Refine
Year of publication
- 2008 (33) (remove)
Document Type
- Doctoral Thesis (33) (remove)
Is part of the Bibliography
- yes (33)
Keywords
- Chitooligosaccharide (3)
- Chitooligosaccharides (3)
- Glycosylation (2)
- Metallnitride (2)
- metal nitrides (2)
- nucleation (2)
- ABC triblock copolymer (1)
- Additive (1)
- Adsorbatschwingungen (1)
- Amin (1)
Institute
- Institut für Chemie (33) (remove)
The three major biopolymers, proteins, nucleic acids and glycoconjugates are mainly responsible for the information transfer, which is a fundamental process of life. The biological importance of proteins and nucleic acids are well explored and oligosaccharides in the form of glycoconjugates have gained importance recently. The β-(1→4) linked N-acetylglucosamine (GlcNAc) moiety is a frequently occurring structural unit in various naturally and biologically important oligosaccharides and related conjugates. Chitin which is the most abundant polymer of GlcNAc is widely distributed in nature whereas the related polysaccharide chitosan (polymer of GlcN and GlcNAc) occurs in certain fungi. Chitooligosaccharides of mixed acetylation patterns are of interest for the determination of the substrate specificities and mechanism of chitinases. In this report, we describe the chemical synthesis of three chitotetraoses namely GlcNAc-GlcN-GlcNAc-GlcN, GlcN-GlcNAc-GlcNAc-GlcN and GlcN-GlcN-GlcNAc-GlcNAc. Benzyloxycarbonyl (Z) and p-nitrobenzyloxycarbonyl (PNZ) were used for the amino functionality due to their ability to form the β-linkage during the glycosylation reactions through neighboring group participation and the trichloroacetimidate approach was utilized for the donor. Monomeric, dimeric acceptors and donors have been prepared by utilizing the Z and PNZ groups and coupling between the appropriate donor and acceptors in the presence of Lewis acid yielded the protected tetrasaccharides. Finally cleavage of PNZ followed by reacetylation and the deblocking of other protecting groups afforded the N,N’-diacetyl chitotetraoses in good yield. Successful syntheses for the protected diacetyl chitotetraoses by solid phase synthesis have also been described.
For the first time stabilizer-free vinylidene fluoride (VDF) polymerizations were carried out in homogeneous phase with supercritical CO₂. Polymerizations were carried out at 140°C, 1500 bar and were initiated with di-tert-butyl peroxide (DTBP). In-line FT-NIR (Fourier Transform- Near Infrared) spectroscopy showed that complete monomer conversion may be obtained. Molecular weights were determined via size-exclusion chromatography (SEC) and polymer end group analysis by 1H-NMR spectroscopy. The number average molecular weights were below 104 g∙mol−1 and polydispersities ranged from 3.1 to 5.7 depending on DTBP and VDF concentration. To allow for isothermal reactions high CO₂ contents ranging from 61 to 83 wt.% were used. The high-temperature, high-pressure conditions were required for homogeneous phase polymerization. These conditions did not alter the amount of defects in VDF chaining. Scanning electron microscopy (SEM) indicated that regular stack-type particles were obtained upon expansion of the homogeneous polymerization mixture. To reduce the required amount of initiator, further VDF polymerizations using chain transfer agents (CTAs) to control molecular weights were carried out in homogeneous phase with supercritical carbon dioxide (scCO₂) at 120 °C and 1500 bar. Using perfluorinated hexyl iodide as CTA, polymers of low polydispersity ranging from 1.5 to 1.2 at the highest iodide concentration of 0.25 mol·L-1 were obtained. Electrospray ionization- mass spectroscopy (ESI-MS) indicates the absence of initiator derived end groups, supporting livingness of the system. The “livingness” is based on the labile C-I bond. However, due to the weakness of the C-I bond perfluorinated hexyl iodide also contributes to initiation. To allow for kinetic analyses of VDF polymerizations the CTA should not contribute to initiation. Therefore, additional CTAs were applied: BrCCl3, C6F13Br and C6F13H. It was found that C6F13H does not contribute to initiation. At 120°C and 1500 bar kp/kt0.5~ 0.64 (L·mol−1·s−1)0.5 was derived. The chain transfer constant (CT) at 120°C has been determined to be 8·10−1, 9·10−2 and 2·10−4 for C6F13I, C6F13Br and C6F13H, respectively. These CT values are associated with the bond energy of the C-X bond. Moreover, the labile C-I bond allows for functionalization of the polymer to triazole end groups applying click reactions. After substitution of the iodide end group by an azide group 1,3 dipolar cycloadditions with alkynes yield polymers with 1,2,3 triazole end groups. Using symmetrical alkynes the reactions may be carried out in the absence of any catalyst. This end-functionalized poly (vinylidene fluoride) (PVDF) has higher thermal stability as compared to the normal PVDF. PVDF samples from homogeneous phase polymerizations in supercritical CO₂ and subsequent expansion to ambient conditions were analyzed with respect to polymer end groups, crystallinity, type of polymorphs and morphology. Upon expansion the polymer was obtained as white powder. Scanning electron microscopy (SEM) showed that DTBP derived polymer end groups led to stack-type particles whereas sponge- or rose-type particles were obtained in case of CTA fragments as end groups. Fourier-Transform Infrared spectroscopy and wide angle X-ray diffraction indicated that the type of polymorph, α or β crystal phase was significantly affected by the type of end group. The content of β-phase