Keywords
- biomaterials (8)
- Polymer (6)
- polymer (6)
- shape-memory effect (6)
- biomaterial (5)
- stimuli-sensitive polymers (5)
- Biomaterial (4)
- Langmuir monolayer (4)
- mesenchymal stem cells (4)
- shape memory (4)
Institute
- Institut für Chemie (175) (remove)
Hemocompatible materials are needed for internal and extracorporeal biomedical applications, which should be realizable by reducing protein and thrombocyte adhesion to such materials. Polyethers have been demonstrated to be highly efficient in this respect on smooth surfaces. Here, we investigate the grafting of oligo- and polyglycerols to rough poly(ether imide) membranes as a polymer relevant to biomedical applications and show the reduction of protein and thrombocyte adhesion as well as thrombocyte activation. It could be demonstrated that, by performing surface grafting with oligo- and polyglycerols of relatively high polydispersity (>1.5) and several reactive groups for surface anchoring, full surface shielding can be reached, which leads to reduced protein adsorption of albumin and fibrinogen. In addition, adherent thrombocytes were not activated. This could be clearly shown by immunostaining adherent proteins and analyzing the thrombocyte covered area. The presented work provides an important strategy for the development of application relevant hemocompatible 3D structured materials.
The thermally induced shape-memory effect of polymers is typically characterized by cyclic uniaxial thermomechanical tests. Here, a molecular-dynamics (MD) simulation approach of such a cyclic uniaxial thermomechanical test is presented for amorphous switching domains of poly(L-lactide) (PLLA). Uniaxial deformation of the constructed PLLA models is simulated with a Parinello-Rahman scheme, as well as a pragmatic geometrical approach. We are able to describe two subsequent test cycles using the presented simulation approach. The obtained simulated shape-memory properties in both test cycles are similar and independent of the applied deformation protocols. The simulated PLLA shows high shape fixity ratios (Rf 94%), but only a moderate shape recovery ratio is obtained (Rr 30%). Finally, the structural changes during the simulated test are characterized by analysis of the changes in the dihedral angle distributions.
The chain length and end groups of linear PEG grafted on smooth surfaces is known to influence protein adsorption and thrombocyte adhesion. Here, it is explored whether established structure function relationships can be transferred to application relevant, rough surfaces. Functionalization of poly(ether imide) (PEI) membranes by grafting with monoamino PEG of different chain lengths (M-n=1kDa or 10kDa) and end groups (methoxy or hydroxyl) is proven by spectroscopy, changes of surface hydrophilicity, and surface shielding effects. The surface functionalization does lead to reduction of adsorption of BSA, but not of fibrinogen. The thrombocyte adhesion is increased compared to untreated PEI surfaces. Conclusively, rough instead of smooth polymer or gold surfaces should be investigated as relevant models.
Shape-memory polymers (SMPs) are stimuli-sensitive materials capable of performing complex movements on demand, which makes them interesting candidates for various applications, for example, in biomedicine or aerospace. This trend article highlights current approaches in the chemistry of SMPs, such as tailored segment chemistry to integrate additional functions and novel synthetic routes toward permanent and temporary netpoints. Multiphase polymer networks and multimaterial systems illustrate that SMPs can be constructed as a modular system of different building blocks and netpoints. Future developments are aiming at multifunctional and multistimuli-sensitive SMPs.
Purpose: The formation of photoresponsive hydrogels were reported by irradiation of star-shaped poly(ethylene glycol)s with terminal cinnamylidene acetic acid (CAA) groups, which are capable of a photoinduced [2+2] cycloaddition. In this study we explored whether oligo(ethylene glycol) s and oligo(propylene glycol)s of varying molecular architecture (linear or star-shaped) or molecular weights could be functionalized with CAA as terminal groups by esterification or by amide formation.
Methods: Oligo(ethylene glycol) (OEG) and oligo(propylene glycol) (OPG) with varying molecular architecture (linear, star-shaped) and weight average molecular weights between 1000 and 5000 g.mol(-1) were functionalized by means of esterification of hydroxyl or amine endgroups with cinnamylidene acetic acid (CAA) or cinnamylidene acetyl chloride (CAC) as telechelic endgroups. The chemical structure, thermal properties, and molecular weights of the oligoethers obtained were determined by NMR spectroscopy, UV spectroscopy, DSC, and MALDI-TOF.
Results: CAA-functionalized linear and star-shaped OEGs or OPGs could be obtained with a degree of functionalization higher than 90%. In MALDI-TOF measurements an increase in Mw of about 150 g.mol(-1) (for each terminal end) after the functionalization reaction was observed. OEGCAA and OPGCAA showed an increase in glass transition temperature (T-g) from about -70 degrees C to -50 degrees C, compared to the unfunctionalized oligoethers. In addition, the melting temperature (T-m) of OEGCAA decreased from about 55 C to 30 degrees C, which can be accounted for by the hampered crystallization of the precursors because of the bulky CAA end groups as well as by the loss of the hydroxyl telechelic end groups.
