Lanthanide-doped upconverting nanoparticles (UCNP) are being extensively studied for bioapplications due to their unique photoluminescence properties and low toxicity. Interest in RET applications involving UCNP is also increasing, but due to factors such as large sizes, ion emission distributions within the particles, and complicated energy transfer processes within the UCNP, there are still many questions to be answered. In this study, four types of core and core-shell NaYF4-based UCNP co-doped with Yb3+ and Tm3+ as sensitizer and activator, respectively, were investigated as donors for the Methyl 5-(8-decanoylbenzo[1,2-d:4,5-d ']bis([1,3]dioxole)-4-yl)-5-oxopentanoate (DBD-6) dye. The possibility of resonance energy transfer (RET) between UCNP and the DBD-6 attached to their surface was demonstrated based on the comparison of luminescence intensities, band ratios, and decay kinetics. The architecture of UCNP influenced both the luminescence properties and the energy transfer to the dye: UCNP with an inert shell were the brightest, but their RET efficiency was the lowest (17%). Nanoparticles with Tm3+ only in the shell have revealed the highest RET efficiencies (up to 51%) despite the compromised luminescence due to surface quenching.
Lanthanide-doped upconverting nanoparticles (UCNP) are being extensively studied for bioapplications due to their unique photoluminescence properties and low toxicity. Interest in RET applications involving UCNP is also increasing, but due to factors such as large sizes, ion emission distributions within the particles, and complicated energy transfer processes within the UCNP, there are still many questions to be answered. In this study, four types of core and core-shell NaYF4-based UCNP co-doped with Yb3+ and Tm3+ as sensitizer and activator, respectively, were investigated as donors for the Methyl 5-(8-decanoylbenzo[1,2-d:4,5-d ']bis([1,3]dioxole)-4-yl)-5-oxopentanoate (DBD-6) dye. The possibility of resonance energy transfer (RET) between UCNP and the DBD-6 attached to their surface was demonstrated based on the comparison of luminescence intensities, band ratios, and decay kinetics. The architecture of UCNP influenced both the luminescence properties and the energy transfer to the dye: UCNP with an inert shell were the brightest, but their RET efficiency was the lowest (17%). Nanoparticles with Tm3+ only in the shell have revealed the highest RET efficiencies (up to 51%) despite the compromised luminescence due to surface quenching.
Bioinspired confinement of upconversion nanoparticles for improved performance in aqueous solution
(2020)
The resonance energy transfer (RET) from NaYF4:Yb,Er upconverting nanoparticles (UNCPs) to a dye (5-carboxytetramethylrhodamine (TAMRA)) was investigated by photoluminescence experiments and microscale thermophoresis (MST). The dye was excited via RET from the UCNPs which was excited in the near-infrared (NIR). The change of the dye diffusion speed (free vs coupled) was investigated by MST. RET shows significant changes in the decay times of the dye as well as of the UCNPs. MST reveals significant changes in the diffusion speed. A unique amphiphilic coating polymer (customized mussel protein (CMP) polymer) for UCNP surface coating was used, which mimics blood protein adsorption and mussel food protein adhesion to transfer the UCNP into the aqueous phase and to allow surface functionalization. The CMP provides very good water dispersibility to the UCNPs and minimizes ligand exchange and subsequent UCNP aging reactions because of the interlinkage of the CMP on the UCNP surface. Moreover, CMP provides N-3-functional groups for dick chemistry-based functionalization demonstrated with the dye 5-carboxytetramethylrhodamine (TAMRA). This establishes the principle coupling scheme for suitable biomarkers such as antibodies. The CMP provides very stable aqueous UCNP dispersions that are storable up to 3 years in a fridge at 5 degrees C without dissolution or coagulation. The outstanding properties of CMP in shielding the UCNP from unwanted solvent effects is reflected in the distinct increase of the photoluminescence decay times after UCNP functionalization. The UCNP-to-TAMRA energy transfer is also spectroscopically investigated at low temperatures (4-200 K), revealing that one of the two green Er(III) emission bands contributes the major part to the energy transfer. The TAMRA fluorescence decay time increases by a factor of 9500 from 2.28 ns up to 22 mu s due to radiationless energy transfer from the UCNP after NIR excitation of the latter. This underlines the unique properties of CMP as a versatile capping ligand for distinctly improving the UCNPs' performance in aqueous solutions, for coupling of biomolecules, and for applications for in vitro and in vivo experiments using UCNPs as optical probes in life science applications.
Lanthanide resonance energy transfer (LRET) was used to investigate the motion of dopant ions during the synthesis of core-shell-shell-nanocrystals (NCs) that are frequently used as frequency upconversion materials. Reaction conditions (temperature, solvent) as well as lattice composition and precursors were adapted from a typical hydrothermal synthesis approach used to obtain upconversion nanoparticles (UCNPs). Instead of adding the lanthanide ions Yb3+/Er3+ as the sensitizer/activator couple, Eu3+/Nd3+ as the donor/acceptor were added as the LRET pair to the outer shell (Eu-3) and the core (Nd-3). By tailoring the thickness of the insulation shell ("middle shell"), the expected distance between the donor and the acceptor was increased beyond 2 R-0, a distance for which no LRET is expected. The successful synthesis of core- shell-shell NCs with different thicknesses of the insulation layer was demonstrated by high-resolution transmission electron microscopy measurement. The incorporation of the Eu3+ ions into the NaYF4 lattice was investigated by high-resolution time-resolved luminescence measurements. Two major Eu3+ species (bulk and surface) were found. This was supported by steady-state as well as time-resolved luminescence data. Based on the luminescence decay kinetics, the intermixing of lanthanides during synthesis of core- shell UCNPs was evaluated. The energy transfer between Eu3+ (donor) and Nd3+ (acceptor) ions was exploited to quantify the motion of the dopant ions. This investigation reveals the migration of Ln(3+) ions between different compatiments in core-shell NCs and affects the concept of using core-shell architectures to increase the efficiency of UCNPs. In order to obtain well-separated core and shell structures with different dopants, alternative concepts are needed.
Here we report on photo-isomerization of azobenzene containing surfactants induced during irradiation with near-infrared (NIR) light in the presence of upconversion nanoparticles (UCNPs) acting as mediator. The surfactant molecule consists of charged head group and hydrophobic tail with azobenzene group incorporated in alkyl chain. The azobenzene group can be reversible photo-isomerized between two states: trans- and cis- by irradiation with light of an appropriate wavelength. The trans-cis photo-isomerization is induced by UV light, while cis-trans isomerization proceeds either thermally in darkness, or can be accelerated by exposure to illumination with a longer wavelength typically in a blue/green range. We present the application of lanthanide doped UCNPs to successfully switch azobenzene containing surfactants from cis to trans conformation in bulk solution using NIR light. Using Tm-3(+) or Er-3(+) as activator ions, the UCNPs provide emissions in the spectral range of 450 nm < lambda(em) < 480 nm (for Tm-3(+), three and four photon induced emission) or 525 nm < lambda(em) < 545 nm (for Er-3(+), two photon induced emission), respectively. Especially for UCNPs containing Tm-3(+) a good overlap of the emissions with the absorption bands of the azobenzene is present. Under illumination of the surfactant solution with NIR light (lambda(ex) = 976 nm) in the presence of the Tm-3(+)-doped UCNPs, the relaxation time of cis-trans photo-isomerization was increased by almost 13 times compared to thermally induced isomerization. The influence of thermal heating due to the irradiation using NIR light was shown to be minor for solvents not absorbing in NIR spectral range (e.g. CHCl3) in contrast to water, which shows a distinct absorption in the NIR.