The aim of this study was to develop a one-step synthesis of gold nanotriangles (NTs) in the presence of mixed phospholipid vesicles followed by a separation process to isolate purified NTs. Negatively charged vesicles containing AOT and phospholipids, in the absence and presence of additional reducing agents (polyampholytes, polyanions or low molecular weight compounds), were used as a template phase to form anisotropic gold nanoparticles. Upon addition of the gold chloride solution, the nucleation process is initiated and both types of particles, i.e., isotropic spherical and anisotropic gold nanotriangles, are formed simultaneously. As it was not possible to produce monodisperse nanotriangles with such a one-step procedure, the anisotropic nanoparticles needed to be separated from the spherical ones. Therefore, a new type of separation procedure using combined polyelectrolyte/micelle depletion flocculation was successfully applied. As a result of the different purification steps, a green colored aqueous dispersion was obtained containing highly purified, well-defined negatively charged flat nanocrystals with a platelet thickness of 10 nm and an edge length of about 175 nm. The NTs produce promising results in surface-enhanced Raman scattering.
Hybrid nanomaterials offer the combination of individual properties of different types of nanoparticles. Some strategies for the development of new nanostructures in larger scale rely on the self-assembly of nanoparticles as a bottom-up approach. The use of templates provides ordered assemblies in defined patterns. In a typical soft-template, nanoparticles and other surface-active agents are incorporated into non-miscible liquids. The resulting self-organized dispersions will mediate nanoparticle interactions to control the subsequent self-assembly. Especially interactions between nanoparticles of very different dispersibility and functionality can be directed at a liquid-liquid interface.
In this project, water-in-oil microemulsions were formulated from quasi-ternary mixtures with Aerosol-OT as surfactant. Oleyl-capped superparamagnetic iron oxide and/or silver nanoparticles were incorporated in the continuous organic phase, while polyethyleneimine-stabilized gold nanoparticles were confined in the dispersed water droplets. Each type of nanoparticle can modulate the surfactant film and the inter-droplet interactions in diverse ways, and their combination causes synergistic effects. Interfacial assemblies of nanoparticles resulted after phase-separation. On one hand, from a biphasic Winsor type II system at low surfactant concentration, drop-casting of the upper phase afforded thin films of ordered nanoparticles in filament-like networks. Detailed characterization proved that this templated assembly over a surface is based on the controlled clustering of nanoparticles and the elongation of the microemulsion droplets. This process offers versatility to use different nanoparticle compositions by keeping the surface functionalization, in different solvents and over different surfaces. On the other hand, a magnetic heterocoagulate was formed at higher surfactant concentration, whose phase-transfer from oleic acid to water was possible with another auxiliary surfactant in ethanol-water mixture. When the original components were initially mixed under heating, defined oil-in-water, magnetic-responsive nanostructures were obtained, consisting on water-dispersible nanoparticle domains embedded by a matrix-shell of oil-dispersible nanoparticles.
Herein, two different approaches were demonstrated to form diverse hybrid nanostructures from reverse microemulsions as self-organized dispersions of the same components. This shows that microemulsions are versatile soft-templates not only for the synthesis of nanoparticles, but also for their self-assembly, which suggest new approaches towards the production of new sophisticated nanomaterials in larger scale.
