Refine
Has Fulltext
- no (15)
Document Type
- Article (15) (remove)
Language
- English (15)
Is part of the Bibliography
- yes (15)
Keywords
- electrospinning (3)
- biomaterials (2)
- microstructure (2)
- migration (2)
- poly(ether imide) (2)
- shape-memory polymers (2)
- Chondrocytes (1)
- Endothelial cells (1)
- Endothelialization (1)
- FAK-MAPK (1)
Institute
- Institut für Biochemie und Biologie (15) (remove)
The variation of the molecular architecture of multiblock copolymers has enabled the introduction of functional behaviour and the control of key mechanical properties. In the current study, we explore the synergistic relationship of two structural components in a shape-memory material formed of a multiblock copolymer with crystallizable poly(epsilon-caprolactone) and crystallizable polyfoligo(3S-iso-butylmorpholine-2,5-dione) segments (PCL-PIBMD). The thermal and structural properties of PCL-PIBMD films were compared with PCI.-PU and PMMD-PU investigated by means of DSC, SAXS and WARS measurements. The shape-memory properties were quantified by cyclic, thermomechanical tensile tests, where deformation strains up to 900% were applied for programming PCL-PIBMD films at 50 degrees C. Toluene vapor treatment experiments demonstrated that the temporary shape was fixed mainly by glassy PIBMD domains at strains lower than 600% with the PCL contribution to fixation increasing to 42 +/- 2% at programming strains of 900% This study into the shape-memory mechanism of PCL-PIBMD provides insight into the structure function relation in multiblock copolymers with both crystallizable and glassy switching segments.
Degradable polymers with a tailorable degradation rate might be promising candidate materials for biomaterial-based cartilage repair. In view of the poor intrinsic healing capability of cartilage, implantation of autologous chondrocytes seeded on a biocompatible slow degrading polymer might be an encouraging approach to improve cartilage repair in the future. This study was undertaken to test if the fiber orientation (random versus aligned) of two different degradable polymers and a polymer intended for long term applications could influence primary articular chondrocytes growth and ultrastructure.
A degradable copoly(ether) esterurethane (PDC) was synthesized via co-condensation of poly(p-dioxanone) diol and poly(epsilon-caprolactone) diol using an aliphatic diisocyanate as linker. Poly(p-dioxanone) (PPDO) was applied as commercially available degradable polymer, while polyetherimide (PEI) was chosen as biomaterial enabling surface functionalization. The fibrous scaffolds of PDC and PPDO were obtained by electrospinning using 1,1,1,3,3,3 hexafluoro-2-propanol (HFP), while for PEI dimethyl acetamide (DMAc) was applied as solvent. Primary porcine articular chondrocytes were seeded at different cell densities on the fibrous polymer scaffolds and analyzed for viability (fluorescein diacetate/ethidiumbromide staining), for type II collagen synthesis (immunolabelling), ultrastructure and orientation on the fibers (SEM: scanning electron microscopy).
Vital chondrocytes adhered on all electrospun scaffolds irrespective of random and aligned topologies. In addition, the chondrocytes produced the cartilage-specific type II collagen on all tested polymer topologies suggesting their differentiated functions. SEM revealed an almost flattened chondrocytes shape on scaffolds with random fiber orientation: whereby chondrocytes growth remained mainly restricted to the scaffold surface. On aligned fibers the chondrocytes exhibited a more spindle-shaped morphology with rougher cell surfaces but only a minority of the cells aligned according to the fibers. As a next step the reduction of the fiber diameter of electrospun scaffolds should be addressed as an important parameter to mimic cartilage ECM structure.
Shape-memory properties of polyetherurethane foams prepared by thermally induced phase separation
(2012)
In this study, we report the preparation of two structurally different shape-memory polymer foams by thermally induced phase separation (TIPS) from amorphous polyetherurethanes. Foams with either a homogeneous, monomodal, or with a hierarchically structured, bimodal, pore size distribution are obtained by adoption of the cooling protocol. The shape-memory properties have been investigated for both foam structures by cyclic, thermomechanical experiments, while the morphological changes on the micro scale (pore level) have been compared to the macro scale by an in situ micro compression device experiment. The results show that the hierarchically structured foam achieves higher shape-recovery rates and a higher total recovery as compared to the homogeneous foam, which is due to an increased energy storage capability by micro scale bending of the hierarchically structured foam compared to pure compression of the homogeneous foam.
