Refine
Document Type
- Doctoral Thesis (28)
- Habilitation Thesis (1)
Is part of the Bibliography
- yes (29)
Keywords
- Nanopartikel (3)
- Salzschmelze-Templating (2)
- magnetic resonance imaging (2)
- perovskite solar cells (2)
- salt melt templating (2)
- Aktuator (1)
- Alkylpyridinium salts (1)
- Alkylpyridinium-Salze (1)
- Antifouling (1)
- Aufkonversion (1)
Institute
- Institut für Chemie (28)
- Extern (4)
- Institut für Physik und Astronomie (1)
We live in an era driven by fossil fuels. The prevailing climate change suggests that we have to significantly reduce greenhouse gas emissions. The only way forward is to use renewable energy sources. Among those, solar energy is a clean, affordable, and sustainable source of energy. It has the potential to satisfy the world’s energy demand in the future. However, there is a need to develop new materials that can make solar energy usable. Photovoltaics (PV) are devices that convert photon energy into electrical energy. The most commonly used solar cells are based on crystalline silicon. However, the fabrication process for silicon solar cells is technologically difficult and costly. Solar cells based on lead halide perovskites (PSCs) have emerged as a new candidate for PV applications since 2009. To date, PSCs have achieved 26% power-conversion-efficiency (PCE) for its single junction, and 33.7% PCE for tandem junction devices. However, there is still room for improvement in overall performance. The main challenge for the commercialization of this technology is the stability of the solar cells under operational conditions. Inorganic perovskite CsPbI3 has attracted researchers’ interest due to its stability at elevated temperatures, however, inorganic perovskites also have associated challenges, e.g. phase stability, larger voltage loss compared to their organic-inorganic hybrid counterparts, and interface energy misalignment. The most efficient inorganic perovskite solar cell is stable for up to a few hundred hours while the most stable device in the field of inorganic PSCs reported so far is at 17% PCE. This suggests the need for improvement of the interfaces for enhanced open circuit voltage (VOC), and optimization of the energy alignment at the interfaces. This dissertation presents the study on interfaces between the perovskite layer and hole transport layer (HTL) for stable CsPbI3 solar cells.
The first part of the thesis presents an investigation of the CsPbI3 film annealing environment and its subsequent effects on the perovskite/HTL interface dynamics. Thin films annealed in dry air were compared with thin films annealed in ambient air. Synchrotron-based hard X-ray spectroscopy (HAXPES) measurements reveal that annealing in ambient air does not have an adverse effect; instead, those samples undergo surface band bending. This surface band modification induces changes in interface charge dynamics and, consequently, an improvement in charge extraction at the interfaces. Further, transient surface photovoltage (tr-SPV) simulations show that air-annealed samples exhibit fewer trap states compared to samples annealed in dry air. Finally, by annealing the CsPbI3 films in ambient air, a PCE of 19.8% and Voc of 1.23 V were achieved for an n-i-p structured device.
Interface engineering has emerged as a strategy to extract the charge and optimize the energy alignment in perovskite solar cells (PSCs). An interface with fewer trap states and energy band levels closer to the selective contact helps to attain improved efficiencies in PSCs. The second part of the thesis presents a design for the CsPbI3/HTM interface. In this work, an interface between CsPbI3 perovskite and its hole selective contact N2,N2,N2′,N2′,N7,N7,N7′,N7′-octakis(4-methoxyphenyl)-9,9′-spirobi[9H-fluorene]-2,2′,7,7′-tetramine(Spiro-OMeTAD), realized by trioctylphosphine oxide (TOPO), a dipole molecule is introduced. On top of a perovskite film well-passivated by n-octyl ammonium Iodide (OAI), it created an upward surface band-bending at the interface byTOPO that optimizes energy level alignment and enhances the extraction of holes from the perovskite layer to the hole transport material. Consequently, a Voc of 1.2 V and high-power conversion efficiency (PCE) of over 19% were achieved for inorganic CsPbI3 perovskite solar cells. In addition, the work also sheds light on the interfacial charge-selectivity and the long-term stability of CsPbI3 perovskite solar cells.
The third part of the thesis extends the previous studies to polymeric poly(3-hexylthiophene-2,5-diyl) (P3HT) as HTL. The CsPbI3/P3HT interface is critical due to high non-radiative recombination. This work presents a CsPbI3/P3HT interface modified with a long-chain alkyl halide molecule, n-hexyl trimethyl ammonium bromide (HTAB). This molecule largely passivates the CsPbI3 perovskite surface and improves the charge extraction across the interface. Consequently, a Voc of over 1.00 V and 14.2% PCE were achieved for CsPbI3 with P3HT as HTM.
