Refine
Year of publication
Document Type
- Article (69)
- Postprint (8)
- Review (3)
- Conference Proceeding (1)
- Habilitation Thesis (1)
- Other (1)
- Preprint (1)
Language
- English (84)
Is part of the Bibliography
- yes (84)
Keywords
- ring-opening polymerization (6)
- biomaterials (5)
- biodegradable polymers (4)
- self-assembly (4)
- XPS (3)
- crystallization (3)
- metathesis (3)
- nanoparticles (3)
- photochemistry (3)
- spider silk (3)
Institute
Yolk@Shell Nanoarchitectures with Bimetallic Nanocores - Synthesis and Electrocatalytic Applications
(2016)
Due to the adsorption of biomolecules, the control of the biodistribution of nanoparticles is still one of the major challenges of nanomedicine. Poly(2-ethyl-2-oxazoline) (PEtOx) for surface modification of nanoparticles is applied and both protein adsorption and cellular uptake of PEtOxylated nanoparticles versus nanoparticles coated with poly(ethylene glycol) (PEG) and non-coated positively and negatively charged nanoparticles are compared. Therefore, fluorescent poly(organosiloxane) nanoparticles of 15 nm radius are synthesized, which are used as a scaffold for surface modification in a grafting onto approach. With multi-angle dynamic light scattering, asymmetrical flow field-flow fractionation, gel electrophoresis, and liquid chromatography-mass spectrometry, it is demonstrated that protein adsorption on PEtOxylated nanoparticles is extremely low, similar as on PEGylated nanoparticles. Moreover, quantitative microscopy reveals that PEtOxylation significantly reduces the non-specific cellular uptake, particularly by macrophage-like cells. Collectively, studies demonstrate that PEtOx is a very effective alternative to PEG for stealth modification of the surface of nanoparticles.
Langmuir polymers films (LPFs) frequently form non-equilibrium states which are manifested in a decay of the surface pressure with time when the system is allowed to relax. Monitoring and manipulating the temporal evolution of these relaxations experimentally helps to shed light on the associated molecular reorganization processes. We present a systematic study based on different compression protocols and show how these reorganization processes impact the morphology of LPFs of poly(gamma-benzyl-L-glutamate) (PBLG); visualized by means of atomic force microscopy. Upon continuous compression, a fibrillar morphology was formed with a surface decorated by squeezed-out islands. By contrast, stepwise compression promoted the formation of a fibrillar network with a bimodal distribution of fibril diameters, caused by merging of fibrils. Finally, isobaric compression induced in-plane compaction of the monolayer. We correlate these morphological observations with the kinetics of the corresponding relaxations, described best by a sum of two exponential functions with different time scales representing two molecular processes. We discuss the observed kinetics and the resulting morphologies in the context of nucleation and growth, characteristic for first-order phase transitions. Our results demonstrate that the preparation conditions of LPFs have tremendous impact on ordering of the molecules and hence various macroscopic properties of such films.
The nucleophilic thiol-ene (thia-Michael) reaction between molecular rods bearing terminal thiols and bis-maleimides was investigated. The molecular rods have oligospiroketal (OSK) and oligospirothioketal (OSTK) backbones. Contrary to the expectations, cyclic oligomers were always obtained instead of linear rigid-rod polymers. Replacing the OS(T)K rods with a flexible chain yielded polymeric products, suggesting that the OS(T) K structure is responsible for the formation of cyclic products. The reason for the preferred formation of cyclic products is due to the presence of folded conformations, which have already been described for articulated rods.
