Keywords
- Mesenchymal stem cells (2)
- crystallization behavior (2)
- poly(ether imide) (2)
- Biocompatibility testing (1)
- Biopolymer (1)
- Degradation (1)
- Depsipeptide (1)
- Drug delivery systems (1)
- FAK-MAPK (1)
- Hydrogel (1)
Nanocarriers
(2017)
Controlling mesenchymal stem cells (MSCs) behavior is necessary to fully exploit their therapeutic potential. Various approaches are employed to effectively influence the migration capacity of MSCs. Here, topographic microstructures with different microscale roughness were created on polystyrene (PS) culture vessel surfaces as a feasible physical preconditioning strategy to modulate MSC migration. By analyzing trajectories of cells migrating after reseeding, we demonstrated that the mobilization velocity of human adipose derived mesenchymal stem cells (hADSCs) could be promoted by and persisted after brief preconditioning with the appropriate microtopography. Moreover, the elevated activation levels of focal adhesion kinase (FAK) and mitogen-activated protein kinase (MAPK) in hADSCs were also observed during and after the preconditioning process. These findings underline the potential enhancement of in vivo therapeutic efficacy in regenerative medicine via transplantation of topographic microstructure preconditioned stem cells.
Polymeric matrices mimicking multiple functions of the ECM are expected to enable a material induced regeneration of tissues. Here, we investigated the adipogenic differentiation of human adipose derived mesenchymal stem cells (hADSCs) in a 3D architectured gelatin based hydrogel (ArcGel) prepared from gelatin and L-lysine diisocyanate ethyl ester (LDI) in an one-step process, in which the formation of an open porous morphology and the chemical network formation were integrated. The ArcGel was designed to support adipose tissue regeneration with its 3D porous structure, high cell biocompatibility, and mechanical properties compatible with human subcutaneous adipose tissue. The ArcGel could support initial cell adhesion and survival of hADSCs. Under static culture condition, the cells could migrate into the inner part of the scaffold with a depth of 840 +/- 120 mu m after 4 days, and distributed in the whole scaffold (2mm in thickness) within 14 days. The cells proliferated in the scaffold and the fold increase of cell number after 7 days of culture was 2.55 +/- 0.08. The apoptotic rate of hADSCs in the scaffold was similar to that of cells maintained on tissue culture plates. When cultured in adipogenic induction medium, the hADSCs in the scaffold differentiated into adipocytes with a high efficiency (93 +/- 1%). Conclusively, this gelatin based 3D scaffold presented high cell compatibility for hADSC cultivation and differentiation, which could serve as a potential implant material in clinical applications for adipose tissue reparation and regeneration.
Polymeric biomaterials are of specific relevance in medical and pharmaceutical applications due to their wide range of tailorable properties and functionalities. The knowledge about interactions of biomaterials with their biological environment is of crucial importance for developing highly sophisticated medical devices. To achieve optimal in vivo performance, a description at the molecular level is required to gain better understanding about the surface of synthetic materials for tailoring their properties. This is still challenging and requires the comprehensive characterization of morphological structures, polymer chain arrangements and degradation behaviour. The review discusses selected aspects for evaluating polymeric biomaterial-environment interfaces by Langmuir monolayer methods as powerful techniques for studying interfacial properties, such as morphological and degradation processes. The combination of spectroscopic, microscopic and scattering methods with the Langmuir techniques adapted to polymers can substantially improve the understanding of their in vivo behaviour.
Glycoproteins adsorbing on an implant upon contact with body fluids can affect the biological response in vitro and in vivo, depending on the type and conformation of the adsorbed biomacromolecules. However, this process is poorly characterized and so far not controllable. Here, protein monolayers of high molecular cohesion with defined density are transferred onto polymeric substrates by the Langmuir-Schaefer (LS) technique and were compared with solution deposition (SO) method. It is hypothesized that on polydimethylsiloxane (PDMS), a substrate with poor cell adhesion capacity, the fibronectin (FN) layers generated by the LS and SO methods will differ in their organization, subsequently facilitating differential stem cell adhesion behavior. Indeed, atomic force microscopy visualization and immunofluorescence images indicated that organization of the FN layer immobilized on PDMS was uniform and homogeneous. In contrast, FN deposited by SO method was rather heterogeneous with appearance of structures resembling protein aggregates. Human mesenchymal stem cells showed reduced absolute numbers of adherent cells, and the vinculin expression seemed to be higher and more homogenously distributed after seeding on PDMS equipped with FN by LS in comparison with PDMS equipped with FN by SO. These divergent responses could be attributed to differences in the availability of adhesion molecule ligands such as the Arg-Gly-Asp (RGD) peptide sequence presented at the interface. The LS method allows to control the protein layer characteristics, including the thickness and the protein orientation or conformation, which can be harnessed to direct stem cell responses to defined outcomes, including migration and differentiation. Copyright (c) 2016 John Wiley & Sons, Ltd.