In dieser Arbeit wurden sphärische Gold Nanopartikel (NP) mit einem Durchmesser größer ~ 2 nm, Gold Quantenpunkte (QDs) mit einem Durchmesser kleiner ~ 2 nm sowie Gold Nanostäbchen (NRs) unterschiedlicher Länge hergestellt und optisch charakterisiert. Zudem wurden zwei neue Synthesevarianten für die Herstellung thermosensitiver Gold QDs entwickelt werden. Sphärische Gold NP zeigen eine Plasmonenbande bei ~ 520 nm, die auf die kollektive Oszillation von Elektronen zurückzuführen ist. Gold NRs weisen aufgrund ihrer anisotropen Form zwei Plasmonenbanden auf, eine transversale Plasmonenbande bei ~ 520 nm und eine longitudinale Plasmonenbande, die vom Länge-zu-Durchmesser-Verhältnis der Gold NRs abhängig ist. Gold QDs besitzen keine Plasmonenbande, da ihre Elektronen Quantenbeschränkungen unterliegen. Gold QDs zeigen jedoch aufgrund diskreter Energieniveaus und einer Bandlücke Photolumineszenz (PL). Die synthetisierten Gold QDs besitzen eine Breitbandlumineszenz im Bereich von ~ 500-800 nm, wobei die Lumineszenz-eigenschaften (Emissionspeak, Quantenausbeute, Lebenszeiten) stark von den Herstellungs-bedingungen und den Oberflächenliganden abhängen. Die PL in Gold QDs ist ein sehr komplexes Phänomen und rührt vermutlich von Singulett- und Triplett-Zuständen her. Gold NRs und Gold QDs konnten in verschiedene Polymere wie bspw. Cellulosetriacetat eingearbeitet werden. Polymernanokomposite mit Gold NRs wurden erstmals unter definierten Bedingungen mechanisch gezogen, um Filme mit optisch anisotropen (richtungsabhängigen) Eigenschaften zu erhalten. Zudem wurde das Temperaturverhalten von Gold NRs und Gold QDs untersucht. Es konnte gezeigt werden, dass eine lokale Variation der Größe und Form von Gold NRs in Polymernanokompositen durch Temperaturerhöhung auf 225-250 °C erzielt werden kann. Es zeigte sich, dass die PL der Gold QDs stark temperaturabhängig ist, wodurch die PL QY der Proben beim Abkühlen (-7 °C) auf knapp 30 % verdoppelt und beim Erhitzen auf 70 °C nahezu vollständig gelöscht werden konnte. Es konnte demonstriert werden, dass die Länge der Alkylkette des Oberflächenliganden einen Einfluss auf die Temperaturstabilität der Gold QDs hat. Zudem wurden verschiedene neuartige und optisch anisotrope Sicherheitslabels mit Gold NRs sowie thermosensitive Sicherheitslabel mit Gold QDs entwickelt. Ebenso scheinen Gold NRs und QDs für die und die Optoelektronik (bspw. Datenspeicherung) und die Medizin (bspw. Krebsdiagnostik bzw. -therapie) von großem Interesse zu sein.
With the rise of nanotechnology in the last decade, nanofluidics has been established as a research field and gained increased interest in science and industry. Natural aqueous nanofluidic systems are very complex, there is often a predominance of liquid interfaces or the fluid contains charged or differently shaped colloids. The effects, promoted by these additives, are far from being completely understood and interesting questions arise with regards to the confinement of such complex fluidic systems. A systematic study of nanofluidic processes requires designing suitable experimental model nano – channels with required characteristics. The present work employed thin liquid films (TLFs) as experimental models. They have proven to be useful experimental tools because of their simple geometry, reproducible preparation, and controllable liquid interfaces. The thickness of the channels can be adjusted easily by the concentration of electrolyte in the film forming solution. This way, channel dimensions from 5 – 100 nm are possible, a high flexibility for an experimental system. TLFs have liquid IFs of different charge and properties and they offer the possibility to confine differently shaped ions and molecules to very small spaces, or to subject them to controlled forces. This makes the foam films a unique “device” available to obtain information about fluidic systems in nanometer dimensions. The main goal of this thesis was to study nanofluidic processes using TLFs as models, or tools, and to subtract information about natural systems plus deepen the understanding on physical chemical conditions. The presented work showed that foam films can be used as experimental models to understand the behavior of liquids in nano – sized confinement. In the first part of the thesis, we studied the process of thinning of thin liquid films stabilized with the non – ionic surfactant n – dodecyl – β – maltoside (β – C₁₂G₂) with primary interest in interfacial diffusion processes during the thinning process dependent on surfactant concentration 64. The surfactant concentration in the film forming solutions was varied at constant electrolyte (NaCl) concentration. The velocity of thinning was analyzed combining previously developed theoretical approaches. Qualitative information about the