Refine
Has Fulltext
- no (23)
Year of publication
Document Type
- Article (23) (remove)
Language
- English (23)
Is part of the Bibliography
- yes (23) (remove)
Keywords
- cyclic voltammetry (2)
- hydrogels (2)
- polymers (2)
- Block copolymer (1)
- DFB lasers (1)
- LCST (1)
- RAFT polymerization (1)
- Responsive polymer (1)
- Schizophrenic self-assembly (1)
- Sulfobetaine methacrylate (1)
Institute
The functionalization of polyelectrolyte multilayers often implies the use of bulky functional fragments, attached to a standard polyelectrolyte matrix. Despite of the high density of non-charged, often hydrophobic substituents, regular film growth by sequential adsorption proceeds easily when an appropriate polyelectrolyte counter ion is chosen. However, the functional fragments may cluster or aggregate. This complication is particularly evident when using chromophores and fluorophores as bulky pendant groups. Attention has to be paid to this phenomenon for the design of functional polyelectrolyte films, as aggregation may modify crucially the properties. The use of charged spacer groups does not necessarily suppress the aggregation of functional side groups. Still, clustering and aggregation depend on the detailed system employed, and are not obligatory. In the case of cationic poly(acrylamide)s labeled with naphthalene and pyrene fluorophores, for instance, the polymers form intramolecular hydrophobic associates in solution, as indicated by strong excimer formation. But the polymers can undergo a conformational rearrangement upon adsorption so that they are decoiled in the adsorbed films. Analogous observations are made for polyanions bearing mesogenic biphenyls fragments. In contrast, polycations functionalized with the dye coumarin 343 show little aggregation in solution, but a marked aggregation in the ESA films
Tuning the thickness of polymer brushes grafted from nonlinearly growing multilayer assemblies
(2009)
A new versatile method for tuning the thickness of surface-tethered polymer brushes is introduced. It is based on the combination of polyelectrolyte multilayer deposition and surface-initiated atom transfer radical polymerization. To control the thickness of the brushes, the nonlinear growth of certain polyelectrolyte multilayer systems is exploited. The method is demonstrated to work with different polyelectrolytes and different monomers. The relevance for applications is demonstrated by cell adhesion experiments oil grafted thermoresponsive polymer layers with varying thickness.
Recently, we introduced a thermoresponsive copolymer that consists of oligo(ethylene glycol) methacrylate (OEGMA) and 2-(2- methoxyethoxy) ethyl methacrylate (MEO(2)MA). The polymer exhibited an LCST at 35 degrees C in PBS buffer and was anchored onto gold substrates using disulfide polymerisation initiators. It allows the noninvasive detachment of adherent cells from their substrate. As the mechanisms that determine the interaction of cells with such polymers are not well understood, we employed Total Internal Reflection Fluorescence (TIRF) microscopy in order to monitor the detachment process of cells of two different types. We identified contact area and average cell-substrate distance as crucial parameters for the evaluation of the detachment process. The sensitivity of TIRF microscopy allowed us to correlate the specific adhesion pattern of MCF-7 breast cancer cells with the morphology of cell deposits that may serve as fingerprints for a nondestructive characterisation of live cells.
Smart bioactive surfaces
(2010)
The purpose of this highlight is to define the emerging field of bioactive surfaces. In recent years, various types of synthetic materials capable of "communicating'' with biological objects such as nucleic acids, proteins, polysaccharides, viruses, bacteria or living cells have been described in the literature. This novel area of research certainly goes beyond the traditional field of smart materials and includes different types of sophisticated interactions with biological entities, such as reversible adhesion, conformational control, biologically-triggered release and selective permeation. These novel materials may be 2D planar surfaces as well as colloidal objects or 3D scaffolds. Overall, they show great promise for numerous applications in biosciences and biotechnology. For instance, practical applications of bioactive surfaces in the fields of bioseparation, cell engineering, biochips and stem-cell differentiation are briefly discussed herein.
A thermosensitive statistical copolymer based on oligo(ethylene glycol) methacrylates incorporating biotin was synthesized by free radical copolymerisation. The influence of added avidin on its thermoresponsive behaviour was investigated. The specific binding of avidin to the biotinylated copolymers provoked a marked increase of the lower critical solution temperature.