Degradable multiblock copolymers prepared from equal weight amounts of poly(epsilon-caprolactone)-diol (PCL-diol) and poly[oligo(3S-iso-butylmorpholine-2,5-dione)]-diol (PIBMD-diol), named PCL-PIBMD, provide a phase-segregated morphology. It exhibits a low melting temperature from PCL domains (T-m,T-PCL) of 382 degrees C and a high T-m,T-PIBMD of 170 +/- 2 degrees C with a glass transition temperature (T-g,T-PIBMD) at 42 +/- 2 degrees C from PIBMD domains. In this study, we explored the influence of applying different thermal treatments on the resulting morphologies of solution-cast and spin-coated PCL-PIBMD thin films, which showed different initial surface morphologies. Differential scanning calorimetry results and atomic force microscopy images after different thermal treatments indicated that PCL and PIBMD domains showed similar crystallization behaviors in 270 +/- 30 mu m thick solution-cast films as well as in 30 +/- 2 and 8 +/- 1nm thick spin-coated PCL-PIBMD films. Existing PIBMD crystalline domains highly restricted the generation of PCL crystalline domains during cooling when the sample was annealed at 180 degrees C. By annealing the sample above 120 degrees C, the PIBMD domains crystallized sufficiently and covered the free surface, which restricted the crystallization of PCL domains during cooling. The PCL domains can crystallize by hindering the crystallization of PIBMD domains via the fast vitrification of PIBMD domains when the sample was cooled/quenched in liquid nitrogen after annealing at 180 degrees C. These findings contribute to a better fundamental understanding of the crystallization mechanism of multi-block copolymers containing two crystallizable domains whereby the T-g of the higher melting domain type is in the same temperature range as the T-m of the lower melting domain type. Copyright (c) 2016 John Wiley & Sons, Ltd.
In this study, a multiblock copolymer containing oligo(3-methyl-morpholine-2, 5-dione) (oMMD) and oligo(3-sec-butyl-morpholine-2, 5-dione) (oBMD) building blocks obtained by ring-opening polymerization (ROP) of the corresponding monomers, was synthesized in a polyaddition reaction using an aliphatic diisocyanate. The multiblock copolymer (pBMD-MMD) provided a molecular weight of 40, 000 g·mol−1, determined by gel permeation chromatography (GPC). Incorporation of both oligodepsipeptide segments in multiblock copolymers was confirmed by 1H NMR and Matrix Assisted Laser Desorption/Ionization Time Of Flight Mass Spectroscopy (MALDI-TOF MS) analysis. pBMD-MMD showed two separated glass transition temperatures (61 °C and 74 °C) indicating a microphase separation. Furthermore, a broad glass transition was observed by DMTA, which can be attributed to strong physical interaction i.e. by H-bonds formed between amide, ester, and urethane groups of the investigated copolymers. The obtained multiblock copolymer is supposed to own the capability to exhibit strong physical interactions.
Poly(ether imide) (PEI), which can be chemically functionalized with biologically active ligands, has emerged as a potential biomaterial for medical implants. Electrospun PEI scaffolds have shown advantageous properties, such as enhanced endothelial cell adherence, proliferation and low platelet adhesion in in vitro experiments. In this study, the in vivo behaviour of electrospun PEI scaffolds and PEI films was examined in a murine subcutaneous implantation model. Electrospun PEI scaffolds and films were surgically implanted subcutaneously in the dorsae of mice. The surrounding subcutaneous tissue response was examined via histopathological examination at 7 and 28days after implantation. No serious adverse events were observed for both types of PEI implants. The presence of macrophages or foreign body giant cells in the vicinity of the implants and the formation of a fibrous capsule indicated a normal foreign body reaction towards PEI films and scaffolds. Capsule thickness and inflammatory infiltration cells significantly decreased for PEI scaffolds during days 7-28 while remaining unchanged for PEI films. The infiltration of cells into the implant was observed for PEI scaffolds 7days after implantation and remained stable until 28days of implantation. Additionally some, but not all, PEI scaffold implants induced the formation of functional blood vessels in the vicinity of the implants. Conclusively, this study demonstrates the in vivo biocompatibility of PEI implants, with favourable properties of electrospun PEI scaffolds regarding tissue integration and wound healing.
Highly porous poly(ether imide) (PEI) microparticles prepared by a spraying/coagulation process are discussed as candidate adsorber materials for apheresis applications, i.e. removal of uremic toxins from the blood of renal failure patients. PEI particles obtained by the aforementioned procedure can have a broad size distribution with particle diameters ranging from 20 to 800 mu m. In order to further estimate the adsorption behavior of PEI microparticles packed in application relevant apheresis modules, a quantitative information about the relation between particle size and pore morphology is required. In this study, we explored whether the intraparticle porosity of PEI microparticles varies with altering the diameter of the particulate adsorbers. By an analytical wet sieving procedure, the obtained PEI microparticles were separated into five size fractions, which were analyzed by mercury intrusion porosimetry, nitrogen adsorption, and scanning electron microscopy. Mercury intrusion porosimetry revealed for all size fractions high porosity values in the range from 78% to 84% with pore diameters in the range from 10 to 1000nm. A bimodal pore size distribution was found having a first peak at around 100nm, while a second pronounced peak maximum was found at higher pore sizes that increased with raising particle diameter from 300nm for the smallest particle size fraction (50-100 mu m) to 700nm for particles with a diameter of 200 to 250 mu m. Based on these findings, it can be assumed that the main PEI particle size fraction (200-250 mu m) should exhibit the highest adsorption capacity in an apheresis module. Copyright (c) 2016 John Wiley & Sons, Ltd.