This work presents the development of entropy-elastic gelatin based networks in the form of films or scaffolds. The materials have good prospects for biomedical applications, especially in the context of bone regeneration. Entropy-elastic gelatin based hydrogel films with varying crosslinking densities were prepared with tailored mechanical properties. Gelatin was covalently crosslinked above its sol gel transition, which suppressed the gelatin chain helicity. Hexamethylene diisocyanate (HDI) or ethyl ester lysine diisocyanate (LDI) were applied as chemical crosslinkers, and the reaction was conducted either in dimethyl sulfoxide (DMSO) or water. Amorphous films were prepared as measured by Wide Angle X-ray Scattering (WAXS), with tailorable degrees of swelling (Q: 300-800 vol. %) and wet state Young’s modulus (E: 70 740 kPa). Model reactions showed that the crosslinking reaction resulted in a combination of direct crosslinks (3-13 mol.-%), grafting (5-40 mol.-%), and blending of oligoureas (16-67 mol.-%). The knowledge gained with this bulk material was transferred to the integrated process of foaming and crosslinking to obtain porous 3-D gelatin-based scaffolds. For this purpose, a gelatin solution was foamed in the presence of a surfactant, Saponin, and the resulting foam was fixed by chemical crosslinking with a diisocyanate. The amorphous crosslinked scaffolds were synthesized with varied gelatin and HDI concentrations, and analyzed in the dry state by micro computed tomography (µCT, porosity: 65±11–73±14 vol.-%), and scanning electron microscopy (SEM, pore size: 117±28–166±32 µm). Subsequently, the work focused on the characterization of the gelatin scaffolds in conditions relevant to biomedical applications. Scaffolds showed high water uptake (H: 630-1680 wt.-%) with minimal changes in outer dimension. Since a decreased scaffold pore size (115±47–130±49 µm) was revealed using confocal laser scanning microscopy (CLSM) upon wetting, the form stability could be explained. Shape recoverability was observed after removal of stress when compressing wet scaffolds, while dry scaffolds maintained the compressed shape. This was explained by a reduction of the glass transition temperature upon equilibration with water (dynamic mechanical analysis at varied temperature (DMTA)). The composition dependent compression moduli (Ec: 10 50 kPa) were comparable to the bulk micromechanical Young’s moduli, which were measured by atomic force microscopy (AFM). The hydrolytic degradation profile could be adjusted, and a controlled decrease of mechanical properties was observed. Partially-degraded scaffolds displayed an increase of pore size. This was likely due to the pore wall disintegration during degradation, which caused the pores to merge. The scaffold cytotoxicity and immunologic responses were analyzed. The porous scaffolds enabled proliferation of human dermal fibroblasts within the implants (up to 90 µm depth). Furthermore, indirect eluate tests were carried out with L929 cells to quantify the material cytotoxic response. Here, the effect of the sterilization method (Ethylene oxide sterilization), crosslinker, and surfactant were analyzed. Fully cytocompatible scaffolds were obtained by using LDI as crosslinker and PEO40 PPO20-PEO40 as surfactant. These investigations were accompanied by a study of the endotoxin material contamination. The formation of medical-grade materials was successfully obtained (<0.5 EU/mL) by using low-endotoxin gelatin and performing all synthetic steps in a laminar flow hood.
In this work, thermosensitive hydrogels having tunable thermo-mechanical properties were synthesized. Generally the thermal transition of thermosensitive hydrogels is based on either a lower critical solution temperature (LCST) or critical micelle concentration/ temperature (CMC/ CMT). The temperature dependent transition from sol to gel with large volume change may be seen in the former type of thermosensitive hydrogels and is negligible in CMC/ CMT dependent systems. The change in volume leads to exclusion of water molecules, resulting in shrinking and stiffening of system above the transition temperature. The volume change can be undesired when cells are to be incorporated in the system. The gelation in the latter case is mainly driven by micelle formation above the transition temperature and further colloidal packing of micelles around the gelation temperature. As the gelation mainly depends on concentration of polymer, such a system could undergo fast dissolution upon addition of solvent. Here, it was envisioned to realize a thermosensitive gel based on two components, one responsible for a change in mechanical properties by formation of reversible netpoints upon heating without volume change, and second component conferring degradability on demand. As first component, an ABA triblockcopolymer (here: Poly(ethylene glycol)-b-poly(propylene glycol)-b-poly(ethylene glycol) (PEPE) with thermosensitive properties, whose sol-gel transition on the molecular level is based on micellization and colloidal jamming of the formed micelles was chosen, while for the additional macromolecular component crosslinking the formed micelles biopolymers were employed. The synthesis of the hydrogels was performed in two ways, either by physical mixing of compounds showing electrostatic interactions, or by covalent coupling of the components. Biopolymers (here: the polysaccharides hyaluronic acid, chondroitin sulphate, or pectin, as well as the protein