This work demonstrates the production of high-performing p- type and n-type hybrid AgxTe/poly(3,4-ethylenedioxythiopene):polystyrene sulfonic acid (PE-DOT:PSS) thermoelectric materials from the same Te/PEDOT:PSS parent structure during aqueous-based synthesis. All samples were solution-processed and analyzed in thin- film architectures. We were able to demonstrate a power factor of 44 mu W m(-1) K-2 for our highest-performing n-type material. In addition, we were also able to realize a 68% improvement in the power factor of our p-type compositions relative to the parent structure through manipulation of the inorganic nanostructure composition. We demonstrate control over the thermoelectric properties by varying the stoichiometry of AgxTe nanoparticles in AgxTe/PEDOT:PSS hybrid materials via a topotactic chemical transformation process at room temperature. This process offers a simple, low-temperature, and cost-effective route toward the production of both efficient n-type and p-type hybrid thermoelectric materials.
CuI has been recently rediscovered as a p-type transparent conductor with a high figure of merit. Even though many metal iodides are hygroscopic, the effect of moisture on the electrical properties of CuI has not been clarified. In this work, we observe a 2-fold increase in the conductivity of CuI after exposure to ambient humidity for 5 h, followed by slight long-term degradation. Simultaneously, the work function of CuI decreases by almost 1 eV, which can explain the large spread in the previously reported work function values. The conductivity increase is partially reversible and is maximized at intermediate humidity levels. On the basis of the large intragrain mobility measured by THz spectroscopy, we suggest that hydration of grain boundaries may be beneficial for the overall hole mobility.