Flow birefringence induced in dilute solutions of poly[(1,4-naphthylene)-2,5-diyl-1,3,4-oxadiazole] and poly[2,6-naphthylene)-2,5-diyl-1,3,4-oxadiazole] in conc. sulphuric acid has been investigated. The shear optical coefficient was found for these polymers to be approximately double the value of that obtained in the same solvent for poly[(para-phenylene) -2,5-diyl-1,3,4-oxadiazole]. Rigid-chain behaviour of the polymers was characterized by hydrodynamic and dynamo-optical parameters evaluated with application of the worm-like chain model and the "method of similar structures". Change in optical anisotropy of a chain unit induced by incorporation of naphthylene groups into the main chain has been evaluated.
Translational diffusion of the macromolecules, intrinsic viscosity and flow birefringence induced in dilute solutions of poly(1,3-phenylene-1,3,4-oxadiazole) (PMOD) in conc. sulphuric acid has been investigated. Molecular-weight dependences of hydrodynamic and dynamo-optical properties are established over the M range from 8.1 103 to 87 103. Experimental data agree well with the theories developed for translational friction and intrinsic viscosity of the wormlike chains with the following molecular parameters: mass per chain unit ML = 22.7 Dalton/Å, the Kuhn segment length A = 59 ± 4 Å, the chain diameter d = 4 ± 1.5 Å. Hindrance to intramolecular rotation is characterized by the parameter s = 1.7. The shear optical coefficient was found to be approximately 1.7 times lower the value of that obtained in the same solvent for the para-phenylene isomer of this polymer, being in good agreement with higher equilibrium flexibility of the PMOD molecule chains in solutions as determined herein from the hydrodynamic data.
Poly[(1,4-naphthalene)-2,5-diyl-1,3,4-oxadiazole] and poly[(2,6-naphthalene)-2,5-diyl-1,3,4-oxadiazole] have been synthesized and investigated in conc. H2S04, by the flow birefringence method in comparison with poly(1,4- phenylene)-2,5-diyl-1,3,4-oxadiazole]. Changes in conformation parameters and optical anisotropy of a chain unit induced by incorporation of the naphthalene groups into the macromolecule backbone have been evaluated.