Untersuchungen PEG-basierter thermo-responsiver Polymeroberflächen zur Steuerung der Zelladhäsion
(2010)
Moderne Methoden für die Einzelzellanalyse werden dank der fortschreitenden Weiterentwicklung immer sensitiver. Dabei steigen jedoch auch die Anforderungen an das Probenmaterial. Viele Aufbereitungsprotokolle adhärenter Zellen beinhalten eine enzymatische Spaltung der Oberflächenproteine, um die Ablösung vom Zellkultursubstrat zu ermöglichen. Verschiedene Methoden, wie die Patch-Clamp-Technik oder eine auf der Markierung extrazellulärer Domänen von Membranproteinen basierende Durchflusszytometrie können dann nur noch eingeschränkt eingesetzt werden. Daher ist die Etablierung neuer Zellablösemethoden dringend notwendig. In der vorliegenden Arbeit werden erstmals PEG-basierte thermo-responsive Oberflächen erfolgreich für die Zellkultur eingesetzt. Dabei wird das zerstörungsfreie Ablösen verschiedener Zelllinien von den Oberflächen durch Temperatursenkung realisiert. Die Funktionalität der Oberflächen wird durch Variation der Polymerstruktur, sowie der Konzentration der Beschichtungslösung, durch Beschichtung der Oberflächen mit einem zelladhäsionsfördernden Protein (Fibronektin) und durch Adsorption zelladhäsionsvermittelnder Peptide (RGD) optimiert. Um den Zellablösungsprozess detaillierter zu untersuchen, wird hier zum ersten Mal der direkte Zellkontakt mit thermo-responsiven Oberflächen mittels oberflächensensitiver Mikroskopie (TIRAF) sichtbar gemacht. Mit dieser Technik sind die exakte Quantifizierung und die Analyse der Reduktion der Zelladhäsionsfläche während des Abkühlens möglich. Hierbei werden in Abhängigkeit von der Zelllinie Unterschiede im Zellverhalten während des Ablösens festgestellt: Zellen, wie eine Brustkrebszelllinie und eine Ovarzelllinie, die bekanntermaßen stärker mit ihrer Umgebung in Kontakt treten, vergrößern im Verlauf des Beobachtungszeitraumes den Abstand zwischen Zellmembran und Oberfläche, reduzieren jedoch ihre Zell-Substratkontaktfläche kaum. Mausfibroblasten hingegen verkleinern drastisch die Zelladhäsionsfläche. Der Ablösungsprozess wird vermutlich aktiv von den Zellen gesteuert. Diese Annahme wird durch zwei Beobachtungen gestützt: Erstens verläuft die Reduktion der Zelladhäsionsfläche bei Einschränkung des Zellmetabolismus durch eine Temperatursenkung auf 4 °C verzögert. Zweitens hinterlassen die Zellen Spuren, die nach dem Ablösen der Zellen auf den Oberflächen zurückbleiben. Mittels Kombination von TIRAF- und TIRF-Mikroskopie werden die Zelladhäsionsfläche und die Aktinstruktur gleichzeitig beobachtet. Die Verknüpfung beider Methoden stellt eine neue Möglichkeit dar, intrazelluläre Prozesse mit der Zellablösung von thermo-responsiven Oberflächen zu korrelieren.
The behaviour of an adhering cell is strongly influenced by the chemical, topographical and mechanical properties of the surface it attaches to. During recent years, it has been found experimentally that adhering cells actively sense the elastic properties of their environment by pulling on it through numerous sites of adhesion. The resulting build-up of force at sites of adhesion depends on the elastic properties of the environment and is converted into corresponding biochemical signals, which can trigger cellular programmes like growth, differentiation, apoptosis, and migration. In general, force is an important regulator of biological systems, for example in hearing and touch, in wound healing, and in rolling adhesion of leukocytes on vessel walls. In the habilitation thesis by Ulrich Schwarz, several theoretical projects are presented which address the role of forces and elasticity in cell adhesion. (1) A new method has been developed for calculating cellular forces exerted at sites of focal adhesion on micro-patterned elastic substrates. The main result is that cell-matrix contacts function as mechanosensors, converting internal force into protein aggregation. (2) A one-step master equation for the stochastic dynamics of adhesion clusters as a function of cluster size, rebinding rate and force has been solved both analytically and numerically. Moreover this model has been applied to the regulation of cell-matrix contacts, to dynamic force spectroscopy, and to rolling adhesion. (3) Using linear elasticity theory and the concept of force dipoles, a model has been introduced and solved which predicts the positioning and orientation of mechanically active cells in soft material, in good agreement with experimental observations for fibroblasts on elastic substrates and in collagen gels.
Polymer multicomponent coatings such as multilayers mimic an extracellular, matrix (ECM) that attracts significant attention for the use of the multilayers as functional supports for advanced cell culture and tissue engineering. Herein, biodegradation and molecular transport in hyaluronan/polylysine multilayers coated with gold nanoparticles were described. Nanoparticle coating acts as a semipermeable barrier that governs molecular transport into/from the multilayers, and makes them biodegradation-resistant. Model protein lysozyme (mimics of ECM-soluble signals) diffuses into the multilayers as fast- and, slow-diffusing populations existing in an equilibrium,. Such a. composite system may have high potential to be exploited as degradation-resistant drug-delivery platforms suitable for cell-based applications.
