This thesis discusses heat and charge transport phenomena in single-crystalline Silicon penetrated by nanometer-sized pores, known as mesoporous Silicon (pSi). Despite the extensive attention given to it as a thermoelectric material of interest, studies on microscopic thermal and electronic transport beyond its macroscopic characterizations are rarely reported. In contrast, this work reports the interplay of both.
PSi samples synthesized by electrochemical anodization display a temperature dependence of specific heat 𝐶𝑝 that deviates from the characteristic 𝑇^3 behaviour (at 𝑇<50𝐾). A thorough analysis reveals that both 3D and 2D Einstein and Debye modes contribute to this specific heat. Additional 2D Einstein modes (~3 𝑚𝑒𝑉) agree reasonably well with the boson peak of SiO2 in pSi pore walls. 2D Debye modes are proposed to account for surface acoustic modes causing a significant deviation from the well-known 𝑇^3 dependence of 𝐶𝑝 at 𝑇<50𝐾.
A novel theoretical model gives insights into the thermal conductivity of pSi in terms of porosity and phonon scattering on the nanoscale. The thermal conductivity analysis utilizes the peculiarities of the pSi phonon dispersion probed by the inelastic neutron scattering experiments. A phonon mean-free path of around 10 𝑛𝑚 extracted from the presented model is proposed to cause the reduced thermal conductivity of pSi by two orders of magnitude compared to p-doped bulk Silicon. Detailed analysis indicates that compound averaging may cause a further 10-50% reduction. The percolation threshold of 65% for thermal conductivity of pSi samples is subsequently determined by employing theoretical effective medium models.
Temperature-dependent electrical conductivity measurements reveal a thermally activated transport process. A detailed analysis of the activation energy 𝐸𝐴𝜎 in the thermally activated transport exhibits a Meyer Neldel compensation rule between different samples that originates in multi-phonon absorption upon carrier transport. Activation energies 𝐸𝐴𝑆 obtained from temperature-dependent thermopower measurements provide further evidence for multi-phonon assisted hopping between localized states as a dominant charge transport mechanism in pSi, as they systematically differ from the determined 𝐸𝐴𝜎 values.
Metals are often used in environments that are conducive to corrosion, which leads to a reduction in their mechanical properties and durability. Coatings are applied to corrosion-prone metals such as aluminum alloys to inhibit the destructive surface process of corrosion in a passive or active way. Standard anticorrosive coatings function as a physical barrier between the material and the corrosive environment and provide passive protection only when intact. In contrast, active protection prevents or slows down corrosion even when the main barrier is damaged. The most effective industrially used active corrosion inhibition for aluminum alloys is provided by chromate conversion coatings. However, their toxicity and worldwide restriction provoke an urgent need for finding environmentally friendly corrosion preventing systems. A promising approach to replace the toxic chromate coatings is to embed particles containing nontoxic inhibitor in a passive coating matrix. This work presents the development and optimization of effective anticorrosive coatings for the industrially important aluminum alloy, AA2024-T3 using this approach. The protective coatings were prepared by dispersing mesoporous silica containers, loaded with the nontoxic corrosion inhibitor 2-mercaptobenzothiazole, in a passive sol-gel (SiOx/ZrOx) or organic water-based layer. Two types of porous silica containers with different sizes (d ≈ 80 and 700 nm, respectively) were investigated. The studied robust containers exhibit high surface area (≈ 1000 m² g-1), narrow pore size distribution (dpore ≈ 3 nm) and large pore volume (≈ 1 mL g-1) as determined by N2 sorption measurements. These properties favored the subsequent adsorption and storage of a relatively large amount of inhibitor as well as its release in response to pH changes induced by the corrosion process. The concentration, position and size of the embedded containers were varied to ascertain the optimum conditions for overall anticorrosion performance. Attaining high anticorrosion efficiency was found to require a compromise between delivering an optimal amount of corrosion inhibitor and preserving the coating barrier properties. This study broadens the knowledge about the main factors influencing the coating anticorrosion efficiency and assists the development of optimum active anticorrosive coatings doped with inhibitor loaded containers.