Overall the results presented in this dissertation introduce and discuss methods to design and study the interfaces in CsPbI3-based solar cells. This study can pave the way for novel interface designs between CsPbI3 and HTM for charge extraction, efficiency and stability.
Core-shell upconversion nanoparticles - investigation of dopant intermixing and surface modification
(2022)
Frequency upconversion nanoparticles (UCNPs) are inorganic nanocrystals capable to up-convert incident photons of the near-infrared electromagnetic spectrum (NIR) into higher energy photons. These photons are re-emitted in the range of the visible (Vis) and even ultraviolet (UV) light. The frequency upconversion process (UC) is realized with nanocrystals doped with trivalent lanthanoid ions (Ln(III)). The Ln(III) ions provide the electronic (excited) states forming a ladder-like electronic structure for the Ln(III) electrons in the nanocrystals. The absorption of at least two low energy photons by the nanoparticle and the subsequent energy transfer to one Ln(III) ion leads to the promotion of one Ln(III) electron into higher excited electronic states. One high energy photon will be emitted during the radiative relaxation of the electron in the excited state back into the electronic ground state of the Ln(III) ion. The excited state electron is the result of the previous absorption of at least two low energy photons.
The UC process is very interesting in the biological/medical context. Biological samples (like organic tissue, blood, urine, and stool) absorb high-energy photons (UV and blue light) more strongly than low-energy photons (red and NIR light). Thanks to a naturally occurring optical window, NIR light can penetrate deeper than UV light into biological samples. Hence, UCNPs in bio-samples can be excited by NIR light. This possibility opens a pathway for in vitro as well as in vivo applications, like optical imaging by cell labeling or staining of specific organic tissue. Furthermore, early detection and diagnosis of diseases by predictive and diagnostic biomarkers can be realized with bio-recognition elements being labeled to the UCNPs. Additionally, "theranostic" becomes possible, in which the identification and the treatment of a disease are tackled simultaneously.
For this to succeed, certain parameters for the UCNPs must be met: high upconversion efficiency, high photoluminescence quantum yield, dispersibility, and dispersion stability in aqueous media, as well as availability of functional groups to introduce fast and easy bio-recognition elements. The UCNPs used in this work were prepared with a solvothermal decomposition synthesis yielding in particles with NaYF4 or NaGdF4 as host lattice. They have been doped with the Ln(III) ions Yb3+ and Er3+, which is only one possible upconversion pair. Their upconversion efficiency and photoluminescence quantum yield were improved by adding a passivating shell to reduce surface quenching.
However, the brightness of core-shell UCNPs stays behind the expectations compared to their bulk material (being at least μm-sized particles). The core-shell structures are not clearly separated from each other, which is a topic in literature. Instead, there is a transition layer between the core and the shell structure, which relates to the migration of the dopants within the host lattice during the synthesis. The ion migration has been examined by time-resolved laser spectroscopy and the interlanthanoid resonance energy transfer (LRET) in the two different host lattices from above. The results are
presented in two publications, which dealt with core-shell-shell structured nanoparticles. The core is doped with the LRET-acceptor (either Nd3+ or Pr3+). The intermediate shell serves as an insulation shell of pure host lattice material, whose shell thickness has been varied within one set of samples having the same composition, so that the spatial separation of LRET-acceptor and -donor changes. The outer shell with the same host lattice is doped with the LRET-donor (Eu3+). The effect of the increasing insulation shell thickness is significant, although the LRET cannot be suppressed completely.
Next to the Ln(III) migration within a host lattice, various phase transfer reactions were investigated in order to subsequently perform surface modifications for bioapplications. One result out of this research has been published using a promising ligand, that equips the UCNP with bio-modifiable groups and has good potential for bio-medical applications. This particular ligand mimics natural occurring mechanisms of mussel protein adhesion and of blood coagulation, which is why the UCNPs are encapsulated very effectively. At the same time, bio-functional groups are introduced. In a proof-of-concept, the encapsulated UCNP has been coupled successfully with a dye (which is representative for a biomarker) and the system’s photoluminescence properties have been investigated.
