Refine
Document Type
- Article (2)
- Doctoral Thesis (1)
Language
- English (3)
Is part of the Bibliography
- yes (3)
Keywords
- Kohlenstoffmaterialien (1)
- Li deposition (1)
- Li dissolution (1)
- Li metal (1)
- Mesoporosity (1)
- Mesoporosität (1)
- Weitwinkelröntgenstreuung (1)
- advanced characterization (1)
- anodes (1)
- carbon materials (1)
- hierarchical porosity (1)
- hierarchische Porosität (1)
- mechanistic understanding (1)
- soft and hard templating (1)
- solid-electrolyte-interphase (1)
- theoretical simulation (1)
- weiche und harte Templatierung (1)
- wide-angle x-ray scattering (1)
Institute
- Institut für Chemie (3) (remove)
The aim of this work was the generation of carbon materials with high surface area, exhibiting a hierarchical pore system in the macro- and mesorange. Such a pore system facilitates the transport through the material and enhances the interaction with the carbon matrix (macropores are pores with diameters > 50 nm, mesopores between 2 – 50 nm). Thereto, new strategies for the synthesis of novel carbon materials with designed porosity were developed that are in particular useful for the storage of energy. Besides the porosity, it is the graphene structure itself that determines the properties of a carbon material. Non-graphitic carbon materials usually exhibit a quite large degree of disorder with many defects in the graphene structure, and thus exhibit inherent microporosity (d < 2nm). These pores are traps and oppose reversible interaction with the carbon matrix. Furthermore they reduce the stability and conductivity of the carbon material, which was undesired for the proposed applications. As one part of this work, the graphene structures of different non-graphitic carbon materials were studied in detail using a novel wide-angle x-ray scattering model that allowed precise information about the nature of the carbon building units (graphene stacks). Different carbon precursors were evaluated regarding their potential use for the synthesis shown in this work, whereas mesophase pitch proved to be advantageous when a less disordered carbon microstructure is desired. By using mesophase pitch as carbon precursor, two templating strategies were developed using the nanocasting approach. The synthesized (monolithic) materials combined for the first time the advantages of a hierarchical interconnected pore system in the macro- and mesorange with the advantages of mesophase pitch as carbon precursor. In the first case, hierarchical macro- / mesoporous carbon monoliths were synthesized by replication of hard (silica) templates. Thus, a suitable synthesis procedure was developed that allowed the infiltration of the template with the hardly soluble carbon precursor. In the second case, hierarchical macro- / mesoporous carbon materials were synthesized by a novel soft-templating technique, taking advantage of the phase separation (spinodal decomposition) between mesophase pitch and polystyrene. The synthesis also allowed the generation of monolithic samples and incorporation of functional nanoparticles into the material. The synthesized materials showed excellent properties as an anode material in lithium batteries and support material for supercapacitors.
Porous silicon carbide monoliths were obtained using the infiltration of preformed SiO2 frameworks with appropriate carbon precursors such as mesophase pitch. The initial SiO2 monoliths possessed a hierarchical pore system, composed of an interpenetrating bicontinuous macropore structure and 13 nm mesopores confined in the macropore walls. After carbonization, further heat treatment at ca. 1400 degrees C resulted in the formation of a SiC-SiO2 composite, which was converted into a porous SiC monolith by post-treatment with ammonium fluoride solution. The resulting porous SiC featured high crystallinity, high chemical purity and showed a surface area of 280 m(2) g(-1) and a pore volume of 0.8 ml g(-1)
In recent years, due to its great promise in boosting the energy density of lithium batteries for future energy storage, research on the Li metal anode, as an alternative to the graphite anode in Li-ion batteries, has gained significant momentum. However, the practical use of Li metal anodes has been plagued by unstable Li (re)deposition and poor cyclability. Although tremendous efforts have been devoted to the stabilization of Li metal anodes, the mechanisms of electrochemical (re-)deposition/dissolution of Li and solid-electrolyte-interphase (SEI) formation remain elusive. This article highlights the recent mechanistic understandings and observations of Li deposition/dissolution and SEI formation achieved from advanced characterization techniques and simulation methods, and discusses major limitations and open questions in these processes. In particular, the authors provide their perspectives on advanced and emerging/potential methods for obtaining new insights into these questions. In addition, they give an outlook into cutting-edge interdisciplinary research topics for Li metal anodes. It pushes beyond the current knowledge and is expected to accelerate development toward a more in-depth and comprehensive understanding, in order to guide future research on Li metal anodes toward practical application.