The construction of nano-sized, two-dimensionally ordered nanoparticle (NP) superstructures is important for various advanced applications such as photonics, sensing, catalysis, or nano-circuitry. Currently, such structures are fabricated using the templated organization approach, in which the templates are mainly created by photo-lithography or laser-lithography and other invasive top-down etching procedures. In this work, we present an alternative bottom-up preparation method for the controlled deposition of NPs into hierarchical structures. Lamellar polystyrene-block-poly(2-vinylpyridinium) thin films featuring alternating stripes of neutral PS and positively charged P2VP domains serve as templates, allowing for the selective adsorption of negatively charged gold NPs. Dense NP assembly is achieved by a simple immersion process, whereas two-dimensionally ordered arrays of NPs are realized by microcontact printing (mu CP), utilizing periodic polydimethylsiloxane wrinkle grooves loaded with gold NPs. This approach enables the facile construction of hierarchical NP arrays with variable geometries. Copyright (C) 2016 John Wiley & Sons, Ltd.
Understanding the principles of self-organisation exhibited by block copolymers requires the combination of synthetic and physicochemical knowledge. The ability to synthesise block copolymers with desired architecture facilitates the ability to manipulate their aggregation behaviour, thus providing the key to nanotechnology. Apart from relative block volumes, the size and morphology of the produced nanostructures is controlled by the effective incompatibility between the different blocks. Since polymerisation techniques allowing for the synthesis of well-defined block copolymers are restricted to a limited number of monomers, the ability to tune the incompatibility is very limited. Nevertheless, Polymer Analogue Reactions can offer another possibility for the production of functional block copolymers by chemical modifications of well-defined polymer precursors. Therefore, by applying appropriate modification methods both volume fractions and incompatibility, can be adjusted. Moreover, copolymers with introduced functional units allow utilization of the concept of molecular recognition in the world of synthetic polymers. The present work describes a modular synthetic approach towards functional block copolymers. Radical addition of functional mercaptanes was employed for the introduction of diverse functional groups to polybutadiene-containing block copolymers. Various modifications of 1,2-polybutadiene-poly(ethylene oxide) block copolymer precursors are described in detail. Furthermore, extension of the concept to 1,2-polybutadiene-polystyrene block copolymers is demonstrated. Further investigations involved the self-organisation of the modified block copolymers. Formed aggregates in aqueous solutions of block copolymers with introduced carboxylic acid, amine and hydroxyl groups as well as fluorinated chains were characterised. Study of the aggregation behaviour allowed general conclusions to be drawn regarding the influence of the introduced groups on the self-organisation of the modified copolymers. Finally, possibilities for the formation of complexes, based on electrostatic or hydrogen-bonding interactions in mixtures of block copolymers bearing mutually interacting functional groups, were investigated.
Synthesis of artificial building blocks for sortase-mediated ligation and their enzymatic linkage
(2018)
The enzyme Sortase A catalyzes the formation of a peptide bond between the recognition sequence LPXTG and an oligoglycine. While manifold ligations between proteins and various biomolecules, proteins and small synthetic molecules as well as proteins and surfaces have been reported, the aim of this thesis was to investigate the sortase-catalyzed linkage between artificial building blocks. Hence, this could pave the way for the use of sortase A for tasks from a chemical point of view and maybe even materials science.
For the proof of concept, the studied systems were kept as simple as possible at first by choosing easily accessible silica NPs and commercially available polymers. These building blocks were functionalized with peptide motifs for sortase-mediated ligation. Silica nanoparticles were synthesized with diameters of 60 and 200 nm and surface modified with C=C functionalities. Then, peptides bearing a terminal cysteine were covalently linked by means of a thiol-ene reaction. 60 nm SiO2 NPs were functionalized with pentaglycines, while peptides with LPETG motif were linked to 200 nm silica particles. Polyethyleneglycol (PEG) and poly(N isopropylacrylamide) (PNIPAM) were likewise functionalized with peptides by thiol-ene reaction between cysteine residues and C=C units in the polymer end groups. Hence, G5-PEG and PNIPAM-LPETG conjugates were obtained. With this set of building blocks, NP–polymer hybrids, NP–NP, and polymer–polymer structures were generated by sortase-mediated ligation and the product formation shown by transmission electron microscopy, MALDI-ToF mass spectrometry and dynamic light scatting, among others. Thus, the linkage of these artificial building blocks by the enzyme sortase A could be demonstrated.
