Dielectric Relaxation Spectroscopy (DRS) and Thermally Stimulated Depolarization Current (TSDC) measurements were employed to study dielectric-relaxation processes, structural transitions and electric-polarization phenomena in poly(vinylidenefluoride-trifluoroethylene-chlorofluoroethylene) (P(VDF-TrFE-CFE)) terpolymer films. Results from DRS confirm the existence of two separate dispersion regions related to a para-to-ferroelectric phase transition and to the glass transition. The dipolar TSDC peak correlates with the loss peak of the ? relaxation that represents the glass transition. The electric polarization calculated from the dipolar TSDC peak (glass transition) shows a non-linear electric-field dependence and saturates at high electric poling fields. As the observed behaviour is essentially the same as that of the electric polarization obtained from direct polarization-versus-electric-field hysteresis measurements, TSDC experiments are also suitable for studying the polarization in relaxor-ferroelectric polymers. A saturation polarization of 44 mC m(?2) was found for an electric field of 190 MV m(?1).
Three poly(tetrafluoroethylene-hexafluoropropylene-vinylidenefluoride) (TFE-HFP-VDF or THV) terpolymers (Dyneon (R)) with different monomer ratios are investigated to demonstrate the concept of "modified" PTFE for space-charge electrets. HFP and VDF monomers distort the highly ordered PTFE molecules, which effectively enhances processability and adversely affects space-charge storage. Particularly, VDF component renders the material polar and probably also more conductive, partially undermining the space-charge-storage capabilities of PTFE. Nevertheless, the terpolymer THV815 with a TFE/HFP/VDF wt% ratio of 76.1/10.9/13 combines easy processability and relatively good space-charge stability. Our results shed light on novel concepts for space-charge electret materials with enhanced processing properties and reasonable charge-storage capabilities.