As climate change worsens, there is a growing urgency to promote renewable energies and improve their accessibility to society. Here, solar energy harvesting is of particular importance. Currently, metal halide perovskite (MHP) solar cells are indispensable in future solar energy generation research. MHPs are crystalline semiconductors increasingly relevant as low-cost, high-performance materials for optoelectronics. Their processing from solution at low temperature enables easy fabrication of thin film elements, encompassing solar cells and light-emitting diodes or photodetectors. Understanding the coordination chemistry of MHPs in their precursor solution would allow control over the thin film crystallization, the material properties and the final device performance.
In this work, we elaborate on the key parameters to manipulate the precursor solution with the long-term objective of enabling systematic process control. We focus on the nanostructural characterization of the initial arrangements of MHPs in the precursor solutions. Small-angle scattering is particularly well suited for measuring nanoparticles in solution. This technique proved to be valuable for the direct analyzes of perovskite precursor solutions in standard processing concentrations without causing radiation damage. We gain insights into the chemical nature of widely used precursor structures such as methylammonium lead iodide (MAPbI3), presenting first insights into the complex arrangements and interaction within this precursor state. Furthermore, we transfer the preceding results to other more complex perovskite precursors. The influence of compositional engineering is investigated using the addition of alkali cations as an example. As a result, we propose a detailed working mechanism on how the alkali cations suppress the formation of intermediate phases and improve the quality of the crystalline thin film. In addition, we investigate the crystallization process of a tin-based perovskite composition (FASnI3) under the influence of fluoride chemistry. We prove that the frequently used additive, tin fluoride (SnF2), selectively binds undesired oxidized tin (Sn(IV)) in the precursor solution. This prevents its incorporation into the actual crystal structure and thus reduces the defect density of the material. Furthermore, SnF2 leads to a more homogeneous crystal growth process, which results in improved crystal quality of the thin film material.
In total, this study provides a detailed characterization of the complex system of perovskite precursor chemistry. We thereby cover relevant parameters for future MHP solar cell process control, such as (I) the environmental impact based on concentration and temperature (II) the addition of counter ions to reduce the diffuse layer surrounding the precursor nanostructures and (III) the targeted use of additives to eliminate unwanted components selectively and to ensure a more homogeneous crystal growth.
The development and optimization of carbonaceous materials is of great interest for several applications including gas sorption, electrochemical storage and conversion, or heterogeneous catalysis. In this thesis, the exploration and optimization of nitrogen containing carbonaceous materials by direct condensation of smart chosen, molecular precursors will be presented. As suggested with the concept of noble carbons, the choice of a stable, nitrogen-containing precursor will lead to an even more stable, nitrogen doped carbonaceous material with a controlled structure and electronic properties. Molecules fulfilling this requirement are for example nucleobases. The direct condensation of nucleobases leads to highly nitrogen containing carbonaceous materials without any further post or pretreatment. By using salt melt templating, pore structure adjustment is possible without the use of hazardous or toxic reagents and the template can be reused.
Using these simple tools, the synergetic effect of the pore structure and nitrogen content of the materials can be explored. Within this thesis, the influence of the condensation parameters will be correlated to the structure and performance of the materials. First, the influence of the condensation temperature to the porosity and nitrogen content of guanine will be discussed and the exploration of highly CO2 selective structural pores in C1N1 materials will be shown. Further tuning the pore structure of the materials by salt melt templating will be then explored, the potential of the prepared materials as heterogeneous catalysts and their basic catalytic strength will be correlated to their nitrogen content and pore morphology. A similar approach is used to explore the water sorption behavior of uric acid derived carbonaceous materials as potential sorbents for heat transformation applications. Changes in maximum water uptake and hydrophilicity of the prepared materials will be correlated to the nitrogen content and pore architecture. Due to the high thermal stability, porosity, and nitrogen content of ionic liquid derived nitrogen doped carbonaceous materials, a simple impregnation and calcination route can be conducted to obtain copper nano cluster decorated nitrogen-doped carbonaceous materials. The activity as catalyst for the oxygen reduction reaction of the obtained materials will be shown and structure performance relations are discussed.
In conclusion, the versatility of nitrogen doped carbonaceous materials with a nitrogen to carbon ratio of up to one will be shown. The possibility to tune the pore structure as well as the nitrogen content by using a simple procedure including salt melt templating as well as the use of molecular precursors and their effect on the performance will be discussed.
Hybrid organic-inorganic perovskites have attracted attention in recent years, caused by the incomparable increase in efficiency in energy convergence, which implies the application as an absorber material for solar cells. A disadvantage of these materials is, among others, the instability to moisture and UV-radiation. One possible solution for these problems is the reduction of the size towards the nano world. With that nanosized perovskites are showing superior stability in comparison to e.g. perovskite layers. Additionally to this the nanosize even enables stable perovskite structures, which could not be achieved otherwise at
room temperature.
