with adsorbed PAH and alumina nanoparticles with adsorbed PMAA be-come interfacially active and thus able to stabilize o/w emulsions when the degree of dissociation of the polye-lectrolyte layer is below 80 %. The average droplet size after emulsification of dodecane in water depends on the thickness and the degree of dissociation of the adsorbed PE-layer. The visualization of the particle-stabilized o/w emulsions by cryogenic SEM shows that for colloidally stable alumina-PMAA composites the oil-water interface is covered with a closely packed monolayer of particles, while for the colloidally unstable case closely packed aggregated particles deposit on the interface. (iii) By emulsifying a mixture of the corrosion inhibitor 8-hydroxyquinoline (8-HQ) and styrene with silica nanoparticles a highly stable o/w emulsion can be obtained in a narrow pH window. The amphoteric character of 8-HQ enables a pH dependent electrostatic interaction with silica nanoparticles, which can render them interfa-cially active. Depending on the concentration and the degree of dissociation of 8-HQ the adsorption onto silica results from electrostatic or aromatic interactions between 8-HQ and the particle-surface. At intermediate amounts of adsorbed 8-HQ the oil wettability of the particles becomes sufficient for stabilizing o/w emulsions. Cryogenic SEM visualization shows that the particles arrange then in a closely packed shell consisting of partly of aggregated domains on the droplet interface. For further increasing amounts of adsorbed 8-HQ the oil wet-tability is reduced again and the particles ability to stabilize emulsions decreases. By the addition of hexadecane to the oil phase the size of the droplets can be reduced down to 200 nm by in-creasing the silica mass fraction. Subsequent polymerization produces corrosion inhibitor filled (20 wt-%) poly-styrene-silica composite particles. The measurement of the release of 8-hydroxyquinoline shows a rapid increase of 8-hydroxyquinoline in a stirred aqueous solution indicating the release of the total content in less than 5 min-utes. The method is extended for the encapsulation of other organic corrosion inhibitors. The silica-polymer-inhibitor composite particles are then dispersed in a water based alkyd emulsion, and the dispersion is used to coat flat aluminium substrates. After drying and cross-linking the polmer-film Confocal Laser Scanning Micros-copy is employed revealing a homogeneous distribution of the particles in the film. Electrochemical Impedance Spectroscopy in aqueous electrolyte solutions shows that films with aggregated particle domains degrade with time and don’t provide long-term corrosion protection of the substrate. However, films with highly dispersed particles have high barrier properties for corrosive species. The comparison of films containing silica-polystyrene composite particles with and without 8-hydroxyquinoline shows higher electrochemical impedances when the inhibitor is present in the film. By applying the Scanning Vibrating Electrode Technique the localized corrosion rate in the fractured area of scratched polymer films containing the silica-polymer-inhibitor composite particles is studied. Electrochemical corrosion cannot be suppressed but the rate is lowered when inhibitor filled composite particles are present in the film. By depositing six polyelectrolyte layers on particle stabilized emulsion droplets their surface morphology changes significantly as shown by SEM visualization. When the oil wettability of the outer polyelectrolyte layer increases, the polyelectrolyte coated droplets can act as emulsion stabilizers themselves by attaching onto bigger oil droplets in a closely packed arrangement. In the presence of 3 mM LaCl3 8-HQ hydrophobized silica particles aggregate strongly on the oil-water inter-face. The application of an ultrasonic field can remove two dimensional shell-compartments from the droplet surface, which are then found in the aqueous bulk phase. Their size ranges up to 1/4th of the spherical particle shell.
Conventional energy sources are diminishing and non-renewable, take million years to form and cause environmental degradation. In the 21st century, we have to aim at achieving sustainable, environmentally friendly and cheap energy supply by employing renewable energy technologies associated with portable energy storage devices. Lithium-ion batteries can repeatedly generate clean energy from stored materials and convert reversely electric into chemical energy. The performance of lithium-ion batteries depends intimately on the properties of their materials. Presently used battery electrodes are expensive to be produced; they offer limited energy storage possibility and are unsafe to be used in larger dimensions restraining the diversity of application, especially in hybrid electric vehicles (HEVs) and electric vehicles (EVs). This thesis presents a major progress in the development of LiFePO4 as a cathode material for lithium-ion batteries. Using simple procedure, a completely novel morphology has been synthesized (mesocrystals of LiFePO4) and excellent electrochemical behavior was recorded (nanostructured LiFePO4). The newly developed reactions for synthesis of LiFePO4 are single-step processes and are taking place in an autoclave at significantly lower temperature (200 deg. C) compared to the conventional solid-state method (multi-step and up to 800 deg. C). The use of inexpensive environmentally benign precursors offers a green manufacturing approach for a large scale production. These newly developed experimental procedures can also be extended to other phospho-olivine materials, such as LiCoPO4 and LiMnPO4. The material with the best electrochemical behavior (nanostructured LiFePO4 with carbon coating) was able to delive a stable 94% of the theoretically known capacity.
