Refine
Has Fulltext
- no (140) (remove)
Year of publication
Document Type
- Article (133)
- Conference Proceeding (3)
- Review (3)
- Other (1)
Language
- English (140)
Is part of the Bibliography
- yes (140)
Keywords
- Hydrogel (3)
- LCST behavior (3)
- Thermoresponsive (3)
- cyclic voltammetry (3)
- synthesis (3)
- Block copolymers (2)
- Polyelectrolytes (2)
- Thin film (2)
- diblock copolymers (2)
- hydrogels (2)
Institute
The thermal behavior of poly(methoxydiethylenglycol acrylate) (PMDEGA) is studied in thin hydrogel films on solid supports and is compared with the behavior in aqueous solution. The PMDEGA hydrogel film thickness is varied from 2 to 422 nm. Initially, these films are homogenous, as measured with optical microscopy, atomic force microscopy, X-ray reflectivity, and grazing-incidence small-angle X-ray scattering (GISAXS). However, they tend to de-wet when stored under ambient conditions. Along the surface normal, no long-ranged correlations between substrate and film surface are detected with GISAXS, due to the high mobility of the polymer at room temperature. The swelling of the hydrogel films as a function of the water vapor pressure and the temperature are probed for saturated water vapor pressures between 2,380 and 3,170 Pa. While the swelling capability is found to increase with water vapor pressure, swelling in dependence on the temperature revealed a collapse phase transition of a lower critical solution temperature type. The transition temperature decreases from 40.6 A degrees C to 36.6 A degrees C with increasing film thickness, but is independent of the thickness for very thin films below a thickness of 40 nm. The observed transition temperature range compares well with the cloud points observed in dilute (0.1 wt.%) and semi-dilute (5 wt.%) solution which decrease from 45 A degrees C to 39 A degrees C with increasing concentration.
The rehydration of thermoresponsive poly(monomethoxydiethylene glycol acrylate) (PMDEGA) films exhibiting a lower critical solution temperature (LCST) type demixing phase transition in aqueous environments, induced by a decrease in temperature, is investigated in situ with real-time neutron reflectivity. Two different starting conditions (collapsed versus partially swollen chain conformation) are compared. In one experiment, the temperature is reduced from above the demixing temperature to well below the demixing temperature. In a second experiment, the starting temperature is below the demixing temperature, but within the transition regime, and reduced to the same final temperature. In both cases, the observed rehydration process can be divided into three stages: first condensation of water from the surrounding atmosphere, then absorption of water by the PMDEGA film and evaporation of excess water, and finally, rearrangement of the PMDEGA chains. The final rehydrated film is thicker and contains more absorbed water as compared with the initially swollen film at the same temperature well below the demixing temperature.
Thin thermoresponsive films of the triblock copolymer polystyrene-block-poly(methoxydiethylene glycol acrylate)-block-polystyrene (P(S-b-MDEGA-b-S)) are investigated on silicon substrates. By spin coating, homogeneous and smooth films are prepared for a range of film thicknesses from 6 to 82 nm. Films are stable with respect to dewetting as investigated with optical microscopy and atomic force microscopy. P(S-b-MDEGA-b-S) films with a thickness of 39 nm exhibit a phase transition of the lower critical solution temperature (LCST) type at 36.5 degrees C. The swelling and the thermoresponsive behavior of the films with respect to a sudden thermal stimulus are probed with in-situ neutron reflectivity. In undersaturated water vapor swelling proceeds without thickness increase. The thermoresponse proceeds in three steps: First, the film rejects water as the temperature is above LCST. Next, it stays constant for 600 s, before the collapsed film takes up water again. With ATR-FTIR measurements, changes of bound water in the film caused by different thermal stimuli are studied. Hydrogen bonds only form between C=O and water in the swollen film. Above the LCST most hydrogen bonds with water are broken, but some amount of bound water remains inside the film in agreement with the neutron reflectivity data. Grazing-incidence small-angle X-ray scattering (GISAXS) shows that the inner lateral structure is not significantly influenced by the different thermal stimuli.
The switching kinetics of thin thermo-responsive hydrogel films of poly(monomethoxy-diethyleneglycol-acrylate) (PMDEGA) are investigated. Homogeneous and smooth PMDEGA films with a thickness of 35.9 nm are prepared on silicon substrates by spin coating. As probed with white light interferometry, PMDEGA films with a thickness of 35.9 nm exhibit a phase transition temperature of the lower critical solution temperature (LCST) type of 40 degrees C. In situ neutron reflectivity is performed to investigate the thermo-responsive behavior of these PMDEGA hydrogel films in response to a sudden thermal stimulus in deuterated water vapor atmosphere. The collapse transition proceeds in a complex way which can be seen as three steps. The first step is the shrinkage of the initially swollen film by a release of water. In the second step the thickness remains constant with water molecules embedded in the film. In the third step, perhaps due to a conformational rearrangement of the collapsed PMDEGA chains, water is reabsorbed from the vapor atmosphere, thereby giving rise to a relaxation process. Both the shrinkage and relaxation processes can be described by a simple model of hydrogel deswelling.
Thick poly(styrene-b-monomethoxydiethylenglycol-acrylate-b-styrene) [P(S-b-MDEGA-b-S)] films (thickness 5 mu m) are prepared from different solvents on flexible substrates by solution casting and investigated with small-angle X-ray scattering. As the solvents are either PS- or PMDEGA-selective, micelles with different core-shell micellar structures are formed. In PMDEGA-selective solvents, the PS block is the core and PMDEGA is the shell, whereas in PS-selective solvents, the order is reversed. After exposing the films to liquid D2O, the micellar structure inside the films prepared from PMDEGA-selective solvents remains unchanged and only the PMDEGA (shell part) swells. On the contrary, in the films prepared from PS-selective solvents, the micelles revert the core and the shell. This reversal causes more entanglements of the PMDEGA chains between the micelles. Moreover, the thermal collapse transition of the PMDEGA block in liquid D2O is significantly broadened. Irrespective of the solvent used for film preparation, the swollen PMDEGA shell does not show a prominent shrinkage when passing the phase transition, and the transition process occurs via compaction. The collapsed micelles have a tendency to densely pack above the transition temperature.
