A rare example of in situ linker generation with the formation of soft porous Zn- and Co-MOFs (IFP-9 and -10, respectively) is reported. The flexible ethoxy groups of IFP-9 and -10 protrude into the 1D hexagonal channels. The gas- sorption behavior of both materials for H2, CO2 and CH4 showed wide hysteretic isotherms, typical for MOFs having a flexible substituent which can give rise to a gate effect.
A Co(II)-imidazolate-4-amide-5-imidate based MOF, IFP-5, is synthesized by using an imidazolate anion-based novel ionic liquid as a linker precursor under solvothermal conditions. IFP-5 shows significant amounts of gas (N2, CO2, CH4 and H2) uptake capacities. IFP-5 exhibits an independent high spin Co(II) centre and antiferromagnetic coupling.
In this work the adsorption of CO2 and CH4 on a series of isoreticular microporous metal-organic frameworks based on 2-substituted imidazolate-4-amide-5-imidates, IFP-1-IFP-6 (IFP Imidazolate Framework Potsdam), is studied firstly by pure gas adsorption at 273 K. All experimental isotherms can be nicely described by using the Toth isotherm model and show the preferred adsorption of CO2 over CH4. At low pressures the Toth isotherm equation exhibits a Henry region, wherefore Henry's law constants for CO2 and CH4 uptake could be determined and ideal selectivity (alpha CO2/CH4) has been calculated. Secondly, selectivities were calculated from mixture data by using nearly equimolar binary mixtures of both gases by a volumetric-chromatographic method to examine the IFPs. Results showed the reliability of the selectivity calculation. Values of (alpha CO2/CH4) around 7.5 for IFP-5 indicate that this material shows much better selectivities than IFP-1, IFP-2, IFP-3, IFP-4 and IFP-6 with slightly lower selectivity (alpha CO2/CH4) = 4-6. The preferred adsorption of CO2 over CH4 especially of IFP-5 and IFP-4 makes these materials suitable for gas separation application.
The sharply rising level of atmospheric carbon dioxide resulting from anthropogenic emissions is one of the greatest environmental concerns facing our civilization today. Metal-organic frameworks (MOFs) are a new class of materials that constructed by metal-containing nodes bonded to organic bridging ligands. MOFs could serve as an ideal platform for the development of next generation CO2 capture materials owing to their large capacity for the adsorption of gases and their structural and chemical tunability. The ability to rationally select the framework components is expected to allow the affinity of the internal pore surface toward CO2 to be precisely controlled, facilitating materials properties that are optimized for the specific type of CO2 capture to be performed (post-combustion capture, precombustion capture, or oxy-fuel combustion) and potentially even for the specific power plant in which the capture system is to be installed. For this reason, significant effort has been made in recent years in improving the gas separation performance of MOFs and some studies evaluating the prospects of deploying these materials in real-world CO2 capture systems have begun to emerge. We have developed six new MOFs, denoted as IFPs (IFP-5, -6, -7, -8, -9, -10, IFP = Imidazolate Framework Potsdam) and two hydrogen-bonded molecular building block (MBB, named as 1 and 2 for Zn and Co based, respectively) have been synthesized, characterized and applied for gas storage. The structure of IFP possesses 1D hexagonal channels. Metal centre and the substituent groups of C2 position of the linker protrude into the open channels and determine their accessible diameter. Interestingly, the channel diameters (range : 0.3 to 5.2 Å) for IFP structures are tuned by the metal centre (Zn, Co and Cd) and substituent of C2 position of the imidazolate linker. Moreover hydrogen bonded MBB of 1 and 2 is formed an in situ functionalization of a ligand under solvothermal condition. Two different types of channels are observed for 1 and 2. Materials contain solvent accessible void space. Solvent could be easily removed by under high vacuum. The porous framework has maintained the crystalline integrity even without solvent molecules. N2, H2, CO2 and CH4 gas sorption isotherms were performed. Gas uptake capacities are comparable with other frameworks. Gas uptake capacity is reduced when the channel diameter is narrow. For example, the channel diameter of IFP-5 (channel diameter: 3.8 Å) is slightly lower than that of IFP-1 (channel diameter: 4.2 Å); hence, the gas uptake capacity and Brunauer-Emmett-Teller (BET) surface area are slightly lower than IFP-1. The selectivity does not depend only on the size of the gas components (kinetic diameter: CO2 3.3 Å, N2 3.6 Å and CH4 3.8 ) but also on the polarizability of the surface and of the gas components. IFP-5 and-6 have the potential applications for the separation of CO2 and CH4 from N2-containing gas mixtures and CO2 and CH4 containing gas mixtures. Gas sorption isotherms of IFP-7, -8, -9, -10 exhibited hysteretic behavior due to flexible alkoxy (e.g., methoxy and ethoxy) substituents. Such phenomenon is a kind of gate effects which is rarely observed in microporous MOFs. IFP-7 (Zn-centred) has a flexible methoxy substituent. This is the first example where a flexible methoxy substituent shows the gate opening behavior in a MOF. Presence of methoxy functional group at the hexagonal channels, IFP-7 acted as molecular gate for N2 gas. Due to polar methoxy group and channel walls, wide hysteretic isotherm was observed during gas uptake. The N2 The estimated BET surface area for 1 is 471 m2 g-1 and the Langmuir surface area is 570 m2 g-1. However, such surface area is slightly higher than azolate-based hydrogen-bonded supramolecular assemblies and also comparable and higher than some hydrogen-bonded porous organic molecules.
A rare example of in situ linker generation with the formation of soft porous Zn- and Co-MOFs (IFP-9 and -10, respectively) is reported. The flexible ethoxy groups of IFP-9 and -10 protrude into the 1D hexagonal channels. The gas-sorption behavior of both materials for H2, CO2 and CH4 showed wide hysteretic isotherms, typical for MOFs having a flexible substituent which can give rise to a gate effect.
A Co(II)–imidazolate-4-amide-5-imidate based MOF, IFP-5, is synthesized by using an imidazolate anion-based novel ionic liquid as a linker precursor under solvothermal conditions. IFP-5 shows significant amounts of gas (N2, CO2, CH4 and H2) uptake capacities. IFP-5 exhibits an independent high spin Co(II) centre and antiferromagnetic coupling.
A rare example of in situ linker generation with the formation of soft porous Zn- and Co-MOFs (IFP-9 and -10, respectively) is reported. The flexible ethoxy groups of IFP-9 and -10 protrude into the 1D hexagonal channels. The gas-sorption behavior of both materials for H-2, CO2 and CH4 showed wide hysteretic isotherms, typical for MOFs having a flexible substituent which can give rise to a gate effect.