Shape-Memory Capability of Copolyetheresterurethane Microparticles Prepared via Electrospraying
- Multifunctional thermo-responsive and degradable microparticles exhibiting a shapememory effect (SME) have attracted widespread interest in biomedicine as switchable delivery vehicles or microactuators. In this work almost spherical solid microparticles with an average diameter of 3.9 +/- 0.9 mm are prepared via electrospraying of a copolyetheresterurethane named PDC, which is composed of crystallizable oligo(p-dioxanone) (OPDO) hard and oligo(e-caprolactone) (OCL) switching segments. The PDC microparticles are programmed via compression at different pressures and their shapememory capability is explored by off-line and online heating experiments. When a low programming pressure of 0.2 MPa is applied a pronounced thermally-induced shape-memory effect is achieved with a shape recovery ratio about 80%, while a high programming pressure of 100 MPa resulted in a weak shape-memory performance. Finally, it is demonstrated that an array of PDC microparticles deposited on a polypropylene (PP) substrate can be successfully programmed into aMultifunctional thermo-responsive and degradable microparticles exhibiting a shapememory effect (SME) have attracted widespread interest in biomedicine as switchable delivery vehicles or microactuators. In this work almost spherical solid microparticles with an average diameter of 3.9 +/- 0.9 mm are prepared via electrospraying of a copolyetheresterurethane named PDC, which is composed of crystallizable oligo(p-dioxanone) (OPDO) hard and oligo(e-caprolactone) (OCL) switching segments. The PDC microparticles are programmed via compression at different pressures and their shapememory capability is explored by off-line and online heating experiments. When a low programming pressure of 0.2 MPa is applied a pronounced thermally-induced shape-memory effect is achieved with a shape recovery ratio about 80%, while a high programming pressure of 100 MPa resulted in a weak shape-memory performance. Finally, it is demonstrated that an array of PDC microparticles deposited on a polypropylene (PP) substrate can be successfully programmed into a smart temporary film, which disintegrates upon heating to 60 degrees C.…
Verfasserangaben: | Quanchao Zhang, Tilman SauterGND, Liang Fang, Karl KratzORCiD, Andreas LendleinORCiDGND |
---|---|
DOI: | https://doi.org/10.1002/mame.201400267 |
ISSN: | 1438-7492 |
ISSN: | 1439-2054 |
Titel des übergeordneten Werks (Englisch): | Macromolecular materials and engineering |
Verlag: | Wiley-VCH |
Verlagsort: | Weinheim |
Publikationstyp: | Wissenschaftlicher Artikel |
Sprache: | Englisch |
Jahr der Erstveröffentlichung: | 2015 |
Erscheinungsjahr: | 2015 |
Datum der Freischaltung: | 27.03.2017 |
Freies Schlagwort / Tag: | biomaterials; microparticles; processing; shape-memory effect; stimuli-sensitive polymers |
Band: | 300 |
Ausgabe: | 5 |
Seitenanzahl: | 9 |
Erste Seite: | 522 |
Letzte Seite: | 530 |
Fördernde Institution: | China Scholarship Council (CSC) [201206240020] |
Organisationseinheiten: | Mathematisch-Naturwissenschaftliche Fakultät / Institut für Chemie |
Peer Review: | Referiert |