Refine
Has Fulltext
- no (26)
Year of publication
Document Type
- Article (26) (remove)
Is part of the Bibliography
- yes (26)
Keywords
- Ferroelectret (1)
- Ferroelectrets (1)
- Paschen's law (1)
- Polymer (1)
- Thermal diffusivity (1)
- Thermal wave method (1)
- Thermoplastics (1)
- dielectric barrier discharge (DBD) (1)
- dielectric barrier discharges (1)
- effective polarization (1)
Institute
A package of programs written using the symbolic mathematics program, Mathematicatrademark, has been developed. Its principal usage is in teaching the LIMM method to students and demonstrating data analysis by means of the Polynomial Regularization Method (PRM). A large number of variables can be changed in the program and their effects can be shown graphically. Students at the University of Potsdam and Monash University have used the program successfully
Space-charge depth profiles in various electret polymers have been measured in both the time and the frequency domain using thermal pulses and waves, respectively. A comparison of the two techniques on corona-charged polytetrafluoroethylene showed that the thermal-pulse method yielded similar results as the thermal-wave technique, but approximately 20-50 times faster. The article discusses sensitivity limitations as well as possible applications, including the real-time monitoring of space-charge decay under UV irradiation. (C) 2005 American Institute of Physics
The thermal-wave technique or laser-intensity modulation method is an important tool for the non-destructive probing of space-charge and polarization profiles in electrets. Analysing the experimental data requires solving a Fredholm integral equation which is known to be an ill-conditioned problem. This paper presents an iterative approach that is capable of reconstructing inherently unsmooth distributions. The deviations from the true profiles are slightly smaller than those obtained with Tikhonov regularization, while the computational burden is not a limiting factor on modem personal computers. The optimum number of iterations is estimated using the randomized generalized cross- validation technique. Results are shown for a number of model distributions, as well as for experimental data from a layered polyvinylidene fluoride film sandwich
The stability of space charge in electrets such as polytetrafluoroethylene (PTFE), polyethylene terephthalate (PETP) and polypropylene (PP) under ultraviolet irradiation has been investigated using photostimulated discharge spectroscopy. While only weak discharge currents were observed in PTFE coated with semitransparent gold electrodes, up to 15 pA/cm(2) were found in PETP around the UV absorption edge near 310 nm. Space charge profiles obtained with the piezoelectrically generated pressure step method indicate that near-surface charges were almost completely removed. In PP foam, recent findings of a UV-reduced d(33) coefficient were confirmed for exposure times of up to 3.5 h, and a discharge peak at 200 urn could be assigned to the charges stored on the surfaces of the voids. The unique morphology and the (quasi-) piezoelectric properties of cellular PP make it a role model for the future investigation of charge storage in electrets
Polymer-dispersed liquid crystals (PDLCs) are prepared from poly(vinylidene fluoride-trifluoroethylene) (P(VDF- TrFE)) and a nematic liquid-crystal (LC). The anchoring effect was studied using dielectric relaxation spectroscopy. Two dispersion regions are observed in the dielectric spectra of the pure P(VDF-TrFE) film. They are related to the glass transition and to a space-charge relaxation. In PDLC films containing 10 wt% of LC, an additional, bias field-dependent relaxation peak is found that can be attributed to the motion of LC molecules. Due to the hindered movement of the LC molecules, this relaxation process is considerably slowed down, compared with the related process in the pure LC.
Charged cellular polypropylene foams (i.e., ferro-or piezoelectrets) demonstrate high piezoelectric activity upon being electrically charged. When an external electric field is applied, dielectric barrier discharges (DBDs) occur, resulting in a separation of charges which are subsequently deposited on dielectric surfaces of internal micrometer sized voids. This deposited space charge is responsible for the piezoelectric activity of the material. Previous studies have indicated charging fields larger than predicted by Townsend's model of Paschen breakdown applied to a multilayered electromechanical model; a discrepancy which prompted the present study. The actual breakdown fields for micrometer sized voids were determined by constructing single cell voids using polypropylene spacers with heights ranging from 8 to 75 mu m, "sandwiched" between two polypropylene dielectric barriers and glass slides with semi-transparent electrodes. Subsequently, a bipolar triangular charging waveform with a peak voltage of 6 kV was applied to the samples. The breakdown fields were determined by monitoring the emission of light due to the onset of DBDs using an electron multiplying CCD camera. The breakdown fields at absolute pressures from 101 to 251 kPa were found to be in good agreement with the standard Paschen curves. Additionally, the magnitude of the light emission was found to scale linearly with the amount of gas, i.e., the height of the voids. Emissions were homogeneous over the observed regions of the voids for voids with heights of 25 lm or less and increasingly inhomogeneous for void heights greater than 40 lm at high electric fields.
Polymer foams and void-containing polymer-film systems with internally charged voids combine large piezoelectricity with mechanical flexibility and elastic compliance. This new class of soft materials (often called ferro-or piezoelectrets) has attracted considerable attention from science and industry. It has been found that the voids can be internally charged by means of dielectric barrier discharges (DBDs) under high electric fields. The charged voids can be considered as man-made macroscopic dipoles. Depending on the ferroelectret structure and the pressure of the internal gas, the voids may be highly compressible. Consequently, very large dipole-moment changes can be induced by mechanical or electrical stresses, leading to large piezoelectricity. DBD charging of the voids is a critical process for rendering polymer foams piezoelectric. Thus a comprehensive exploration of DBD charging is essential for the understanding and the optimization of piezoelectricity in ferroelectrets. Recent studies show that DBDs in the voids are triggered when the internal electric field reaches a threshold value according to Townsend's model of Paschen breakdown. During the DBDs, charges of opposite polarity are generated and trapped at the top and bottom internal surfaces of the gas-filled voids, respectively. The deposited charges induce an electric field opposite to the externally applied one and thus extinguish the DBDs. Back discharges may eventually be triggered when the external voltage is reduced or turned off. In order to optimize the efficiency of DBD charging, the geometry (in particular the height) of the voids, the type of gas and its pressure inside the voids are essential factors to be considered and to be optimized. In addition, the influence of the plasma treatment on the internal void surfaces during the DBDs should be taken into consideration.
Breakdown threshold of dielectric barrier discharges in ferroelectrets where Paschen's law fails
(2011)
The piezoelectric activity of charged cellular foams (so-called ferroelectrets) is compared against simulations based on a multi-layer electromechanical model and Townsend's model of Paschen breakdown, with the distribution of void heights determined from scanning electron micrographs. While the calculated space charge hysteresis curves are in good agreement with experimental data, the onset of piezoelectric activity is observed at significantly higher electric fields than predicted by Paschen's law. One likely explanation is that the commonly accepted Paschen curve for electric breakdown in air poorly describes the critical electric field for dielectric barrier discharges in micrometer-size cavities.
Measurement of through-thickness thermal diffusivity of thermoplastics using thermal wave method
(2015)
Thermo-physical properties, such as thermal conductivity, thermal diffusivity and specific heat are important quantities that are needed to interpret and characterize thermoplastic materials. Such characterization is necessary for many applications, ranging from aerospace engineering to food packaging, electrical and electronic industry and medical science. In this work, the thermal diffusivity of commercially available polymeric films is measured in the thickness direction at room temperature using thermal wave method. The results obtained with this method are in good agreement with theoretical and experimental values.