Filtern
Volltext vorhanden
- nein (2) (entfernen)
Erscheinungsjahr
- 2019 (2) (entfernen)
Dokumenttyp
- Wissenschaftlicher Artikel (2) (entfernen)
Sprache
- Englisch (2)
Gehört zur Bibliographie
- ja (2)
Schlagworte
- Electrosensing (1)
- H2O2 (1)
- Iron/silver microflowers (1)
- Nanostructures (1)
- Nonenzymatic (1)
- nanoflowers (1)
- nanoparticles (1)
- nanotriangles (1)
- optical-properties (1)
- sers (1)
Institut
- Institut für Chemie (2) (entfernen)
Silver-Iron Hierarchical Microflowers for Highly Efficient H2O2 Nonenzymatic Amperometric Detection
(2019)
This study addresses the fabrication of monodispersed iron-doped silver meso-hierarchical flower-like structures via a facile chemical procedure. The morphology of the obtained silver particles has been tuned by changing the concentration of the structure-directing agent (malonic acid). Ball-shaped silver particles were formed in the absence of malonic acid (MA), while silver particles with craspedia-globosa, chrysanthemum, and dahlia flower-like structures were obtained in the presence of 0.2, 0.5, and 1 mM malonic acid, respectively. The doping of these dahlia flower-like structures with trace amounts of iron (<= 5% Fe weight percent) led to the formation of globe-amaranth iron-doped microflowers (AgFeamaranth). The as-prepared AgFeamaranth exhibited better performance as a nonenzymatic H2O2 sensor compared to undoped silver particles as demonstrated by their higher catalytic activity and stability together with superior sensitivity (1350 mu M-1 cm(-2), 61 times higher) and lower detection limit (0.1 mu M). These enhancements are attributed to the AgFe unique flower-like structures and to the fact that the iron dopants provide a higher number of electroactive sites and reduce the charge transfer resistance of H2O2 reduction. Additionally, the good stability of AgFe is believed to originate from the faster detachment rate of the in situ-formed gas bubbles from their surfaces compared to undoped silver structures.
Due to the enhanced electromagnetic field at the tips of metal nanoparticles, the spiked structure of gold nanostars (AuNSs) is promising for surface-enhanced Raman scattering (SERS). Therefore, the challenge is the synthesis of well designed particles with sharp tips. The influence of different surfactants, i.e., dioctyl sodium sulfosuccinate (AOT), sodium dodecyl sulfate (SDS), and benzylhexadecyldimethylammonium chloride (BDAC), as well as the combination of surfactant mixtures on the formation of nanostars in the presence of Ag⁺ ions and ascorbic acid was investigated. By varying the amount of BDAC in mixed micelles the core/spike-shell morphology of the resulting AuNSs can be tuned from small cores to large ones with sharp and large spikes. The concomitant red-shift in the absorption toward the NIR region without losing the SERS enhancement enables their use for biological applications and for time-resolved spectroscopic studies of chemical reactions, which require a permanent supply with a fresh and homogeneous solution. HRTEM micrographs and energy-dispersive X-ray (EDX) experiments allow us to verify the mechanism of nanostar formation according to the silver underpotential deposition on the spike surface in combination with micelle adsorption.