mobility of the surfactant molecules at the film surfaces was obtained. We found that above a certain limiting surfactant concentration the film surfaces were completely immobile and they behaved as non – deformable, which decelerated the thinning process. This follows the predictions for Reynolds flow of liquid between two non – deformable disks. In the second part of the thesis, we designed a TLF nanofluidic system containing rod – like multivalent ions and compared this system to films containing monovalent ions. We presented first results which recognized for the first time the existence of an additional attractive force in the foam films based on the electrostatic interaction between rod – like ions and oppositely charged surfaces. We may speculate that this is an ion bridging component of the disjoining pressure. The results show that for films prepared in presence of spermidine the transformation of the thicker CF to the thinnest NBF is more probable as films prepared with NaCl at similar conditions of electrostatic interaction. This effect is not a result of specific adsorption of any of the ions at the fluid surfaces and it does not lead to any changes in the equilibrium properties of the CF and NBF. Our hypothesis was proven using the trivalent ion Y3+ which does not show ion bridging. The experimental results are compared to theoretical predictions and a quantitative agreement on the system’s energy gain for the change from CF to NBF could be obtained. In the third part of the work, the behavior of nanoparticles in confinement was investigated with respect to their impact on the fluid flow velocity. The particles altered the flow velocity by an unexpected high amount, so that the resulting changes in the dynamic viscosity could not be explained by a realistic change of the fluid viscosity. Only aggregation, flocculation and plug formation can explain the experimental results. The particle systems in the presented thesis had a great impact on the film interfaces due to the stabilizer molecules present in the bulk solution. Finally, the location of the particles with respect to their lateral and vertical arrangement in the film was studied with advanced reflectivity and scattering methods. Neutron Reflectometry studies were performed to investigate the location of nanoparticles in the TLF perpendicular to the IF. For the first time, we study TLFs using grazing incidence small angle X – ray scattering (GISAXS), which is a technique sensitive to the lateral arrangement of particles in confined volumes. This work provides preliminary data on a lateral ordering of particles in the film.
The importance of plasmonic heating for the plasmondriven photodimerization of 4-nitrothiophenol
(2018)
Metal nanoparticles form potent nanoreactors, driven by the optical generation of energetic electrons and nanoscale heat. The relative influence of these two factors on nanoscale chemistry is strongly debated. This article discusses the temperature dependence of the dimerization of 4-nitrothiophenol (4-NTP) into 4,4′-dimercaptoazobenzene (DMAB) adsorbed on gold nanoflowers by Surface-Enhanced Raman Scattering (SERS). Raman thermometry shows a significant optical heating of the particles. The ratio of the Stokes and the anti-Stokes Raman signal moreover demonstrates that the molecular temperature during the reaction rises beyond the average crystal lattice temperature of the plasmonic particles. The product bands have an even higher temperature than reactant bands, which suggests that the reaction proceeds preferentially at thermal hot spots. In addition, kinetic measurements of the reaction during external heating of the reaction environment yield a considerable rise of the reaction rate with temperature. Despite this significant heating effects, a comparison of SERS spectra recorded after heating the sample by an external heater to spectra recorded after prolonged illumination shows that the reaction is strictly photo-driven. While in both cases the temperature increase is comparable, the dimerization occurs only in the presence of light. Intensity dependent measurements at fixed temperatures confirm this finding.
Synthesis of artificial building blocks for sortase-mediated ligation and their enzymatic linkage
(2018)
The enzyme Sortase A catalyzes the formation of a peptide bond between the recognition sequence LPXTG and an oligoglycine. While manifold ligations between proteins and various biomolecules, proteins and small synthetic molecules as well as proteins and surfaces have been reported, the aim of this thesis was to investigate the sortase-catalyzed linkage between artificial building blocks. Hence, this could pave the way for the use of sortase A for tasks from a chemical point of view and maybe even materials science.