This thesis is separated into two major parts. The separation is done by the composition and the band gap of the material and at the same time the shape and size of the nanoparticles. Here the division is made by the methylammonium lead tribromide nanoplatelets and the caesium lead triiodide nanocubes.
The first part is focusing on the hybrid organic-inorganic perovskite (methylammonium lead tribromide) nanoplatelets with a band gap of 2.35 eV and their thermal behaviour. Due to the challenging character of this material, several analysis methods are used to investigate the sub nano and nanostructures under the influence of temperature. As a result, a shift of phase-transition temperatures towards higher temperatures is observed. This unusual behaviour can be explained by the ligand, which is incorporated in the perovskite outer structure and adds phase-stability into the system.
The second part of this thesis is focusing on the inorganic caesium lead triiodide nanocubes with a band gap of 1.83 eV. These nanocrystals are first investigated and compared by TEM, XRD and other optical methods. Within these methods, a cuboid and orthorhombic structure are revealed instead of the in literature described cubic shape and structure. Furthermore, these cuboids are investigated towards their self-assembly on a substrate. Here a high degree in self-assembly is shown. As a next step, the ligands of the nanocuboids are exchanged against other ligands to increase the charge carrier mobility. This is further investigated by the above-mentioned methods. The last section is dealing with the enhancement of the CsPbI3 structure, by incorporating potassium in the crystal structure. The results are suggesting here an increase in stability.
Im Rahmen dieser Arbeit wird anhand von neuartigen Materialien das Potential der Europium-Lumineszenz für die strukturelle Analyse dargestellt. Bei diesen Materialien handelt es sich zum einen um Nanopartikel mit Matrizes aus mehreren Metall-Mischoxiden und Dotierungen durch die Sonde Europium und zum anderen um Metallorganische Netzwerke (MOFs), die mit Neodym , Samarium- und Europium-Ionen beladen sind.
Die Synthese der aus der Kombination von Metalloxiden enthaltenen Nanopartikel ist unter milden Bedingungen mithilfe von speziell dafür hergestellten Reagenzien erfolgt und hat zu sehr kleinen, amorphen Nanopartikeln geführt. Durch eine nachfolgende Temperaturbehandlung hat sich die Kristallinität erhöht. Damit verbunden haben sich auch die Kristallstruktur sowie die Position des Dotanden Europium verändert.
Während die etablierte Methode der Röntgendiffraktometrie einen Blick auf das Kristallgitter als Gesamtes ermöglicht, so trifft die Lumineszenz des Europiums durch die Sichtbarkeit einzelner Stark-Aufspaltungen Aussagen über dessen lokale Symmetrien. Die Symmetrie wird durch Sauerstofffehlstellen verändert, welche die Sauerstoffleitfähigkeit der Nanopartikel beeinflussen. Diese ist für die Anwendung als Katalysatoren in industriellen Prozessen und ebenso als Sensoren und Therapeutika in biologischen Systemen von Bedeutung.
Zur ersten katalytischen Charakterisierung werden die Proben mittels Temperatur-programmierter Reduktion untersucht. Des Weiteren werden die Mischoxid-Nanopartikel auch hinsichtlich ihrer Verwendbarkeit als Matrix in Aufkonversionsprozessen untersucht.
Die Metallorganischen Netzwerke eignen sich aufgrund ihrer mikroporösen Struktur für Anwendungen in der Speicherung gleichermaßen von Nutzgasen wie auch von Schadstoffen. Ebenfalls ist eine biologische Anwendung denkbar, die insbesondere den Bereich der drug delivery-Reagenzien betrifft.
Erfolgt in die mikroporösen Strukturen der Metallorganischen Netzwerke die Einlagerung von Lanthanoid-Ionen, so können diese bei der entsprechenden Kombination als Weißlicht-Emittierer fungieren. Dabei ist neben den Verhältnissen zwischen den Lanthanoid-Ionen auch die genaue Position innerhalb des Netzwerks sowie die Distanz zu anderen Ionen von Interesse. Zur Untersuchung dieser Fragestellungen wird die Umgebungssensitivität der Europium-Lumineszenz ausgenutzt. Die auf diese Weise festgestellte Formiat-Bildung hängt von zahlreichen Parametern ab.