However, when using commercially available polymers, the purification of the polymer–peptide conjugates was impossible and resulted in a mixture containing unmodified polymer. Therefore, strategies were developed for the own synthesis of pure peptide-polymer and polymer-peptide conjugates as building blocks for sortase-mediated ligation. The designed routes are based on preparing polymer blocks via RAFT polymerization from CTAs that are attached to N- or C-terminus, respectively, of a peptide. GG-PNIPAM was synthesized through attachment of a suitable RAFT CTA to Fmoc-GG in an esterification reaction, followed by polymerization of NIPAM and cleavage of the Fmoc protection group. Furthermore, several peptides were synthesized by solid-phase peptide synthesis. The linkage of a RAFT CTA (or
polymerization initiator) to the N-terminus of a peptide can be conducted in an automated fashion as last step in a peptide synthesizer. The synthesis of such a conjugate couldn’t be realized in the time frame of this thesis, but many promising strategies exist to continue this strategy using different coupling reagents. Such polymer building blocks can be used to synthesize protein-polymer conjugates catalyzed by sortase A and the approach can be carried on to the synthesis of block copolymers by using polymer blocks with peptide motifs on both ends.
Although the proof of concept demonstrated in this thesis only shows examples that can be also synthesized by exclusively chemical techniques, a toolbox of such building blocks will enable the future formation of new materials and pave the way for the application of enzymes in materials science. In addition to nanoparticle systems and block copolymers, this also includes combination with protein-based building blocks to form hybrid materials. Hence, sortase could become an enzymatic tool that complements established chemical linking technologies and provides specific peptide motifs that are orthogonal to all existing chemical functional groups.
Sortase A (SrtA) from Staphylococcus aureus has been often used for ligating a protein with other natural or synthetic compounds in recent years. Here we show that SrtA-mediated ligation (SML) is universally applicable for the linkage of two purely artificial building blocks. Silica nanoparticles (NPs), poly(ethylene glycol) and poly(N-isopropyl acrylamide) are chosen as synthetic building blocks. As a proof of concept, NP-polymer, NP-NP, and polymer-polymer structures are formed by SrtA catalysis. Therefore, the building blocks are equipped with the recognition sequence needed for SrtA reaction-the conserved peptide LPETG-and a pentaglycine motif. The successful formation of the reaction products is shown by means of transmission electron microscopy (TEM), matrix assisted laser desorption ionization-time of flight mass spectrometry (MALDI-ToF MS), and dynamic light scattering (DLS). The sortase catalyzed linkage of artificial building blocks sets the stage for the development of a new approach to link synthetic structures in cases where their synthesis by established chemical methods is complicated.
It is demonstrated that the orientation of striped patterns can be reversibly switched between two perpendicular in-plane orientations upon exposure to electric fields. The results on thin films of symmetric polystyrene-block-poly(2-vinyl pyridine) polymer in the intermediate segregation regime disclose two types of reorientation mechanisms from perpendicular to parallel relative to the electric field orientation. Domains orient via grain rotation and via formation of defects such as stretched undulations and temporal phase transitions. The contribution of additional fields to the structural evolution is also addressed to elucidate the generality of the observed phenomena. In particular solvent effects are considered. This study reveals the stabilization of the meta-stable in-plane oriented lamella due to sequential swelling and quenching of the film. Further, the reorientation behavior of lamella domains blended with selective nanoparticles is addressed, which affect the interfacial tensions of the blocks and hence introduce another internal field to the studied system. Switching the orientation of aligned block copolymer patterns between two orthogonal directions may open new applications of nanomaterials as switchable electric nanowires or optical gratings.
In the present thesis, self-assembly of hydrophilic polymers, reinforced hydrogels and inorganic/polymer hybrids were examined. The thesis describes an avenue from polymer synthesis via various methods over polymer self-assembly to the formation of polymer materials that have promising properties for future applications.
