Transparent, ion-conducting, luminescent, and flexible ionogels based on the room temperature ionic liquid (IL) 1-butyl-3-methylimidazolium bis(trifluoromethane sulfonyl) imide [Bmim][N(Tf)(2)], a PtEu2 chromophore, and poly(methylmethacrylate) (PMMA) have been prepared. The thermal stability of the PMMA significantly increases with IL incorporation. In particular, the onset weight loss observed at ca. 229 degrees C for pure PMMA increases to 305 degrees C with IL addition. The ionogel has a high ionic conductivity of 10(-3) S cm(-1) at 373 K and exhibits a strong emission in the red with a long average luminescence decay time of tau = 890 mu s. The resulting material is a new type of soft hybrid material featuring useful thermal, optical, and ion transport properties.
Mesoporous carbon/iron carbide hybrid materials with surface areas reaching 800 m(2) g(-1) were synthesized via an exotemplating route using monolithic mesoporous silica as template and the ionic liquid 1-butyl-3-methylimidazolium tetrachloridoferrate(III) [Bmim][FeCl4] as carbon and iron source. After heat treatment (750 degrees C under argon) of the [Bmim][FeCl4] precursor confined within the silica matrix, the silica exotemplate was removed with HF leaving the mesoporous C/Fe3C hybrid behind. The surface areas and the pore sizes depend on the exotemplate and the surface areas a significantly larger than any other surface area reported for C/Fe3C hybrid materials so far. The approach is thus a prototype for the synthesis of high-surface area iron carbide-based hybrid materials with potential application in catalysis.
Thin films of ferroelectric beta-phase poly(vinylidene fluoride) (PVDF) were spin-coated from a solution that contained small amounts of the ionic liquid (IL) 1-ethyl-3-methylimidazolium nitrate. A remanent polarization of 60 mC/m(2) and a quasi-static pyroelectric coefficient of 19 mu C/m(2)K at 30 degrees C were observed in the films. It is suggested that the IL promotes the formation of the beta phase through dipolar interactions between PVDF chain-molecules and the IL. The dipolar interactions are identified as Coulomb attraction between hydrogen atoms in PVDF chains and anions in IL. The strong crystallinity increase is probably caused by the same dipolar interaction as well.