Insgesamt stellt sich die im Rahmen dieser Arbeit verwendete Methodik des Einsatzes von Europium als strukturelle Sonde in höchstem Maße vielseitig dar und zeigt seine größte Stärke in der Kombination mit weiteren Methoden der Strukturanalytik. Die auf diese Weise genauestens charakterisierten neuartigen Materialien können nun gezielt und anwendungsfokussiert weiterentwickelt werden.
In recent years people have realised non-renewability of our modern society which relays on spending huge amounts of energy mostly produced from fosil fuels, such as oil and coal, and the shift towards more sustainable energy sources has started. However, sustainable sources of energy, such as wind-, solar- and hydro-energy, produce primarily electrical energy and can not just be poured in canister like many fosil fuels, creating necessity for rechragable batteries. However, modern Li-ion batteries are made from toxic heavy metals and sustainable alternatives are needed. Here we show that naturally abundant catecholic and guaiacyl groups can be utilised to replace heavy metals in Li-ion batteries.
Foremost vanillin, a naturally occurring food additive that can be sustainably synthesised from industrial biowaste, lignin, was utilised to synthesise materials that showed extraordinary performance as cathodes in Li-ion batteries. Furthermore, behaviour of catecholic and guiacyl groups in Li-ion system was compared, confirming usability of guiacayl containing biopolymers as cathodes in Li-ion batteries. Lastly, naturally occurring polyphenol, tannic acid, was incorporated in fully bioderived hybrid material that shows performance comparable to commercial Li-ion batteries and good stability.
This thesis presents an important advancement in understanding of biowaste derived cathode materials for Li-ion batteries. Further research should be conducted to better understand behaviour of guaiacyl groups during Li-ion battery cycling. Lastly, challenges of incorporation of lignin, an industrial biowaste, have to be addressed and lignin should be incorporated as a cathode material in Li-ion batteries.
The remarkable antifouling properties of zwitterionic polymers in controlled environments are often counteracted by their delicate mechanical stability. In order to improve the mechanical stabilities of zwitterionic hydrogels, the effect of increased crosslinker densities was thus explored. In a first approach, terpolymers of zwitterionic monomer 3-[N -2(methacryloyloxy)ethyl-N,N-dimethyl]ammonio propane-1-sulfonate (SPE), hydrophobic monomer butyl methacrylate (BMA), and photo-crosslinker 2-(4-benzoylphenoxy)ethyl methacrylate (BPEMA) were synthesized. Thin hydrogel coatings of the copolymers were then produced and photo-crosslinked. Studies of the swollen hydrogel films showed that not only the mechanical stability but also, unexpectedly, the antifouling properties were improved by the presence of hydrophobic BMA units in the terpolymers.
Based on the positive results shown by the amphiphilic terpolymers and in order to further test the impact that hydrophobicity has on both the antifouling properties of zwitterionic hydrogels and on their mechanical stability, a new amphiphilic zwitterionic methacrylic monomer, 3-((2-(methacryloyloxy)hexyl)dimethylammonio)propane-1-sulfonate (M1), was synthesized in good yields in a multistep synthesis. Homopolymers of M1 were obtained by free-radical polymerization. Similarly, terpolymers of M1, zwitterionic monomer SPE, and photo-crosslinker BPEMA were synthesized by free-radical copolymerization and thoroughly characterized, including its solubilities in selected solvents.
Also, a new family of vinyl amide zwitterionic monomomers, namely 3-(dimethyl(2-(N -vinylacetamido)ethyl)ammonio)propane-1-sulfonate (M2), 4-(dimethyl(2-(N-vinylacetamido)ethyl)ammonio)butane-1-sulfonate (M3), and 3-(dimethyl(2-(N-vinylacetamido)ethyl)ammonio)propyl sulfate (M4), together with the new photo-crosslinker 4-benzoyl-N-vinylbenzamide (M5) that is well-suited for copolymerization with vinylamides, are introduced within the scope of the present work. The monomers are synthesized with good yields developing a multistep synthesis. Homopolymers of the new vinyl amide zwitterionic monomers are obtained by free-radical polymerization and thoroughly characterized. From the solubility tests, it is remarkable that the homopolymers produced are fully soluble in water, evidence of their high hydrophilicity. Copolymerization of the vinyl amide zwitterionic monomers, M2, M3, and M4 with the vinyl amide photo-crosslinker M5 proved to require very specific polymerization conditions. Nevertheless, copolymers were successfully obtained by free-radical copolymerization under appropriate conditions.