Conclusion: The synthesis of photoresponsive oligoethers containing cinnamylidene acetic acid as telechelic endgroup was reported and high degrees of functionalization could be achieved. Such photosensitive oligomers are promising candidates as reactive precursors, for the preparation of biocompatible high molecular weight polymers and polymer networks.
Although the shape-changing capabilities of LCEs hold great potential for applications ranging from micropumps to artificial muscles, customization of the LCE functionality to the applications' requirements is still a challenge. It is studied whether the orientation of NMC-LCPs and NMC-LCEs based on 2-tert-butyl-1,4-bis[4-(4-pentenyloxy)benzoyl]hydroquinone can be enhanced by copolymerization with 2-methyl-1,4-bis[4-(4-pentenyloxy)benzoyl]hydroquinone or 2,6-bis[4-(4-pentenyl-oxy)-benzoyl]anthracene. An increasing content of the comonomers stabilizes the nematic phase, which enables a tailoring of T-NI for the NMC-LCP between 45 and 68 degrees C, while for the NMC-LCE T-NI ranges between 69 and 76 degrees C. In addition, NMC-LCE show an increased actuation performance.
Hybrid magnetic nanoparticles (mgNP) with a magnetite core diameter of 10 +/- 1 nm surface functionalized with oligo(omega-pentadecalactone) (OPDL) oligomers with M-n between 1300 and 3300 g mol(-1) could be successfully prepared having OPDL grafted from 200 mg g(-1) to 2170 mg g(-1). The particles are dispersible in chloroform resulting in stable suspensions. Magnetic response against an external magnetic field proved the superparamagnetic nature of the particles with a low coercivity (B-c) value of 297 mu T. The combination of the advantageous superparamagnetism of the mgNP with the exceptional stability of OPDL makes these novel hybrid mgNP promising candidates as multifunctional building blocks for magnetic nanocomposites with tunable physical properties.
Aim: The hydrolytic degradation behavior of degradable aliphatic polyester-based polymers is strongly influenced by the uptake or transport of water into the polymer matrix and also the hydrolysis rate of ester bonds.
Methods: We examined the volumetric swelling behavior of poly[(rac-lactide)-co-glycolide] (PLGA) and PLGA-based polyurethanes (PLGA-PU) with water contents of 0 wt%, 2 wt% and 7 wt% water at 310 K using a molecular modeling approach. Polymer systems with a number average molecular weight of M-n = 10,126 g.mol(-1) were constructed from PLGA with a lactide content of 67 mol%, whereby PLGA-PU systems were composed of five PLGA segments with M-n = 2052 g.mol(-1), which were connected via urethane linkers originated from 2,2,4-trimethyl hexamethylene-1,6-diisocyanate (TMDI), hexamethyl-1,6-diisocyanate (HDI), or L-lysine-1,6-diisocyanate (LDI).
Results: The calculated densities of the dry PLGA-PU systems were found to be lower than for pure PLGA. The obtained volumetric swelling of the PLGA-PU was depending on the type of urethane linker, whereby all swollen PLGA-PUs contained larger free volume distribution compared to pure PLGA. The mean square displacement curves for dry PLGA and PLGA-PUs showed that urethane linker units reduce the mobility of the polymer chains, while an increase in backbone atoms mobility was found, when water was added to these systems. Consequently, an increased water uptake of PLGA-PU matrices combined with a higher mobility of the chain segments should result in an accelerated hydrolytic chain scission rate in comparison to PLGA.
Conclusions: It can be anticipated that the incorporation of urethane linkers might be a helpful tool to adjust the degradation behavior of polyesters.
Aim: Multifunctional polymer-based biomaterials, which combine degradability with a shape-memory capability and in this way enable the design of actively moving implants such as self-anchoring implants or controlled release systems, have been recently introduced. Of particular interest are approved degradable polymers such as poly(L-lactide) (PLLA), which can be easily functionalized with a shape-memory effect. In the case of semicrystalline PLLA, the glass transition can be utilized as shape-memory switching domain.
Methods: In this work we applied a fully atomistic molecular dynamics simulation to study the shape-memory behavior of PLLA. A heating-deformation-cooling programming procedure was applied to atomistic PLLA packing models followed by a recovery module under stress-free conditions allowing the shape recovery. The recovery was simulated by heating the samples from T-low = 250 K to T-high = 500 K with different heating rates beta of 125, 40 and 4 K.ns(-1).
Results: We could demonstrate that the obtained strain recovery rate (R-r) was strongly influenced by the applied simulation time and heating rate, whereby R-r values in the range from 46% to 63% were achieved. On its own the application of a heating rate of 4 K.ns(-1) enabled us to determine a characteristic switching temperature of T-sw = 473 K for the modeled samples.
Conclusions: We anticipate that the atomistic modeling approach presented should be capable of enabling further study of T-sw with respect to the molecular structure of the investigated SMP and therefore could be applied in the context of design and development of new shape-memory (bio) materials.