Refine
Has Fulltext
- no (16)
Year of publication
Document Type
- Article (16) (remove)
Language
- English (16)
Is part of the Bibliography
- yes (16) (remove)
Keywords
- HRTEM (3)
- Maltose-modified poly(ethyleneimine) (2)
- SERS (2)
- nanotriangles (2)
- AOT (1)
- Anisotropic gold nanoplatelets (1)
- Biomineralization (1)
- Bone repair material (1)
- Calcium phosphates (1)
- DNA complexation (1)
- DNA polyplexes (1)
- Field flow fractionation (1)
- Gold cluster (1)
- Gold nanoparticles (1)
- Gold triangles (1)
- Hexagons and nanorods (1)
- L-Cysteine (1)
- LSPR (1)
- Magnetite-gold nanoparticles (1)
- Maltose-modified PEI (1)
- Microemulsion (1)
- Microemulsions (1)
- Morphology (1)
- Nanocrystal growth (1)
- Nanotriangle stacking and welding (1)
- Percolation (1)
- Polyampholytes (1)
- Polymer capped gold nanoparticles (1)
- Polyplexes (1)
- SEM (1)
- Satellite hybrid (1)
- Superparamagnetic magnetite (1)
- Supramolecular ball structure (1)
- TEM (1)
- Templated self-assembly (1)
- Tube-like template phase (1)
- Tubular network structure (1)
- UV-Vis-NIR (1)
- Winsor phases (1)
- catanionic surfactant bilayer (1)
- catanionic vesicles (1)
- crystal growth (1)
- gold cluster (1)
- gold nanoflowers (1)
- gold nanostructures (1)
- gold nanotriangles (1)
- hyaluronic acid (1)
- monolayer formation (1)
- mu-DSC (1)
- nanoflowers (1)
- nanoparticles (1)
- nanostructures (1)
- optical-properties (1)
- sers (1)
- size (1)
- ultrafast (1)
- undulated nanoplatelets (1)
- wavelength (1)
Institute
By adding hyaluronic acid (HA) to dioctyl sodium sulfosuccinate (AOT)-stabilized gold nanotriangles (AuNTs) with an average thickness of 7.5 +/- 1 nm and an edge length of about 175 +/- 17 nm, the AOT bilayer is replaced by a polymeric HA-layer leading to biocompatible nanoplatelets. The subsequent reduction process of tetrachloroauric acid in the HA-shell surrounding the AuNTs leads to the formation of spherical gold nanoparticles on the platelet surface. With increasing tetrachloroauric acid concentration, the decoration with gold nanoparticles can be tuned. SAXS measurements reveal an increase of the platelet thickness up to around 14.5 nm, twice the initial value of bare AuNTs. HRTEM micrographs show welding phenomena between densely packed particles on the platelet surface, leading to a crumble formation while preserving the original crystal structure. Crumbles crystallized on top of the platelets enhance the Raman signal by a factor of around 20, and intensify the plasmon-driven dimerization of 4-nitrothiophenol (4-NTP) to 4,4 '-dimercaptoazobenzene in a yield of up to 50 %. The resulting crumbled nanotriangles, with a biopolymer shell and the absorption maximum in the second window for in vivo imaging, are promising candidates for biomedical sensing.
This work describes the synthesis of hybrid particles of gold nanotriangles (AuNTs) with magnetite nanoparticles (MNPs) by using 1-mercaptopropyl-3-trimethoxysilan (MPTMS) and L-cysteine as linker molecules. Due to the combination of superparamagnetic properties of MNPs with optical properties of the AuNTs, nanoplatelet-satellite hybrid nanostructures with combined features become available. By using MPTMS with silan groups as linker molecule a magnetic "cloud" with embedded AuNTs can be separated. In presence of L-cysteine as linker molecule at pH > pH(iso) a more unordered aggregate structure of MNPs is obtained due to the dimerization of the L-cysteine. At pH < pH(iso) water soluble positively charged AuNTs with satellite MNPs can be synthesized. The time-dependent loading with MNP satellites under release of the extinction and magnetization offer a hybrid material, which is of special relevance for biomedical applications and plasmonic catalysis.