With the rise of nanotechnology in the last decade, nanofluidics has been established as a research field and gained increased interest in science and industry. Natural aqueous nanofluidic systems are very complex, there is often a predominance of liquid interfaces or the fluid contains charged or differently shaped colloids. The effects, promoted by these additives, are far from being completely understood and interesting questions arise with regards to the confinement of such complex fluidic systems. A systematic study of nanofluidic processes requires designing suitable experimental model nano – channels with required characteristics. The present work employed thin liquid films (TLFs) as experimental models. They have proven to be useful experimental tools because of their simple geometry, reproducible preparation, and controllable liquid interfaces. The thickness of the channels can be adjusted easily by the concentration of electrolyte in the film forming solution. This way, channel dimensions from 5 – 100 nm are possible, a high flexibility for an experimental system. TLFs have liquid IFs of different charge and properties and they offer the possibility to confine differently shaped ions and molecules to very small spaces, or to subject them to controlled forces. This makes the foam films a unique “device” available to obtain information about fluidic systems in nanometer dimensions. The main goal of this thesis was to study nanofluidic processes using TLFs as models, or tools, and to subtract information about natural systems plus deepen the understanding on physical chemical conditions. The presented work showed that foam films can be used as experimental models to understand the behavior of liquids in nano – sized confinement. In the first part of the thesis, we studied the process of thinning of thin liquid films stabilized with the non – ionic surfactant n – dodecyl – β – maltoside (β – C₁₂G₂) with primary interest in interfacial diffusion processes during the thinning process dependent on surfactant concentration 64. The surfactant concentration in the film forming solutions was varied at constant electrolyte (NaCl) concentration. The velocity of thinning was analyzed combining previously developed theoretical approaches. Qualitative information about the mobility of the surfactant molecules at the film surfaces was obtained. We found that above a certain limiting surfactant concentration the film surfaces were completely immobile and they behaved as non – deformable, which decelerated the thinning process. This follows the predictions for Reynolds flow of liquid between two non – deformable disks. In the second part of the thesis, we designed a TLF nanofluidic system containing rod – like multivalent ions and compared this system to films containing monovalent ions. We presented first results which recognized for the first time the existence of an additional attractive force in the foam films based on the electrostatic interaction between rod – like ions and oppositely charged surfaces. We may speculate that this is an ion bridging component of the disjoining pressure. The results show that for films prepared in presence of spermidine the transformation of the thicker CF to the thinnest NBF is more probable as films prepared with NaCl at similar conditions of electrostatic interaction. This effect is not a result of specific adsorption of any of the ions at the fluid surfaces and it does not lead to any changes in the equilibrium properties of the CF and NBF. Our hypothesis was proven using the trivalent ion Y3+ which does not show ion bridging. The experimental results are compared to theoretical predictions and a quantitative agreement on the system’s energy gain for the change from CF to NBF could be obtained. In the third part of the work, the behavior of nanoparticles in confinement was investigated with respect to their impact on the fluid flow velocity. The particles altered the flow velocity by an unexpected high amount, so that the resulting changes in the dynamic viscosity could not be explained by a realistic change of the fluid viscosity. Only aggregation, flocculation and plug formation can explain the experimental results. The particle systems in the presented thesis had a great impact on the film interfaces due to the stabilizer molecules present in the bulk solution. Finally, the location of the particles with respect to their lateral and vertical arrangement in the film was studied with advanced reflectivity and scattering methods. Neutron Reflectometry studies were performed to investigate the location of nanoparticles in the TLF perpendicular to the IF. For the first time, we study TLFs using grazing incidence small angle X – ray scattering (GISAXS), which is a technique sensitive to the lateral arrangement of particles in confined volumes. This work provides preliminary data on a lateral ordering of particles in the film.