gelatin) were employed as additional macromolecular crosslinker to simultaneously incorporate an enzyme responsiveness into the systems. In order to have strong ionic/electrostatic interactions between PEPE and polysaccharides, PEPE was aminated to yield predominantly mono- or di-substituted PEPEs. The systems based on aminated PEPE physically mixed with HA showed an enhancement in the mechanical properties such as, elastic modulus (G′) and viscous modulus (G′′) and a decrease of the gelation temperature (Tgel) compared to the PEPE at same concentration. Furthermore, by varying the amount of aminated PEPE in the composition, the Tgel of the system could be tailored to 27-36 °C. The physical mixtures of HA with di-amino PEPE (HA·di-PEPE) showed higher elastic moduli G′ and stability towards dissolution compared to the physical mixtures of HA with mono-amino PEPE (HA·mono-PEPE). This indicates a strong influence of electrostatic interaction between –COOH groups of HA and –NH2 groups of PEPE. The physical properties of HA with di-amino PEPE (HA·di-PEPE) compare beneficially with the physical properties of the human vitreous body, the systems are highly transparent, and have a comparable refractive index and viscosity. Therefore,this material was tested for a potential biological application and was shown to be non-cytotoxic in eluate and direct contact tests. The materials will in the future be investigated in further studies as vitreous body substitutes. In addition, enzymatic degradation of these hydrogels was performed using hyaluronidase to specifically degrade the HA. During the degradation of these hydrogels, increase in the Tgel was observed along with decrease in the mechanical properties. The aminated PEPE were further utilised in the covalent coupling to Pectin and chondroitin sulphate by using EDC as a coupling agent. Here, it was possible to adjust the Tgel (28-33 °C) by varying the grafting density of PEPE to the biopolymer. The grafting of PEPE to Pectin enhanced the thermal stability of the hydrogel. The Pec-g-PEPE hydrogels were degradable by enzymes with slight increase in Tgel and decrease in G′ during the degradation time. The covalent coupling of aminated PEPE to HA was performed by DMTMM as a coupling agent. This method of coupling was observed to be more efficient compared to EDC mediated coupling. Moreover, the purification of the final product was performed by ultrafiltration technique, which efficiently removed the unreacted PEPE from the final product, which was not sufficiently achieved by dialysis. Interestingly, the final products of these reaction were in a gel state and showed enhancement in the mechanical properties at very low concentrations (2.5 wt%) near body temperature. In these hydrogels the resulting increase in mechanical properties was due to the combined effect of micelle packing (physical interactions) by PEPE and covalent netpoints between PEPE and HA. PEPE alone or the physical mixtures of the same components were not able to show thermosensitive behavior at concentrations below 16 wt%. These thermosensitive hydrogels also showed on demand solubilisation by enzymatic degradation. The concept of thermosensitivity was introduced to 3D architectured porous hydrogels, by covalently grafting the PEPE to gelatin and crosslinking with LDI as a crosslinker. Here, the grafted PEPE resulted in a decrease in the helix formation in gelatin chains and after fixing the gelatin chains by crosslinking, the system showed an enhancement in the mechanical properties upon heating (34-42 °C) which was reversible upon cooling. A possible explanation of the reversible changes in mechanical properties is the strong physical interactions between micelles formed by PEPE being covalently linked to gelatin. Above the transition temperature, the local properties were evaluated by AFM indentation of pore walls in which an increase in elastic modulus (E) at higher temperature (37 °C) was observed. The water uptake of these thermosensitive architectured porous hydrogels was also influenced by PEPE and temperature (25 °C and 37 °C), showing lower water up take at higher temperature and vice versa. In addition, due to the lower water uptake at high temperature, the rate of hydrolytic degradation of these systems was found to be decreased when compared to pure gelatin architectured porous hydrogels. Such temperature sensitive architectured porous hydrogels could be important for e.g. stem cell culturing, cell differentiation and guided cell migration, etc. Altogether, it was possible to demonstrate that the crosslinking of micelles by a macromolecular crosslinker increased the shear moduli, viscosity, and stability towards dissolution of CMC-based gels. This effect could be likewise be realized by covalent or non-covalent mechanisms such as, micelle interactions, physical interactions of gelatin chains and physical interactions between gelatin chains and micelles. Moreover, the covalent grafting of PEPE will create additional net-points which also influence the mechanical properties of thermosensitive architectured porous hydrogels. Overall, the physical and chemical interactions and reversible physical interactions in such thermosensitive architectured porous hydrogels gave a control over the mechanical properties of such complex system. The hydrogels showing change of mechanical properties without a sol-gel transition or volume change are especially interesting for further study with cell proliferation and differentiation.