Die vorliegende Arbeit beschäftigt sich mit der Synthese und Charakterisierung mesoporöser monolithischer Silica und deren Hybridmaterialien mit Ionischen Flüssigkeiten (ILs, ionic liquids). Zur Synthese der Silicaproben wurde ein Sol-Gel-Verfahren, ausgehend von einer Präkursorverbindung wie Tetramethylorthosilicat angewendet. Der Katalysator mit der geringsten Basizität führte zum Material mit der kleinsten Porengröße und der größten spezifischen Oberfläche. Eine Kombination von porösen Silica mit ILs führt zur Materialklasse der Silica-Ionogele. Diese Hybridmaterialien verbinden die Eigenschaften eines porösen Festkörpers mit denen einer IL (Leitfähigkeit, weites elektrochemisches Fenster, gute thermische Stabilität) und bieten vielfältige Einsatzmöglichkeiten z.B. in der Katalyse- Solar- und Sensortechnik. Um diese Materialien für ihren Verwendungszweck zu optimieren, bedarf es deren umfassenden Charakterisierung. Daher wurde in der vorliegenden Arbeit das thermische Verhalten von Silica-Ionogelen unter Verwendung verschiedener 1-Ethyl-3-methylimidazolium [Emim]-basierter ILs untersucht. Interessanterweise zeigen die untersuchten ILs deutliche Änderungen in ihrem thermischen Verhalten, wenn diese in porösen Materialien eingeschlossen werden (Confinement). Während sich die untersuchten reinen ILs durch klar unterscheidbare Phasenübergänge auszeichnen, konnten für die entsprechenden Hybridmaterialien deutlich schwächer ausgeprägte Übergänge beobachtet werden. Einzelne Phasenübergänge wurden unterdrückt (Glas- und Kristallisationsübergänge), während z.B. Schmelzübergänge in verbreiterten Temperaturbereichen, zum Teil als einzeln getrennte Schmelzpeaks beobachtet wurden. Diese Untersuchungen belegen deutliche Eigenschaftsänderungen der ILs in eingeschränkten Geometrien. Über Festkörper-NMR-Spektroskopie konnte außerdem gezeigt werden, daß die ILs in den mesoporösen Silicamaterialien eine unerwartet hohe Mobilität aufweisen. Die ILs können als quasi-flüssig bezeichnet werden und zeigen die nach bestem Wissen höchste Mobilität, die bisher für vergleichbare Hybridmaterialien beobachtet wurde. Durch Verwendung von funktionalisierten Präkursoren, sowie der Wahl der Reaktionsbedingungen, kann die Oberfläche der Silicamaterialien chemisch funktionalisiert werden und damit die Materialeigenschaften in der gewünschten Weise beeinflußt werden. In der vorliegenden Arbeit wurde der Einfluß der Oberflächenfunktionalität auf das thermische Verhalten hin untersucht. Dazu wurden zwei verschiedene Möglichkeiten der Funktionalisierung angewendet und miteinander verglichen. Bei der in-situ-Funktionalisierung wird die chemische Funktionalität während der Sol-Gel-Synthese über ein entsprechend funktionalisiertes Silan mit in das Silicamaterial einkondensiert. Eine postsynthetische Funktionalisierung erfolgt durch Reaktion der Endgruppen eines Silicamaterials mit geeigneten Reaktionspartnern. Um den Einfluß der physikalischen Eigenschaften der Probe auf die Reaktion zu untersuchen, wurden pulverisierte und monolithische Silicamaterialien miteinander verglichen. Im letzten Teil der Arbeit wurde die Vielfältigkeit, mit der Silicamaterialien postsynthetisch funktionalisiert werden können demonstriert. Durch die Kenntnis von Struktur-Eigenschaftsbeziehungen können die Eigenschaften von Silica-Ionogelen durch die geeignete Kombination von fester und mobiler Phase in der gewünschten Weise verändert werden. Die vorliegende Arbeit soll einen Beitrag zur Untersuchung dieser Beziehungen leisten, um das Potential dieser interessanten Materialien für Anwendungen nutzen zu können.