This work demonstrates the production of high-performing p- type and n-type hybrid AgxTe/poly(3,4-ethylenedioxythiopene):polystyrene sulfonic acid (PE-DOT:PSS) thermoelectric materials from the same Te/PEDOT:PSS parent structure during aqueous-based synthesis. All samples were solution-processed and analyzed in thin- film architectures. We were able to demonstrate a power factor of 44 mu W m(-1) K-2 for our highest-performing n-type material. In addition, we were also able to realize a 68% improvement in the power factor of our p-type compositions relative to the parent structure through manipulation of the inorganic nanostructure composition. We demonstrate control over the thermoelectric properties by varying the stoichiometry of AgxTe nanoparticles in AgxTe/PEDOT:PSS hybrid materials via a topotactic chemical transformation process at room temperature. This process offers a simple, low-temperature, and cost-effective route toward the production of both efficient n-type and p-type hybrid thermoelectric materials.
CuI has been recently rediscovered as a p-type transparent conductor with a high figure of merit. Even though many metal iodides are hygroscopic, the effect of moisture on the electrical properties of CuI has not been clarified. In this work, we observe a 2-fold increase in the conductivity of CuI after exposure to ambient humidity for 5 h, followed by slight long-term degradation. Simultaneously, the work function of CuI decreases by almost 1 eV, which can explain the large spread in the previously reported work function values. The conductivity increase is partially reversible and is maximized at intermediate humidity levels. On the basis of the large intragrain mobility measured by THz spectroscopy, we suggest that hydration of grain boundaries may be beneficial for the overall hole mobility.
Transparent conductive materials based on indium oxide remain yet irreplaceable in various optoelectronic applications. Amorphous oxides appear especially attractive for technology as they are isotropic, demonstrate relatively high electron mobility and can be processed at low temperatures. Among them is indium zinc oxide (IZO) with a large zinc content that is crucial for keeping the amorphous state but redundant for the doping. In this work we investigated water-free and water containing IZO films obtained by radio frequency sputtering. The correlation between temperature driven changes of the chemical state, the optical and electrical properties as well as the progression of crystallization was in focus. Such characterization methods as: scanning electron microscopy, X-ray diffraction, X-ray photoelectron spectroscopy, Raman spectroscopy, temperature dependent Hall-effect measurements and others were applied. Temperature dependent electrical properties of amorphous IZO and IZO:H2O films were found to evolve similarly. Based on our experience in In2O3:H2O (In2O3:H or IOH) we proposed an explanation for the changes observed. Water admixture was found to decrease crystallization temperature of IZO significantly from similar to 550 degrees C to similar to 280 degrees C. Herewith, the presence and concentration of water and/or hydroxyls was found to determine Zn distribution in the film. In particular, Zn enrichment was detected at the film's surface respective to the high water and/or hydroxyl amount. Raman spectra revealed a two-dimensional crystallization of w-ZnO which precedes regardless water presence an extensive In2O3 crystallization. An abrupt loss of electron mobility as a result of crystallization was attributed to the formation of ZnO interlayer on grain boundaries.