Hydrophilic polymers were utilized to form multi-phase systems, water-in-water emulsions and self-assembled structures, e.g. particles/aggregates or hollow structures from completely water-soluble building blocks. The structuring of aqueous environments by hydrophilic homo and block copolymers was further utilized in the formation of supramolecular hydrogels with compartments or specific thermal behavior. Furthermore, inorganic graphitic carbon nitride (g-CN) was utilized as photoinitiator for hydrogel formation and as reinforcer for hydrogels. As such, hydrogels with remarkable mechanical properties were synthesized, e.g. high compressibility, high storage modulus or lubricity. In addition, g-CN was combined with polymers for a broad range of materials, e.g. coatings, films or latex, that could be utilized in photocatalytic applications. Another inorganic material class was combined with polymers in the present thesis as well, namely metal-organic frameworks (MOFs). It was shown that the pore structure of MOFs enables improved control over tacticity and achievement of high molar masses. Furthermore, MOF-based polymerization catalysis was introduced with improved control for coordinating monomers, catalyst recyclability and decreased metal contamination in the product. Finally, the effect of external influence on MOF morphology was studied, e.g. via solvent or polymer additives, which allowed the formation of various MOF structures.
Overall, advances in several areas of polymer science are presented in here. A major topic of the thesis was hydrophilic polymers and hydrogels that currently constitute significant materials in the polymer field due to promising future applications in biomedicine. Moreover, the combination of polymers with materials from other areas of research, i.e. g-CN and MOFs, provided various new materials with remarkable properties also of interest for applications in the future, e.g. coatings, particle structures and catalysis.
Water-soluble, amphiphilic diblock copolymers were synthesized by reversible addition fragmentation chain transfer polymerization. They consist of poly(butyl acrylate) as hydrophobic block with a low glass transition temperature and three different nonionic water-soluble blocks, namely, the classical hydrophilic block poly(dimethylacrylamide), the strongly hydrophilic poly(acryloyloxyethyl methylsulfoxide), and the thermally sensitive poly(N-acryloylpyrrolidine). Aqueous micellar solutions of the block copolymers were prepared and characterized by static and dynamic light scattering analysis (DLS and SLS). No critical micelle concentration could be detected. The micellization was thermodynamically favored, although kinetically slow, exhibiting a marked dependence on the preparation conditions. The polymers formed micelles with a hydrodynamic diameter from 20 to 100 nm, which were stable upon dilution. The micellar size was correlated with the composition of the block copolymers and their overall molar mass. The micelles formed with the two most hydrophilic blocks were particularly stable upon temperature cycles, whereas the thermally sensitive poly(N-acryloylpyrrolidine) block showed a temperature-induced precipitation. According to combined SLS and DLS analysis, the micelles exhibited an elongated shape such as rods or worms. It should be noted that the block copolymers with the most hydrophilic poly(sulfoxide) block formed inverse micelles in certain organic solvents.
The self-assembly of amphiphilic polymers in aqueous systems is important for a plethora of applications, in particular in the field of cosmetics and detergents. When introducing thermoresponsive blocks, the aggregation behavior of these polymers can be controlled by changing the temperature. While confined to simple diblock copolymer systems for long, the complexity - and thus the versatility - of such smart systems can be strongly enlarged, once designed monomers, specific block sizes, different architectures, or additional functional groups such as hydrophobic stickers are implemented. In this work, the structure-property relationship of such thermoresponsive amphiphilic block copolymers was investigated by varying their structure systematically. The block copolymers were generally composed of a permanently hydrophobic sticker group, a permanently hydrophilic block, and a thermoresponsive block exhibiting a Lower Critical Solution Temperature (LCST) behavior. While the hydrophilic block consisted of N,N dimethylacrylamide (DMAm), different monomers were used for the thermoresponsive block, such as N n propylacrylamide (NPAm), N iso propylacrylamide (NiPAm), N,N diethylacrylamide (DEAm), N,N bis(2 methoxyethyl)acrylamide (bMOEAm), or N acryloylpyrrolidine (NAP) with different reported LCSTs of 25, 32, 33, 42 and 56 °C, respectively. The block copolymers were synthesized by successive reversible addition fragmentation chain transfer (RAFT) polymerization. For the polymers with the basic linear, the twinned hydrophobic and the symmetrical quasi miktoarm architectures, the results were well defined block sizes and end groups as well as narrow molar mass distributions (Ɖ ≤ 1.3). More complex architectures, such as the twinned thermoresponsive and the non-symmetrical quasi miktoarm one, were achieved by combining RAFT polymerization with a second technique, namely atom transfer radical polymerization (ATRP) or single unit monomer insertion (SUMI), respectively. The obtained block copolymers showed well defined block sizes, but due to the complexity of these reaction paths, the dispersities were generally higher (Ɖ ≤ 1.8) and some end groups were lost.