Swelling of Polyelectrolyte Multilayers: The Relation Between, Surface and Bulk Characteristics
(2015)
The odd even effect, i.e., the influence of the outermost layer of polyelectrolyte multilayers (PEMs) on their swelling behavior, is investigated. For that purpose poly(styrene sodium sulfonate) (PSS)/poly(diallyl-dimethylammonium chloride) (PDADMAC) polyelectrolyte multilayers are studied in air with 1% relative humidity (RH), 30% RH, 95% RH, and in liquid water by ellipsometry, atomic force microscopy (AFM), and X-ray reflectometry (XRR). Since the total amount of water uptake in swollen PEMs is divided into two fractions, the void water and the swelling water, a correct evaluation of the odd even effect is only possible if both fractions are examined separately. In order to allow measuring samples over a larger thickness regime the investigation of a larger amount of samples is required. Therefore, the concept of separating void water from swelling water using neutron reflectometry is for the first time transferred to ellipsometry. The subsequent analysis of swelling water, void water, and roughness revealed the existence of two types of odd even effects: an odd even effect which addresses only the surface of the PEM (surface-odd even effect) and an odd even effect which addresses also the bulk of the PEM (bulk-odd even effect). The appearance of both effects is dependent on the environment; the surface-odd even effect is only detectable in humid air while the bulk-odd even effect is only detectable in liquid water. The bulk-odd even effect is related to the osmotic pressure between the PEM and the surrounding water. A correlation between the amount of void water and both odd even effects is not found. The amount of void water is independent of the terminated layer and the thickness of PEMs.
Molecular brush diblock copolymers were synthesized by the orthogonal overlay of the RAFT (reversible addition-fragmentation chain transfer), the ATRP (atom transfer radical polymerization), and the NMP (nitroxide-mediated polymerization) techniques. This unique combination enabled the synthesis of the complex amphiphilic polymers without the need of postpolymerization modifications, using a diblock copolymer intermediate made from two selectively addressable inimers and applying a sequence of four controlled free radical polymerization steps in total. The resulting polymers are composed of a thermosensitive poly(N-isopropylacrylamide) brush as hydrophilic block and a polystyrene brush as hydrophobic block, thus translating the structure of the established amphiphilic diblock copolymers known as macro surfactants to the higher size level of "giant surfactants". The dual molecular brushes and the aggregates formed on ultra flat solid substrates were visualized by scanning force microscopy (SFM).
The combination of two techniques of controlled free radical polymerization, namely the reversible addition fragmentation chain transfer (RAFT) and the atom transfer radical polymerization (ATRP) techniques, together with the use of a macromonomer allowed the synthesis of symmetrical triblock copolymers, designed as amphiphilic dual brushes. One type of brush was made of poly(n-butyl acrylate) as soft hydrophobic block, i.e. characterized by a low glass transition temperature, while the other one was made of hydrophilic poly(ethylene glycol) (PEG). The new triblock polymers represent "giant surfactants" according to their molecular architecture. The hydrophobic and hydrophilic blocks microphase separate in the bulk. In aqueous solution, they aggregate into globular micellar aggregates, their size being determined by the length of the stretched polymer molecules. As determined by the combination of various scattering techniques for the dual brush copolymer, a rather compact structure is formed, which is dominated by the large hydrophobic poly(n-butyl acrylate) block. The aggregation number for the dual brush is about 10 times larger than for the "semi-brush" precursor copolymer, due to the packing requirements for the much bulkier hydrophobic core. On mica surfaces the triblock copolymers adsorb with worm-like backbones and stretched out side chains.
Amphiphilic dual brush block copolymers as "giant surfactants" and their aqueous self-assembly
(2010)
Amphiphilic dual brush diblock as well as symmetrical triblock polymers were synthesized by the overlay of the reversible addition-fragmentation chain transfer and the nitroxide mediated polymerization (NMP) techniques. While poly(ethylene glycol) brushes served as hydrophilic block, the hydrophobic block was made of polystyrene brushes. The resulting "giant surfactants" correspond structurally to the established amphiphilic diblock and triblock copolymer known as macrosurfactants. The aggregation behavior of the novel "giant surfactants" in aqueous solution was studied by dynamic light scattering, small-angle neutron scattering (SANS), and small-angle X-ray scattering (SAXS) over a large range in reciprocal space. Further, the self-assembled aggregates Were investigated by scanning force microscopy (SFM) after deposition on differently functionalized ultraflat solid substrates. Despite the high fraction of hydrophobic segments, the polymers form stable mesoscopic, spherical aggregates with hydrodynamic diameters in the range of 150-350 nm. Though prepared from well-defined individual polymers, the aggregates show several similarities to hard core latexes. They are stable enough to he deposited without much changes onto surfaces, where they cluster and show Spontaneous sorting according to their size within the clusters, with the larger aggregates being in the center.
Tuning the thickness of polymer brushes grafted from nonlinearly growing multilayer assemblies
(2009)
A new versatile method for tuning the thickness of surface-tethered polymer brushes is introduced. It is based on the combination of polyelectrolyte multilayer deposition and surface-initiated atom transfer radical polymerization. To control the thickness of the brushes, the nonlinear growth of certain polyelectrolyte multilayer systems is exploited. The method is demonstrated to work with different polyelectrolytes and different monomers. The relevance for applications is demonstrated by cell adhesion experiments oil grafted thermoresponsive polymer layers with varying thickness.
Smart bioactive surfaces
(2010)
The purpose of this highlight is to define the emerging field of bioactive surfaces. In recent years, various types of synthetic materials capable of "communicating'' with biological objects such as nucleic acids, proteins, polysaccharides, viruses, bacteria or living cells have been described in the literature. This novel area of research certainly goes beyond the traditional field of smart materials and includes different types of sophisticated interactions with biological entities, such as reversible adhesion, conformational control, biologically-triggered release and selective permeation. These novel materials may be 2D planar surfaces as well as colloidal objects or 3D scaffolds. Overall, they show great promise for numerous applications in biosciences and biotechnology. For instance, practical applications of bioactive surfaces in the fields of bioseparation, cell engineering, biochips and stem-cell differentiation are briefly discussed herein.
Stimuli-responsive macromolecules (i.e., pH-, thermo-, photo-, chemo-, and bioresponsive polymers) have gained exponential importance in materials science, nanotechnology, and biotechnology during the last two decades. This chapter describes the usefulness of this class of polymer for preparing smart surfaces (e.g., modified planar surfaces, particles surfaces, and surfaces of three-dimensional scaffolds). Some efficient pathways for connecting these macromolecules to inorganic, polymer, or biological substrates are described. In addition, some emerging bioapplications of smart polymer surfaces (e.g., antifouling surfaces, cell engineering, protein chromatography, tissue engineering, biochips, and bioassays) are critically discussed.