Random copolymers of 4-vinylbenzyl tri(oxyethylene) and tetra(oxyethylene) ethers, as well as alternating copolymers of 4-vinylbenzyl methoxytetra(oxyethylene) ether and a series of N-substituted maleimides, were synthesised by conventional free radical polymerisation, reversible addition fragmentation chain transfer (RAFT) and atom transfer radical polymerisation (ATRP). Their thermosensitive behaviour in aqueous solution was studied by turbidimetry and dynamic light scattering. Depending on the copolymer composition, a LCST type phase transition was observed in water. The transition temperature of the obtained random as well as alternating copolymers could be varied within a broad temperature window. In the case of the random copolymers, transition temperatures could be easily fine-tuned, as they showed a linear dependence on the copolymer composition, and were additionally modified by the nature of the polymer end-groups. Alternating copolymers were extremely versatile for implementing a broad range of variations of the phase transition temperatures. Further, while alternating copolymers derived from 4-vinylbenzyl methoxytetra(oxyethylene) ether and maleimides with small hydrophobic side chains underwent macroscopic phase separation when dissolved in water and heated above their cloud point, the incorporation of maleimides bearing larger hydrophobic substituents resulted in the formation of mesoglobules above the phase transition temperature, with hydrodynamic diameters of less than 100 nm.
Solid surfaces are modified using photo-crosslinkable copolymers based on oligo(ethylene glycol) methacrylate (OEGMA) bearing 2-(4-benzoylphenoxy) ethyl methacrylate (BPEM) as a photosensitive crosslinking unit. Thin films of about 100 nm are formed by spin-coating these a priori highly biocompatible copolymers onto silicon substrates. Subsequent UV-irradiation assures immobilization and crosslinking of the hydrogel films. Their stability is controlled by the number of crosslinker units per chain and the molar mass of the copolymers. The swelling of the hydrogel layers, as investigated by ellipsometry, can be tuned by the crosslinker content in the copolymer. If films are built from the ternary copolymers of OEGMA, BPEM and 2-(2-methoxyethoxy) ethyl methacrylate (MEO(2)MA), the hydrogel films exhibit a swelling/deswelling transition of the lower critical solution temperature (LCST) type. The observed thermally induced hydrogel collapse is fully reversible and the onset temperature of the transition can be tuned at will by the copolymer composition. Different from analogously prepared thermo-responsive hydrogel films of photocrosslinked poly(N-isopropylacrylamide), the swelling-deswelling transition occurs more gradually, but shows no hysteresis.
A water soluble fluorescent polymer as a dual colour sensor for temperature and a specific protein
(2013)
We present two thermoresponsive water soluble copolymers prepared via free radical statistical copolymerization of N-isopropylacrylamide (NIPAm) and of oligo(ethylene glycol) methacrylates (OEGMAs), respectively, with a solvatochromic 7-(diethylamino)-3-carboxy-coumarin (DEAC)-functionalized monomer. In aqueous solutions, the NIPAm-based copolymer exhibits characteristic changes in its fluorescence profile in response to a change in solution temperature as well as to the presence of a specific protein, namely an anti-DEAC antibody. This polymer emits only weakly at low temperatures, but exhibits a marked fluorescence enhancement accompanied by a change in its emission colour when heated above its cloud point. Such drastic changes in the fluorescence and absorbance spectra are observed also upon injection of the anti-DEAC antibody, attributed to the specific binding of the antibody to DEAC moieties. Importantly, protein binding occurs exclusively when the polymer is in the well hydrated state below the cloud point, enabling a temperature control on the molecular recognition event. On the other hand, heating of the polymer-antibody complexes releases a fraction of the bound antibody. In the presence of the DEAC-functionalized monomer in this mixture, the released antibody competitively binds to the monomer and the antibody-free chains of the polymer undergo a more effective collapse and inter-aggregation. In contrast, the emission properties of the OEGMA-based analogous copolymer are rather insensitive to the thermally induced phase transition or to antibody binding. These opposite behaviours underline the need for a carefully tailored molecular design of responsive polymers aimed at specific applications, such as biosensing.