The thermoresponsive behavior of the block copolymers was investigated by turbidimetry and dynamic light scattering (DLS). Below the phase transition temperature, the polymers were soluble in water and small micellar structures were visible. However, above the phase transition temperature, the aggregation behavior was strongly dependent on the architecture and the chemical structure of the thermoresponsive block. Thermoresponsive blocks comprising PNAP and PbMOEAm with DPn = 40 showed no cloud point (CP), since their already high LCSTs were further increased by the attached hydrophilic block. Depending on the architecture as well as on the block size, block copolymers with PNiPAm, PDEAm and PNPAm showed different CP’s. Large aggregates were visible for block copolymers with PNiPAm and PDEAm above their CP. For PNPAm containing block copolymers, the phase transition was very sensitive towards the architecture resulting in either small or large aggregates.
In addition, fluorescence studies were performed using PDMAm and PNiPAm homo and block copolymers with linear architecture, functionalized with complementary fluorescence dyes introduced at the opposite chain ends. The thermoresponsive behavior was studied in pure aqueous solution as well as in an oil in water (o/w) microemulsion. The findings indicate that the block copolymer behaves as polymeric surfactant at low temperatures, with one relatively small hydrophobic end group and an extended hydrophilic chain forming ‘hairy micelles’ similar as the other synthesized architectures. Above the phase transition temperature of the PNiPAm block, however, the copolymer behaves as associative telechelic polymer with two non-symmetrical hydrophobic end groups, which do not mix. Thus, instead of a network of bridged ‘flower micelles’, large dynamic aggregates are formed. These are connected alternatingly by the original micellar cores as well as by clusters of the collapsed PNiPAm blocks. This type of bridged micelles is even more favored in the o/w microemulsion than in pure aqueous solution.
This work describes the synthesis and characterization of stimuli-responsive polymers made by reversible addition-fragmentation chain transfer (RAFT) polymerization and the investigation of their self-assembly into “smart” hydrogels. In particular the hydrogels were designed to swell at low temperature and could be reversibly switched to a collapsed hydrophobic state by rising the temperature. Starting from two constituents, a short permanently hydrophobic polystyrene (PS) block and a thermo-responsive poly(methoxy diethylene glycol acrylate) (PMDEGA) block, various gelation behaviors and switching temperatures were achieved. New RAFT agents bearing tert-butyl benzoate or benzoic acid groups, were developed for the synthesis of diblock, symmetrical triblock and 3-arm star block copolymers. Thus, specific end groups were attached to the polymers that facilitate efficient macromolecular characterization, e.g by routine 1H-NMR spectroscopy. Further, the carboxyl end-groups allowed functionalizing the various polymers by a fluorophore. Because reports on PMDEGA have been extremely rare, at first, the thermo-responsive behavior of the polymer was investigated and the influence of factors such as molar mass, nature of the end-groups, and architecture, was studied. The use of special RAFT agents enabled the design of polymer with specific hydrophobic and hydrophilic end-groups. Cloud points (CP) of the polymers proved to be sensitive to all molecular variables studied, namely molar mass, nature and number of the end-groups, up to relatively high molar masses. Thus, by changing molecular parameters, CPs of the PMDEGA could be easily adjusted within the physiological interesting range of 20 to 40°C. A second responsivity, namely to light, was added to the PMDEGA system via random copolymerization of MDEGA with a specifically designed photo-switchable azobenzene acrylate. The composition of the copolymers was varied in order to determine the optimal conditions for an isothermal cloud point variation triggered by light. Though reversible light-induced solubility changes were achieved, the differences between the cloud points before and after the irradiation were small. Remarkably, the response to light differed from common observations for azobenzene-based systems, as CPs decreased after UV-irradiation, i.e with increasing content of cis-azobenzene units. The viscosifying and gelling abilities of the various block copolymers made from PS and PMDEGA blocks were studied by rheology. Important differences were observed between diblock copolymers, containing one hydrophobic PS block only, the telechelic symmetrical triblock copolymers made of two associating PS termini, and the star block copolymers having three associating end blocks. Regardless of their hydrophilic block length, diblock copolymers PS11 PMDEGAn were freely flowing even at concentrations as high as 40 wt. %. In contrast, all studied symmetrical triblock copolymers PS8-PMDEGAn-PS8 formed gels at low temperatures and at concentrations as low as 3.5 wt. % at best. When heated, these gels underwent a gel-sol transition at intermediate temperatures, well below the cloud point where phase separation occurs. The gel-sol transition shifted to markedly higher transition temperatures with increasing length of the hydrophilic inner block. This effect increased also with the number of arms, and with the length of the hydrophobic end blocks. The mechanical properties of the gels were significantly altered at the cloud point and liquid-like dispersions were formed. These could be reversibly transformed into hydrogels by cooling. This thesis demonstrates that high molar mass PMDEGA is an easily accessible, presumably also biocompatible and at ambient temperature well water-soluble, non-ionic thermo-responsive polymer. PMDEGA can be easily molecularly engineered via the RAFT method, implementing defined end-groups, and producing different, also complex, architectures, such as amphiphilic triblock and star block copolymers, having an analogous structure to associative telechelics. With appropriate design, such amphiphilic copolymers give way to efficient, “smart” viscosifiers and gelators displaying tunable gelling and mechanical properties.