H-1 NMR relaxation is used to study the self-assembly of a double thermoresponsive diblock copolymer in dilute aqueous solution. Above the first transition temperature, at which aggregation into micellar structures is observed, the trimethylsilyl (TMS)-labeled end group attached to the shell-forming block shows a biphasic T-2 relaxation. The slow contribution reflects the TMS groups located at the periphery of the hydrophilic shell, in agreement with a star-like micelle. The fast T-2 contribution corresponds to the TMS groups, which fold back toward the hydrophobic core, reflecting a flower-like micelle. These results confirm the formation of block copolymer micelles of an intermediate nature (i.e., of partial flower-like and star-like character), in which a part of the TMS end groups folds back to the core due to hydrophobic interactions.
Random copolymers of 4-vinylbenzyl tri(oxyethylene) and tetra(oxyethylene) ethers, as well as alternating copolymers of 4-vinylbenzyl methoxytetra(oxyethylene) ether and a series of N-substituted maleimides, were synthesised by conventional free radical polymerisation, reversible addition fragmentation chain transfer (RAFT) and atom transfer radical polymerisation (ATRP). Their thermosensitive behaviour in aqueous solution was studied by turbidimetry and dynamic light scattering. Depending on the copolymer composition, a LCST type phase transition was observed in water. The transition temperature of the obtained random as well as alternating copolymers could be varied within a broad temperature window. In the case of the random copolymers, transition temperatures could be easily fine-tuned, as they showed a linear dependence on the copolymer composition, and were additionally modified by the nature of the polymer end-groups. Alternating copolymers were extremely versatile for implementing a broad range of variations of the phase transition temperatures. Further, while alternating copolymers derived from 4-vinylbenzyl methoxytetra(oxyethylene) ether and maleimides with small hydrophobic side chains underwent macroscopic phase separation when dissolved in water and heated above their cloud point, the incorporation of maleimides bearing larger hydrophobic substituents resulted in the formation of mesoglobules above the phase transition temperature, with hydrodynamic diameters of less than 100 nm.
The copolymerization of an excess of a functionalized styrene monomer, 4-vinylbenzyl methoxytetrakis(oxyethylene) ether, with various N-substituted maleimides yields tapered diblock copolymers in a one-step procedure, when applying reversible deactivation radical polymerization (RDRP) methods, such as ATRP and RAFT. The particular chemical structure of the diblock copolymers prepared results in reversible temperature-responsive two-step aggregation behavior in dilute aqueous solution. In this way, a double hydrophilic block copolymer is transformed step by step into an amphiphilic macrosurfactant, and finally into a double hydrophobic copolymer, as followed by turbidimetry and dynamic light scattering. Copolymers in which the maleimide repeat units bear short hydrophobic side chains are freely water-soluble at low temperature and form micellar aggregates above their cloud point. Further heating above the phase transition temperature of the second block results in secondary aggregation. Copolymers with maleimides that bear strongly hydrophobic substituents undergo two thermally induced aggregation steps upon heating, too, but show in addition intramolecular hydrophobic association in water already at low temperatures, similar to the behavior of polysoaps.
Temperature-induced self-assembly of triple-responsive triblock copolymers in aqueous solutions
(2011)
A series of triple-thermoresponsive triblock copolymers from poly(N-n-propylacrylamide) (PNPAM, A), poly(methoxydiethylene glycol acrylate) (PMDEGA, B), and poly(N-ethylacrylamide) (PNEAM, C) was synthesized by sequential reversible addition-fragmentation chain transfer polymerizations. Polymers of differing block sequences, ABC, BAC, and ACB, with increasing phase transition temperatures in the order A < B < C were prepared. Their aggregation behavior in dilute aqueous solution was investigated using dynamic light scattering, turbidimetry, and NMR spectroscopy. The self-organization of such polymers was found to dependent strongly on the block sequence. While polymers with a terminal low-LCST (lower critical solution temperature) block undergo aggregation above the first phase transition temperature at 20-25 degrees C, triblock copolymers with the low-LCST block in the middle show aggregation only above the second phase transition. The collapse of the middle block is not sufficient to induce aggregation but produces instead stable, unimolecular micelles with a collapsed middle block, as supported by NMR and fluorescence probe data. Continued heating of all copolymers led to two additional thermal transitions at 40-55 and 70-80 degrees C, which could be correlated to the phase transitions of the B and C blocks, respectively. All polymers show a high tendency for cluster formation, once aggregation is induced. The carrier abilities of the triple responsive triblock copolymers for hydrophobic agents were probed with the solvatochromic fluorescence dye Nile Red. With passing through the first thermal transition, the block copolymers are capable of solubilizing Nile Red. In the case of block copolymers with sequences ABC or ACB, which bear the low-LCST block at one terminus, notable amounts of dye are solubilized already at this stage. In contrast, the hydrophobic probe is much less efficiently incorporated by the BAC triblock copolymer, which forms unimolecular micelles. Only after the collapse of the B block, when reaching the second phase transition at about 45 degrees C, does aggregation occur and solubilization becomes efficient. In the case of ABC and ACB polymers, the hydrophobic probe seems to partition between the originally collapsed A chains and the additional hydrophobic chains formed after the collapse of the less hydrophobic B block.
A set of double thermoresponsive diblock copolymers poly(N-n-propylacrylamide)-block-poly(N-ethylacrylamide) (PNPAM-b-PNEAM) was synthesised by sequential reversible addition-fragmentation chain transfer (RAFT) polymerisations. Using a twofold trimethylsilyl (TMS)-labeled RAFT-agent, the relative size of the two blocks was varied. While soluble as unimers below 15 degrees C, all copolymers exhibited thermally induced two-step self-assembly in water, due to distinct lower critical solution temperature (LCST) phase transitions of PNPAM (around 20 degrees C) and PNEAM (around 70 degrees C). Their temperature-dependent self-organisation in dilute aqueous solution was studied by turbidimetry, dynamic light scattering, transmission electron microscopy, and (1)H NMR spectroscopy. The copolymers show distinct, two-step self-organisation behaviour with respect to transition temperatures, aggregate type and size, which can be correlated to the relative lengths of the low and high LCST blocks. For polymers having short blocks with low LCST, the first thermal transition induces the formation of individual micelles. Further heating above the second thermal transition results reversibly either in a shrink of the micelle size or in aggregation of the micelles, with hydrodynamic diameters below 250 nm. In contrast in the case of polymers having a long block with low LCST, the first thermal transition already leads to clusters of micelles, while the second thermal transition makes the clusters shrink. Noteworthy, the twofold TMS-labeled end groups report not only on the molar masses of the polymers, but can simultaneously serve as NMR-probes for the self-assembly process. The signal of the TMS-aryl end group displays a reversible temperature dependent, two-step splitting that is indicative of the self-organisation of the block copolymers.
