It was the goal of this work to explore two different synthesis pathways using green chemistry. The first part of this thesis is focusing on the use of the urea-glass route towards single phase manganese nitride and manganese nitride/oxide nano-composites embedded in carbon, while the second part of the thesis is focusing on the use of the “saccharide route” (namely cellulose, sucrose, glucose and lignin) towards metal (Ni0), metal alloy (Pd0.9Ni0.1, Pd0.5Ni0.5, Fe0.5Ni0.5, Cu0.5Ni0.5 and W0.15Ni0.85) and ternary carbide (Mn0.75Fe2.25C) nanoparticles embedded in carbon. In the interest of battery application, MnN0.43 nanoparticles surrounded by a graphitic shell and embedded in carbon with a high surface area (79 m^2/g) were synthesized, following a previously set route.The comparison of the material characteristics before and after the discharge showed no remarkable difference in terms of composition and just slight differences in the morphological point of view, meaning the particles are stable but agglomerate. The graphitic shell is contributing to the resistance of the material and leads to a fine cyclic stability over 140 cycles of 230 mAh/g after the first charge/discharge and coulombic efficiencies close to 100%. Due to the low voltage towards Li/Li+ and the low polarization, it might be an attractive anode material for lithium ion batteries. However, the capacity is still noticeably lower than the theoretical value for MnN0.43. A mixture of MnN0.43 and MnO nanoparticles embedded in carbon (surface area 93 m^2/g) was able to improve the cyclic stability to over 160 cycles giving a capacity of 811 mAh/g, which is considerably higher than the capacity of the conventional material graphite (372 mAh/g). This nano-composite seems to agglomerate less during the process of discharge. Interestingly, although the capacity is much higher than of the single phase manganese nitride, the nano-composite seems to only contain MnN0.43 nanoparticles after the process of discharge with no oxide phase to be found. Concerning catalysis application, different metal, metal alloy, and metal carbide nanoparticles were synthesized using the saccharide route. At first, systems that were already investigated before, being Pd0.9Ni0.1, Pd0.5Ni0.5, Fe0.5Ni0.5 and Mn0.75Fe2.25C using cellulose as the carbon source were prepared and tested in an alkylation reaction of toluene with benzylchloride. Unexpectedly, the metal alloys did not show any catalytic activity, but the ternary carbide Mn0.75Fe2.25C showed fine catalytic activity of 98% conversion after 9 hour reaction time (110 °C). In a second step, the saccharide route was modified towards other carbon sources and carbon to metal ratios in order to improve the homogeneity of the samples and accessibility of the particle surfaces. The used carbon sources sucrose and glucose are similar in their basic structure of carbohydrates, but reducing the (polymeric) chain length. Indeed, the cellulose could be successfully replaced by sucrose and glucose. A lower carbon to metal ratio was found to influence the size, homogeneity and accessibility (as evidenced by TEM) of the samples. Since sucrose is an aliment, glucose is the better choice as a carbon source. Using glucose, the synthesis of Cu0.5Ni0.5 and W0.15Ni0.85 nano-composites was also possible, although the later was never obtained as pure phase. These alloy nano-composites were tested, along with nickel0 nanoparticles also prepared with glucose and on their catalytic activity towards the reduction of phenylacetylene. The results obtained let believe that any (poly) saccharide, including lignin, could be used as carbon source. The nickel0 nano-composites prepared with lignin as a carbon source were tested along with those prepared with cellulose and sucrose for their catalytic activity in the transfer hydrogenation of nitrobenzene (results compared with exposed nickel nanoparticles and nickel supported on carbon) leading to very promising results. Based on the urea-glass route and the saccharide route, simple equipment and transition metals, it was possible to have a one-pot synthesize with scale-up possibilities towards new material that can be applied in catalysis and battery systems.
The negative impact of crude oil on the environment has led to a necessary transition toward alternative, renewable, and sustainable resources. In this regard, lignocellulosic biomass (LCB) is a promising renewable and sustainable alternative to crude oil for the production of fine chemicals and fuels in a so-called biorefinery process. LCB is composed of polysaccharides (cellulose and hemicellulose), as well as aromatics (lignin). The development of a sustainable and economically advantageous biorefinery depends on the complete and efficient valorization of all components. Therefore, in the new generation of biorefinery, the so-called biorefinery of type III, the LCB feedstocks are selectively deconstructed and catalytically transformed into platform chemicals. For this purpose, the development of highly stable and efficient catalysts is crucial for progress toward viability in biorefinery. Furthermore, a modern and integrated biorefinery relies on process and reactor design, toward more efficient and cost-effective methodologies that minimize waste. In this context, the usage of continuous flow systems has the potential to provide safe, sustainable, and innovative transformations with simple process integration and scalability for biorefinery schemes.
This thesis addresses three main challenges for future biorefinery: catalyst synthesis, waste feedstock valorization, and usage of continuous flow technology. Firstly, a cheap, scalable, and sustainable approach is presented for the synthesis of an efficient and stable 35 wt.-% Ni catalyst on highly porous nitrogen-doped carbon support (35Ni/NDC) in pellet shape. Initially, the performance of this catalyst was evaluated for the aqueous phase hydrogenation of LCB-derived compounds such as glucose, xylose, and vanillin in continuous flow systems. The 35Ni/NDC catalyst exhibited high catalytic performances in three tested hydrogenation reactions, i.e., sorbitol, xylitol, and 2-methoxy-4-methylphenol with yields of 82 mol%, 62 mol%, and 100 mol% respectively. In addition, the 35Ni/NDC catalyst exhibited remarkable stability over a long time on stream in continuous flow (40 h). Furthermore, the 35Ni/NDC catalyst was combined with commercially available Beta zeolite in a dual–column integrated process for isosorbide production from glucose (yield 83 mol%).
Finally, 35Ni/NDC was applied for the valorization of industrial waste products, namely sodium lignosulfonate (LS) and beech wood sawdust (BWS) in continuous flow systems. The LS depolymerization was conducted combining solvothermal fragmentation of water/alcohol mixtures (i.e.,methanol/water and ethanol/water) with catalytic hydrogenolysis/hydrogenation (SHF). The depolymerization was found to occur thermally in absence of catalyst with a tunable molecular weight according to temperature. Furthermore, the SHF generated an optimized cumulative yield of lignin-derived phenolic monomers of 42 mg gLS-1. Similarly, a solvothermal and reductive catalytic fragmentation (SF-RCF) of BWS was conducted using MeOH and MeTHF as a solvent. In this case, the optimized total lignin-derived phenolic monomers yield was found of 247 mg gKL-1.