Modular toolkit of multifunctional block copoly(2-oxazoline)s for the synthesis of nanoparticles
(2021)
Post-polymerization modification provides an elegant way to introduce chemical functionalities onto macromolecules to produce tailor-made materials with superior properties. This concept was adapted to well-defined block copolymers of the poly(2-oxazoline) family and demonstrated the large potential of these macromolecules as universal toolkit for numerous applications. Triblock copolymers with separated water-soluble, alkyne- and alkene-containing segments were synthesized and orthogonally modified with various low-molecular weight functional molecules by copper(I)-catalyzed azide-alkyne cycloaddition (CuAAC) and thiol-ene (TE) click reactions, respectively. Representative toolkit polymers were used for the synthesis of gold, iron oxide and silica nanoparticles.
Electrostatic attraction between charged nano particles and oppositely charged nanopatterned polymeric films enables tailored structuring of functional nanoscopic surfaces. The bottom-up fabrication of organic/inorganic composites for example bears promising potential toward cheap fabrication of catalysts, optical sensors, and the manufacture of miniaturized electric circuitry. However, only little is known about the time-dependent adsorption behavior and the electronic or ionic charge transfer in the film bulk and at interfaces during nanoparticle assembly via electrostatic interactions. In situ electrochemical impedance spectroscopy (EIS) in combination with a microfluidic system for fast and reproducible liquid delivery was thus applied to monitor the selective deposition of negatively charged gold nanoparticles on top of positively charged poly(2-vinylpyridinium) (qP2VP) domains of phase separated lamellar poly(styrene)-block-poly(2-vinylpyridinium) (PS-b-qP2VP) diblock copolymer thin films. The acquired impedance data delivered information with respect to interfacial charge alteration, ionic diffusion, and the charge dependent nanoparticle adsorption kinetics, considering this yet unexplored system. We demonstrate that the selective adsorption of negatively charged gold nanoparticles (AuNPs) on positively charged qP2VP domains of lamellar PS-b-qP2VP thin films can indeed be tracked by EIS. Moreover, we show that the nanoparticle adsorption kinetics and the nanoparticle packing density are functions of the charge density in the qP2VP domains.
Neue Systeme für triphile, fluorkohlenstofffreie Blockcopolymere in Form von Acrylat-basierten thermoresponsiven Blockcopolymeren sowie Acrylat- bzw. Styrol-basierten Terblock-Polyelektrolyten mit unterschiedlich chaotropen Kationen des jeweiligen polyanionischen Blocks wurden entwickelt. Multikompartiment-Mizellen, mizellare Aggregate mit ultrastrukturiertem hydrophobem Mizellkern die biologischen Strukturen wie dem Humanalbumin nachempfunden sind, sollten bei der Selbstorganisation in wässriger Umgebung entstehen. Durch Verwendung apolarer und polarer Kohlenwasserstoff-Domänen anstelle von fluorophilen Fluorkohlenstoff-Domänen sollte erstmals anhand solcher triphilen Systeme nachgewiesen werden, ob diese in der Lage zur selektiven Aufnahme hydrophober Substanzen in unterschiedliche Domänen des Mizellkerns sind.