For the proof of concept, the studied systems were kept as simple as possible at first by choosing easily accessible silica NPs and commercially available polymers. These building blocks were functionalized with peptide motifs for sortase-mediated ligation. Silica nanoparticles were synthesized with diameters of 60 and 200 nm and surface modified with C=C functionalities. Then, peptides bearing a terminal cysteine were covalently linked by means of a thiol-ene reaction. 60 nm SiO2 NPs were functionalized with pentaglycines, while peptides with LPETG motif were linked to 200 nm silica particles. Polyethyleneglycol (PEG) and poly(N isopropylacrylamide) (PNIPAM) were likewise functionalized with peptides by thiol-ene reaction between cysteine residues and C=C units in the polymer end groups. Hence, G5-PEG and PNIPAM-LPETG conjugates were obtained. With this set of building blocks, NP–polymer hybrids, NP–NP, and polymer–polymer structures were generated by sortase-mediated ligation and the product formation shown by transmission electron microscopy, MALDI-ToF mass spectrometry and dynamic light scatting, among others. Thus, the linkage of these artificial building blocks by the enzyme sortase A could be demonstrated.
However, when using commercially available polymers, the purification of the polymer–peptide conjugates was impossible and resulted in a mixture containing unmodified polymer. Therefore, strategies were developed for the own synthesis of pure peptide-polymer and polymer-peptide conjugates as building blocks for sortase-mediated ligation. The designed routes are based on preparing polymer blocks via RAFT polymerization from CTAs that are attached to N- or C-terminus, respectively, of a peptide. GG-PNIPAM was synthesized through attachment of a suitable RAFT CTA to Fmoc-GG in an esterification reaction, followed by polymerization of NIPAM and cleavage of the Fmoc protection group. Furthermore, several peptides were synthesized by solid-phase peptide synthesis. The linkage of a RAFT CTA (or
polymerization initiator) to the N-terminus of a peptide can be conducted in an automated fashion as last step in a peptide synthesizer. The synthesis of such a conjugate couldn’t be realized in the time frame of this thesis, but many promising strategies exist to continue this strategy using different coupling reagents. Such polymer building blocks can be used to synthesize protein-polymer conjugates catalyzed by sortase A and the approach can be carried on to the synthesis of block copolymers by using polymer blocks with peptide motifs on both ends.
Although the proof of concept demonstrated in this thesis only shows examples that can be also synthesized by exclusively chemical techniques, a toolbox of such building blocks will enable the future formation of new materials and pave the way for the application of enzymes in materials science. In addition to nanoparticle systems and block copolymers, this also includes combination with protein-based building blocks to form hybrid materials. Hence, sortase could become an enzymatic tool that complements established chemical linking technologies and provides specific peptide motifs that are orthogonal to all existing chemical functional groups.