material, which is responsible for piezoelectricity of PVDF, is the highest for polymer with DTBP-derived end groups. In addition, the crystallinity of the material, as determined via differential scanning calorimetry is affected by the end groups and polymer molecular weights. For example, crystallinity ranges from around 26 % for DTBP-derived end groups to a maximum of 62 % for end groups originating from perfluorinated hexyl iodide for polymers with Mn ~2200 g·mol–1. Expansion of the homogeneous polymerization mixture results in particle formation by a non-optimized RESS (Rapid Expansion from Supercritical Solution) process. Thus, it was tested how polymer end groups affect the particles size distribution obtained from RESS process under controlled conditions (T = 50°C and P = 200 bar). In all RESS experiments, small primary PVDF with diameters less than 100 nm without the use of liquid solvents, surfactants, or other additives were produced. A strong correlation between particle size and particle size distribution with polymer end groups and molecular weight of the original material was observed. The smallest particles were found for RESS of PVDF with Mn~ 4000 g·mol–1 and PFHI (C6F13I) - derived end groups.
Chitooligosaccharides are composed of linear β-(1→4)-linked 2-acetamido-2-deoxy-β-D-glucopyranose (GlcNAc) and/or 2-amino-2-deoxy-β-D-glucopyranose (GlcN). They are of interest due to their remarkable biological properties including antibacterial, antitumor, antifungal and elicitor activities. They can be obtained from the aminoglucan chitosan by chemical or enzymatic degradation which obviously affords rather heterogenous mixtures. On the other hand, chemical synthesis provides pure compounds with defined sequences of GlcNAc and GlcN monomers. The synthesis of homo- and hetero-chitobioses and hetero-chitotetraoses is described in this thesis. Dimethylmaleoyl and phthaloyl groups were used for protection of the amines. The donor was activated as the trichloroacetimidate in order to form the β-linkages. Glycosylation in the presence of trimethylsilyl trifluoromethanesulfonate, followed by N- and O-deprotection furnished chitobioses and chitotetraoses in good yields.
For more than 70 years, understanding of the mechanism of particle nucleation in emulsion polymerization has been one of the most challenging issues in heterophase polymerization research. Within this work a comprehensive experimental study of particle nucleation in emulsion polymerization of styrene at 70 °C and variety of conditions has been performed. To follow the onset of nucleation, on-line conductivity measurements were applied. This technique is highly sensitive to the mobility of conducting species and hence, it can be employed to follow aggregation processes leading to particle formation. On the other hand, by recording the optical transmission (turbidity) of the reaction mixture particle growth was followed. Complementary to the on-line investigations, off-line characterizations of the particle morphology and the molecular weight have been performed. The aim was to achieve a better insight in the processes taking place after starting the reaction via particle nucleation until formation of colloidally stable latex particles. With this experimental protocol the initial period of styrene emulsion polymerization in the absence as well as in the presence of various surfactants (concentrations above and below the critical micellization concentration) and also in the presence of seed particles has been investigated. Ionic and non-ionic initiators (hydrophilic and hydrophobic types) have been applied to start the polymerizations. Following the above algorithm, experimental evidence has been obtained showing the possibility of performing surfactant-free emulsion polymerization of styrene with oil-soluble initiators. The duration of the pre-nucleation period (that is the time between starting the polymerization and nucleation) can be precisely adjusted with the initiator hydrophobicity, the equilibration time of styrene in water, and the surfactant concentration. Spontaneous emulsification of monomer in water, as soon as both phases are brought into contact, is a key factor to explain the experimental results. The equilibration time of monomer in water as well as the type and concentration of other materials in water (surfactants, seed particles, etc.) control the formation rate and the size of the emulsified droplets and thus, have a strong influence on the particle nucleation and the particle morphology. One of the main tasks was to investigate the effect of surfactant molecules and especially micelles on the nucleation mechanism. Experimental results revealed that in the presence of emulsifier micelles the conductivity pattern does not change essentially. This means that the presence of emulsifiers does not change the mechanism of particle formation qualitatively. However, surfactants assist in the nucleation process as they lower the activation free energy of particle formation. Contrary, seed particles influence particle nucleation, substantially. In the presence of seed particles above a critical volume fraction the formation of new particles can be suppressed. However, micelles and seed particles as absorbers exhibit a common behavior under conditions where monomer equilibration is not allowed. Results prove that the nucleation mechanism comprises the initiation of water soluble oligomers in the aqueous phase followed by their aggregation. The process is heterogeneous in nature due to the presence of monomer droplets.