Mit Hilfe von sequentieller RAFT-Polymerisation wurden diese neuen triphilen Systeme hergestellt, die über einen permanent hydrophilen, eine permanent stark hydrophoben und einen dritten Block verfügen, der durch externe Einflüsse, speziell die Induzierung eines thermischen Coil-to-globule-Übergangs bzw. die Zugabe von organischen, hydrophoben Gegenionen von einem wasserlöslichen in einen polar-hydrophoben Block umgewandelt werden kann. Als RAFT-Agens wurde 4-(Trimethylsilyl)benzyl(3-(trimethylsilyl)-propyl)-trithiocarbonat mit zwei unterschiedlichen TMS-Endgruppen verwendet, das kontrollierte Reaktions-bedingungen sowie die molekulare Charakterisierung der komplexen Copolymere ermöglichte.
Die beiden Grundtypen der linearen ternären Blockcopolymere wurden jeweils in zwei 2 Modell-Systeme, die geringfügig in ihren chemischen Eigenschaften sowie in dem Blocklängenverhältnis von hydrophilen und hydrophoben Polymersegmenten variierten, realisiert und unterschiedliche Permutation der Blöcke aufwiesen.
Als ersten Polymertyp wurden amphiphile thermoresponsive Blockcopolymere verwendet. Modell-System 1 bestand aus dem permanent hydrophoben Block Poly(1,3-Bis(butylthio)-prop-2-yl-acrylat), permanent hydrophilen Block Poly(Oligo(ethylenglykol)monomethyletheracrylat) und den thermoresponsiven Block Poly(N,N‘-Diethylacrylamid), dessen Homopolymer eine LCST-Phasenübergang (LCST, engl.: lower critical solution temperature) bei ca. 36°C aufweist. Das Modell-System 2 bestand aus dem permanent hydrophilen Block Poly(2-(Methylsulfinyl)ethylacrylat), dem permanent hydrophoben Block Poly(2-Ethylhexylacrylat) und wiederum Poly(N,N‘-Diethylacrylamid). Im ternären Blockcopolymer erhöhte sich, je nach Blocksequenz und relativen Blocklängen, der LCST-Übergang auf 50 – 65°C. Bei der Untersuchung der Selbstorganisation für die Polymer-Systeme dieses Typs wurde die Temperatur variiert, um verschieden mizellare Überstrukturen in wässriger Umgebung zu erzeugen bzw. oberhalb des LCST-Übergangs Multikompartiment-Mizellen nachzuweisen. Die Unterschiede in der Hydrophilie bzw. den sterischen Ansprüche der gewählten hydrophilen Blöcke sowie die Variation der jeweiligen Blocksequenzen ermöglichte darüber hinaus die Bildung verschiedenster Morphologien mizellarer Aggregate.
Der zweite Typ basierte auf ein Terblock-Polyelektrolyt-System mit Polyacrylaten bzw. Polystyrolen als Polymerrückgrat. Polymere ionische Flüssigkeiten wurden als Vorlage der Entwicklung zweier Modell-Systeme genommen. Eines der beiden Systeme bestand aus dem permanent hydrophilen Block Poly(Oligo(ethylenglykol)monomethyletheracrylat, dem permanent hydrophoben Block Poly(2-Ethylhexylacrylat) sowie dem Polyanion-Block Poly(3-Sulfopropylacrylat). Die Hydrophobie des Polyanion-Blocks variierte durch Verwendung großer organischer Gegenionen, nämlich Tetrabutylammonium, Tetraphenylphosphonium und Tetraphenylstibonium.
Analog wurde in einem weiteren System aus dem permanent hydrophilen Block Poly(4-Vinylbenzyltetrakis(ethylenoxy)methylether), dem permanent hydrophoben Block Poly(para-Methylstyrol) und Poly(4-Styrolsulfonat) mit den entsprechenden Gegenionen gebildet. Aufgrund unterschiedlicher Kettensteifigkeit in beiden Modell-Systemen sollte es bei der Selbstorganisation der mizellarer Aggregate zu unterschiedlichen Überstrukturen kommen.