Moreover, in an attempt to mitigate the intrinsic hydrophobicity introduced in the copolymers by the photo-crosslinkers, and based on the proven affinity of quaternized diallylamines to copolymerize with vinyl amides, a new quaternized diallylamine sulfobetaine photo-crosslinker 3-(diallyl(2-(4-benzoylphenoxy)ethyl)ammonio)propane-1-sulfonate (M6) is synthesized. However, despite a priori promising copolymerization suitability, copolymerization with the vinyl amide zwitterionic monomers could not be achieved.
Magnetische Eisenoxidnanopartikel werden bereits seit geraumer Zeit erfolgreich als MRT-Kontrastmittel in der klinischen Bildgebung eingesetzt. Durch Optimierung der magnetischen Eigenschaften der Nanopartikel kann die Aussagekraft von MR-Aufnahmen verbessert und somit der diagnostische Wert einer MR-Anwendung weiter erhöht werden. Neben der Verbesserung bestehender Verfahren wird die bildgebende Diagnostik ebenso durch die Entwicklung neuer Verfahren, wie dem Magnetic Particle Imaging, vorangetrieben. Da hierbei das Messsignal von den magnetischen Nanopartikeln selbst erzeugt wird, birgt das MPI einen enormen Vorteil hinsichtlich der Sensitivität bei gleichzeitig hoher zeitlicher und räumlicher Auflösung. Da es aktuell jedoch keinen kommerziell vertriebenen in vivo-tauglichen MPI-Tracer gibt, besteht ein dringender Bedarf an geeigneten innovativen Tracermaterialien. Daraus resultierte die Motivation dieser Arbeit biokompatible und superparamagnetische Eisenoxidnanopartikel für den Einsatz als in vivo-Diagnostikum insbesondere im Magnetic Particle Imaging zu entwickeln. Auch wenn der Fokus auf der Tracerentwicklung für das MPI lag, wurde ebenso die MR-Performance bewertet, da geeignete Partikel somit alternativ oder zusätzlich als MR-Kontrastmittel mit verbesserten Kontrasteigenschaften eingesetzt werden könnten.
Die Synthese der Eisenoxidnanopartikel erfolgte über die partielle Oxidation von gefälltem Eisen(II)-hydroxid und Green Rust sowie eine diffusionskontrollierte Kopräzipitation in einem Hydrogel.
Mit der partiellen Oxidation von Eisen(II)-hydroxid und Green Rust konnten erfolgreich biokompatible und über lange Zeit stabile Eisenoxidnanopartikel synthetisiert werden. Zudem wurden geeignete Methoden zur Formulierung und Sterilisierung etabliert, wodurch zahlreiche Voraussetzungen für eine Anwendung als in vivo-Diagnostikum geschaffen wurden. Weiterhin ist auf Grundlage der MPS-Performance eine hervorragende Eignung dieser Partikel als MPI-Tracer zu erwarten, wodurch die Weiterentwicklung der MPI-Technologie maßgeblich vorangetrieben werden könnte. Die Bestimmung der NMR-Relaxivitäten sowie ein initialer in vivo-Versuch zeigten zudem das große Potential der formulierten Nanopartikelsuspensionen als MRT-Kontrastmittel. Die Modifizierung der Partikeloberfläche ermöglicht ferner die Herstellung zielgerichteter Nanopartikel sowie die Markierung von Zellen, wodurch das mögliche Anwendungsspektrum maßgeblich erweitert wurde.
Im zweiten Teil wurden Partikel durch eine diffusionskontrollierte Kopräzipitation im Hydrogel, wobei es sich um eine bioinspirierte Modifikation der klassischen Kopräzipitation handelt, synthetisiert, wodurch Partikel mit einer durchschnittlichen Kristallitgröße von 24 nm generiert werden konnten. Die Bestimmung der MPS- und MR-Performance elektrostatisch stabilisierter Partikel ergab vielversprechende Resultate. In Vorbereitung auf die Entwicklung eines in vivo-Diagnostikums wurden die Partikel anschließend erfolgreich sterisch stabilisiert, wodurch der kolloidale Zustand in MilliQ-Wasser über lange Zeit aufrechterhalten werden konnte. Durch Zentrifugation konnten die Partikel zudem erfolgreich in verschiedene Größenfraktionen aufgetrennt werden. Dies ermöglichte die Bestimmung der idealen Aggregatgröße dieses Partikelsystems in Bezug auf die MPS-Performance.