Enhancement of human induced pluripotent stem cells adhesion through multilayer laminin coating
(2019)
Bioengineered cell substrates are a highly promising tool to govern the differentiation of stem cells in vitro and to modulate the cellular behavior in vivo. While this technology works fine for adult stem cells, the cultivation of human induced pluripotent stem cells (hiPSCs) is challenging as these cells typically show poor attachment on the bioengineered substrates, which among other effects causes substantial cell death. Thus, very limited types of surfaces have been demonstrated suitable for hiPSC cultures. The multilayer coating approach that renders the surface with diverse chemical compositions, architectures, and functions can be used to improve the adhesion of hiPSCs on the bioengineered substrates. We hypothesized that a multilayer formation based on the attraction of molecules with opposite charges could functionalize the polystyrene (PS) substrates to improve the adhesion of hiPSCs. Polymeric substrates were stepwise coated, first with dopamine to form a polydopamine (PDA) layer, second with polylysine and last with Laminin-521. The multilayer formation resulted in the variation of hydrophilicity and chemical functionality of the surfaces. Hydrophilicity was detected using captive bubble method and the amount of primary and secondary amines on the surface was quantified by fluorescent staining. The PDA layer effectively immobilized the upper layers and thereby improved the attachment of hiPSCs. Cell adhesion was enhanced on the surfaces coated with multilayers, as compared to those without PDA and/or polylysine. Moreover, hiPSCs spread well over this multilayer laminin substrate. These cells maintained their proliferation capacity and differentiation potential. The multilayer coating strategy is a promising attempt for engineering polymer-based substrates for the cultivation of hiPSCs and of interest for expanding the application scope of hiPSCs.
BACKGROUND: Physical and chemical characteristics of implant materials determine the fate of long-term cardiovascular devices. However, there is still a lack of fundamental understanding of the molecular mechanisms occurring in the material-tissue interphase. In a previous study, soft covalently crosslinked poly(n-butyl acrylate) networks (cPnBA) were introduced as sterilizable, non-toxic and immuno-compatible biomaterials with mechanical properties adjustable to blood vessels. Here we study the influence of different surface treatments in particular oxygen plasma modification and fibrinogen deposition as well as a combinatorial approach on the adhesion and viability of fibroblasts. RESULTS: Compared to non-treated cPnBAs the advancing water-contact angles were found to be reduced after all surface modifications (p<0.05, each), while lowest values were observed after the combined surface treatment (OPT+FIB). The latter differed significantly from the single OPT and FIB. The number of adherent fibroblasts and their adherence behavior differed on both pristine cPnBA networks. The fibroblast density on cPnBA04 was 743 +/- 434 cells. mm(-2), was about 6.5 times higher than on cPnBA73 with 115 +/- 73 cells. mm(-2). On cPnBA04 about 20% of the cells were visible as very small, round and buckled cells while all other cells were in a migrating status. On cPnBA73, nearly 50% of fibroblasts were visible as very small, round and buckled cells. The surface functionalization either using oxygen plasma treatment or fibrinogen coating led to a significant increase of adherent fibroblasts, particularly the combination of both techniques, for both cPnBA networks. It is noteworthy to mention that the fibrinogen coating overruled the characteristics of the pristine surfaces; here, the fibroblast densities after seeding were identical for both cPnBAnetworks. Thus, the binding rather depended on the fibrinogen coating than on the substrate characteristics anymore. While the integrity of the fibroblasts membrane was comparable for both polymers, the MTS tests showed a decreased metabolic activity of the fibroblasts on cPnBA. CONCLUSION: The applied surface treatments of cPnBA successfully improved the adhesion of viable fibroblasts. Under resting conditions as well as after shearing the highest fibroblast densities were found on surfaces with combined post-treatment.
In this thesis the interplay between hydrodynamic transport and specific adhesion is theoretically investigated. An important biological motivation for this work is the rolling adhesion of white blood cells experimentally investigated in flow chambers. There, specific adhesion is mediated by weak bonds between complementary molecular building blocks which are either located on the cell surface (receptors) or attached to the bottom plate of the flow chamber (ligands). The model system under consideration is a hard sphere covered with receptors moving above a planar ligand-bearing wall. The motion of the sphere is influenced by a simple shear flow, deterministic forces, and Brownian motion. An algorithm is given that allows to numerically simulate this motion as well as the formation and rupture of bonds between receptors and ligands. The presented algorithm spatially resolves receptors and ligands. This opens up the perspective to apply the results also to flow chamber experiments done with patterned substrates based on modern nanotechnological developments. In the first part the influence of flow rate, as well as of the number and geometry of receptors and ligands, on the probability for initial binding is studied. This is done by determining the mean time that elapses until the first encounter between a receptor and a ligand occurs. It turns out that besides the number of receptors, especially the height by which the receptors are elevated above the surface of the sphere plays an important role. These findings are in good agreement with observations of actual biological systems like white blood cells or malaria-infected red blood cells. Then, the influence of bonds which have formed between receptors and ligands, but easily rupture in response to force, on the motion of the sphere is studied. It is demonstrated that different states of motion-for example rolling-can be distinguished. The appearance of these states depending on important model parameters is then systematically investigated. Furthermore, it is shown by which bond property the ability of cells to stably roll in a large range of applied flow rates is increased. Finally, the model is applied to another biological process, the transport of spherical cargo particles by molecular motors. In analogy to the so far described systems molecular motors can be considered as bonds that are able to actively move. In this part of the thesis the mean distance the cargo particles are transported is determined.
