Atomic force microscopy inspection of the early state of formation of polymer surface relief grating
(2001)
We report on light-induced deformation of colloidal spheres consisting of azobenzene-containing polymers. The colloids of the size between 60 nm and 2 mu m in diameter were drop casted on a glass surface and irradiated with linearly polarized light. It was found that colloidal particles can be deformed up to ca. 6 times of their initial diameter. The maximum degree of deformation depends on the irradiation wavelength and intensity, as well as on colloidal particles size. On the basis of recently proposed theory by Toshchevikov et al. [J. Phys. Chem. Lett. 2017, 8, 1094], we calculated the optomechanical stresses (ca. 100 MPa) needed for such giant deformations and compared them with the experimental results.
In this work, it is revealed how the photoinduced deformation of azobenzene containing polymers relates to the local direction of optomechanical stresses generated during irradiation with interference patterns (IPs). It can be substantiated by the modeling approach proposed by Saphiannikova et al., which describes the directional photodeformations in glassy side-chain azobenzene polymers, and proves that these deformations arise from the reorientation of rigid backbone segments along the light polarization direction. In experiments and modeling, surface relief gratings in pre-elongated photosensitive colloids of few micrometers length are inscribed using different IPs such as SS, PP, +/- 45, SP, RL, and LR. The deformation of colloidal particles is studied in situ, whereby the local variation of polymer topography is assigned to the local distribution of the electrical field vector for all IPs. Experimentally observed shapes are reproduced exactly with modeling azopolymer samples as visco-plastic bodies in the finite element software ANSYS. Orientation approach correctly predicts local variations of the main axis of light-induced stress in each interference pattern for both initially isotropic and highly oriented materials. With this work, it is suggested that the orientation approach implements a self-sufficient and convincing mechanism to describe photoinduced deformation in azopolymer films that in principle does not require auxiliary assumptions.
Photo-induced deformations in azobenzene-containing side-chain polymers : molecular dynamics study
(2006)
We perform molecular dynamics simulations of azobenzene containing side-chain liquid crystalline polymer subject to an external model field that mimicks the reorientations of the azobenzenes upon irradiation with polarized light. The smectic phase of the polymer is studied with the field applied parallel to the nematic director, forcing the trans isomers to reorient perpendicularly to the field (the direction of which can be assosiated with the light polarization). The coupling between the reorientation of azobenzenes and mechanical deformation of the sample is found to depend on the field strength. In a weak field the original smectic order is melted gradually with no apparent change in the simulation box shape, whereas in a strong field two regimes are observed. During the first one a rapid melting of the liquid crystalline order is accompanied by the contraction of the polymer along the field direction (the effect similar to the one observed experimentally in azopenzene containing elastomers). During the slower second regime, the smectic layers are rebuilt to accomodate the preferential direction of chromophores perperdicular to the field.
Thin azobenzene polymer films show a very unusual property, namely optically induced material transport. The underlying physics for this phenomenon has not yet been thoroughly explained. Nevertheless, this effect enables one to inscribe different patterns onto film surfaces, including one- and two-dimensional periodic structures. Typical sizes of such structures are of the order of micrometers, i.e. related to the interference pattern made by the laser used for optical excitation. In this study we have measured the mechanical properties of one- and two-dimensional gratings, with a high lateral resolution, using force-distance curves and pulse force mode of the atomic force microscope. We also report on the generation of considerably finer structures, with a typical size of 100 nm, which were inscribed onto the polymer surface by the tip of a scanning near-field optical microscope used as an optical pen. Such inscription not only opens new application possibilities but also gives deeper insight into the fundamentals physics underlying optically induced material transport
Thermodynamic theory of light-induced material transport in amorphous azobenzene polymer films
(2005)
It was discovered 10 years ago that the exposure of an initially flat layer of an azobenzene-containing polymer to an inhomogeneous light pattern leads to the formation of surface relief structures, accompanied by a mass transport over several micrometers. However, the driving force of this process is still unclear. We propose a new thermodynamic approach that explains a number of experimental findings including the light-induced deformation of free-standing films and the formation of surface relief gratings for main inscription geometries. Our basic assumption is that under homogeneous illumination, an initially isotropic sample should stretch itself along the polarization direction to compensate the entropy decrease produced by the photoinduced reorientation of azobenzene chromophores. The magnitude of the elastic stress, estimated by taking the derivative of the free energy over the sample deformation, is shown to be sufficient to induce plastic deformation of the polymer film. Orientational distributions of chromophores predicted by our model are compared with those deduced from Raman intensity measurements
Surface relief gratings on azobenzene containing polymer films were prepared under irradiation by actinic light. Finite element modeling of the inscription process was carried out using linear viscoelastic analysis. It was assumed that under illumination the polymer film undergoes considerable plastification, which reduces its original Young's modulus by at least three orders of magnitude. Force densities of about 10(11) N/m(3) were necessary to reproduce the growth of the surface relief grating. It was shown that at large deformations the force of surface tension becomes comparable to the inscription force and therefore plays an essential role in the retardation of the inscription process. In addition to surface profiling the gradual development of an accompanying density grating was predicted for the regime of continuous exposure. Surface grating development under pulselike exposure cannot be explained in the frame of an incompressible fluid model. However, it was easily reproduced using the viscoelastic model with finite compressibility. (C) 2004 American Institute of Physics
Photoinduced changes in the mechanical and dielectric properties of azobenzene polymer films were measured utilizing the method of electromechanical spectroscopy. The measurements revealed a strong correlation between the time- dependent behavior of the plate compliance and the dielectric constant under irradiation. Actinic light causes a light softening of the film that also manifests itself in the increase of the dielectric constant, whereas ultraviolet irradiation results in an initial plasticization of the film followed by its hardening. The latter is accompanied by decrease of the dielectric constant. A semiquantitative model based on the kinetics of the photoisomerization process in azobenzene polymers is proposed. We assume that both visible and ultraviolet irradiation increase the free volume in the layer due to photoisomerization. Additionally, ultraviolet light increases the modulus of the polymer matrix due to the presence of a high density of azobenzene moieties in the cis state. These assumptions allowed us to reproduce the time- dependent behavior of the bulk compliance as well as the dielectric constant at different irradiation intensities, for both visible and ultraviolet light, with only two adjustable parameters