Analytical ultracentrifugation (AUC) has made an important contribution to polymer and particle characterization since its invention by Svedberg (Svedberg and Nichols 1923; Svedberg and Pederson 1940) in 1923. In 1926, Svedberg won the Nobel price for his scientific work on disperse systems including work with AUC. The first important discovery performed with AUC was to show the existence of macromolecules. Since that time AUC has become an important tool to study polymers in biophysics and biochemistry. AUC is an absolute technique that does not need any standard. Molar masses between 200 and 1014 g/mol and particle size between 1 and 5000 nm can be detected by AUC. Sample can be fractionated into its components due to its molar mass, particle size, structure or density without any stationary phase requirement as it is the case in chromatographic techniques. This very property of AUC earns it an important status in the analysis of polymers and particles. The distribution of molar mass, particle sizes and densities can be measured with the fractionation. Different types of experiments can give complementary physicochemical parameters. For example, sedimentation equilibrium experiments can lead to the study of pure thermodynamics. For complex mixtures, AUC is the main method that can analyze the system. Interactions between molecules can be studied at different concentrations without destroying the chemical equilibrium (Kim et al. 1977). Biologically relevant weak interactions can also be monitored (K ≈ 10-100 M-1). An analytical ultracentrifuge experiment can yield the following information: • Molecular weight of the sample • Number of the components in the sample if the sample is not a single component • Homogeneity of the sample • Molecular weight distribution if the sample is not a single component • Size and shape of macromolecules & particles • Aggregation & interaction of macromolecules • Conformational changes of macromolecules • Sedimentation coefficient and density distribution Such an extremely wide application area of AUC allows the investigation of all samples consisting of a solvent and a dispersed or dissolved substance including gels, micro gels, dispersions, emulsions and solutions. Another fact is that solvent or pH limitation does not exist for this method. A lot of new application areas are still flourishing, although the technique is 80 years old. In 1970s, 1500 AUC were operational throughout the world. At those times, due to the limitation in detection technologies, experimental results were obtained with photographic records. As time passed, faster techniques such as size exclusion chromatography (SEC), light scattering (LS) or SDS-gel electrophoresis occupied the same research fields with AUC. Due to these relatively new techniques, AUC began to loose its importance. In the 1980s, only a few AUC were in use throughout the world. In the beginning of the 1990s a modern AUC -the Optima XL-A - was released by Beckman Instruments (Giebeler 1992). The Optima XL-A was equipped with a modern computerized scanning absorption detector. The addition of Rayleigh Interference Optics is introduced which is called XL-I AUC. Furthermore, major development in computers made the analysis easier with the help of new analysis software. Today, about 400 XL-I AUC exist worldwide. It is usually applied in the industry of pharmacy, biopharmacy and polymer companies as well as in academic research fields such as biochemistry, biophysics, molecular biology and material science. About 350 core scientific publications which use analytical ultracentrifugation are published every year (source: SciFinder 2008 ) with an increasing number of references (436 reference in 2008). A tremendous progress has been made in method and analysis software after digitalization of experimental data with the release of XL-I. In comparison to the previous decade, data analysis became more efficient and reliable. Today, AUC labs can routinely use sophisticated data analysis methods for determination of sedimentation coefficient distributions (Demeler and van Holde 2004; Schuck 2000; Stafford 1992), molar mass distributions (Brookes and Demeler 2008; Brookes et al. 2006; Brown and Schuck 2006), interaction constants (Cao and Demeler 2008; Schuck 1998; Stafford and Sherwood 2004), particle size distributions with Angstrom resolution (Cölfen and Pauck 1997) and the simulations determination of size and shape distributions from sedimentation velocity experiments (Brookes and Demeler 2005; Brookes et al. 2006). These methods are also available in powerful software packages that combines various methods, such as, Ultrascan (Demeler 2005), Sedift/Sedphat (Schuck 1998; Vistica et al. 2004) and Sedanal (Stafford and Sherwood 2004). All these powerful packages are free of charge. Furthermore, Ultrascans source code is licensed under the GNU Public License (http://www.gnu.org/copyleft/gpl.html). Thus, Ultrascan can be further improved by any research group. Workshops are organized to support these software packages. Despite of the tremendous developments in data analysis, hardware for the system has not developed much. Although there are