It was the goal of this work to explore two different synthesis pathways using green chemistry. The first part of this thesis is focusing on the use of the urea-glass route towards single phase manganese nitride and manganese nitride/oxide nano-composites embedded in carbon, while the second part of the thesis is focusing on the use of the “saccharide route” (namely cellulose, sucrose, glucose and lignin) towards metal (Ni0), metal alloy (Pd0.9Ni0.1, Pd0.5Ni0.5, Fe0.5Ni0.5, Cu0.5Ni0.5 and W0.15Ni0.85) and ternary carbide (Mn0.75Fe2.25C) nanoparticles embedded in carbon. In the interest of battery application, MnN0.43 nanoparticles surrounded by a graphitic shell and embedded in carbon with a high surface area (79 m^2/g) were synthesized, following a previously set route.The comparison of the material characteristics before and after the discharge showed no remarkable difference in terms of composition and just slight differences in the morphological point of view, meaning the particles are stable but agglomerate. The graphitic shell is contributing to the resistance of the material and leads to a fine cyclic stability over 140 cycles of 230 mAh/g after the first charge/discharge and coulombic efficiencies close to 100%. Due to the low voltage towards Li/Li+ and the low polarization, it might be an attractive anode material for lithium ion batteries. However, the capacity is still noticeably lower than the theoretical value for MnN0.43. A mixture of MnN0.43 and MnO nanoparticles embedded in carbon (surface area 93 m^2/g) was able to improve the cyclic stability to over 160 cycles giving a capacity of 811 mAh/g, which is considerably higher than the capacity of the conventional material graphite (372 mAh/g). This nano-composite seems to agglomerate less during the process of discharge. Interestingly, although the capacity is much higher than of the single phase manganese nitride, the nano-composite seems to only contain MnN0.43 nanoparticles after the process of discharge with no oxide phase to be found. Concerning catalysis application, different metal, metal alloy, and metal carbide nanoparticles were synthesized using the saccharide route. At first, systems that were already investigated before, being Pd0.9Ni0.1, Pd0.5Ni0.5, Fe0.5Ni0.5 and Mn0.75Fe2.25C using cellulose as the carbon source were prepared and tested in an alkylation reaction of toluene with benzylchloride. Unexpectedly, the metal alloys did not show any catalytic activity, but the ternary carbide Mn0.75Fe2.25C showed fine catalytic activity of 98% conversion after 9 hour reaction time (110 °C). In a second step, the saccharide route was modified towards other carbon sources and carbon to metal ratios in order to improve the homogeneity of the samples and accessibility of the particle surfaces. The used carbon sources sucrose and glucose are similar in their basic structure of carbohydrates, but reducing the (polymeric) chain length. Indeed, the cellulose could be successfully replaced by sucrose and glucose. A lower carbon to metal ratio was found to influence the size, homogeneity and accessibility (as evidenced by TEM) of the samples. Since sucrose is an aliment, glucose is the better choice as a carbon source. Using glucose, the synthesis of Cu0.5Ni0.5 and W0.15Ni0.85 nano-composites was also possible, although the later was never obtained as pure phase. These alloy nano-composites were tested, along with nickel0 nanoparticles also prepared with glucose and on their catalytic activity towards the reduction of phenylacetylene. The results obtained let believe that any (poly) saccharide, including lignin, could be used as carbon source. The nickel0 nano-composites prepared with lignin as a carbon source were tested along with those prepared with cellulose and sucrose for their catalytic activity in the transfer hydrogenation of nitrobenzene (results compared with exposed nickel nanoparticles and nickel supported on carbon) leading to very promising results. Based on the urea-glass route and the saccharide route, simple equipment and transition metals, it was possible to have a one-pot synthesize with scale-up possibilities towards new material that can be applied in catalysis and battery systems.
In the course of this thesis gold nanoparticle/polyelectrolyte multilayer structures were prepared, characterized, and investigated according to their static and ultrafast optical properties. Using the dip-coating or spin-coating layer-by-layer deposition method, gold-nanoparticle layers were embedded in a polyelectrolyte environment with high structural perfection. Typical structures exhibit four repetition units, each consisting of one gold-particle layer and ten double layers of polyelectrolyte (cationic+anionic polyelectrolyte). The structures were characterized by X-ray reflectivity measurements, which reveal Bragg peaks up to the seventh order, evidencing the high stratication of the particle layers. In the same measurements pronounced Kiessig fringes were observed, which indicate a low global roughness of the samples. Atomic force microscopy (AFM) images veried this low roughness, which results from the high smoothing capabilities of polyelectrolyte layers. This smoothing effect facilitates the fabrication of stratified nanoparticle/polyelectrolyte multilayer structures, which were nicely illustrated in a transmission electron microscopy image. The samples' optical properties were investigated by static spectroscopic measurements in the visible and UV range. The measurements revealed a frequency shift of the reflectance and of the plasmon absorption band, depending on the thickness of the polyelectrolyte layers that cover a nanoparticle layer. When the covering layer becomes thicker than the particle interaction range, the absorption spectrum becomes independent of the polymer thickness. However, the reflectance spectrum continues shifting to lower frequencies (even for large thicknesses). The range of plasmon interaction was determined to be in the order of the particle diameter for 10 nm, 20 nm, and 150 nm particles. The transient broadband complex dielectric function of a multilayer structure was determined experimentally by ultrafast pump-probe spectroscopy. This was achieved by simultaneous measurements of the changes in the reflectance and transmittance of the excited sample over a broad spectral range. The changes in the real and imaginary parts of the dielectric function were directly deduced from the measured data by using a recursive formalism based on the Fresnel equations. This method can be applied to a broad range of nanoparticle systems where experimental data on the transient dielectric response are rare. This complete experimental approach serves as a test ground for modeling the dielectric function of a nanoparticle compound structure upon laser excitation.
