Nanoporous microparticles prepared from poly(ether imide) (PEI) are discussed as candidate adsorber materials for the removal of uremic toxins during apheresis. Polymers exhibiting such porosity can induce the formation of micro-gas/air pockets when exposed to fluids. Such air presenting material surfaces are reported to induce platelet activation and thrombus formation. Physical or chemical treatments prior to implantation are discussed to reduce the formation of such gas nuclei. Here, we report about the influence of different rewetting procedures - as chemical treatments with solvents on the thrombogenicity of hydrophobic PEI microparticles and PEI microparticles hydrophilized by covalent attachment of poly(vinyl pyrrolidone) (PVP) of two different chain lengths. <br /> Autoclaved dry PEI particles of all types with a diameter range of 200 - 250 mu m and a porosity of about 84%+/- 2% were either rewetted directly with phosphate buffered saline (24 h) or after immersion in an ethanol-series. Thrombogenicity of the particles was studied in vitro upon contact with human sodium citrated whole blood for 60 min at 5 rpm vertical rotation. Numbers of non-adherent platelets were quantified, and adhesion of blood cells was qualitatively analyzed by bright field microscopy. Platelet activation (percentage of CD62P positive platelets and amounts of soluble P-Selectin) and platelet function (PFA100 closure times) were analysed. <br /> Retention of blood platelets on the particles was similar for all particle types and both rewetting procedures. Non-adherent platelets were less activated after contact with ethanol-treated particles of all types compared to those rewetted with phosphate buffered saline as assessed by a reduced number of CD62P-positive platelets and reduced amounts of secreted P-Selectin (P < 0.05 each). Interestingly, the hydrophilic surfaces significantly increased the number of activated platelets compared to hydrophobic PEI regardless of the rewetting agent. This suggests that, apart from wettability, other material properties might be more important to regulate platelet activation. PFA100 closure times were reduced and within the reference ranges in the ethanol group, however, significantly increased in the saline group. No substantial difference was detected between the tested surface modifications. In summary, rewetting with ethanol resulted in a reduced thrombogenicity of all studied microparticles regardless of their wettability, most likely resulting from the evacuation of air from the nanoporous particles.
Insufficient endothelialization of cardiovascular grafts is a major hurdle in vascular surgery and regenerative medicine, bearing a risk for early graft thrombosis. Neither of the numerous strategies pursued to solve these problems were conclusive. Endothelialization is regulated by the endothelial basement membrane (EBM), a highly specialized part of the vascular extracellular matrix. Thus, a detailed understanding of the structure-function interrelations of the EBM components is fundamental for designing biomimetic materials aiming to mimic EBM functions. In this review, a detailed description of the structure and functions of the EBM are provided, including the luminal and abluminal interactions with adjacent cell types, such as vascular smooth muscle cells. Moreover, in vivo as well as in vitro strategies to build or renew EBM are summarized and critically discussed. The spectrum of methods includes vessel decellularization and implant biofunctionalization strategies as well as tissue engineering-based approaches and bioprinting. Finally, the limitations of these methods are highlighted, and future directions are suggested to help improve future design strategies for EBM-inspired materials in the cardiovascular field.
High crystallization rate and thermomechanical stability make polylactide stereocomplexes effective nanosized physical netpoints. Here, we address the need for soft, form-stable degradable elastomers for medical applications by designing such blends from (co)polyesters, whose mechanical properties are ruled by their nanodimensional architecture and which are applied as single components in implants. By careful controlling of the copolymer composition and sequence structure of poly[(L-lactide)-co-(epsilon-caprolactone)], it is possible to prepare hyperelastic polymer blends formed through stereocomplexation by adding poly(D-lactide) (PDLA). Low glass transition temperature T-g <= 0 degrees C of the mixed amorphous phase contributes to the low Young's modulus E. The formation of stereocomplexes is shown in DSC by melting transitions T-m > 190 degrees C and in WAXS by distinct scattering maxima at 2 theta = 12 degrees and 21 degrees. Tensile testing demonstrated that the blends are soft (E = 12-80 MPa) and show an excellent hyperelastic recovery R-rec = 66-85% while having high elongation at break epsilon(b) up to >1000%. These properties of the blends are attained only when the copolymer has 56-62 wt% lactide content, a weight average molar mass >140 kg center dot mol(-1), and number average lactide sequence length >= 4.8, while the blend is formed with a content of 5-10 wt% of PDLA. The devised strategy to identify a suitable copolymer for stereocomplexation and blend formation is transferable to further polymer systems and will support the development of thermoplastic elastomers suitable for medical applications.