The tissue integration of synthetic polymers can be promoted by displaying RGD peptides at the biointerface with the objective of enhancing colonization of the material by endogenous cells. A firm but flexible attachment of the peptide to the polymer matrix, still allowing interaction with receptors, is therefore of interest. Here, the covalent coupling of flexible physical anchor groups, allowing for temporary immobilization on polymeric surfaces via hydrophobic or dipole-dipole interactions, to a RGD peptide was investigated. For this purpose, a stearate or an oligo(ethylene glycol) (OEG) was attached to GRGDS in 51-69% yield. The obtained RGD linker constructs were characterized by NMR, IR and MALDI-ToF mass spectrometry, revealing that the commercially available OEG and stearate linkers are in fact mixtures of similar compounds. The RGD linker constructs were co-electrospun with poly(p-dioxanone) (PPDO). After electrospinning, nitrogen could be detected on the surface of the PPDO fibers by X-ray photoelectron spectroscopy. The nitrogen content exceeded the calculated value for the homogeneous material mixture suggesting a pronounced presentation of the peptide on the fiber surface. Increasing amounts of RGD linker constructs in the electrospinning solution did not lead to a detection of an increased amount of peptide on the scaffold surface, suggesting inhomogeneous distribution of the peptide on the PPDO fiber surface. Human adipose-derived stem cells cultured on the patches showed similar viability as when cultured on PPDO containing pristine RGD. The fully characterized RGD linker constructs could serve as valuable tools for the further development of tissue-integrating polymeric scaffolds. Copyright (c) 2016 John Wiley & Sons, Ltd.
Es ist schon seit längerer Zeit bekannt, dass nach Kontakt des Biomaterials mit der biologischen Umgebung bei Implantation oder extrakorporaler Wechselwirkung zunächst Proteine aus dem umgebenden Milieu adsorbiert werden, wobei die Oberflächeneigenschaften des Materials die Zusammensetzung der Proteinschicht und die Konformation der darin enthaltenden Proteine determinieren. Die nachfolgende Wechselwirkung von Zellen mit dem Material wird deshalb i.d.R. von der Adsorbatschicht vermittelt. Der Einfluss der Oberflächen auf die Zusammensetzung und Konformation der Proteine und die nachfolgende Wechselwirkung mit Zellen ist von besonderem Interesse, da einerseits eine Aussage über die Anwendbarkeit ermöglicht wird, andererseits Erkenntnisse über diese Zusammenhänge für die Entwicklung neuer Materialien mit verbesserter Biokompatibilität genutzt werden können. In der vorliegenden Habilitationsschrift wurde deshalb der Einfluss der Zusammensetzung von Polymeren bzw. von deren Oberflächeneigenschaften auf die Adsorption von Proteinen, den Aktivitätszustand der plasmatischen Gerinnung und die Adhäsion von Zellen untersucht. Dabei wurden auch Möglichkeiten zur Beeinflussung dieser Vorgänge über eine Veränderung der Volumenzusammensetzung oder durch Oberflächenmodifikationen von Biomaterialien vorgestellt. Erkenntnisse aus diesen Arbeiten konnten für die Entwicklung von Membranen für Biohybrid-Organe genutzt werden.
Adhesion of biological cells to their environment is mediated by two-dimensional clusters of specific adhesion molecules which are assembled in the plasma membrane of the cells. Due to the activity of the cells or external influences, these adhesion sites are usually subject to physical forces. In recent years, the influence of such forces on the stability of cellular adhesion clusters was increasingly investigated. In particular, experimental methods that were originally designed for the investigation of single bond rupture under force have been applied to investigate the rupture of adhesion clusters. The transition from single to multiple bonds, however, is not trivial and requires theoretical modelling. Rupture of biological adhesion molecules is a thermally activated, stochastic process. In this work, a stochastic model for the rupture and rebinding dynamics of clusters of parallel adhesion molecules under force is presented. In particular, the influence of (i) a constant force as it may be assumed for cellular adhesion clusters is investigated and (ii) the influence of a linearly increasing force as commonly used in experiments is considered. Special attention is paid to the force-mediated cooperativity of parallel adhesion bonds. Finally, the influence of a finite distance between receptors and ligands on the binding dynamics is investigated. Thereby, the distance can be bridged by polymeric linker molecules which tether the ligands to a substrate.