Conventional energy sources are diminishing and non-renewable, take million years to form and cause environmental degradation. In the 21st century, we have to aim at achieving sustainable, environmentally friendly and cheap energy supply by employing renewable energy technologies associated with portable energy storage devices. Lithium-ion batteries can repeatedly generate clean energy from stored materials and convert reversely electric into chemical energy. The performance of lithium-ion batteries depends intimately on the properties of their materials. Presently used battery electrodes are expensive to be produced; they offer limited energy storage possibility and are unsafe to be used in larger dimensions restraining the diversity of application, especially in hybrid electric vehicles (HEVs) and electric vehicles (EVs). This thesis presents a major progress in the development of LiFePO4 as a cathode material for lithium-ion batteries. Using simple procedure, a completely novel morphology has been synthesized (mesocrystals of LiFePO4) and excellent electrochemical behavior was recorded (nanostructured LiFePO4). The newly developed reactions for synthesis of LiFePO4 are single-step processes and are taking place in an autoclave at significantly lower temperature (200 deg. C) compared to the conventional solid-state method (multi-step and up to 800 deg. C). The use of inexpensive environmentally benign precursors offers a green manufacturing approach for a large scale production. These newly developed experimental procedures can also be extended to other phospho-olivine materials, such as LiCoPO4 and LiMnPO4. The material with the best electrochemical behavior (nanostructured LiFePO4 with carbon coating) was able to delive a stable 94% of the theoretically known capacity.
Nonaqueous synthesis of metal oxide nanoparticles and their assembly into mesoporous materials
(2006)
This thesis mainly consist of two parts, the synthesis of several kinds of technologically interesting crystalline metal oxide nanoparticles via nonaqueous sol-gel process and the formation of mesoporous metal oxides using some of these nanoparticles as building blocks via evaporation induced self-assembly (EISA) technique. In the first part, the experimental procedures and characterization results of successful syntheses of crystalline tin oxide and tin doped indium oxide (ITO) nanoparticles are reported. SnO2 nanoparticles exhibit monodisperse particle size (3.5 nm in average), high crystallinity and particularly high dispersibility in THF, which enable them to become the ideal particulate precursor for the formation of mesoporous SnO2. ITO nanoparticles possess uniform particle morphology, narrow particle size distribution (5-10 nm), high crystallinity as well as high electrical conductivity. The synthesis approaches and characterization of various mesoporous metal oxides, including TiO2, SnO2, mixture of CeO2 and TiO2, mixture of BaTiO3 and SnO2, are reported in the second part of this thesis. Mesoporous TiO2 and SnO2 are presented as highlights of this part. Mesoporous TiO2 was produced in the forms of both films and bulk material. In the case of mesoporous SnO2, the study was focused on the high order of the porous structure. All these mesoporous metal oxides show high crystallinity, high surface area and rather monodisperse pore sizes, which demonstrate the validity of EISA process and the usage of preformed crystalline nanoparticles as nanobuilding blocks (NBBs) to produce mesoporous metal oxides.