Open porous foams with identical foam density but different pore-size distributions (bimodal or monomodal) are prepared from a shape-memory polyetherurethane (PEU) by thermally induced phase separation. The shape-memory effect of the two PEU foams is explored by cyclic thermomechanical compression tests and microstructural analysis. The obtained results reveal that the PEU foam with a bimodal pore-size distribution exhibits an increased shape-recovery under stress-free conditions, both on the macro- (foam level) as well as the microscale (pore level). While bimodal pore-size distributions induce microscale bending during compression, buckling occurs in foams with monomodal pore-size distributions, leading to both a reduced and delayed shape recovery.
Soft actuator performance can be tuned by chemistry or mechanical manipulation, but this adjustability is limited especially in view of their growing technological relevance. Inspired from textile engineering, we designed and fabricated fiber mesh actuators and introduced new features like anisotropic behavior and soft-tissue like elastic deformability. Design criteria for the meshes are the formation of fiber bundles, the angle between fiber bundles in different stacked layers and covalent crosslinks forming within and between fibers at their interfacial contact areas. Through crosslinking the interfiber bond strength increased from a bond transmitting neither axial nor rotational loads (pin joint) to a bond strength capable of both (welded joint). For non-linear elastic stiffening, stacked fiber bundles with four embracing fibers were created forming microstructural rhombus shapes. Loading the rhombus diagonally allowed generation of “soft tissue”-like mechanics. By adjustment of stacking angles, the point of strong increase in stress is tuned. While the highest stresses are observed in aligned and crosslinked fiber mats along the direction of the fiber, the strongest shape-memory actuation behavior is found in randomly oriented fiber mats. Fiber mesh actuators controlled by temperature are of high significance as soft robot skins and as for active patches supporting tissue regeneration.
Cardiovascular metallic stents established in clinical application are typically coated by a thin polymeric layer on the stent struts to improve hemocompatibility, whereby often a drug is added to the coating to inhibit neointimal hyperplasia. Besides such thin film coatings recently nano/microfiber coated stents are investigated, whereby the fibrous coating was applied circumferential on stents. Here, we explored whether a thin fibrous encasement of metallic stents with preferentially longitudinal aligned fibers and different local fiber densities can be achieved by electrospinning. An elastic degradable copolyetheresterurethane, which is reported to selectively enhance the adhesion of endothelial cells, while simultaneously rejecting smooth muscle cells, was utilized for stent coating. The fibrous stent encasements were microscopically assessed regarding their single fiber diameters, fiber covered area and fiber alignment at three characteristic stent regions before and after stent expansion. Stent coatings with thicknesses in the range from 30 to 50 mu m were achieved via electrospinning with 1,1,1,3,3,3-hexafluoro-2-propanol (HFP)-based polymer solution, while a mixture of HFP and formic acid as solvent resulted in encasements with a thickness below 5 mu m comprising submicron sized single fibers. All polymeric encasements were mechanically stable during expansion, whereby the fibers deposited on the struts remained their position. The observed changes in fiber density and diameter indicated diverse local deformation mechanisms of the microfibers at the different regions between the struts. Based on these results it can be anticipated that the presented fibrous encasement of stents might be a promising alternative to stents with polymeric strut coatings releasing anti-proliferative drugs. Copyright (c) 2015 John Wiley & Sons, Ltd.
Polymers exhibiting cell-selective effects represent an extensive research field with high relevance for biomedical applications e.g. in the cardiovascular field supporting re-endothelialization while suppressing smooth muscle cell overgrowth. Such an endothelial cell-selective effect could be recently demonstrated for a copolyetheresterurethane (PDC) containing biodegradable poly(p-dioxanone) and poly(epsilon-caprolactone) segments, which selectively enhanced the adhesion of human umbilical vein endothelial cells (HUVEC) while suppressing the attachment of smooth muscle cells (SMC).
In this study we investigated the influence of the fibre orientation (random and aligned) and fibre diameter (2 mu m and 500 nm) of electrospun PDC scaffolds on the adhesion, proliferation and apoptosis of HUVEC and SMC.
Adhesion, viability and proliferation of HUVEC was diminished when the fibre diameter was reduced to a submicron scale, while the orientation of the microfibres did only slightly influence the cellular behaviour. In contrast, a submicron fibre diameter improved SMC viability. In conclusion, PDC scaffolds with micron-sized single fibres could be promising candidate materials for cell-selective stent coatings.
