The surface of carbon black (CB) nanoparticles was functionalized with poly(vinylidene fluoride) (PVDF) either by trapping of macroradicals or by cycloaddition. PVDF with two iodine end groups (I-PVDF-I) obtained from iodine transfer polymerization in supercritical CO2 was heated in the presence of CB and the C-I bond was cleaved resulting in a reaction between the macroradical and the CB surface. To allow for cycloaddition of PVDF to the CB surface for a number of polymers, the iodine end groups were replaced by azide end groups. In addition, microwave irradiation was applied to the functionalization. The influence of temperature, time, polymer concentration, and polymer molar mass on the functionalization reaction was examined.
The surface of single-walled carbon nanotubes (SWCNTs) was functionalized with azide-terminated poly(vinylidene fluoride) (PVDF). Functionalization was confirmed by dispersibility, Raman spectroscopy, and thermogravimetric analyses. Raman spectra show disordering of the SWCNTs, thus, strongly suggesting that PVDF was covalently attached to SWCNTs. Functionalized SWCNTs were mixed with commercially available PVDF in a twin-screw extruder and thin films were obtained by melt-pressing. Films containing 0.5 and 1 wt% PVDF-functionalized SWCNTs exhibited significantly improved electrical conductivity compared to PVDF films containing pristine SWCNTs.
Fullerenes decorated with poly(vinylidene fluoride) (PVDF) were synthesized in a three-step procedure: Iodine transfer polymerization of vinylidene fluoride with C(6)F(12)I(2) as the chain transfer agent was carried out in supercritical carbon dioxide to synthesize iodine-terminated PVDF, which was subsequently transformed to azide-terminated polymer. Finally, azide-terminated PVDF chains were attached to a fullerene core under microwave irradiation at 160 degrees C in 1.5 h. The materials were characterized by NMR, FT-IR, UV/vis, GPC, elemental analysis, and DSC. On average, 4-5 PVDF chains are attached to one C(60) moiety. FT-IR spectra and DSC measurements indicate that the polymer end groups strongly affect the crystallinity of the material. For PVDF with azide end groups and PVDF attached to fullerenes the fraction of the beta polymorph is dominant while alpha polymorphs are almost absent.
The synthesis of block copolymers consisting of poly(vinylidene fluoride) (PVDF) and polystyrene (PS) is reported. Firstly, a propargyl-functionalized alkoxyamine initiator (PgOTIPNO) was prepared and subsequently used for the preparation of a propargyl-terminated PS homopolymer of different chain lengths with low dispersities via nitroxide-mediated radical polymerization. A tailored PVDF homopolymer with iodine end groups originating from iodine transfer polymerization was transformed to PVDF with azide end group. Then, alkyne-terminated PS with different molecular weights and azide-terminated PVDF were joined together via copper-catalyzed alkyne-azide coupling. The block copolymers were characterized using H-1-NMR, F-19-NMR, IR, SEC, and DSC.