Actuators based on oligo[(epsilon-caprolactone)-co-glycolide] with accelerated hydrolytic degradation
- Polyester-based shape-memory polymer actuators are multifunctional materials providing reversible macroscopic shape shifts as well as hydrolytic degradability. Here, the function-function interdependencies (between shape shifts and degradation behaviour) will determine actuation performance and its life time. In this work, glycolide units were incorporated in poly(epsilon-caprolactone) based actuator materials in order to achieve an accelerated hydrolytic degradation and to explore the function-function relationship. Three different oligo[(epsilon-caprolactone)-co-glycolide] copolymers (OCGs) with similar molecular weights (10.5 +/- 0.5 kg center dot mol(-1)) including a glycolide content of 8, 16, and 26 mol% (ratio 1:1:1 wt%) terminated with methacrylated moieties were crosslinked. The obtained actuators provided a broad melting transition in the range from 27 to 44 degrees C. The hydrolytic degradation of programmed OCG actuators (200% of elongation) resulted in a reduction of sample mass to 51 wt% within 21 days at pH = 7.4 and 40Polyester-based shape-memory polymer actuators are multifunctional materials providing reversible macroscopic shape shifts as well as hydrolytic degradability. Here, the function-function interdependencies (between shape shifts and degradation behaviour) will determine actuation performance and its life time. In this work, glycolide units were incorporated in poly(epsilon-caprolactone) based actuator materials in order to achieve an accelerated hydrolytic degradation and to explore the function-function relationship. Three different oligo[(epsilon-caprolactone)-co-glycolide] copolymers (OCGs) with similar molecular weights (10.5 +/- 0.5 kg center dot mol(-1)) including a glycolide content of 8, 16, and 26 mol% (ratio 1:1:1 wt%) terminated with methacrylated moieties were crosslinked. The obtained actuators provided a broad melting transition in the range from 27 to 44 degrees C. The hydrolytic degradation of programmed OCG actuators (200% of elongation) resulted in a reduction of sample mass to 51 wt% within 21 days at pH = 7.4 and 40 degrees C. Degradation results in a decrease of T-m associated to the actuating units and increasing T-m associated to the skeleton forming units. The actuation capability decreased almost linear as function of time. After 11 days of hydrolytic degradation the shape-memory functionality was lost. Accordingly, a fast degradation behaviour as required, e.g., for actuator materials intended as implant material can be realized.…
Author details: | Maria BalkGND, Marc BehlORCiDGND, Andreas LendleinORCiDGND |
---|---|
DOI: | https://doi.org/10.1557/adv.2019.447 |
ISSN: | 2059-8521 |
Title of parent work (English): | MRS advances : a journal of the Materials Research Society (MRS) |
Publisher: | Cambridge University Press |
Place of publishing: | New York, NY |
Publication type: | Article |
Language: | English |
Date of first publication: | 2020/09/17 |
Publication year: | 2020 |
Release date: | 2023/06/09 |
Tag: | actuation; crystalline; polymer; shape memory |
Volume: | 5 |
Issue: | 12-13 |
Number of pages: | 12 |
First page: | 655 |
Last Page: | 666 |
Funding institution: | Helmholtz AssociationHelmholtz Association; European Union European; Commission [824074] |
Organizational units: | Mathematisch-Naturwissenschaftliche Fakultät / Institut für Chemie |
DDC classification: | 5 Naturwissenschaften und Mathematik / 54 Chemie / 540 Chemie und zugeordnete Wissenschaften |
Peer review: | Referiert |