various user developed detectors in research laboratories, they are not commercially available. Since 1992, only one new optical system called “the fluorescence optics” (Schmidt and Reisner, 1992, MacGregor et al. 2004, MacGregor, 2006, Laue and Kroe, in press) has been commercialized. However, except that, there has been no commercially available improvement in the optical system. The interesting fact about the current hardware of the XL-I is that it is 20 years old, although there has been an enormous development in microelectronics, software and in optical systems in the last 20 years, which could be utilized for improved detectors. As examples of user developed detector, Bhattacharyya (Bhattacharyya 2006) described a Multiwavelength-Analytical Ultracentrifuge (MWL-AUC), a Raman detector and a small angle laser light scattering detector in his PhD thesis. MWL-AUC became operational, but a very high noise level prevented to work with real samples. Tests with the Raman detector were not successful due to the low light intensity and thus high integration time is required. The small angle laser light scattering detector could only detect latex particles but failed to detect smaller particles and molecules due to low sensitivity of the detector (a photodiode was used as detector). The primary motivation of this work is to construct a detector which can measure new physico-chemical properties with AUC with a nicely fractionated sample in the cell. The final goal is to obtain a multiwavelength detector for the AUC that measures complementary quantities. Instrument development is an option for a scientist only when there is a huge potential benefit but there is no available commercial enterprise developing appropriate equipment, or if there is not enough financial support to buy it. The first case was our motivation for developing detectors for AUC. Our aim is to use today’s technological advances in microelectronics, programming, mechanics in order to develop new detectors for AUC and improve the existing MWL detector to routine operation mode. The project has multiple aspects which can be listed as mechanical, electronical, optical, software, hardware, chemical, industrial and biological. Hence, by its nature it is a multidisciplinary project. Again by its nature it contains the structural problem of its kind; the problem of determining the exact discipline to follow at each new step. It comprises the risk of becoming lost in some direction. Having that fact in mind, we have chosen the simplest possible solution to any optical, mechanical, electronic, software or hardware problem we have encountered and we have always tried to see the overall picture. In this research, we have designed CCD-C-AUC (CCD Camera UV/Vis absorption detector for AUC) and SLS-AUC (Static Light Scattering detector for AUC) and tested them. One of the SLS-AUC designs produced successful test results, but the design could not be brought to the operational stage. However, the operational state Multiwavelength Analytical Ultracentrifuge (MWL-AUC) AUC has been developed which is an important detector in the fields of chemistry, biology and industry. In this thesis, the operational state Multiwavelength Analytical Ultracentrifuge (MWL-AUC) AUC is to be introduced. Consequently, three different applications of MWL-AUC to the aforementioned disciplines shall be presented. First of all, application of MWL-AUC to a biological system which is a mixture of proteins lgG, aldolase and BSA is presented. An application of MWL-AUC to a mass-produced industrial sample (β-carotene gelatin composite particles) which is manufactured by BASF AG, is presented. Finally, it is shown how MWL-AUC will impact on nano-particle science by investigating the quantum size effect of CdTe and its growth mechanism. In this thesis, mainly the relation between new technological developments and detector development for AUC is investigated. Pioneering results are obtained that indicate the possible direction to be followed for the future of AUC. As an example, each MWL-AUC data contains thousands of wavelengths. MWL-AUC data also contains spectral information at each radial point. Data can be separated to its single wavelength files and can be analyzed classically with existing software packages. All the existing software packages including Ultrascan, Sedfit, Sedanal can analyze only single wavelength data, so new extraordinary software developments are needed. As a first attempt, Emre Brookes and Borries Demeler have developed mutliwavelength module in order to analyze the MWL-AUC data. This module analyzes each wavelength separately and independently. We appreciate Emre Brookes and Borries Demeler for their important contribution to the development of the software. Unfortunately, this module requires huge amount of computer power and does not take into account the spectral information during the analysis. New software algorithms are needed which take into account the spectral information and analyze all wavelengths accordingly. We would like also invite the programmers of Ultrascan, Sedfit, Sedanal and the other programs, to develop new algorithms in this direction.