Microobjects with programmable mechanical functionality are highly desirable for the creation of flexible electronics, sensors, and microfluidic systems, where fabrication/programming and quantification methods are required to fully control and implement dynamic physical behavior. Here, programmable microcuboids with defined geometries are prepared by a template-based method from crosslinked poly[ethylene-co-(vinyl acetate)] elastomers. These microobjects could be programmed to exhibit a temperature-memory effect or a shape-memory polymer actuation capability. Switching temperaturesT(sw)during shape recovery of 55 +/- 2, 68 +/- 2, 80 +/- 2, and 86 +/- 2 degrees C are achieved by tuning programming temperatures to 55, 70, 85, and 100 degrees C, respectively. Actuation is achieved with a reversible strain of 2.9 +/- 0.2% to 6.7 +/- 0.1%, whereby greater compression ratios and higher separation temperatures induce a more pronounced actuation. Micro-geometry change is quantified using optical microscopy and atomic force microscopy. The realization and quantification of microparticles, capable of a tunable temperature responsive shape-change or reversible actuation, represent a key development in the creation of soft microscale devices for drug delivery or microrobotics.
Controlling mesenchymal stem cells (MSCs) behavior is necessary to fully exploit their therapeutic potential. Various approaches are employed to effectively influence the migration capacity of MSCs. Here, topographic microstructures with different microscale roughness were created on polystyrene (PS) culture vessel surfaces as a feasible physical preconditioning strategy to modulate MSC migration. By analyzing trajectories of cells migrating after reseeding, we demonstrated that the mobilization velocity of human adipose derived mesenchymal stem cells (hADSCs) could be promoted by and persisted after brief preconditioning with the appropriate microtopography. Moreover, the elevated activation levels of focal adhesion kinase (FAK) and mitogen-activated protein kinase (MAPK) in hADSCs were also observed during and after the preconditioning process. These findings underline the potential enhancement of in vivo therapeutic efficacy in regenerative medicine via transplantation of topographic microstructure preconditioned stem cells.
BACKGROUND: The formation of a functionally-confluent endothelial cell (EC) monolayer affords proliferation of EC, which only happens in case of appropriate migratory activity. AIM OF THE STUDY: The migratory pathway of human umbilical endothelial cells (HUVEC) was investigated on different polymeric substrates. MATERIAL AND METHODS: Surface characterization of the polymers was performed by contact angle measurements and atomic force microscopy under wet conditions. 30,000 HUVEC per well were seeded on polytetrafluoroethylene (PTFE) (theta(adv) = 119 degrees +/- 2 degrees), on low-attachment plate LAP (theta(adv) = 28 degrees +/- 2 degrees) and on polystyrene based tissue culture plates (TCP, theta(adv) = 22 degrees +/- 1 degrees). HUVEC tracks (trajectories) were recorded by time lapse microscopy and the euclidean distance (straight line between starting and end point), the total distance and the velocities of HUVEC not leaving the vision field were determined. RESULTS: On PTFE, 42 HUVEC were in the vision field directly after seeding. The mean length of single migration steps (SML) was 6.1 +/- 5.2 mu m, the mean velocity (MV) 0.40 +/- 0.3 mu m.min(-1) and the complete length of the trajectory (LT) was 710 +/- 440 mu m. On TCP 82 HUVEC were in the vision field subsequent to seeding. The LT was 840 +/- 550 mu m, the SML 6.1 +/- 5.2 mu m and the MV 0.44 +/- 0.3 mu m.min(-1). The trajectories on LAP differed significantly in respect to SML (2.4 +/- 3.9 mu m, p <0.05), the MV (0.16 +/- 0.3 mu m.min(-1), p <0.05) and the LT (410 +/- 300 mu m, p <0.05), compared to PTFE and TCP. Solely on TCP a nearly confluent EC monolayer developed after three days. While on TCP diffuse signals of vinculin were found over the whole basal cell surface organizing the binding of the cells by focal adhesions, on PTFE vinculin was merely arranged at the cell rims, and on the hydrophilic material (LAP) no focal adhesions were found. CONCLUSION: The study revealed that the wettability of polymers affected not only the initial adherence but also the migration of EC, which is of importance for the proliferation and ultimately the endothelialization of polymer-based biomaterials.