1,4-Polymyrcene was synthesized by anionic polymerization of -myrcene and was subjected to photochemical functionalization with various thiols (i.e. methyl thioglycolate, methyl 3-mercaptopropionate, butyl 3-mercaptopropionate, ethyl 2-mercaptopropionate and 2-methyl-2-propanethiol) using benzophenone/UV light as the radical source. The yield of thiol addition to the trisubstituted double bonds of 1,4-polymyrcene decreased in the order 1 degrees thiol (ca 95%) > 2 degrees thiol (ca 80%) > 3 degrees thiol (<5%), due to the reversibility of the thiol-ene reaction. Remarkably, thiol addition to the side-chain double bonds was 8 - 10 times (1 degrees thiol) or 24 times (2 degrees thiol) faster than to the main-chain double bonds, which can be explained by the different accessibility of the double bonds and steric hindrance. Despite the use of a 10-fold excess of thiol with respect to myrcene units, the thiol-ene addition was accompanied by chain coupling reactions, which in the extreme case of 3 degrees thiol (or in the absence of thiol) resulted in the formation of insoluble crosslinked material. As an example, a methyl-thioglycolate-functionalized 1,4-polymyrcene was saponified/crosslinked to give submicron polyelectrolyte particles in dilute alkaline solution. (c) 2018 Society of Chemical Industry
This article presents a simple and facile method to fabricate thermoresponsive polymer-grafted silica particles by direct surface-initiated photopolymerization of N-isopropylacrylamide (NIPAM). This method is based on silica particles bearing thiol functionalities, which are transformed into thiyl radicals by irradiation with UV light to initiate the polymerization of NIPAM in aqueous media at room temperature. The photopolymerization of NIPAM could be applied to smaller thiol-functionalized particles (approximate to 48 nm) as well as to larger particles (approximate to 692 nm). Hollow poly(NIPAM) capsules could be formed after etching away the silica cores from the composite particles. It is possible to produce tailor-made composite particles or capsules for particular applications by extending this approach to other vinyl monomers. (c) 2015 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 2015, 53, 1260-1267
The aqueous solution behavior of thermoresponsive-hydrophilic block copolypeptoids, i.e., poly(N-(n-propyl)glycine) (x) -block-poly(N-methylglycine) (y) (x = 70; y = 23, 42, 76), in the temperature range of 20-45 A degrees C is studied. Turbidimetric analyses of the 0.1 wt% aqueous solutions reveal two cloud points at T (cp)similar to 30 and 45 A degrees C and a clearing point in between at T (cl)similar to 42 A degrees C. Temperature-dependent dynamic light scattering (DLS) suggest that right above the first collapse temperature, single polymer molecules assemble into large structures which upon further heating, i.e., at the clearing point temperature, disassemble into micelle-like structures. Upon further heating, the aggregates start to grow again in size, as recognized by the second cloud point, through a crystallization process.
Block copolypeptoids comprising a thermosensitive, crystallizable poly(N-(n-propyl)glycine) block and a watersoluble poly(N-methylglycine) block, P70My (y = 23, 42, 76, 153, and 290), were synthesized bY ring-opening polymerization of the corresponding N-alkylglycine N-carboxyanhydrides (NCAs) and examined according to their thermo-induced aggregation and crystallization in water by turbidimetty, micro-differential scanning calorimetry (micro-DSC); cryogenic scanning electron microscopy (cryo-SEM), analytical ultracentrifugation (AUC), and static light scattering (SLS). At a temperature above the cloud point temperature, the initially formed micellar aggregates started to crystallize and grow into larger complex assemblies of about 100-500 nm, exhibiting flower-like (P70M23), ellipsoidal (P70M42 and P70M72) or irregular shapes (P70M153 and.P70M290).
As polypeptoids become increasingly popular, they present a more soluble and processable alternative to natural and synthetic polypeptides; the breadth of their potential functionality slowly comes into focus. This report analyzes the ability of an alkyne-functionalized polypeptoid, poly(N-propargyl glycine), to crosslink upon heating. The crosslinking process is analyzed by thermal analysis (differential scanning calorimetry and thermogravimetric analysis), Fourier-transform infrared, electron paramagnetic resonance, and solid-state NMR spectroscopy. While a precise mechanism cannot be confidently assigned, it is clear that the reaction proceeds by a radical mechanism that exclusively involves the alkyne functionality, which, upon crosslinking, yields alkene and aromatic products.
A one-step moderate energy vibrational emulsification method was successfully employed to produce thermo-responsive olive/silicone-based Janus emulsions stabilized by poly(N,N-diethylacrylamide) carrying 0.7 mol% oleoyl side chains. Completely engulfed emulsion droplets remained stable at room temperature and could be destabilized on demand upon heating to the transition temperature of the polymeric stabilizer. Time-dependent light micrographs demonstrate the temperature-induced breakdown of the Janus droplets, which opens new aspects of application, for instance in biocatalysis.
A one-step moderate energy vibrational emulsification method was successfully employed to produce thermo-responsive olive/silicone-based Janus emulsions stabilized by poly(N,N-diethylacrylamide) carrying 0.7 mol% oleoyl side chains. Completely engulfed emulsion droplets remained stable at room temperature and could be destabilized on demand upon heating to the transition temperature of the polymeric stabilizer. Time-dependent light micrographs demonstrate the temperature-induced breakdown of the Janus droplets, which opens new aspects of application, for instance in biocatalysis.
