Keywords
- permittivity enhancement (2)
- Dielectric elastomer actuator (DEA) (1)
- allycyanide (1)
- broad-spectrum permittivity enhancement (1)
- compatibilized filler molecules (1)
- compliant electrodes (1)
- dipole grafting (1)
- elastic conductor (1)
- electroactive polymer (1)
- metal nanoparticles (1)
- nanocomposite (1)
- rotation (1)
- silicone based dielectric elastomer actuators (1)
- silicone-based dielectric elastomer actuators (1)
- soft electrical connections (1)
- stretchable electronics (1)
- uniform spatial arrangement (1)
Institute
- Institut für Physik und Astronomie (9) (remove)
A new strategy for the synthesis of high permittivity polymer composites is demonstrated based on well-defined spatial distribution of ultralow amounts of conductive nanoparticles. The spatial distribution Was realized by immobilizing Cu nanoparticles within the pore system of Alia microspheres, preventing direct contact between individual Cu particles. Both Cu-loaded and unloaded silica microspheres were-then used as fillers in polymer composites prepared with thermoplastic SEBS rubber is the matrix. With a metallic Cu content of about 0.26 vol % In the compoilte, a relative increase of 94% In real permittivity was obtained. No Cu-induced relaxations were observed in the dielectric spectrum within the studied frequency range of 0.1 Hz to 1 MHz. When related to the amount of conductive nanoparticles, the obtained composites achieve the highest broad spectrum enhancement of permittivity ever reported for a polymer based composite.
A novel method is established for permittivity enhancement of a silicone matrix for dielectric elastomer actuators (DEAs) by molecular level modifications of the elastomer matrix. A push-pull dipole is synthesized to be compatible with the silicone crosslinking chemistry, allowing for direct grafting to the crosslinker molecules in a one-step film formation process. This method prevents agglomeration and yields elastomer films that are homogeneous down to the molecular level. The dipole-to-silicone network grafting reaction is studied by FTIR. The chemical, thermal, mechanical and electrical properties of films with dipole contents ranging from 0 wt% to 13.4 wt% were thoroughly characterized. The grafting of dipoles modifies the relative permittivity and the stiffness, resulting in the actuation strain at a given electrical field being improved by a factor of six.
The properties of dielectric elastomer actuators can be optimized by modifying the dielectric or mechanical properties of the dielectric elastomer. This paper presents the simultaneous control of both dielectric and mechanical properties, in a silicone elastomer network comprising cross-linker, chains and grafted molecular dipoles. Chains with two different molecular weights were each combined with varying amounts of grafted dipole. Chemical and physical characterization showed that networks with stoichiometric control of cross-linking density and permittivity were obtained, and that longer chain lengths resulted in higher electrical field response due to the reduction in cross-linking density and correspondingly in mechanical stiffness. Both actuation sensitivities were enhanced by 6.3 and 4.6 times for the short and long chain matrix material, respectively.
Electroactive polymers can be used for actuators with many desirable features, including high electromechanical energy density, low weight, compactness, direct voltage control, and complete silence during actuation. These features may enable personalized robotics with much higher ability to delicately manipulate their surroundings than can be achieved with currently available actuators; however, much work is still necessary to enhance the electroactive materials. Electric field-driven actuator materials are improved by an increase in permittivity and by a reduction in stiffness. Here, a synergistic enhancement method based on a macromolecular plasticizing filler molecule with a combination of both high dipole moment and compatibilizer moieties, synthesized to simultaneously ensure improvement of electromechanical properties and compatibility with the host matrix is presented. Measurements show an 85% increase in permittivity combined with 290% reduction in mechanical stiffness. NMR measurements confirm the structure of the filler while DSC measurements confirm that it is compatible with the host matrix at all the mixture ratios investigated. Actuation strain measurements in the pure shear configuration display an increase in sensitivity to the electrical field of more than 450%, confirming that the filler molecule does not only improve dielectric and mechanical properties, it also leads to a synergistic enhancement of actuation properties by simple means.
Dielectric elastomer actuators (DEAs) draw their function from their dielectric and mechanical properties. The paper describes the fabrication and various properties of molecularly grafted silicone elastomer films. This was achieved by addition of high-dipole molecular co-substituents to off-the-shelf silicone elastomer kits, Elastosil RT 625 and Sylgard 184 by Wacker and Dow Corning, respectively. Strong push-pull dipoles were chemically grafted to both polymer networks during a one step film formation process. All manufactured films were characterized using (13) C-NMR and FT-IR spectroscopy, confirming a successful attachment of the dipoles to the silicone network. Differential scanning calorimetry (DSC) results showed that grafted dipoles were distributed homogeneously throughout the material avoiding the formation of nano-scale aggregates. The permittivity increased with the amount of dipole at all frequencies, while the Young's modulus and electrical breakdown strength were reduced. Actuation strain measurements in the pure shear configuration independently confirmed the increase in electromechanical sensitivity. The ability to enhance electromechanical properties of off-the-shelf materials could strongly expand the range of actuator properties available to researchers and end-users.
Soft, physically crosslinking, block copolymer elastomers were filled with surface-treated nanoparticles, in order to evaluate the possibility for improvement of their properties when used as soft dielectric actuators. The nanoparticles led to improvements in dielectric properties, however they also reinforced the elastomer matrix. Comparing dielectric spectra of composites with untreated and surface-treated particles showed a measurable influence of the surface on the dielectric loss behaviour for high filler amounts, strongly indicating an improved host-guest interaction for the surface-treated particles. Breakdown strength was measured using a test bench and was found to be in good agreement with the results from the actuation measurements. Actuation responses predicted by a model for prestrained actuators agreed well with measurements up to a filler amount of 20%(vol). Strong improvements in actuation behaviour were observed, with an optimum near 15%(vol) nanoparticles, corresponding to a reduction in electrical field of 27% for identical actuation strains. The use of physically crosslinking elastomer ensured the mechanical properties of the matrix elastomer were unchanged by nanoparticles effecting the crosslinking reaction, contrary to similar experiments performed with chemically crosslinking elastomers. This allows for a firm conclusion about the positive effects of surface-treated nanoparticles on actuation behavior.
Block copolymer elastomer conductors (BEC) are mixtures of block copolymers grafted with conducting polymers, which are found to support very large strains, while retaining a high level of conductivity. These novel materials may find use in stretchable electronics. The use of BEC is demonstrated in a capacitive strain sensor and in an artificial muscle of the dielectric elastomer actuator type, supporting more than 100% actuation strain and capacity strain sensitivity up to 300%.
This paper reports a new way to produce a rotation motion actuated by dielectric elastomer actuators. Two specific electrode designs have been developed and the rotation of the actuator centers has been demonstrated and measured. At low strains, the rotation shows a nearly quadratic dependence with the voltage. This behavior was used to compare the performances between the two proposed designs. Among the tested configurations, a maximal rotation of 10 degrees was achieved.