Mittels DSC-Messungen konnte nachgewiesen werden, dass für alle Modell-Systeme die Blöcke in Volumen-Phase miteinander inkompatibel waren, was eine Voraussetzung für Multikompartimentierung von mizellaren Aggregaten ist. Die Größe mizellarer Aggregate sowie der Einfluss externer Einflüsse wie der Veränderung der Temperatur bzw. der Hydrophobie und Größe von Gegenionen auf den hydrodynamischen Durchmesser mittels DLS-Untersuchungen wurden für alle Modell-Systeme untersucht. Die Ergebnisse zu den thermoresponsiven ternären Blockcopolymeren belegten , dass sich oberhalb der Phasenübergangstemperatur des thermoresponsiven Blocks die Struktur der mizellaren Aggregate änderte, indem der p(DEAm)-Block scheinbar kollabierte und so zusammen mit den permanent hydrophoben Block den jeweiligen Mizellkern bildete. Nach gewisser Equilibrierungszeit konnten bei Raumtemperatur dir ursprünglichen mizellaren Strukturen regeneriert werden. Hingegen konnte für die Terblock-Polyelektrolyt-Systeme bei Verwendung der unterschiedlich hydrophoben Gegenionen kein signifikanter Unterschied in der Größe der mizellaren Aggregate beobachtet werden.
Zur Abbildung der mizellaren Aggregate mittels kryogene Transmissionselektronenmikroskopie (cryo-TEM) der mizellaren Aggregate war mit Poly(1,3-Bis(butylthio)-prop-2-yl-acrylat) ein Modell-System so konzipiert, dass ein erhöhter Elektronendichtekontrast durch Schwefel-Atome die Visualisierung ultrastrukturierter hydrophober Mizellkerne ermöglichte. Dieser Effekt sollte in den Terblock-Polyelektrolyt-Systemen auch durch die Gegenionen Tetraphenylphosphonium und Tetraphenylstibonium nachgestellt werden. Während bei den thermoresponsiven Systemen auch oberhalb des Phasenübergangs kein Hinweis auf Ultrastrukturierung beobachtet wurde, waren für die Polyelektrolyt-Systeme, insbesondere im Fall von Tetraphenylstibonium als Gegenion Überstrukturen zu erkennen. Der Nachweis der Bildung von Multikompartiment-Mizellen war für beide Polymertypen mit dieser abbildenden Methode nicht möglich. Die Unterschiede in der Elektronendichte einzelner Blöcke müsste möglicherweise weiter erhöht werden um Aussagen diesbezüglich zu treffen.
Die Untersuchung von ortsspezifischen Solubilisierungsexperimenten mit solvatochromen Fluoreszenzfarbstoffen mittels „steady-state“-Fluoreszenzspektroskopie durch Vergleich der Solubilisierungsorte der Terblockcopolymere bzw. –Polyelektrolyte mit den jeweiligen Solubilisierungsorten von Homopolymer- und Diblock-Vorstufen sollten den qualitativen Nachweis der Multikompartimentierung erbringen. Aufgrund der geringen Mengen an Farbstoff, die für die Solubilisierungsexperimente eingesetzt wurden zeigten DLS-Untersuchungen keine störenden Effekte der Sonden auf die Größe der mizellaren Aggregate. Jedoch erschwerten Quench-Effekte im Falle der Polyelektrolyt Modell-Systeme eine klare Interpretation der Daten. Im Falle der Modell-Systeme der thermoresponsiven Blockcopolymere waren dagegen deutliche solvatochrome Effekte zwischen der Solubilisierung in den mizellaren Aggregaten unterhalb und oberhalb des Phasenübergangs zu erkennen. Dies könnte ein Hinweis auf Multikompartimentierung oberhalb des LCST-Übergangs sein. Ohne die Informationen einer Strukturanalyse wie z.B. der Röntgen- oder Neutronenkleinwinkelstreuung (SAXS oder SANS), kann nicht abschließend geklärt werden, ob die Solubilisierung in mizellaren hydrophoben Domänen des kollabierten Poly(N,N‘-Diethylacrylamid) erfolgt oder in einer Mischform von mizellaren Aggregaten mit gemittelter Polarität.