Hypothesis: Bimetallic magnetite-gold nanostructures are interesting candidates to combine and enhance individual properties of each metal element in catalytic and analytical applications. Microemulsions have been employed in templated synthesis of nanoparticles, and their combination with different types of nanoparticles can further mediate interactions at the water-oil interface, providing new forms of hybrid nanostructures.
Experiments: Reverse water-in-oil microemulsions of droplet sizes below 50 nm were prepared from ternary mixtures of Aerosol-OT (AOT) as surfactant, incorporating 4 nm sized superparamagnetic nanoparticles (MNPs) to the hexane-pentanol oil phase and 5 nmsized polyethyleneimine-stabilized gold nanoparticles (Au(PEI)-NPs) to the water phase. The resulting isotropic L-2 phase, Winsor phases and organized nanostructures were investigated using conductometry, calorimetry, UV-Vis spectroscopy, cryoSEM and HRTEM.
Findings: Droplet-droplet interactions, morphology and surfactant film properties of AOT microemulsions could be modulated in different ways by the presence of the different nanoparticles from each liquid phase. Additionally, phase separation into Winsor phases allows the formation upon solvent evaporation of films with bimetallic heterostructures on the micrometer scale. This demonstrates a new way of nanoparticle templated assembly at liquid interfaces by assisted interactions between microemulsions and nanoparticles, as a promising strategy to obtain thin films of small, isotropic nanoparticles with hierarchical ordering.
Negatively charged ultraflat gold nanotriangles (AuNTs) stabilized by the anionic surfactant dioctyl sodium sulfosuccinate (AOT) were reloaded with the cationic surfactant benzylhexadecyldimethylammonium chloride (BDAC). Because of the spontaneous formation of a catanionic AOT micelle/BDAC bilayer onto the surface of the reloaded AuNTs, a reduction of Ag+ ions leads to the formation of spherical silver nanoparticles (AgNPs). With increasing concentration of AgNPs on the AuNTs, the localized surface plasmon resonance (LSPR) is shifted stepwise from 1300 to 800 nm. The tunable LSPR enables to shift the extinction maximum to the wavelength of the excitation laser of the Raman microscope at 785 nm. Surface-enhanced Raman scattering (SERS) experiments performed under resonance conditions show an SERS enhancement factor of the analyte molecule rhodamine RG6 of 5.1 X 10(5), which can be related to the silver hot spots at the periphery of the undulated gold nanoplatelets.
Negatively charged flat gold nanotriangles, formed in a vesicular template phase and separated by an AOT-micelle-based depletion flocculation, were reloaded by adding a cationic polyelectrolyte, that is, a hyperbranched polyethylenimine (PEI). Heating the system to 100 degrees C in the presence of a gold chloride solution, the reduction process leads to the formation of gold nanoparticles inside the polymer shell surrounding the nanoplatelets. The gold nanoparticle formation is investigated by UV-vis spectroscopy, small-angle X-ray scattering, and dynamic light scattering measurements in combination with transmission electron microscopy. Spontaneously formed gold clusters in the hyperbranched PEI shell with an absorption maximum at 350 nm grow on the surface of the nanotriangles as hemispherical particles with diameters of similar to 6 nm. High-resolution micrographs show that the hemispherical gold particles are crystallized onto the {111} facets on the bottom and top of the platelet as well as on the edges without a grain boundary. Undulated gold nanoplatelet superstructures with special properties become available, which show a significantly modified performance in SERS-detected photocatalysis regarding both reactivity and enhancement factor.
Catanionic vesicles spontaneously formed by mixing the anionic surfactant bis(2-ethylhexyl)sulfosuccinate sodium salt with the cationic surfactant cetyltrimethylammonium bromide were used as a reducing medium to produce gold clusters, which are embedded and well-ordered into the template phase. The gold clusters can be used as seeds in the growth process that follows by adding ascorbic acid as a mild reducing component. When the ascorbic acid was added very slowly in an ice bath round-edged gold nanoflowers were produced. When the same experiments were performed at room temperature in the presence of Ag+ ions, sharp-edged nanoflowers could be synthesized. The mechanism of nanoparticle formation can be understood to be a non-diffusion-limited Ostwald ripening process of preordered gold nanoparticles embedded in catanionic vesicle fragments. Surface-enhanced Raman scattering experiments show an excellent enhancement factor of 1.7 . 10(5) for the nanoflowers deposited on a silicon wafer.