The micelle aggregation numbers (N-agg) of several series of cationic oligomeric surfactants were determined by time-resolved fluorescence quenching (TRFQ) experiments, using advantageously 9,10-dimethylanthracene as fluorophore. The study comprises six dimeric ("gemini"), three trimeric, and two tetrameric surfactants, which are quaternary ammonium chlorides, with medium length spacer groups (C-3-C-6) separating the individual surfactant fragments. Two standard cationic surfactants served as references. The number of hydrophobic chains making up a micellar core is relatively low for the oligomeric surfactants, the spacer length playing an important role. For the dimers, the number decreases from 32 to 21 with increasing spacer length. These numbers decrease further with increasing degree of oligomerization down to values of about 15. As for many conventional ionic surfactants, the micelles of all oligomers studied grow only slightly with the concentration, and they remain in the regime of small micelles up to concentrations of at least 3 wt %.
Swelling and switching kinetics of gold coated end-capped poly(N-isopropylacrylamide) thin films
(2010)
Thin thermoresponsive hydrogel films of poly(N-isopropylacrylamide) end-capped with n-butyltrithiocarbonate(nbc- PNIPAM) oil si I icon supports with a gold layer on top, causing an asymmetric confinement, are investigated. For two different gold layer thicknesses (nominally 0.4 and 5 rim), the swelling and switching kinetics are probed with in situ neutron reflectivity. With a temperature jump from 23 to 40 degrees C the film is switched from a swollen into a collapsed state. For the thin gold layer this switching is faster as compared to the thick gold layer. The switching is a two-step process of water release and a subsequent structural relaxation. fit swelling and deswelling cycles, aging of the films is probed. After five cycles, the film exhibits enhanced water storage capacity. Grazing-incidence small-angle X-ray scattering (GISAXS) shows that these gold coated nbc-PNIPAM films do not age with respect to the inner structure but slightly roughen at the gold surface. As revealed by atomic force microscopy, the morphology of the gold layer is changed by the water uptake and release.
The water swelling and subsequent solvent exchange including co-nonsolvency behavior of thin films of a doubly thermo-responsive diblock copolymer (DBC) are studied viaspectral reflectance, time-of-flight neutron reflectometry, and Fourier transform infrared spectroscopy.
The DBC consists of a thermo-responsive zwitterionic (poly(4-((3-methacrylamidopropyl) dimethylammonio) butane-1-sulfonate)) (PSBP) block, featuring an upper critical solution temperature transition in aqueous media but being insoluble in acetone, and a nonionic poly(N-isopropylmethacrylamide) (PNIPMAM) block, featuring a lower critical solution temperature transition in water, while being soluble in acetone.
Homogeneous DBC films of 50-100 nm thickness are first swollen in saturated water vapor (H2OorD2O), before they are subjected to a contraction process by exposure to mixed saturated water/acetone vapor (H2OorD2O/acetone-d6 = 9:1 v/v).
The affinity of the DBC film toward H2O is stronger than for D2O, as inferred from the higher film thickness in the swollen state and the higher absorbed water content, thus revealing a pronounced isotope sensitivity.
During the co-solvent-induced switching by mixed water/acetone vapor, a two-step film contraction is observed, which is attributed to the delayed expulsion of water molecules and uptake of acetone molecules.
The swelling kinetics are compared for both mixed vapors (H2O/acetone-d6 and D2O/acetone-d6) and with those of the related homopolymer films.
Moreover, the concomitant variations of the local environment around the hydrophilic groups located in the PSBP and PNIPMAM blocks are followed.
The first contraction step turns out to be dominated by the behavior of the PSBP block, where as the second one is dominated by the PNIPMAM block.
The unusual swelling and contraction behavior of the latter block is attributed to its co-nonsolvency behavior.
Furthermore, we observe cooperative hydration effects in the DBC films, that is, both polymer blocks influence each other's solvation behavior.
A simple synthetic route to a new poly(diallylammonium) salt functionalized by a styrene group is presented. This reactive polymer was employed for polyelectrolyte multilayer films using electrostatical layer-by-layer self- assembly, together with an inorganic polyanion, namely an exfoliated hectorite clay. To enhance their stability, the final hybrid multilayers were cross-linked by exposure to UV light, leading only to a minor shrinkage. Alternatively, the reactive polycation was cross-linked after each adsorption step. X-ray reflectometry revealed that the two types of films dispose of an internal order with a short length scale, that seems insensitive to the photo-cross-linking. Cross- linking after each adsorption step, however, results in more regular film growth, and reduces the films? roughness and the amount of polyanion deposited. Under these conditions, the films seem to grow by deposition of submonolayers with a combined vertical and lateral expansion, resulting in the self-healing of previously deposited, incomplete layers.
All-in-One "Schizophrenic" self-assembly of orthogonally tuned thermoresponsive diblock copolymers
(2019)
Smart, fully orthogonal switching was realized in a highly biocompatible diblock copolymer system with variable trigger-induced aqueous self-assembly. The polymers are composed of nonionic and zwitterionic blocks featuring lower and upper critical solution temperatures (LCSTs and UCSTs). In the system investigated, diblock copolymers from poly(N-isopropyl methacrylamide) (PNIPMAM) and a poly(sulfobetaine methacrylamide), systematic variation of the molar mass of the latter block allowed for shifting the UCST of the latter above the LCST of the PNIPMAM block in a salt-free condition. Thus, successive thermal switching results in "schizophrenic" micellization, in which the roles of the hydrophobic core block and the hydrophilic shell block are interchanged depending on the temperature. Furthermore, by virtue of the strong electrolyte-sensitivity of the zwitterionic polysulfobetaine block, we succeeded to shift its UCST below the LCST of the PNIPMAM block by adding small amounts of an electrolyte, thus inverting the pathway of switching. This superimposed orthogonal switching by electrolyte addition enabled us to control the switching scenarios between the two types of micelles (i) via an insoluble state, if the LCST-type cloud point is below the UCST-type cloud point, which is the case at low salt concentrations or (ii) via a molecularly dissolved state, if the LCST-type cloud point is above the UCST-type cloud point, which is the case at high salt concentrations. Systematic variation of the block lengths allowed for verifying the anticipated behavior and identifying the molecular architecture needed. The versatile and tunable self-assembly offers manifold opportunities, for example, for smart emulsifiers or for sophisticated carrier systems.