Self-assembly of polymeric building blocks is a powerful tool for the design of novel materials and structures that combine different properties and may respond to external stimuli. In the past decades, most studies were focused on the self-assembly of amphiphilic diblock copolymers in solution. The dissolution of these block copolymers in a solvent selective for one block results mostly in the formation of micelles. The micellar structure of diblock copolymers is inherently limited to a homogeneous core surrounded by a corona, which keeps the micelle in solution. Thus, for drug-delivery applications, such structures only offer a single domain (the hydrophobic inner core) for drug entrapment. Whereas multicompartment micelles composed of a water-soluble shell and a segregated hydrophobic core are novel, interesting morphologies for applications in a variety of fields including medicine, pharmacy and biotechnology. The separated incompatible compartments of the hydrophobic core could enable the selective entrapment and release of various hydrophobic drugs while the hydrophilic shell would permit the stabilization of these nanostructures in physiological media. However, so far, the preparation and control of stable multicompartment micellar systems are in the first stages and the number of morphological studies concerning such micelles is rather low. Thus considerably little is known about their exact inner structures. In the present study, we concentrate on four different approaches for the preparation of multicompartment micelles by self-assembly in aqueous media. A similarity of all approaches was that hydrocarbon and fluorocarbon blocks were selected for all employed copolymers since such segments tend to be strongly incompatible, and thus favor the segregation into distinct domains. Our studies have shown that the self-assembly of the utilized copolymers in aqueous solution leads in three cases to the formation of multicompartment micelles. As expected the shape and size of the micelles depend on the molecular architecture and to some extent also on the way of preparation. These novel structured colloids may serve as models as well as mimics for biological structures such as globular proteins, and may open interesting opportunities for nanotechnology applications.
H-1 NMR relaxation is used to study the self-assembly of a double thermoresponsive diblock copolymer in dilute aqueous solution. Above the first transition temperature, at which aggregation into micellar structures is observed, the trimethylsilyl (TMS)-labeled end group attached to the shell-forming block shows a biphasic T-2 relaxation. The slow contribution reflects the TMS groups located at the periphery of the hydrophilic shell, in agreement with a star-like micelle. The fast T-2 contribution corresponds to the TMS groups, which fold back toward the hydrophobic core, reflecting a flower-like micelle. These results confirm the formation of block copolymer micelles of an intermediate nature (i.e., of partial flower-like and star-like character), in which a part of the TMS end groups folds back to the core due to hydrophobic interactions.
Copolyesterurethanes (PDLCLs) based on oligo(epsilon-caprolactone) (OCL) and oligo(omega-pentadecalactone) (OPDL) segments are biodegradable thermoplastic temperature-memory polymers. The temperature-memory capability in these polymers with crystallizable control units is implemented by a thermomechanical programming process causing alterations in the crystallite arrangement and chain organization. These morphological changes can potentially affect degradation. Initial observations on the macroscopic level inspire the hypothesis that switching of the controlling units causes an accelerated degradation of the material, resulting in programmable degradation by sequential coupling of functions. Hence, detailed degradation studies on Langmuir films of a PDLCL with 40 wt% OPDL content are carried out under enzymatic catalysis. The temperature-memory creation procedure is mimicked by compression at different temperatures. The evolution of the chain organization and mechanical properties during the degradation process is investigated by means of polarization-modulated infrared reflection absorption spectroscopy, interfacial rheology and to some extend by X-ray reflectivity. The experiments on PDLCL Langmuir films imply that degradability is not enhanced by thermal switching, as the former depends on the temperature during cold programming. Nevertheless, the thin film experiments show that the leaching of OCL segments does not induce further crystallization of the OPDL segments, which is beneficial for a controlled and predictable degradation.
Self-assembly of macromolecules is fundamental to life itself, and historically, these systems have been primitively mimicked by the development of amphiphilic systems, driven by the hydrophobic effect. Herein, we demonstrate that self-assembly of purely hydrophilic systems can be readily achieved with similar ease and success. We have synthesized double hydrophilic block copolymers from polysaccharides and poly(ethylene oxide) or poly(sarcosine) to yield high molar mass diblock copolymers through oxime chemistry. These hydrophilic materials can easily assemble into nanosized (<500nm) and microsized (>5m) polymeric vesicles depending on concentration and diblock composition. Because of the solely hydrophilic nature of these materials, we expect them to be extraordinarily water permeable systems that would be well suited for use as cellular mimics.
Block copolymers of 1H,1H,2H,2H-perfluorodecyl acrylate (AC8) were obtained from ARGET ATRP. To obtain block copolymers of low dispersity the PAC8 block was synthesized in anisole with a CuBr(2)/PMDETA catalyst in the presence of tin(II) 2-ethylhexanoate as a reducing agent. The PAC8 block was subsequently used as macroinitiator for copolymerization with butyl and tert-butyl acrylate carried out in scCO(2). To achieve catalyst solubility in CO(2) two fluorinated ligands were employed. The formation of block copolymers was confirmed by size exclusion chromatography and DSC.