Transparent conductive materials based on indium oxide remain yet irreplaceable in various optoelectronic applications. Amorphous oxides appear especially attractive for technology as they are isotropic, demonstrate relatively high electron mobility and can be processed at low temperatures. Among them is indium zinc oxide (IZO) with a large zinc content that is crucial for keeping the amorphous state but redundant for the doping. In this work we investigated water-free and water containing IZO films obtained by radio frequency sputtering. The correlation between temperature driven changes of the chemical state, the optical and electrical properties as well as the progression of crystallization was in focus. Such characterization methods as: scanning electron microscopy, X-ray diffraction, X-ray photoelectron spectroscopy, Raman spectroscopy, temperature dependent Hall-effect measurements and others were applied. Temperature dependent electrical properties of amorphous IZO and IZO:H2O films were found to evolve similarly. Based on our experience in In2O3:H2O (In2O3:H or IOH) we proposed an explanation for the changes observed. Water admixture was found to decrease crystallization temperature of IZO significantly from similar to 550 degrees C to similar to 280 degrees C. Herewith, the presence and concentration of water and/or hydroxyls was found to determine Zn distribution in the film. In particular, Zn enrichment was detected at the film's surface respective to the high water and/or hydroxyl amount. Raman spectra revealed a two-dimensional crystallization of w-ZnO which precedes regardless water presence an extensive In2O3 crystallization. An abrupt loss of electron mobility as a result of crystallization was attributed to the formation of ZnO interlayer on grain boundaries.
The class of 2,5 disubstituted-1,3,4-oxadiazoles containing a biphenyl unit on one side is intensively used as electron transport materials to enhance the performance of organic light emitting diodes (OLEDs). In contrast to the ongoing research on these materials insights in their structure-property relationships are still incomplete. To overcome the structural tentativeness and ambiguities the crystal structures of 2-(4-biphenylyl)-5-(4-tert-butylphenyl)-1,3,4-oxadiazole, that of the related compound 2-(4-biphenylyl)-5-phenyl-1,3,4-oxadiazole and of 2-(4-biphenylyl)-5-(2,6-dimethylphenyl)-1,3,4-oxadiazole are determined. A comparison with the results of GAUSSIAN03 calculations and similar compounds in the Cambridge Structural Database leads to a profound characterization.