Thermal properties of block copolymer, poly(N-isopropyl acrylamide)-block-poly(3-[N-(3-methacrylamido-propyl)- N,N-dimethyl]-ammonio propane sulfonate), PNIPA-b-PSPP have been studied in pure and saline (NaCl) aqueous solutions by dynamic laser light scattering (DLS). The copolymer [Mw(PNIPA) 10800 g/mol and Mw(PSPP) 9700 g/mol] exhibits both an upper (UCST 9 oC) and lower (LCST 32 oC) critical solution temperatures in pure water. The addition of NaCl enhances the solubility of the zwitterionic polymer, PSPP, leading to the disappearance of the UCST. On the other hand, the solubility of PNIPA in water decreases as NaCl is added. At 20 oC the copolymer shows a bimodal size distribution through the NaCl concentration range of 0-0.93 M above a certain limiting polymer concentration. The slow and fast components of the diffusion coefficients of the polymer have been calculated. A gradual addition of salt turns the mutual interactions from zwitterionic attractions between PSPP blocks to hydrophobic attractions between PNIPA blocks. The formation of the aggregates and the aggregate sizes at T < UCST and T > LCST are influenced by polymer and salt concentrations. Below UCST the aggregates in saline polymer solutions are larger than those in pure polymer solutions. Above LCST the aggregate size is determined by the salt concentration.
Recently, we introduced a thermoresponsive copolymer that consists of oligo(ethylene glycol) methacrylate (OEGMA) and 2-(2- methoxyethoxy) ethyl methacrylate (MEO(2)MA). The polymer exhibited an LCST at 35 degrees C in PBS buffer and was anchored onto gold substrates using disulfide polymerisation initiators. It allows the noninvasive detachment of adherent cells from their substrate. As the mechanisms that determine the interaction of cells with such polymers are not well understood, we employed Total Internal Reflection Fluorescence (TIRF) microscopy in order to monitor the detachment process of cells of two different types. We identified contact area and average cell-substrate distance as crucial parameters for the evaluation of the detachment process. The sensitivity of TIRF microscopy allowed us to correlate the specific adhesion pattern of MCF-7 breast cancer cells with the morphology of cell deposits that may serve as fingerprints for a nondestructive characterisation of live cells.
Fluorocarbon associative polymers of the polysoap type were studied using two fluorescent probes, 1- octanoylpyrene (OcPyH) and 1-perfluorooctanoylpyrene (OcPyF). In aqueous solution the polymers formed hydrophobic domains composed of hydrocarbon, fluorocarbon or both types of polymeric side chains, which could solubilize the probes. This resulted in the appearance of new fluorescence emission bands and changes in the fluorescence polarization of the probes. The differences in the solubilization properties of the polymers are discussed. (c) 2005 Elsevier B.V. All rights reserved
Ionic liquids based on imidazolium, pyridinium, and alkylammonium salts were investigated as solvents in free radical polymerization of the model monomer n-butyl methacrylate. The properties of the ionic liquids were systematically varied by changing the length of the alkyl substituents on the cations, and by employing different anions such as tetrafluoroborate, hexafluorophosphate, tosylate, triflate, alkyl sulfates and dimethyl phosphate. Results were compared to analogous polymerizations in toluene and in bulk. The solvents have no detectable influence on polymer tacticity. However, the molar masses obtained and the degree of polymerization, respectively, are very sensitive to the choice of the solvent. The degrees of polymerization are significantly higher when polymerizations were carried out in ionic liquids compared to polymerization in toluene, and can even exceed the values obtained by bulk polymerization. Imidazolium salts unsubstituted at C-2 result in an increase in the degree of polymerization of the poly(butyl methacrylate) with increasing viscosity of these ionic liquids. Methyl substitution at C-2 of the imidazolium ion results in an increase in the viscosity of the ionic liquid and in a viscosity independent degree of polymerization of the poly(butyl methacrylate). Ionic liquids based on imidazolium salts seem preferable over pyridinium and alkylammonium salts because of the higher degree of polymerization of the poly(butyl methacrylate)s obtained in the imidazolium salts. The glass transition temperatures and thermal stabilities are higher for poly(butyl methacrylate)s synthesized in the ionic liquids compared to the polymer made in toluene
Free radical homo- and copolymerization of the highly polar 3-(N-[2-methacryloyloxyethyl]-N,N-dimethylammonio) propane sulfonate with the nonpolar n-butylmethacrylate was investigated in the ionic liquids 1-butyl-3-methyl imidazolium tetrafluoroborate and 1-butyl-3-methylimidazolium hexafluoro phosphate, and compared to analogous polymerizations in standard solvents. Higher molar masses are obtained for the zwitterionic homopolymer when the polymerization is carried out in an ionic liquid compared to the classical reaction in water. Although homopolymerization of the sulfobetain monomer as well as of n-butylmethacrylate results in phase separation during the polymerization process, copolymerization of a stoichiometric ratio of the two monomers in the ionic liquids produced transparent gels indicating that no macrophase separation occurs. The use of ionic liquids as reaction medium improved the copolymerization behavior of the two methacrylates significantly. Whereas only minor amounts of n-butyl methacrylate were incorporated in the copolymer when synthesized in acetonitrile, the content of the non-polar monomer units in the zwitterionic copolymer approached increasingly its content in the polymerization mixture when ionic liquids were employed as solvents
The spin probes TEMPO, TEMPOL, and CAT-1 were used to investigate microviscosity and micropolarity of imidazolium based ionic liquids bearing either tetrafluoroborate or hexafluorophosphate as anions and a variation of the substitution at the imidazolium ion. The average rotational correlation times (r) obtained by complete simulation of the X-band ESR spectra of TEMPO, TEMPOL, and CAT-1 increase with increasing viscosity of the ionic liquid although no Stokes Einstein behavior is observed. This is caused by microviscosity effects of the ionic liquids shown by application of the Gierer-Wirtz theory. Interestingly, the jump of the probe molecule into the free volume of the ionic liquids is a nonactivated process. The hyperfine coupling constants (A(iso) (N-14)) of TEMPO and TEMPOL dissolved in the ionic liquids do not depend on the structure of the ionic liquids. The A(iso) (N-14) values show a micropolarity of the ionic liquids that is comparable with methylenchloride in case of TEMPO and with dimethylsulfoxide in case of TEMPOL. Micropolarity monitored by CAT-1 strongly depends on structural variation of the ionic liquid. CAT-1 dissolved in imidazolium salts substituted with shorter alkyl chains at the nitrogen atom exhibits a micropolarity comparable with dimethylsulfoxide. A significant lower micropolarity is found for imidazolium. salts bearing a longer alkyl substituent at the nitrogen atom or a methyl substituent at C-2. Copyright (c) 2006 John Wiley & Sons, Ltd