Dual responsive inverse opal hydrogels were designed as autonomous sensor systems for (bio)macromolecules, exploiting the analyte-induced modulation of the opal's structural color. The systems that are based on oligo(ethylene glycol) macromonomers additionally incorporate comonomers with various recognition units. They combine a coil-to-globule collapse transition of the LCST type with sensitivity of the transition temperature toward molecular recognition processes. This enables the specific detection of macromolecular analytes, such as glycopolymers and proteins, by simple optical methods. While the inverse opal structure assists the effective diffusion even of large analytes into the photonic crystal, the stimulus responsiveness gives rise to strong shifts of the optical Bragg peak of more than 100nm upon analyte binding at a given temperature. The systems' design provides a versatile platform for the development of easy-to-use, fast, and low-cost sensors for pathogens.
Physikalische Hydrogele gewinnen derzeit als Zellsubstrate zunehmend an Interesse, da Viskoelastizität oder Stressrelaxation ein bedeutender Parameter in der Mechanotransduktion ist, der bisher vernachlässigt wurde. In dieser Arbeit wurden multi-funktionelle Polyurethane entworfen, die über einen neuartigen Gelierungsmechanismus physikalische Hydrogele bilden. In Wasser bilden die anionischen Polyurethane spontan Aggregate, welche durch elektrostatische Abstoßung in Lösung gehalten werden. Eine schnelle Gelierung kann von hier aus durch Ladungsabschirmung erreicht werden, wodurch die Aggregation voranschreitet und ein Netzwerk ausgebildet wird. Dies kann durch die Zugabe von verschiedenen Säuren oder Salzen geschehen, sodass sowohl saure (pH 4 - 5) als auch pH-neutrale Hydrogele erhalten werden können. Während konventionelle Hydrogele auf Polyurethan-Basis in der Regel durch toxische isocyanat-haltige Präpolymere hergestellt werden, eignet sich der hier beschriebene physikalische Gelierungsmechanismus für in situ Anwendungen in sensitiven Umgebungen. Sowohl Härte als auch Stressrelaxation der Hydrogele können unabhängig voneinander über einen breiten Bereich eingestellt werden. Darüberhinaus zeichnen sich die Hydrogele durch exzellente Stressregeneration aus.
We report on light sensitive microgel particles that can change their volume reversibly in response to illumination with light of different wavelengths. To make the anionic microgels photosensitive we add surfactants with a positively charged polyamine head group and an azobenzene containing tail. Upon illumination, azobenzene undergoes a reversible photo-isomerization reaction from a trans- to a cis-state accompanied by a change in the hydrophobicity of the surfactant. Depending on the isomerization state, the surfactant molecules are either accommodated within the microgel (trans-state) resulting in its shrinkage or desorbed back into water (cis-isomer) letting the microgel swell. We have studied three surfactants differing in the number of amino groups, so that the number of charges of the surfactant head varies between 1 and 3. We have found experimentally and theoretically that the surfactant concentration needed for microgel compaction increases with decreasing number of charges of the head group. Utilization of polyamine azobenzene containing surfactants for the light triggered remote control of the microgel size opens up a possibility for applications of light responsive microgels as drug carriers in biology and medicine.
Utilization of sunlight for energy harvesting has been foreseen as sustainable replacement for fossil fuels, which would also eliminate side effects arising from fossil fuel consumption such as drastic increase of CO2 in Earth atmosphere. Semiconductor materials can be implemented for energy harvesting, and design of ideal energy harvesting devices relies on effective semiconductor with low recombination rate, ease of processing, stability over long period, non-toxicity and synthesis from abundant sources. Aforementioned criteria have attracted broad interest for graphitic carbon nitride (g-CN) materials, metal-free semiconductor which can be synthesized from low cost and abundant precursors. Furthermore, physical properties such as band gap, surface area and absorption can be tuned. g-CN was investigated as heterogeneous catalyst, with diversified applications from water splitting to CO2 reduction and organic coupling reactions. However, low dispersibility of g-CN in water and organic solvents was an obstacle for future improvements.
Tissue engineering aims to mimic natural tissues mechanically and biologically, so that synthetic materials can replace natural ones in future. Hydrogels are crosslinked networks with high water content, therefore are prime candidates for tissue engineering. However, the first requirement is synthesis of hydrogels with mechanical properties that are matching to natural tissues. Among different approaches for reinforcement, nanocomposite reinforcement is highly promising.