The protein corona, which forms on the nanoparticle's surface in most biological media, determines the nanoparticle's physicochemical characteristics. The formation of the protein corona has a significant impact on the biodistribution and clearance of nanoparticles in vivo. Therefore, the ability to influence the formation of the protein corona is essential to most biomedical applications, including drug delivery and imaging. In this study, we investigate the protein adsorption on nanoparticles with a hydrodynamic radius of 30 nm and a coating of thermoresponsive poly(2-isopropyl-2-oxazoline) in serum. Using multiangle dynamic light scattering (DLS) we demonstrate that heating of the nanoparticles above their phase separation temperature induces the formation of agglomerates, with a hydrodynamic radius of 1 mu m. In serum, noticeably stronger agglomeration occurs at lower temperatures compared to serum-free conditions. Cryogenic transmission electron microscopy (cryo-TEM) revealed a high packing density of agglomerates when serum was not present. In contrast, in the presence of serum, agglomerated nanoparticles were loosely packed, indicating that proteins are intercalated between them. Moreover, an increase in protein content is observed upon heating, confirming that protein adsorption is induced by the alteration of the surface during phase separation. After cooling and switching the surface back, most of the agglomerates were dissolved and the main fraction returned to the original size of approximately 30 nm as shown by asymmetrical flow-field flow fractionation (AF-FFF) and DLS. Furthermore, the amounts of adsorbed proteins are similar before and after heating the nanoparticles to above their phase-separation temperature. Overall, our results demonstrate that the thermoresponsivity of the polymer coating enables turning the corona formation on nanoparticles on and off in situ. As the local heating of body areas can be easily done in vivo, the thermoresponsive coating could potentially be used to induce the agglomeration of nanopartides and proteins and the accumulation of nanoparticles in a targeted body region.
Polysarcosine (Mn = 3650–20 000 g mol−1, Đ ∼ 1.1) was synthesized from the air and moisture stable N-phenoxycarbonyl-N-methylglycine. Polymerization was achieved by in situ transformation of the urethane precursor into the corresponding N-methylglycine-N-carboxyanhydride, when in the presence of a non-nucleophilic tertiary amine base and a primary amine initiator.
Polysarcosine (M-n = 3650-20 000 g mol(-1), D similar to 1.1) was synthesized from the air and moisture stable N-phenoxycarbonyl-N-methylglycine. Polymerization was achieved by in situ transformation of the urethane precursor into the corresponding N-methylglycine-N-carboxyanhydride, when in the presence of a non-nucleophilic tertiary amine base and a primary amine initiator.
Polysarcosine (Mn = 3650–20 000 g mol−1, Đ ∼ 1.1) was synthesized from the air and moisture stable N-phenoxycarbonyl-N-methylglycine. Polymerization was achieved by in situ transformation of the urethane precursor into the corresponding N-methylglycine-N-carboxyanhydride, when in the presence of a non-nucleophilic tertiary amine base and a primary amine initiator.
In this study, we present a novel and facile method for the synthesis of multiresponsive plasmonic nanoparticles with an interesting interfacial behavior. We used thiol-initiated photopolymerization technique to graft poly(N-isopropylacrylamide) onto the surface of protein-coated gold nanoparticles. The combination of the protein bovine serum albumin with the thermoresponsive polymer leads to smart hybrid nanoparticles, which show a stimuli-responsive behavior of their aggregation and a precisely controllable phase transfer behavior. Three interconnected stimuli, namely, temperature, ionic strength, and pH, were identified as property tuning switches. The aggregation was completely reversible and was quantified by determining Smoluchowski’s instability ratios with time-resolved dynamic light scattering. The tunable hydrophobicity via the three stimuli was used to study interfacial activity and phase transfer behavior of the nanoparticles at an octanol/water interface. Depending on the type of coating (i.e., protein or protein/polymer) as well as the three external stimuli, the nanoparticles either remained in the aqueous phase (aggregated or nonaggregated), accumulated at the oil/water interface, wet the glass wall between the glass vial and the octanol phase, or even crossed the oil/water interface. Such smart and interfacially active nanoparticles with external triggers that are capable of crossing oil/water interfaces under physiological conditions open up new avenues for a variety of applications ranging from the development of drug-delivery nanosystems across biological barriers to the preparation of new catalytic materials.
We report herein on the polymer-crystallization-assisted thiol-ene photosynthesis of an amphiphilic comb/graft DNA copolymer, or molecular brush, composed of a hydrophobic poly(2-oxazoline) backbone and hydrophilic short single-stranded nucleic acid grafts. Coupling efficiencies are above 60% and thus higher as compared with the straight solid-phase-supported synthesis of amphiphilic DNA block copolymers. The DNA molecular brushes self-assemble into sub-micron-sized spherical structures in water as evidenced by light scattering as well as atomic force and electron microscopy imaging. The nucleotide sequences remain functional, as assessed by UV and fluorescence spectroscopy subsequent to isoindol synthesis at the surface of the structures. The determination of a vesicular morphology is supported by encapsulation and subsequent spectroscopy monitoring of the release of a water-soluble dye and spectroscopic quantification of the hybridization efficiency (30% in average) of the functional nucleic acid strands engaged in structure formation: about one-half of the nucleotide sequences are available for hybridization, whereas the other half are hindered within the self-assembled structure. Because speciation between complementary and non complementary sequences in the medium could be ascertained by confocal laser scanning microscopy, the stable self-assembled molecular brushes demonstrate the potential for sensing applications.