The spin probes 2,2,6,6-tetramethylpiperidine-1-oxyl (TEMPO), 4-hydroxy-2,2,6,6-tetramethylpiperidine-1-oxyl (TEMPOL), and 2,2,6,6-tetramethyl-4-trimethylammoniumpiperidine-1-oxyllodide (CAT-1) are examined in a number of ionic liquids based on substituted imidazolium cations and tetrafluoroborate and hexafluorophosphate anions, respectively. The reorientation correlation times tau(R) of the spin probes in these systems have been determined by complete spectra simulation and, for rapid reortientation, by analysis of the intensities of the hyperfine lines of the electron spin resonance (ESR) spectra. A comparison of the results with those from the model system glycerol/water and selected organic solvents is made. Additions of diamagnetic and paramagnetic ions allow the conclusion that salt effects and spin exchange are present, and that both are superimposed by motional effects. Specific interactions in the ionic liquids, as well as between the spin-probe molecules and the constituents of the ionic liquids are reflected in the spectra of the spin probes, depending on their molecular structure
Linear amphiphilic diblock and ternary triblock copolymers were synthesized by the RAFT method in three Successive Steps, using oligo(ethylene oxide) monomethyl ether acrylate, butyl or 2-ethylhexyl acrylate, and 1H, 1H, 2H, 2H-perfluorodecyl acrylate. The diblock and the triblock copolymers, which consist of a hydrophilic, a lipophilic, and a fluorophilic block, self-assemble in water into spherical micellar aggregates. Imaging by cryogenic transmission electron microscopy (cryo-TEM) revealed that the cores of the micellar aggregates made from these "triphilic" copolymers undergo local phase separation to form various ultrastructures, which depend sensitivity on the given block sequence. While the sequence hydrophilic-lipophilic-fluorophilic resulted in multicompartment cores with core-shell-corona morphology, the sequence lipophilic-hydrophilic-fluorophilic provided new "patched double micelle" and larger "soccer ball" structures.
Examining the UV-vis absorption of RAFT chain transfer agents and their use for polymer analysis
(2011)
The absorption characteristics of a large set of thiocarbonyl based chain transfer agents (CTAs) were studied by UV-vis spectroscopy in order to identify appropriate conditions for exploiting their absorbance bands in end-group analysis of polymers prepared by reversible addition-fragmentation chain transfer (RAFT) polymerisation. Substitution pattern and solvent polarity were found to affect notably the wavelengths and intensities of the pi-pi*- and n-pi*-transition of the thiocarbonyl bond of dithioester and trithiocarbonate RAFT agents. Therefore, it is advisable to refer in end group analysis to the spectral parameters of low molar mass analogues of the active polymer chain ends, rather than to rely on the specific RAFT agent engaged in the polymerisation. When using appropriate conditions, the quantification of the thiocarbonyl end-groups via the pi-pi* band of the thiocarbonyl moiety around 300-310 nm allows a facile, sensitive and surprisingly precise estimation of the number average molar mass of the polymers produced, without the need of particular end group labels. Moreover, when additional methods for absolute molar mass determination can be applied, the quantification of the thiocarbonyl end-groups by UV-spectroscopy provides a good estimate of the degree of active end group for a given polymer sample.
Linear amphiphilic diblock and ternary triblock copolymers were synthesized by the RAFT method in two successive steps using a poly(ethylene oxide) (PEO) macrochain transfer agent, butyl or 2-ethylhexyl acrylate, and 1H, 1H, 2H, 2H-perfluorodecyl acrylate. The diblock and the triblock copolymers, which consist of a hydrophilic, a lipophilic, and a short fluorophilic block, self-assemble in water into spherical micellar aggregates. Imaging by cryogenic transmission electron microscopy (cryo-TEM) revealed that the micellar cores of the aggregates made from these "triphilic" copolymers can undergo local phase separation to form a unique ultrastructure. In these multicompartment micelles, it appears that extended nonspherical domains, presumably made of nanocrystallites of the fluorocarbon block, are embedded in the hydrocarbon matrix forming the spherical micellar core. This novel internal structure of a micellar core is attributed to the mutual incompatibility of the fluorocarbon and hydrocarbon side chains in combination with the tendency of the used fluorocarbon acrylate monomer to undergo side-chain crystallization.
Combining high hydrophilicity with charge neutrality, polyzwitterions are intensely explored for their high biocompatibility and low-fouling properties. Recent reports indicated that in addition to charge neutrality, the zwitterion's segmental dipole orientation is an important factor for interacting with the environment. Accordingly, a series of polysulfobetaines with a novel architecture was designed, in which the cationic and anionic groups of the zwitterionic moiety are placed at equal distances from the backbone. They were investigated by in vitro biofouling assays, covering proteins of different charges and model marine organisms. All polyzwitterion coatings reduced the fouling effectively compared to model polymer surfaces of poly(butyl methacrylate), with a nearly equally good performance as the reference polybetaine poly(3-(N-(2-(methacryloyloxy)ethyl)-N,N-dimethylammonio)propanesulfonate). The specific fouling resistance depended on the detailed chemical structure of the polyzwitterions. Still, while clearly affecting the performance, the precise dipole orientation of the sulfobetaine group in the polyzwitterions seems overall to be only of secondary importance for their antifouling behavior.
The impact of the orientation of zwitterionic groups, with respect to the polymer backbone, on the antifouling performance of thin hydrogel films made of polyzwitterions is explored. In an extension of the recent discussion about differences in the behavior of polymeric phosphatidylcholines and choline phosphates, a quasi-isomeric set of three poly(sulfobetaine methacrylate)s is designed for this purpose. The design is based on the established monomer 3-[N-2-(methacryloyloxy)ethyl-N,N-dimethyl]ammonio-propane-1-sulfonate and two novel sulfobetaine methacrylates, in which the positions of the cationic and the ionic groups relative to the polymerizable group, and thus also to the polymer backbone, are altered. The effect of the varied segmental dipole orientation on their water solubility, wetting behavior by water, and fouling resistance is compared. As model systems, the adsorption of the model proteins bovine serum albumin (BSA), fibrinogen, and lysozyme onto films of the various polyzwitterion surfaces is studied, as well as the settlement of a diatom (Navicula perminuta) and barnacle cyprids (Balanus improvisus) as representatives of typical marine fouling communities. The results demonstrate the important role of the zwitterionic group's orientation on the polymer behavior and fouling resistance.