This thesis aims to investigate aqueous and organic dispersions of g-CN materials. Aqueous g-CN dispersions were utilized for visible light induced hydrogel synthesis, where g-CN acts as reinforcer and photoinitiator. Varieties of methodologies were presented for enhancing g-CN dispersibility, from co-solvent method to prepolymer formation, and it was shown that hydrogels with diversified mechanical properties (from skin-like to cartilage-like) are accessible via g-CN utilization. One pot photografting method was introduced for functionalization of g-CN surface which provides functional groups towards enhanced dispersibility in aqueous and organic media. Grafting vinyl thiazole groups yields stable additive-free organodispersions of g-CN which are electrostatically stabilized with increased photophysical properties. Colloidal stability of organic systems provides transparent g-CN coatings and printing g-CN from commercial inkjet printers.
Overall, application of g-CN in dispersed media is highly promising, and variety of materials can be accessible via utilization of g-CN and visible light with simple chemicals and synthetic conditions. g-CN in dispersed media will bridge emerging research areas from tissue engineering to energy harvesting in near future.
We report on the formation of stimuli-responsive structured hydrogel thin films whose pattern geometry can be adjusted on demand and tuned reversibly by varying solvent quality or by changing temperature. The hydrogel films, similar to 100 nm in thickness, were prepared by depositing layers of random copolymers comprising N-isopropylacrylamide and ultraviolet (UV)-active methacryloyloxybenzophenone units onto solid substrates. A two-beam interference pattern technique was used to cross-link the selected areas of the film; any unreacted material was extracted using ethanol after UV light-assisted cross-linking. In this way, we produced nanoholes, perfectly ordered structures with a narrow size distribution, negligible tortuosity, adjustable periodicity, and a high density. The diameter of the circular holes ranged from a few micrometers down to several tens of nanometers; the hole periodicity could be adjusted readily by changing the optical period of the UV interference pattern. The holes were reversibly closed and opened by swelling/deswelling the polymer networks in the presence of ethanol and water, respectively, at various temperatures. The reversible regulation of the hole diameter can be repeated many times within a few seconds. The hydrogel sheet with circular holes periodically arranged may also be transferred onto different substrates and be employed as tunable templates for the deposition of desired substances.
Quadruple-shape hydrogels
(2019)
The capability of directed movements by two subsequent shape changes could be implemented in shape-memory hydrogels by incorporation of two types of crystallizable side chains While in non-swollen polymer networks even more directed movements could be realized, the creation of multi-shape hydrogels is still a challenge. We hypothesize that a quadruple-shape effect in hydrogels can be realized, when a swelling capacity almost independent of temperature is generated, whereby directed movements could be enabled, which are not related to swelling. In this case, entropy elastic recovery could be realized by hydrophilic segments and the fixation of different macroscopic shapes by means of three semi-crystalline side chains generating temporary crosslinks. Monomethacrylated semi-crystalline oligomers were connected as side chains in a hydrophilic polymer network via radical copolymerization. Computer assisted modelling was utilized to design a demonstrator capable of complex shape shifts by creating a casting mold via 3D printing from polyvinyl alcohol. The demonstrator was obtained after copolymerization of polymer network forming components within the mold, which was subsequently dissolved in water. A thermally-induced quadruple-shape effect was realized after equilibrium swelling of the polymer network in water. Three directed movements were successfully obtained when the temperature was continuously increased from 5 degrees C to 90 degrees C with a recovery ratio of the original shape above 90%. Hence, a thermally-induced quadruple-shape effect as new record for hydrogels was realized. Here, the temperature range for the multi-shape effect was limited by water as swelling media (0 degrees C-100 degrees C), simultaneously distinctly separated thermal transitions were required, and the overall elasticity indispensable for successive deformations was reduced as result of partially chain segment orientation induced by swelling in water. Conclusively the challenges for penta- or hexa-shape gels are the design of systems enabling higher elastic deformability and covering a larger temperature range by switching to a different solvent.
Enzymes can support the synthesis or degradation of biomacromolecules in natural processes. Here, we demonstrate that enzymes can induce a macroscopic-directed movement of microstructured hydrogels following a mechanism that we call a "Jack-in-the-box" effect. The material's design is based on the formation of internal stresses induced by a deformation load on an architectured microscale, which are kinetically frozen by the generation of polyester locking domains, similar to a Jack-in-thebox toy (i.e., a compressed spring stabilized by a closed box lid). To induce the controlled macroscopic movement, the locking domains are equipped with enzyme-specific cleavable bonds (i.e., a box with a lock and key system). As a result of enzymatic reaction, a transformed shape is achieved by the release of internal stresses. There is an increase in entropy in combination with a swelling-supported stretching of polymer chains within the microarchitectured hydrogel (i.e., the encased clown pops-up with a pre-stressed movement when the box is unlocked). This utilization of an enzyme as a physiological stimulus may offer new approaches to create interactive and enzyme-specific materials for different applications such as an optical indicator of the enzyme's presence or actuators and sensors in biotechnology and in fermentation processes.