Polyplexes, composed of Salmon DNA and very small gold nanoparticles embedded into a dendritic glycopolymer architecture of sugar-modified poly(ethyleneimine) (PEI-Mal) with a molar mass of about 25,000 g/mol, were characterized by dynamic light scattering (DLS), zeta potential measurements, micro differential scanning calorimetry (mu-DSC) and transmission electron microscopy (TEM). The PEI-Mal-entrapped gold nanoparticles of about 2 nm in diameter influence the polyplex formation of the hyperbranched PEI containing bulky maltose, and in consequence the DNA is more compactized in the inner part of spherical polyplex particles of about 150 nm in diameter. The resulting more compact core shell polyplex particles with embedded gold nanoparticles in the outer polymer shell will be used as components in forthcoming gene delivery experiments. (C) 2017 Elsevier B.V. All rights reserved.
The aim of this study was to develop a one-step synthesis of gold nanotriangles (NTs) in the presence of mixed phospholipid vesicles followed by a separation process to isolate purified NTs. Negatively charged vesicles containing AOT and phospholipids, in the absence and presence of additional reducing agents (polyampholytes, polyanions or low molecular weight compounds), were used as a template phase to form anisotropic gold nanoparticles. Upon addition of the gold chloride solution, the nucleation process is initiated and both types of particles, i.e., isotropic spherical and anisotropic gold nanotriangles, are formed simultaneously. As it was not possible to produce monodisperse nanotriangles with such a one-step procedure, the anisotropic nanoparticles needed to be separated from the spherical ones. Therefore, a new type of separation procedure using combined polyelectrolyte/micelle depletion flocculation was successfully applied. As a result of the different purification steps, a green colored aqueous dispersion was obtained containing highly purified, well-defined negatively charged flat nanocrystals with a platelet thickness of 10 nm and an edge length of about 175 nm. The NTs produce promising results in surface-enhanced Raman scattering.
Polyplexes between Salmon DNA and non-modified hyperbranched poly(ethyleneimines) of varying molar mass, i.e., PEI(5 k) with 5000 g/mol and PEI(25 k) with 25,000 g/mol, and modified PEI(5 k) with maltose units (PEI-Mal) were investigated in dependence on the molar N/P ratio by using dynamic light scattering (DLS), zeta potential measurements, micro differential scanning calorimetry (mu-DSC), scanning-transmission electron microscopy (STEM), and cryo-scanning electron microscopy (cryo-SEM). A reloading of the polyplexes can be observed by adding the unmodified PEI samples of different molar mass. In excess of PEI a morphological transition from core-shell particles (at N/P 8) to loosely packed onion-like polyplexes (at N/P 40) is observed. The shift of the DSC melting peak from 88 degrees C to 76 degrees C indicates a destabilization of the DNA double helix due to the complexation with the unmodified PEI. Experiments with the maltose-modified PEI show a reloading already at a lower N/P ratio. Due to the presence of the sugar units in the periphery of the polycation electrostatic interactions between DNA become weaker, but cooperative H-bonding forces are reinforced. The resulting less-toxic, more compact polyplexes in excess of the PEI-Mal with two melting points and well distributed DNA segments are of special interest for extended gene delivery experiments. (C) 2015 Elsevier B.V. All rights reserved.
This paper focused on the synthesis of triangular nanoplatelets in the presence of a tubular network structure. The tubular network structure is formed by adding a strongly alternating polyampholyte, i.e., PalPhBisCarb, to a mixed vesicle system with a negatively charged bilayer containing phosphatidylcholin and AOT. Using the tubular network as a reducing agent in a one-step procedure, triangular and hexagonal nanoplatelets are formed. One can show that the nanoplatelet yield is enhanced by increasing the temperature and decreasing the reaction time. The platelet edge length can be decreased by heating the system up to 100 A degrees C. Due to specific interactions between PalPhBisCarb and the AOT/phospholipid bilayer, stacking and welding effects lead to the formation of ordered platelet structures. The reaction pathway to flat gold nanotriangles is discussed with regard to the twin plane growth model of gold nanoplates.