Hydrophobically substituted diallylamines bearing a hexyl, dodecyl, or octadecyl chain were synthesized and homopolymerized as hydrochlorides. Copolymerixation of the diallylamines with maleic acid produces alternating copolymers. The copolymers behave as amphiphilic polyampholytes and dissolve best in the acidic or in the basic form. Only the colpolymer with the hexyl chain could be dissolved in aqueous solvents and shows hydrophobic associaiton. The copolymers with the longer alkyl chains require polar protic organic solvents. All polymers are amorphous, but show a superstructure in bulk due to their amphiphilicity
An unconventional but easily accessible precursor route involving the thermal treatment of hybrid precursors containing an ampholytic polymer matrix is developed to prepare multimetallic oxides of catalytic interest such as transition metal molybdates. A copolymer of diallyldimethylammonium chloride and a functionalized maleamic acid bearing an amine group suited for cation complexation was designed, synthesized and used as a matrix to stabilize inorganic species generated in solution from Ni(NO3)(2)center dot 6H(2)O, Co(NO3)(2)center dot 6H(2)O and/or Mn(NO3)(2)center dot 4H(2)O together with (NH4)(6)Mo(7)O(24)center dot 4H(2)O. UV-vis-NIR as well as C-13-NMR studies suggest that the interactions between the cations and the polymer in solution are mainly electrostatic. Only minor complexation interactions take place under certain conditions. Homogeneous hybrid blends were prepared from these solutions. The presence of a complexing amine group in addition to the charged betaine moieties in the polymer permits stabilization of more than stoichiometric amounts of the metal species in the blends. XRD measurements suggest that the homogeneity in the solid state can be kept up to about 1.5 mol of each metal that is incorporated ( anionic as well as cationic) per mol of repeat units of the copolymer. The blends were calcined under air at 600 degrees C to produce the simple as well as mixed nickel, cobalt and manganese molybdates. Characterization of the final phases by XRD and Raman spectroscopy indicates that the alpha- as well as the beta-molybdate phases can be prepared, and that the mixed structures are solid solutions of the simple NiMoO4, MnMoO4 and CoMoO4. If the precursors engaged are homogeneous, the pH of the precursor solution, the amount of metal that is incorporated in the matrix, and the nature of the polymer matrix seem to exert only a minor influence on the nature of the final phase, which demonstrates the versatility and facile applicability of the method
Homopolymers were prepared from diallylammonium monomers bearing 4-methylcoumarin and 4-cyanobiphenyl as fluorescent and mesogenic side groups, as well as their copolymers with diallyldimethylammonium chloride (DADMAC). Organic-inorganic hybrid films were electrostatically self-assembled via the layer-by-layer technique on silicon wafers and quartz plates from the chromophore-bearing polymers and an exfoliated synthetic hectorite. Photophysical studies performed in solution as well as in the self-assembled films demonstrated only a weak tendency for aggregation of the chromophores in the macromolecules. Moreover, assemblies made from the polymers carrying the cyanobiphenyl mesogen were found to exhibit a pronounced internal order
A new precursor route for the preparation of bulk oxides and thin films of bismuth vanadates is proposed. The method involves the thermal treatment under air and mild conditions of hybrid organic-inorganic precursors, made from a zwitterionic salt-free polymer matrix and selected inorganic species. Monoclinic BiVO4 was obtained in the form of bulk oxide by calcination of the powdered homogeneous hybrid materials at 600 degrees C, from precursors containing Bi and V in stoichiometric amounts. In the same way, thermodiffractometry studies performed on a hybrid material exhibiting a Bi/ V molar ratio of 2 revealed that the ionic conductor gamma-Bi4V2O11 phase can be stabilized under very soft thermal conditions (300 degrees C). Additionally, thin films of yellow monoclinic BiVO4 were for the first time fabricated, by thermal treatment of the same hybrid polymeric precursors deposited on quartz substrates by spin coating, using a layer- by-layer technique. The presence of the target phase at the surface of the plates was confirmed by X-ray diffraction as well as UV-vis measurements
Effect of magnesium salts with chaotropic anions on the swelling behavior of PNIPMAM thin films
(2023)
Poly(N-isopropylmethacrylamide) (PNIPMAM) is a stimuli responsive polymer, which in thin film geometry exhibits a volume-phase transition upon temperature increase in water vapor. The swelling behavior of PNIPMAM thin films containing magnesium salts in water vapor is investigated in view of their potential application as nanodevices. Both the extent and the kinetics of the swelling ratio as well as the water content are probed with in situ time-of-flight neutron reflectometry. Additionally, in situ Fourier-transform infrared (FTIR) spectroscopy provides information about the local solvation of the specific functional groups, while two-dimensional FTIR correlation analysis further elucidates the temporal sequence of solvation events. The addition of Mg(ClO4)2 or Mg(NO3)2 enhances the sensitivity of the polymer and therefore the responsiveness of switches and sensors based on PNIPMAM thin films. It is found that Mg(NO3)2 leads to a higher relative water uptake and therefore achieves the highest thickness gain in the swollen state.
Cationic and perfluorinated polymeric pseudostationary phases for electrokinetic chromatography
(2006)
Separation selectivity in electrokinetic chromatography (EKC) is directly affected by the chemistry and solvent characteristics of the pseudostationary phase (PSP). The chemical selectivity of micellar PSPs has been previously demonstrated to vary significantly between anionic and cationic surfactants as well as between hydrocarbon and fluorocarbon surfactants. Polymeric PSPs have also been demonstrated to provide unique selectivity. In the current study, four cationic polymeric pseudo-stationary phases, two of which have perfluorinated pendant groups, are introduced and characterized as PSPs in EKC. Their performance and selectivity is compared to conventional micellar PSPs with similar structure. The solvation characteristics and selectivity of the four polymers most closely resemble those observed for cationic micelles. The polymers are all more cohesive and more polar than their hydrocarbon micellar counterparts. The fluorocarbon PSPs did show preferential interaction with fluorocarbon solutes, were somewhat more cohesive, and were stronger hydrogen bond donors. However, the presence of fluorocarbon moieties did not have as dramatic an effect on selectivity as was observed and published previously for fluorocarbon micelles. This may result from the selectivity being dominated by the presence of the cationic head groups or from the fluorocarbon character of the pendant groups being moderated by the presence of hydrocarbon functionality on the polymer back-bones.
The aggregation behavior of catanionics formed by the mixture of cationic geminis derived from dodecyltrimethylammonium chloride (DTAC) and anionic sodium dodecylsulfate (SDS) was studied by means of phase studies and comprehensive small-angle neutron scattering (SANS) experiments at 25 degrees C and 50 mM overall concentration. The results are compared to those for the previously studied SDS + DTAC system. Various gemini spacers of different natures and geometries were used, but all of them had similar lengths: an ethoxy bridge, a double bond, and an aromatic ring binding the two DTACs in three different substitutions (ortho, meta, and para). SANS and SAXS data analysis indicates that the spacer has no large effect on the spheroidal micelles of pure surfactants formed at low concentration in water; however, specific effects appear with the addition of electrolytes. Microstructures formed in the catanionic mixtures are rather strongly dependent on the nature of the spacer. The most important finding is that for the hydrophilic, flexible ethoxy bridge, monodisperse vesicles with a fixed anionic/cationic charge ratio (depending only on the surfactant in excess) are formed. Furthermore, the composition of these vesicles shows that strongly charged aggregates are formed. This study therefore provides new opportunities for developing tailor-made gemini surfactants that allow for the fine tuning of catanionic structures.
Polyelectrolytes in dilute solutions (0.01 mmol/L) adsorb in a two-dimensional lamellar phase to oppositely charged lipid monolayers at the air/water interface. The interchain separation is monitored by Grazing Incidence X-ray Diffraction. On monolayer compression, the interchain separation decreases to a factor of two. To investigate the influence of the electrostatic interaction, either the line charge density of the polymer is reduced (a statistic copolymer with 90% and 50% charged monomers) or mixtures between charged and uncharged lipids are used (dipalmitoylphosphatidylcholine (DPPC)/dioctadecyldimethylammonium bromide (DODAB)) On decrease of the surface charge density, the interchain separation increases, while on decrease of the linear charge density, the interchain separation decreases. The ratio between charged monomers and charged lipid molecules is fairly constant; it decreases up to 30% when the lipids are in the fluid phase. With decreasing surface charge or linear charge density, the correlation length of the lamellar order decreases.
Successful layer-by-layer (LbL) growth of short chain (similar to 30 repeat units per chain) poly(sodium styrene sulfonate) (PSS)-poly(diallyl dimethylammonium chloride) (PDADMAC) multilayers is presented for the first time and compared with the growth of equivalent long chain polyelectrolyte multilayers (PEMs). A detailed study performed by quartz crystal microbalance with dissipation (QCM-D) is carried out and three main processes are identified: (i) initial mass uptake, (ii) adsorption desorption during layer equilibration and (iii) desorption during rinsing. In contrast to the high stability and strong layer increment of high molecular weight (HMW) PEMs, layer degradation characterizes low molecular weight (LMW) multilayers. In particular, two different instability phenomena are observed: a constant decrease of sensed mass during equilibration after PDADMAC adsorption, and a strong mass toss by salt-free rinsing after PSS adsorption. Yet, an increase of salt concentration leads to much stronger layer growth. First, when the rinsing medium is changed from pure water to 0.1 M NaCl, the mass loss during rinsing is reduced, irrespective of molecular weight. Second, an increase in salt concentration in the LMW PE solutions causes a larger increment during the initial adsorption step, with no effect on the rinsing. Finally, the mechanical properties of the two systems are extracted from the measured frequency and dissipation shifts, as they offer a deeper insight into the multilayer structures depending on chain length and outermost layer. The paper enriches the field of PE assembly by presenting the use of very short PE chains to form multilayers and elucidates the role of preparation conditions to overcome the limitation of layer stability.
A series of symmetrical, thermo-responsive triblock copolymers was prepared by reversible addition fragmentation chain transfer (RAFT) polymerization, and studied in aqueous solution with respect to their ability to form hydrogels. Triblock copolymers were composed of two identical, permanently hydrophobic outer blocks, made of low molar mass polystyrene, and of a hydrophilic inner block of variable length, consisting of poly(methoxy diethylene glycol acrylate) PMDEGA. The polymers exhibited a LCST-type phase transition in the range of 20-40 degrees C, which markedly depended on molar mass and concentration. Accordingly, the triblock copolymers behaved as amphiphiles at low temperatures, but became water-insoluble at high temperatures. The temperature dependent self-assembly of the amphiphilic block copolymers in aqueous solution was studied by turbidimetry and rheology at concentrations up to 30 wt %, to elucidate the impact of the inner thermoresponsive block on the gel properties. Additionally, small-angle X-ray scattering (SAXS) was performed to access the structural changes in the gel with temperature. For all polymers a gel phase was obtained at low temperatures, which underwent a gel-sol transition at intermediate temperatures, well below the cloud point where phase separation occurred. With increasing length of the PMDEGA inner block, the gel-sol transition shifts to markedly lower concentrations, as well as to higher transition temperatures. For the longest PMDEGA block studied (DPn about 450), gels had already formed at 3.5 wt % at low temperatures. The gel-sol transition of the hydrogels and the LCST-type phase transition of the hydrophilic inner block were found to be independent of each other.
The easily accessible, but virtually overlooked monomer methoxy diethylene glycol acrylate was polymerized by the RAFT method using monofunctional, difunctional, and trifunctional trithiocarbonates to afford thermoresponsive polymers exhibiting lower critical solution temperature-type phase transitions in aqueous solution. The use of the appropriate RAFT agent allowed for the preparation and systematic variation of polymers with defined molar mass, end-groups, and architecture, including amphiphilic diblock, symmetrical triblock, and triarm star-block copolymers, containing polystyrene as permanently hydrophobic constituent. The cloud points (CPs) of the various polymers proved to be sensitive to all varied parameters, namely molar mass, nature, and number of the end-groups, and the architecture, up to relatively high molar masses. Thus, CPs of the polymers can be adjusted within the physiological interesting range of 2040 degrees C. Remarkably, CPs increased with the molar mass, even when hydrophilic end groups were attached to the polymers.